CN104151731A - 一种光致变色的注塑材料 - Google Patents
一种光致变色的注塑材料 Download PDFInfo
- Publication number
- CN104151731A CN104151731A CN201410440112.9A CN201410440112A CN104151731A CN 104151731 A CN104151731 A CN 104151731A CN 201410440112 A CN201410440112 A CN 201410440112A CN 104151731 A CN104151731 A CN 104151731A
- Authority
- CN
- China
- Prior art keywords
- photochromic
- plastic material
- temperature
- district
- injectable plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种光致变色的注塑材料,其中,所述光致变色的注塑材料按质量百分比计包括:苯乙烯-丙烯晴共聚物31~38%;聚碳酸酯25~28%;粘土19~25%;增塑剂7~9%;润滑剂2~4%;分散剂6~8%;抗冲击改性剂3~5%;光致变色剂5~7%。本案提供的注塑材料可知作为装饰塑料制品,在光源刺激下,进行特定的光化学反应,得到产物,由于原光致变色剂和产物在结构或电子组态存在改变而导致其吸收光谱发生明显的变化,减弱了装饰塑料制品的发出光照强度,减弱了日光刺眼强度,保护视力,保证安全,并可起到调节装饰塑料制品空间内的温度和美观的作用。
Description
技术领域
本发明涉及一种注塑材料,特别涉及一种光致变色的注塑材料。
背景技术
注塑是一种工业产品生产造型的方法。产品通常使用橡胶注塑和塑料注塑。注塑还可分注塑成型模压法和压铸法。注射成型机(简称注射机或注塑机)是将热塑性塑料或热固性塑料利用塑料成型模具制成各种形状的塑料制品的主要成型设备,注塑成型是通过注塑机和模具来实现的。所得的形状往往就是最后成品,在安装或作为最终成品使用之前不再需要其他的加工。许多细部,诸如凸起部、肋、螺纹,都可以在注射模塑一步操作中成型出来。
人类在现代文明社会中,用颜色把生活装扮的丰富多彩,颜色已成为各种信号标志的基础和用以传递信息的一种手段及信息存储和读出的一种基质。为此人们不仅广泛应用天然有色材料,而且还大量合成各种燃料和颜料。人们还发现自然界有些动植物的颜色可以在光照下发生可逆性的变化,受此启发,创造和合成了用于变色太阳镜、节能玻璃和变色油墨等受到外界光源刺激能发生颜色变化的光致变色材料。将光致变色色素加入透明高分子材料中,制成光变色材料,可以用于太阳眼镜片,国内在变色眼镜方面已开始应用。将光致变色色素与高聚物连接在一起,可以制成具有光变色性能的材料,在光电技术和光控装置中很有应用前景。用光致变色材料的涂料可以制作呈各种日用品、服装、玩具、装饰品、童车或涂布到内外墙上、公路标牌和建筑物等的各种标示、图案,在光照下会呈现出色彩丰富、艳丽的图案或花纹,美化人们的生活及环境;可以做成透明塑料薄膜,贴到或嵌入汽车玻璃或窗玻璃上,日光照射马上变色,使日光不刺眼,保护视力,保证安全,并可起到调节室内和汽车内温度的作用;还可以溶入或混入塑料薄膜中,用作农业大棚农膜,增加农产品、蔬菜、水果等的产量。另一个重要的用途是用作军事上的隐蔽材料,例如军事人员的服装和战斗武器的外罩等。
基于以上所述,如何开发一种光致变色的注塑材料来制作各种生活装饰品,是本领域技术人员亟需解决的重要技术问题。
发明内容
本发明提供了一种光致变色的注塑材料,该注塑材料制作的装饰塑料制品,在光源的照射下,装饰塑料制品内的光致变色剂在受到一定波长的光照射时,可进行特定的光化学反应,获得产物,由于原光致变色剂和产物在结构或电子组态存在改变而导致其吸收光谱发生明显的变化,减弱了装饰塑料制品的发出光照强度,减弱了日光刺眼强度,保护视力,保证安全,并可起到调节装饰塑料制品空间内的温度和美观的作用。
为了实现上述目的,本发明采用了如下技术方案:
一种光致变色的注塑材料,其中,所述光致变色的注塑材料按质量百分比计包括:
优选地是,所述的光致变色的注塑材料,其中,所述增塑剂选用邻苯二甲酸脂类、脂肪族二元酸酯类、磷酸酯类、氯化石蜡中的一种或几种。
优选地是,所述的光致变色的注塑材料,其中,所述润滑剂选用硅油、脂肪酸、酰胺、聚酯、合成酯、羧酸中的一种或几种。
优选地是,所述的光致变色的注塑材料,其中,所述分散剂选用三乙基己基磷酸、十二烷基硫酸钠和甲基戊醇中的一种或两种混合物。
优选地是,所述的光致变色的注塑材料,其中,所述抗冲击改性剂为35~45%的苯乙烯-丁二烯共聚合体和55~65%的聚丁烯的混合物。
优选地是,所述的光致变色的注塑材料,其中,所述光致变色剂选用螺毗喃、螺唔嗓、六苯基双咪哇、水杨醛缩苯胺类化合物、周蔡靛兰类染料、偶氮化合物、稠环芳香化合物、哗嗓类、俘精酸配类、二芳基乙烯类中的一种或几种。
优选地是,所述的光致变色的注塑材料的制备方法,其中,其工艺步骤包括:
步骤一、按照配比称取除光致变色剂之外的原料,在中速混合器中低速混合240s,再高速混合320s,确保物料混合均匀;
步骤二、将所述步骤一混合好的原料与光致变色剂掺混,高速混合540s;
步骤三、将所述步骤二混合好的原料加入双螺杆挤出机内,在200~350℃融化,再经双螺杆挤出机挤压,以高注塑压力注入模具内。
优选地是,所述的光致变色的注塑材料的制备方法,其中,所述双螺杆挤出机工艺条件:双螺杆挤出机一区温度140~260℃,二区温度240~260℃,三区温度240~260℃,四区温度240~260℃,五区温度240~260℃,六区温度240~260℃,七区温度240~260℃,八区温度240~260℃,模头温度260~280℃,混合料在螺杆中输送时间为1~2分钟。
优选地是,所述的光致变色的注塑材料的制备方法,其中,所述高注塑压力为480~520Pa。
本发明提供的一种光致变色的注塑材料,其有益效果包括:该注塑材料制作的装饰塑料制品,在光源的照射下,装饰塑料制品内的光致变色剂在受到一定波长的光照射时,可进行特定的光化学反应,获得产物,由于原光致变色剂和产物在结构或电子组态存在改变而导致其吸收光谱发生明显的变化,减弱了装饰塑料制品的发出光照强度,减弱了日光刺眼强度,保护视力,保证安全,并可起到调节装饰塑料制品空间内的温度和美观的作用。
具体实施方式
下面对本发明做进一步的详细说明,以令本领域技术人员参照说明书文字能够据以实施。
本发明提供了一种光致变色的注塑材料,其中,所述光致变色的注塑材料按质量百分比计包括:
其中,增塑剂选用邻苯二甲酸脂类、脂肪族二元酸酯类、磷酸酯类、氯化石蜡中的一种或几种。润滑剂选用硅油、脂肪酸、酰胺、聚酯、合成酯、羧酸中的一种或几种。分散剂选用三乙基己基磷酸、十二烷基硫酸钠和甲基戊醇中的一种或两种混合物。抗冲击改性剂为35~45%的苯乙烯-丁二烯共聚合体和55~65%的聚丁烯的混合物。光致变色剂选用螺毗喃、螺唔嗓、六苯基双咪哇、水杨醛缩苯胺类化合物、周蔡靛兰类染料、偶氮化合物、稠环芳香化合物、哗嗓类、俘精酸配类、二芳基乙烯类中的一种或几种。
本案提供的一种光致变色注塑材料的制备方法,其工艺步骤包括:
步骤一、按照配比称取除光致变色剂之外的原料,在中速混合器中低速混合240s,再高速混合320s,确保物料混合均匀;
步骤二、将所述步骤一混合好的原料与光致变色剂掺混,高速混合540s;
步骤三、将所述步骤二混合好的原料加入双螺杆挤出机内,在200~350℃融化,再经双螺杆挤出机挤压,以480~520Pa的高注塑压力注入模具内。其中,在本发明中所述双螺杆挤出机工艺条件:双螺杆挤出机一区温度140~260℃,二区温度240~260℃,三区温度240~260℃,四区温度240~260℃,五区温度240~260℃,六区温度240~260℃,七区温度240~260℃,八区温度240~260℃,模头温度260~280℃,混合料在螺杆中输送时间为1~2分钟。
光致变色材料的用途范围很广。人们对光致变色材料性能刚兴趣的原因:一、由于它具有在不同强度与波长光的照射下发生光色变色的光敏性能,在工业上除作一般装饰与装材料用外,还用在防护核爆炸实验等强光辐射对人眼、人身的损害。二、由于受不同强度与波长光照射性能发生可逆循环的变化性能,可制左各种光闸,录像介质、计算机中信息贮存元件,尤其是激光出现后提供了各种必要的光强度,更推进了它在信息数据处理系统中的应用。三、它对不同程度的热也产生敏感变色,可用作温度提示,控制化学聚合反应。
尽管本发明的实施方案已公开如上,但其并不仅仅限于说明书和实施方式中所列运用,它完全可以被适用于各种适合本发明的领域,对于熟悉本领域的人员而言,可容易地实现另外的修改,因此在不背离权利要求及等同范围所限定的一般概念下,本发明并不限于这里示出的特定细节的描述。
Claims (9)
1.一种光致变色的注塑材料,其特征在于,所述光致变色的注塑材料按质量百分比计包括:
2.根据权利要求1所述的光致变色的注塑材料,其特征在于,所述增塑剂选用邻苯二甲酸脂类、脂肪族二元酸酯类、磷酸酯类、氯化石蜡中的一种或几种。
3.根据权利要求2所述的光致变色的注塑材料,其特征在于,所述润滑剂选用硅油、脂肪酸、酰胺、聚酯、合成酯、羧酸中的一种或几种。
4.根据权利要求3所述的具有隐身功能的注塑材料,其特征在于,所述分散剂选用三乙基己基磷酸、十二烷基硫酸钠和甲基戊醇中的一种或两种混合物。
5.根据权利要求4所述的光致变色的注塑材料,其特征在于,所述抗冲击改性剂为35~45%的苯乙烯-丁二烯共聚合体和55~65%的聚丁烯的混合物。
6.根据权利要求5所述的光致变色的注塑材料,其特征在于,所述光致变色剂选用螺毗喃、螺唔嗓、六苯基双咪哇、水杨醛缩苯胺类化合物、周蔡靛兰类染料、偶氮化合物、稠环芳香化合物、哗嗓类、俘精酸配类、二芳基乙烯类中的一种或几种。
7.一种制备权利要求1~6中任一项所述的光致变色的注塑材料的方法,其特征在于,其工艺步骤包括:
步骤一、按照配比称取除光致变色剂之外的原料,在中速混合器中低速混合240s,再高速混合320s,确保物料混合均匀;
步骤二、将所述步骤一混合好的原料与光致变色剂掺混,高速混合540s;
步骤三、将所述步骤二混合好的原料加入双螺杆挤出机内,在200~350℃融化,再经双螺杆挤出机挤压,以高注塑压力注入模具内。
8.根据权利要求7所述的光致变色的注塑材料的制备方法,其特征在于,所述双螺杆挤出机工艺条件:双螺杆挤出机一区温度140~260℃,二区温度240~260℃,三区温度240~260℃,四区温度240~260℃,五区温度240~260℃,六区温度240~260℃,七区温度240~260℃,八区温度240~260℃,模头温度260~280℃,混合料在螺杆中输送时间为1~2分钟。
9.根据权利要求7所述的光致变色的注塑材料的制备方法,其特征在于,所述高注塑压力为480~520Pa。