CN104151631A - 杯盖密封圈用混炼凝胶 - Google Patents
杯盖密封圈用混炼凝胶 Download PDFInfo
- Publication number
- CN104151631A CN104151631A CN201410273671.5A CN201410273671A CN104151631A CN 104151631 A CN104151631 A CN 104151631A CN 201410273671 A CN201410273671 A CN 201410273671A CN 104151631 A CN104151631 A CN 104151631A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixing
- gel
- bowl cover
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
杯盖密封圈用混炼凝胶，涉及日常用品生产技术领域，其特征在于：由以下重量份数的组分组成，天然橡胶80-120份、硫磺7-15份、石蜡4-9份、聚氯乙烯10-18份、硫酸钡1-5份、滑石粉2-8份、沉淀法白炭黑25-65份、抗氧化剂1-6份、邻苯二甲酸二丁酯3-8份、甲基丙烯酸锌7-14份。本发明组分简单，制备工艺简单，便于操作，制备的产品质量高，而且加入了抗氧化剂、邻苯二甲酸二丁酯、聚氯乙烯等材料，提高了产品的耐磨性能和耐高温性能，这养就使得产品的使用寿命更加的长。
Description
技术领域：
本发明涉及日常用品生产技术领域，具体涉及一种杯盖密封圈用混炼凝胶。
背景技术：
茶杯是盛茶水的用具，水从茶壶而来，倒进茶杯，之后给客人品尝茶水。茶杯分大小两种：小杯主要用于乌龙茶的品啜，亦叫品茗杯，是与闻香杯配合使用的；大杯也可直接作泡茶和盛茶用具，主要用于高级细嫩名茶的品饮。
而许多的杯子都是有杯盖的，这样设有杯盖携带的时候比较方便，并且许多旋钮式的杯盖上都设有密封圈，这样一是起到了一定的保温效果，然后也起到了杯盖与杯体良好的连接、密封的效果，杯子里的水不容易渗漏出来。而普通的密封圈由于自身材料的问题无法长久的使用，非常的容易磨损，往往时间过长就导致密封不紧密、漏水、断裂等情况发生。
发明内容：
本发明所要解决的技术问题在于克服现有的技术缺陷提供一种方法合理、密封效果好、耐高温、耐磨的一种杯盖密封圈用混炼凝胶。
本发明所要解决的技术问题采用以下的技术方案来实现：
杯盖密封圈用混炼凝胶，其特征在于：由以下重量份数的组分组成，
各组分的较佳重量份数为：
本发明还提供一种杯盖密封圈用混炼凝胶的制备方法，包括以下步骤，
步骤一、将天然橡胶、石蜡、邻苯二甲酸二丁酯、硫磺在密炼机上混炼5-9分钟，再加入聚氯乙烯、滑石粉继续混炼9-15分钟，再加入硫酸钡混炼15分钟；
步骤二、将上述混炼好的材料放置在加热器中，依次再加入沉淀法白炭黑、滑石粉、抗氧化剂在95-125℃下混热35-50分钟后，配成胶料即可。
本发明的有益效果为：本发明组分简单，制备工艺简单，便于操作，制备的产品质量高，而且加入了抗氧化剂、邻苯二甲酸二丁酯、聚氯乙烯等材料，提高了产品的耐磨性能和耐高温性能，这养就使得产品的使用寿命更加的长。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面进一步阐述本发明。
实施例1
杯盖密封圈用混炼凝胶，其特征在于：由以下重量份数的组分组成，
本发明还提供一种杯盖密封圈用混炼凝胶的制备方法，包括以下步骤，
步骤一、将天然橡胶、石蜡、邻苯二甲酸二丁酯、硫磺在密炼机上混炼5-9分钟，再加入聚氯乙烯、滑石粉继续混炼9-15分钟，再加入硫酸钡混炼15分钟；
步骤二、将上述混炼好的材料放置在加热器中，依次再加入沉淀法白炭黑、滑石粉、抗氧化剂在95-125℃下混热35-50分钟后，配成胶料即可。
实施例2
杯盖密封圈用混炼凝胶，其特征在于：由以下重量份数的组分组成，
本发明还提供一种杯盖密封圈用混炼凝胶的制备方法，包括以下步骤，
步骤一、将天然橡胶、石蜡、邻苯二甲酸二丁酯、硫磺在密炼机上混炼5-9分钟，再加入聚氯乙烯、滑石粉继续混炼9-15分钟，再加入硫酸钡混炼15分钟；
步骤二、将上述混炼好的材料放置在加热器中，依次再加入沉淀法白炭黑、滑石粉、抗氧化剂在95-125℃下混热35-50分钟后，配成胶料即可。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.杯盖密封圈用混炼凝胶，其特征在于：由以下重量份数的组分组成，
2.根据权利要求1所述的杯盖密封圈用混炼凝胶，其特征在于：由以下重量份数的组分组成，
3.一种制备权利要求1或权利要求2所述的杯盖密封圈用混炼凝胶，其特征在于：包括以下步骤，
步骤一、将天然橡胶、石蜡、邻苯二甲酸二丁酯、硫磺在密炼机上混炼5-9分钟，再加入聚氯乙烯、滑石粉继续混炼9-15分钟，再加入硫酸钡混炼15分钟；
步骤二、将上述混炼好的材料放置在加热器中，依次再加入沉淀法白炭黑、滑石粉、抗氧化剂在95-125℃下混热35-50分钟后，配成胶料即可。