CN104131670A - 一种保温防火隔离噪音的建筑装饰板材及其制备方法 - Google Patents
一种保温防火隔离噪音的建筑装饰板材及其制备方法 Download PDFInfo
- Publication number
- CN104131670A CN104131670A CN201410396105.3A CN201410396105A CN104131670A CN 104131670 A CN104131670 A CN 104131670A CN 201410396105 A CN201410396105 A CN 201410396105A CN 104131670 A CN104131670 A CN 104131670A
- Authority
- CN
- China
- Prior art keywords
- parts
- sheet material
- heat
- noise
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种装饰板材及其制作方法,具体涉及一种保温防火隔离噪音的建筑装饰板材及其制备方法。该保温防火隔离噪音的建筑装饰板材及其制备方法,其原料组成按质量配比为:界面剂10份,玻化微珠保温砂浆25份,防水剂8份,羧甲基纤维素胶黏剂10份,水合硅酸镁超细粉5份,乳胶漆15份,硅藻泥15份,颜料6份,余下是水。
Description
技术领域
本发明涉及一种装饰板材及其制作方法,具体涉及一种保温防火隔离噪音的建筑装饰板材及其制备方法。
背景技术
装饰材料分为两大部分:一部分为室外材料,一部分为室内材料,而室内材料分为实材,板材、片材、型材、线材五个类型,而装饰板材的做法基本上是通过在墙面整体铺上基层板材,外面贴上装饰面板,虽然整体效果雍容华贵,但会使房间显得拥挤。
发明内容
本发明为了弥补现有技术的缺陷,提供了一种环保无毒、无异味、保温性能稳定、光泽好、吸附力强、降低变形、整体性良好,且防止脱落的保温防火隔离噪音的建筑装饰板材及其制备方法。
本发明是通过如下技术方案实现的:
一种保温防火隔离噪音的建筑装饰板材及其制备方法,其原料组成按质量配比为:界面剂10-20份,玻化微珠保温砂浆10-30份,防水剂5-10份,羧甲基纤维素胶黏剂8-15份,水合硅酸镁超细粉5-10份,乳胶漆15-20份,硅藻泥12-15份,颜料6-8份,余下是水。
将上述各组成份制成本发明保温防火隔离噪音的建筑装饰板材的制备方法是:
第一步,将玻化微珠保温砂浆和防水剂加水搅拌均匀,灌注在模槽内,并将其中一侧压制出深3至5毫米、宽2至3厘米的吸附槽,吸附槽等距分布在玻化微珠保温砂浆的表层,吸附槽间距为5-8厘米,并至干燥通风处待其充分凝固。
第二步,将羧甲基纤维素胶黏剂、水合硅酸镁超细粉、乳胶漆、硅藻泥、颜料和水混合搅拌均匀,并均匀的喷涂在凝固后的玻化微珠保温砂浆平整的一层,共喷涂4层,每层厚度在2至3毫米,每层需晾干后再喷涂下一层。
第三步,将压制有吸附槽一侧的玻化微珠保温砂浆的表层均匀涂抹界面剂。
第四步,晾干完成。
本发明的有益效果是:本发明具有环保无毒、无异味,可直接用于墙体装饰使用,良好的施工性,易于掌控板材的厚度,避免室内面积显的拥挤,容量轻,导热系数低,保温性能稳定,整体性良好,良好的耐冻融性和耐水性能,难燃等级高,同时板材表面润滑性高、光泽好、吸附力强,避免硅藻泥脱落,具有消除甲醛、净化空气、杀菌除臭的功能。
具体实施方式
以下给出本发明的具体实施例,用来对本发明的构成进行进一步说明。
实施例1
本发明的保温防火隔离噪音的建筑装饰板材及其制备方法,其原料组成按质量配比为:界面剂10份,玻化微珠保温砂浆10份,防水剂5份,羧甲基纤维素胶黏剂8份,水合硅酸镁超细粉5份,乳胶漆15份,硅藻泥12份,颜料6份,余下是水。
本发明的制备方法如下:
第一步,将玻化微珠保温砂浆和防水剂加水搅拌均匀,灌注在模槽内,并将其中一侧压制出深3毫米、宽2厘米的吸附槽,吸附槽等距分布在玻化微珠保温砂浆的表层,吸附槽间距为5厘米,并至干燥通风处待其充分凝固。
第二步,将羧甲基纤维素胶黏剂、水合硅酸镁超细粉、乳胶漆、硅藻泥、颜料和水混合搅拌均匀,并均匀的喷涂在凝固后的玻化微珠保温砂浆平整的一层,共喷涂4层,每层厚度在2毫米,每层需晾干后再喷涂下一层。
第三步,将压制有吸附槽一侧的玻化微珠保温砂浆的表层均匀涂抹界面剂。
第四步,晾干完成。
实施例2
本发明的保温防火隔离噪音的建筑装饰板材及其制备方法,其原料组成按质量配比为:界面剂15份,玻化微珠保温砂浆20份,防水剂8份,羧甲基纤维素胶黏剂10份,水合硅酸镁超细粉8份,乳胶漆18份,硅藻泥13份,颜料7份,余下是水。
本发明的制备方法如下:
第一步,将玻化微珠保温砂浆和防水剂加水搅拌均匀,灌注在模槽内,并将其中一侧压制出深4毫米、宽3厘米的吸附槽,吸附槽等距分布在玻化微珠保温砂浆的表层,吸附槽间距为6厘米,并至干燥通风处待其充分凝固。
第二步,将羧甲基纤维素胶黏剂、水合硅酸镁超细粉、乳胶漆、硅藻泥、颜料和水混合搅拌均匀,并均匀的喷涂在凝固后的玻化微珠保温砂浆平整的一层,共喷涂4层,每层厚度在2毫米,每层需晾干后再喷涂下一层。
第三步,将压制有吸附槽一侧的玻化微珠保温砂浆的表层均匀涂抹界面剂。
第四步,晾干完成。
实施例3
本发明的保温防火隔离噪音的建筑装饰板材及其制备方法,其原料组成按质量配比为:界面剂20份,玻化微珠保温砂浆30份,防水剂10份,羧甲基纤维素胶黏剂15份,水合硅酸镁超细粉10份,乳胶漆20份,硅藻泥15份,颜料8份,余下是水。
本发明的制备方法如下:
第一步,将玻化微珠保温砂浆和防水剂加水搅拌均匀,灌注在模槽内,并将其中一侧压制出深5毫米、宽3厘米的吸附槽,吸附槽等距分布在玻化微珠保温砂浆的表层,吸附槽间距为8厘米,并至干燥通风处待其充分凝固。
第二步,将羧甲基纤维素胶黏剂、水合硅酸镁超细粉、乳胶漆、硅藻泥、颜料和水混合搅拌均匀,并均匀的喷涂在凝固后的玻化微珠保温砂浆平整的一层,共喷涂4层,每层厚度在2毫米,每层需晾干后再喷涂下一层。
第三步,将压制有吸附槽一侧的玻化微珠保温砂浆的表层均匀涂抹界面剂。
第四步,晾干完成。
本发明不局限于上述实施方式,任何人应得知在本发明的启示下作出的与本发明具有相同或相近的技术方案,均落入本发明的保护范围之内。
本发明未详细描述的技术、形状、构造部分均为公知技术。
Claims (2)
1.一种保温防火隔离噪音的建筑装饰板材及其制备方法,其特征在于,其原料组成按质量配比为:界面剂10-20份,玻化微珠保温砂浆10-30份,防水剂5-10份,羧甲基纤维素胶黏剂8-15份,水合硅酸镁超细粉5-10份,乳胶漆15-20份,硅藻泥12-15份,颜料6-8份,余下是水;
将上述各组成份制成本发明的制备方法是:
第一步,将玻化微珠保温砂浆和防水剂加水搅拌均匀,灌注在模槽内,并将其中一侧压制出深3至5毫米、宽2至3厘米的吸附槽,吸附槽等距分布在玻化微珠保温砂浆的表层,吸附槽间距为5-8厘米,并至干燥通风处待其充分凝固;
第二步,将羧甲基纤维素胶黏剂、水合硅酸镁超细粉、乳胶漆、硅藻泥、颜料和水混合搅拌均匀,并均匀的喷涂在凝固后的玻化微珠保温砂浆平整的一层,共喷涂4层,每层厚度在2至3毫米,每层需晾干后再喷涂下一层;
第三步,将压制有吸附槽一侧的玻化微珠保温砂浆的表层均匀涂抹界面剂;
第四步,晾干完成。
2.根据权利要求1所述的一种保温防火隔离噪音的建筑装饰板材及其制备方法,其特征在于:其原料组成按质量配比为:界面剂10份,玻化微珠保温砂浆25份,防水剂8份,羧甲基纤维素胶黏剂10份,水合硅酸镁超细粉5份,乳胶漆15份,硅藻泥15份,颜料6份,余下是水。