CN104119826A - 一种环保型笔记本粘结用热熔胶 - Google Patents

一种环保型笔记本粘结用热熔胶 Download PDF

Info

Publication number
CN104119826A
CN104119826A CN201410291648.9A CN201410291648A CN104119826A CN 104119826 A CN104119826 A CN 104119826A CN 201410291648 A CN201410291648 A CN 201410291648A CN 104119826 A CN104119826 A CN 104119826A
Authority
CN
China
Prior art keywords
resin
parts
minute
melt adhesive
environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410291648.9A
Other languages
English (en)
Other versions
CN104119826B (zh
Inventor
赵强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI TUQIANG STATIONERY MANUFACTURING Co Ltd
Original Assignee
ANHUI TUQIANG STATIONERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TUQIANG STATIONERY MANUFACTURING Co Ltd filed Critical ANHUI TUQIANG STATIONERY MANUFACTURING Co Ltd
Priority to CN201410291648.9A priority Critical patent/CN104119826B/zh
Publication of CN104119826A publication Critical patent/CN104119826A/zh
Application granted granted Critical
Publication of CN104119826B publication Critical patent/CN104119826B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保型笔记本粘结用热熔胶，其是由下述重量份的原料制得：硬酯酸钠1-2、烟片胶2-3、酚醛树脂34-46、C5石油树脂15-18、有机硅树脂1-2、硅藻土1-2、二氯异氰尿酸钠1-2、硬酯酸钠1-2、硅酸钠2-3、磷酸酐1-2,增粘树脂5-7、抗氧剂1680.3-0.5、环氧大豆油1-2；本发明提供的环保型热熔胶柔软、黏性高,抗氧化性好,干后不掉渣，且环保无毒。

Description

一种环保型笔记本粘结用热熔胶
技术领域
本发明属粘结剂领域，尤其涉及一种环保型笔记本粘结用热熔胶。
背景技术
热熔胶粘合是利用热熔胶机通过热力把热熔胶熔解， 熔胶后的胶成为一种液体，通过热熔胶机的热熔胶管和热熔胶枪，送到被粘合物表面，热熔胶冷却后即完成了粘合。
在我们日常生活中，有时会遇到这种情况：笔记本翻着翻着纸张就掉了。使用好的热熔胶是胶订纸张产品的质量保证。
发明内容
本发明的目的是提供一种环保型笔记本粘结用热熔胶。
为了实现上述目的本发明采用如下技术方案：
一种环保型笔记本粘结用热熔胶，其特征在于，其是由下述重量份的原料制得：硬酯酸钠1-2、 烟片胶2-3、酚醛树脂34-46、C5石油树脂15-18、有机硅树脂1-2、硅藻土1-2、二氯异氰尿酸钠1-2、硬酯酸钠1-2、硅酸钠2-3、磷酸酐1-2,增粘树脂5-7、抗氧剂168 0.3-0.5、环氧大豆油1-2；
所述的增粘树脂由下述重量份的原料制得：
纳米碳0.1-0.3、粘土4-6、瓷粉4-6、烟片胶1-2、凡士林2-4、氧化聚乙烯蜡1-2、抗氧剂1010 1-2、硅烷偶联剂kh530 1-2、松香8-14、双丙酮丙烯酰胺0.3-0.4、丙烯酸树脂5-8、聚乳酸0.2-0.4、硅酸钠0.1-0.2、癸二酸二辛酯1-2、环氧大豆油1-2；
增粘树脂制备方法为：
将松香、粘土、双丙酮丙烯酰胺、纳米碳混匀后，于140-150℃搅拌10-15min，加入粘土、瓷粉，球磨3-5分钟，再加入硅烷偶联剂kh530、烟片胶、凡士林，于130-150℃下搅拌10-20min，再加入其余原料，700-800转/分搅拌15-20min，球磨4-6min，即得。
所述的一种环保型笔记本粘结用热熔胶，其特征在于：制备方法包括以下步骤：
（1）将酚醛树脂、C5石油树脂、硅藻土、磷酸酐、环氧大豆油混匀后，200-300转/分搅拌6-8分钟，再放入捏合机中，于150-155℃捏合20-30分钟，得捏合树脂备用；
（2）将有机硅树脂、增粘树脂、硅酸钠 、烟片胶混匀后，加水适量水，于32-38℃搅拌10-20分钟后，烘干，球磨5-7分钟，得改性树脂粉，备用；
（3）将捏合树脂、改性树脂粉、以及其原料混匀后，于160-165℃捏合20-30分钟，即得。
本发明的有益效果：
本发明提供的环保型热熔胶柔软、黏性高,抗氧化性好,干后不掉渣，且环保无毒。
具体实施方式
一种环保型笔记本粘结用热熔胶，其是由下述重量(kg)的原料制得：硬酯酸钠1、 烟片胶3、酚醛树脂46、C5石油树脂15、有机硅树脂2、硅藻土2、二氯异氰尿酸钠1、硬酯酸钠2、硅酸钠3、磷酸酐1,增粘树脂7、抗氧剂168 0.5、环氧大豆油2；
所述的增粘树脂由下述重量(kg)的原料制得：
纳米碳0.1、粘土6、瓷粉6、烟片胶2、凡士林4、氧化聚乙烯蜡2、抗氧剂1010 1、硅烷偶联剂kh530  1、松香12、双丙酮丙烯酰胺0.4、丙烯酸树脂8、聚乳酸0.4、硅酸钠0.2、癸二酸二辛酯2、环氧大豆油1；
增粘树脂制备方法为：
将松香、粘土、双丙酮丙烯酰胺、纳米碳混匀后，于150℃搅拌15min，加入粘土、瓷粉，球磨5分钟，再加入硅烷偶联剂kh530、烟片胶、凡士林，于140℃下搅拌20min，再加入其余原料，800转/分搅拌18min，球磨5min，即得。
所述的一种环保型笔记本粘结用热熔胶，制备方法包括以下步骤：
（1）将酚醛树脂、C5石油树脂、硅藻土、磷酸酐、环氧大豆油混匀后，300转/分搅拌8分钟，再放入捏合机中，于150℃捏合30分钟，得捏合树脂备用；
（2）将有机硅树脂、增粘树脂、硅酸钠 、烟片胶混匀后，加水适量水，于35℃搅拌15分钟后，烘干，球磨7分钟，得改性树脂粉，备用；
（3）将捏合树脂、改性树脂粉、以及其原料混匀后，于165℃捏合25分钟，即得。
本发明的热熔胶主要技术指标检测如下：
 本实施例的热熔胶的软化点85±5℃，剥离强度64N/2.5cm，初粘力达到5号钢球，开放时间35s，24小时热稳定性状稳定。

Claims (2)

1.一种环保型笔记本粘结用热熔胶，其特征在于，其是由下述重量份的原料制得：硬酯酸钠1-2、 烟片胶2-3、酚醛树脂34-46、C5石油树脂15-18、有机硅树脂1-2、硅藻土1-2、二氯异氰尿酸钠1-2、硬酯酸钠1-2、硅酸钠2-3、磷酸酐1-2,增粘树脂5-7、抗氧剂168 0.3-0.5、环氧大豆油1-2；
所述的增粘树脂由下述重量份的原料制得：
纳米碳0.1-0.3、粘土4-6、瓷粉4-6、烟片胶1-2、凡士林2-4、氧化聚乙烯蜡1-2、抗氧剂1010 1-2、硅烷偶联剂kh530 1-2、松香8-14、双丙酮丙烯酰胺0.3-0.4、丙烯酸树脂5-8、聚乳酸0.2-0.4、硅酸钠0.1-0.2、癸二酸二辛酯1-2、环氧大豆油1-2；
增粘树脂制备方法为：
将松香、粘土、双丙酮丙烯酰胺、纳米碳混匀后，于140-150℃搅拌10-15min，加入粘土、瓷粉，球磨3-5分钟，再加入硅烷偶联剂kh530、烟片胶、凡士林，于130-150℃下搅拌10-20min，再加入其余原料，700-800转/分搅拌15-20min，球磨4-6min，即得。
2.根据权利要求1所述的一种环保型笔记本粘结用热熔胶，其特征在于：制备方法包括以下步骤：
（1）将酚醛树脂、C5石油树脂、硅藻土、磷酸酐、环氧大豆油混匀后，200-300转/分搅拌6-8分钟，再放入捏合机中，于150-155℃捏合20-30分钟，得捏合树脂备用；
（2）将有机硅树脂、增粘树脂、硅酸钠 、烟片胶混匀后，加水适量水，于32-38℃搅拌10-20分钟后，烘干，球磨5-7分钟，得改性树脂粉，备用；
（3）将捏合树脂、改性树脂粉、以及其原料混匀后，于160-165℃捏合20-30分钟，即得。
CN201410291648.9A 2014-06-26 2014-06-26 一种环保型笔记本粘结用热熔胶 Expired - Fee Related CN104119826B (zh)