CN104109341A - 一种松香基高硬度abs塑胶 - Google Patents
一种松香基高硬度abs塑胶 Download PDFInfo
- Publication number
- CN104109341A CN104109341A CN201410344342.5A CN201410344342A CN104109341A CN 104109341 A CN104109341 A CN 104109341A CN 201410344342 A CN201410344342 A CN 201410344342A CN 104109341 A CN104109341 A CN 104109341A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixed
- add
- minute
- rosin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种松香基高硬度ABS塑胶,它是由下述重量份的原料组成的:ABS树脂91-100、松香脂2-3、六氟乙酰丙酮1-2、硫酸锰0.2-0.3、铝矾土2-3、乙氧基化烷基酚硫酸铵0.2-0.4、聚甲基丙烯酸正丁酯2-3、二异丙基乙醇胺1-2、甘露醇2-3、苯丙三氮唑1-2、丙三醇三甘油酸酯2-4、膨胀珍珠岩粉8-10、磷酸二氢铵1-2、改性助剂3-4,本发明的塑胶表面硬度高,抗磨性、抗弯折性好,制品不容易被刮伤,特别应用于制造各种机械仪器设备的零部件,及电器、仪表的外壳。
Description
技术领域
本发明主要涉及材料领域,尤其涉及一种松香基高硬度ABS塑胶。
背景技术
ABS树脂外观微黄不透明,相对密度1.04。它具有良好尺寸稳定性,突出的耐冲击性、耐热性、介电性、耐磨性,表面光泽性好,易涂装和着色等优点。丙烯腈使ABS具有较好的化学稳定性和表面硬度,丁二烯使ABS具有橡胶体的韧性和松香基高硬度性能,苯乙烯使ABS具有良好的加工流动性、着色性和可电镀性;BS 是目前应用最广泛的工程塑料之一,因其具有较强的松香基高硬度强度、比重低、尺寸稳定性好、耐酸碱性能强、易加工等优点,在机械、家用电器、日常用具等行业应用广泛,尤其在电视机、冰箱、洗衣机外壳领域取得了快速的发展。
发明内容
本发明目的就是提供一种松香基高硬度ABS塑胶。
本发明是通过以下技术方案实现的:
一种松香基高硬度ABS塑胶,其特征在于它是由下述重量份的原料组成的:
ABS 树脂91-100、松香脂2-3、六氟乙酰丙酮1-2、硫酸锰0.2-0.3、铝矾土2-3、乙氧基化烷基酚硫酸铵0.2-0.4、聚甲基丙烯酸正丁酯2-3、二异丙基乙醇胺1-2、甘露醇2-3、苯丙三氮唑1-2、丙三醇三甘油酸酯2-4、膨胀珍珠岩粉8-10、磷酸二氢铵1-2、改性助剂3-4;
所述的改性助剂是由下述重量份的原料组成的:
松香10-20、活性白土20-30、溴代十六烷基吡啶1-2、偏钒酸铵1-2、吡咯烷酮羟酸钠1-2、琥珀酸二甲酯2-3、磷酸二氢钠1-2、碳酸锆钾0.2-0.4、抗氧剂1010 0.1-0.2、去离子水6-10;
将松香加热熔化,加入琥珀酸二甲酯,搅拌混合均匀,得凝胶;
将溴代十六烷基吡啶、吡咯烷酮羟酸钠混合加入到去离子水中,搅拌均匀,得分散液;
将活性白土与上述凝胶混合,加入碳酸锆钾,在75-80℃下搅拌混合3-5分钟,降低温度为40-50℃,加入偏钒酸铵,搅拌至常温,加入上述分散液,200-300转/分搅拌10-20分钟,烘干磨粉,与剩余各原料混合,搅拌均匀,即得所述改性助剂。
一种松香基高硬度ABS塑胶的制备方法,其特征在于包括以下步骤:
将松香脂与铝矾土、硫酸锰混合,在72-80℃下搅拌混合10-20分钟,加入苯丙三氮唑、聚甲基丙烯酸正丁酯,300-400转/分搅拌混合6-10分钟;
将乙氧基化烷基酚硫酸铵与甘露醇混合,搅拌均匀后加入膨胀珍珠岩粉,100-200转/分搅拌分散4-7分钟;
将上述处理的各原料与剩余各原料混合,送入高速混合器中干混3-5 分钟,再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装,即得所述松香基高硬度ABS塑胶。
本发明的优点是:
本发明的塑胶表面硬度高,抗磨性、抗弯折性好,制品不容易被刮伤,特别应用于制造各种机械仪器设备的零部件,及电器、仪表的外壳。
具体实施方式
实施例1
一种松香基高硬度ABS塑胶,它是由下述重量份(公斤)的原料组成的:
ABS 树脂100、松香脂3、六氟乙酰丙酮2、硫酸锰0.3、铝矾土3、乙氧基化烷基酚硫酸铵0.4、聚甲基丙烯酸正丁酯3、二异丙基乙醇胺2、甘露醇2、苯丙三氮唑2、丙三醇三甘油酸酯4、膨胀珍珠岩粉8-10、磷酸二氢铵1、改性助剂3;
所述的改性助剂是由下述重量份的原料组成的:
松香20、活性白土30、溴代十六烷基吡啶1、偏钒酸铵1、吡咯烷酮羟酸钠1、琥珀酸二甲酯3、磷酸二氢钠1、碳酸锆钾0.4、抗氧剂1010 0.2、去离子水10;
将松香加热熔化,加入琥珀酸二甲酯,搅拌混合均匀,得凝胶;
将溴代十六烷基吡啶、吡咯烷酮羟酸钠混合加入到去离子水中,搅拌均匀,得分散液;
将活性白土与上述凝胶混合,加入碳酸锆钾,在80℃下搅拌混合5分钟,降低温度为50℃,加入偏钒酸铵,搅拌至常温,加入上述分散液,300转/分搅拌20分钟,烘干磨粉,与剩余各原料混合,搅拌均匀,即得所述改性助剂。
一种松香基高硬度ABS塑胶的制备方法,包括以下步骤:
将松香脂与铝矾土、硫酸锰混合,在80℃下搅拌混合20分钟,加入苯丙三氮唑、聚甲基丙烯酸正丁酯,400转/分搅拌混合10分钟;
将乙氧基化烷基酚硫酸铵与甘露醇混合,搅拌均匀后加入膨胀珍珠岩粉,200转/分搅拌分散4分钟;
将上述处理的各原料与剩余各原料混合,送入高速混合器中干混3分钟,再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装,即得所述松香基高硬度ABS塑胶。
性能测试:
拉伸强度MPa:50;
阻燃等级:V0;
弯曲强度MPa:48。
Claims (2)
1.一种松香基高硬度ABS塑胶,其特征在于它是由下述重量份的原料组成的:
ABS 树脂91-100、松香脂2-3、六氟乙酰丙酮1-2、硫酸锰0.2-0.3、铝矾土2-3、乙氧基化烷基酚硫酸铵0.2-0.4、聚甲基丙烯酸正丁酯2-3、二异丙基乙醇胺1-2、甘露醇2-3、苯丙三氮唑1-2、丙三醇三甘油酸酯2-4、膨胀珍珠岩粉8-10、磷酸二氢铵1-2、改性助剂3-4;
所述的改性助剂是由下述重量份的原料组成的:
松香10-20、活性白土20-30、溴代十六烷基吡啶1-2、偏钒酸铵1-2、吡咯烷酮羟酸钠1-2、琥珀酸二甲酯2-3、磷酸二氢钠1-2、碳酸锆钾0.2-0.4、抗氧剂1010 0.1-0.2、去离子水6-10;
将松香加热熔化,加入琥珀酸二甲酯,搅拌混合均匀,得凝胶;
将溴代十六烷基吡啶、吡咯烷酮羟酸钠混合加入到去离子水中,搅拌均匀,得分散液;
将活性白土与上述凝胶混合,加入碳酸锆钾,在75-80℃下搅拌混合3-5分钟,降低温度为40-50℃,加入偏钒酸铵,搅拌至常温,加入上述分散液,200-300转/分搅拌10-20分钟,烘干磨粉,与剩余各原料混合,搅拌均匀,即得所述改性助剂。
2.一种如权利要求1所述的松香基高硬度ABS塑胶的制备方法,其特征在于包括以下步骤:
将松香脂与铝矾土、硫酸锰混合,在72-80℃下搅拌混合10-20分钟,加入苯丙三氮唑、聚甲基丙烯酸正丁酯,300-400转/分搅拌混合6-10分钟;
将乙氧基化烷基酚硫酸铵与甘露醇混合,搅拌均匀后加入膨胀珍珠岩粉,100-200转/分搅拌分散4-7分钟;
将上述处理的各原料与剩余各原料混合,送入高速混合器中干混3-5 分钟,再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装,即得所述松香基高硬度ABS塑胶。