CN104109304A - 一种高流动聚氯乙烯电缆料及其制备方法 - Google Patents

一种高流动聚氯乙烯电缆料及其制备方法 Download PDF

Info

Publication number
CN104109304A
CN104109304A CN201410284179.8A CN201410284179A CN104109304A CN 104109304 A CN104109304 A CN 104109304A CN 201410284179 A CN201410284179 A CN 201410284179A CN 104109304 A CN104109304 A CN 104109304A
Authority
CN
China
Prior art keywords
resin
polyvinyl chloride
add
flows
fluidity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410284179.8A
Other languages
English (en)
Other versions
CN104109304B (zh
Inventor
谷道荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Rongpeng Intelligent Equipment Co., Ltd
Original Assignee
ANHUI RONGJIU OPTICAL FIBER COMMUNICATION Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI RONGJIU OPTICAL FIBER COMMUNICATION Co Ltd filed Critical ANHUI RONGJIU OPTICAL FIBER COMMUNICATION Co Ltd
Priority to CN201410284179.8A priority Critical patent/CN104109304B/zh
Publication of CN104109304A publication Critical patent/CN104109304A/zh
Application granted granted Critical
Publication of CN104109304B publication Critical patent/CN104109304B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高流动聚氯乙烯电缆料及其制备方法，由下列重量份的原料制成：SG-3型PVC树脂60-80、高流动SAN树脂20-30、高流动PBT树脂10-15、邻苯二甲酸二辛酯20-30、对苯二甲酸二辛酯10-15、碳酸钙12-16、癸二酸二正丁酯10-15、矿物油5-10、硅质页岩15-20、蛭石粉10-15、复合填料5-10、十溴二苯醚8-12、磷酸二氢铵4-7、硬脂酸锌2-3、硬脂酸钙1-2、氧化聚乙烯蜡2-3、加工助剂ACR4011-2；本发明电缆料在保证力学性能的前提下，具有良好的流动性能和挤出成型加工性能。

Description

一种高流动聚氯乙烯电缆料及其制备方法
技术领域
本发明涉及一种聚氯乙烯电缆料及其制备方法，具体涉及一种高流动聚氯乙烯电缆料及其制备方法。
背景技术
聚氯乙烯(PVC)由于具有难燃、耐油、耐电晕、耐化学腐蚀和良好的耐水性能和加工性能，因此广泛应用于电线电缆的护层材料。护套挤出成型时，要求PVC电缆料的的流动性高、塑化速度快；但是现有的PVC电缆料在挤出机上挤出时，容易产生焦料，表面粗糙，不能满足产品质量和要求，限制了其发展和应用。
发明内容
本发明的目的在于针对现有技术存在的PVC电缆料流动性差问题不足，提供一种高流动聚氯乙烯电缆料及其制备方法。
本发明采用的技术方案如下：
一种高流动聚氯乙烯电缆料，由下列重量份的原料制成：SG-3型PVC树脂60-80、高流动SAN树脂(PN-107)20-30、高流动PBT树脂(V2000DM)10-15、邻苯二甲酸二辛酯20-30、对苯二甲酸二辛酯10-15、碳酸钙12-16、癸二酸二正丁酯10-15、矿物油5-10、硅质页岩15-20、蛭石粉10-15、复合填料5-10、十溴二苯醚8-12、磷酸二氢铵4-7、硬脂酸锌2-3、硬脂酸钙1-2、氧化聚乙烯蜡2-3、加工助剂ACR4011-2；
所述复合填料的制备方法如下：a.取下列重量份的原料：膨润土5-10、煤矸石4-8、玻璃微珠3-6、玉石粉2-5、液体古马隆树脂8-12、季戊四醇硬脂酸酯1-2、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷2-3、纳米氮化硼3-5、磁粉2-3、抗氧剂10100.5-1.5；b、将膨润土、煤矸石在500-550℃下煅烧3-6h，破碎后加入适量水打浆制成浓度为40-50％的浆液，加10-15％盐酸溶液调节PH为4.5-5.5，高速研磨10-15min，再加8-12％氢氧化钠溶液调节至中性，然后加入玉石粉和磁粉高速研磨5-10min，喷雾干燥成粉末与玻璃微珠、纳米氮化硼和N-2-(氨乙基)-3-氨丙基三甲氧基硅烷，高速混合10-15min，烘干，粉碎，过400-500目筛，c、将过筛后的粉末与其余原料混合均匀即可。
高流动聚氯乙烯电缆料的制备方法，包括以下步骤：
(1)将高速捏合机加热至80-90℃，依次加入SG-3型聚氯乙烯树脂、高流动SAN树脂、高流动PBT树脂、邻苯二甲酸二辛酯、碳酸钙、复合填料、癸二酸二正丁酯，混炼4-6min，再加入对苯二甲酸二辛酯、硅质页岩、蛭石粉、矿物油、十溴二苯醚、磷酸二氢铵，混炼3-4min，最后加入其余原料混炼2-3min，降温至50℃以下出料；
(2)将上述捏合料投入双螺杆挤出机进行挤出造粒，颗粒料长度控制在2-3mm，双螺杆挤出机温度依次为：140-150℃、145-155℃、150-160℃、155-165℃，螺杆转速为20-30r/min，最后经风冷、筛选磁选、计量、包装，即得所需的电缆料。
本发明的有益效果：
本发明通过PVC树脂与高流动SAN树脂、高流动PBT树脂、邻苯二甲酸二辛酯、苯二甲酸二辛酯等配合使用，在保证电缆料力学性能的前提下，大大提高了电缆料的流动性，本发明还添加了复合填料、加工助剂ACR401等，具有增强、增韧效果添，缩短树脂的塑化时间，降低熔体粘度，提高加工性能和热稳定性能，改善制品表面性能。本发明电缆料具有良好的流动性能和挤出成型加工性能。
具体实施方式
一种高流动聚氯乙烯电缆料，由下列重量(kg)的原料制成：SG-3型PVC树脂70、高流动SAN树脂(PN-107)20、高流动PBT树脂(V2000DM)10、邻苯二甲酸二辛酯25、对苯二甲酸二辛酯12、碳酸钙15、癸二酸二正丁酯10、矿物油8、硅质页岩16、蛭石粉12、复合填料8、十溴二苯醚10、磷酸二氢铵5、硬脂酸锌2、硬脂酸钙1.5、氧化聚乙烯蜡2、加工助剂ACR4011.5；
所述复合填料的制备方法如下：a.取下列重量(kg)的原料：膨润土8、煤矸石6、玻璃微珠4、玉石粉3、液体古马隆树脂10、季戊四醇硬脂酸酯1.5、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷2、纳米氮化硼4、磁粉2、抗氧剂10100.8；b、将膨润土、煤矸石在530℃下煅烧4h，破碎后加入适量水打浆制成浓度为45％的浆液，加15％盐酸溶液调节PH为4.5，高速研磨10min，再加10％氢氧化钠溶液调节至中性，然后加入玉石粉和磁粉高速研磨8min，喷雾干燥成粉末与玻璃微珠、纳米氮化硼和N-2-(氨乙基)-3-氨丙基三甲氧基硅烷，高速混合10min，烘干，粉碎，过400目筛，c、将过筛后的粉末与其余原料混合均匀即可。
高流动聚氯乙烯电缆料的制备方法，包括以下步骤：
(1)将高速捏合机加热至80℃，依次加入SG-3型聚氯乙烯树脂、高流动SAN树脂、高流动PBT树脂、邻苯二甲酸二辛酯、碳酸钙、复合填料、癸二酸二正丁酯，混炼5min，再加入对苯二甲酸二辛酯、硅质页岩、蛭石粉、矿物油、十溴二苯醚、磷酸二氢铵，混炼4min，最后加入其余原料混炼2min，降温至50℃以下出料；
(2)将上述捏合料投入双螺杆挤出机进行挤出造粒，颗粒料长度为3mm，双螺杆挤出机温度依次为：145℃、150℃、155℃、160℃，螺杆转速为25r/min，最后经风冷、筛选磁选、计量、包装，即得所需的电缆料。
制得的电缆料的性能测试结果如下：

Claims (2)

1.一种高流动聚氯乙烯电缆料，其特征在于，由下列重量份的原料制成：SG-3型PVC树脂60-80、高流动SAN树脂（PN-107）20-30、高流动PBT树脂（V2000DM）10-15、邻苯二甲酸二辛酯20-30、对苯二甲酸二辛酯10-15、碳酸钙12-16、癸二酸二正丁酯10-15、矿物油5-10、硅质页岩15-20、蛭石粉10-15、复合填料5-10、十溴二苯醚8-12、磷酸二氢铵4-7、硬脂酸锌2-3、硬脂酸钙1-2、氧化聚乙烯蜡 2-3、加工助剂ACR401 1-2；
所述复合填料的制备方法如下：a.取下列重量份的原料：膨润土5-10、煤矸石4-8、玻璃微珠3-6、玉石粉2-5、液体古马隆树脂8-12、季戊四醇硬脂酸酯 1-2、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷2-3、纳米氮化硼3-5、磁粉2-3、抗氧剂1010 0.5-1.5；b、将膨润土、煤矸石在500-550℃下煅烧3-6h，破碎后加入适量水打浆制成浓度为40-50%的浆液，加10-15%盐酸溶液调节PH为4.5-5.5，高速研磨10-15min，再加8-12%氢氧化钠溶液调节至中性，然后加入玉石粉和磁粉高速研磨5-10min，喷雾干燥成粉末与玻璃微珠、纳米氮化硼和N-2-（氨乙基）-3-氨丙基三甲氧基硅烷，高速混合10-15min，烘干，粉碎，过400-500目筛，c、将过筛后的粉末与其余原料混合均匀即可。
2.如权利要求1所述的高流动聚氯乙烯电缆料的制备方法，其特征在于包括以下步骤：
（1）将高速捏合机加热至80-90℃，依次加入SG-3型聚氯乙烯树脂、高流动SAN树脂、高流动PBT树脂、邻苯二甲酸二辛酯、碳酸钙、复合填料、癸二酸二正丁酯，混炼4-6min，再加入对苯二甲酸二辛酯、硅质页岩、蛭石粉、矿物油、十溴二苯醚、磷酸二氢铵，混炼3-4min，最后加入其余原料混炼2-3min，降温至50℃以下出料；
（2）将上述捏合料投入双螺杆挤出机进行挤出造粒，颗粒料长度控制在2-3mm，双螺杆挤出机温度依次为：140-150℃、145-155℃、150-160℃、155-165℃，螺杆转速为20-30r/min，最后经风冷、筛选磁选、计量、包装，即得所需的电缆料。
CN201410284179.8A 2014-06-23 2014-06-23 一种高流动聚氯乙烯电缆料及其制备方法 Active CN104109304B (zh)