CN103289222A - 高流动性pvc护套料 - Google Patents

高流动性pvc护套料 Download PDF

Info

Publication number
CN103289222A
CN103289222A CN2012100516232A CN201210051623A CN103289222A CN 103289222 A CN103289222 A CN 103289222A CN 2012100516232 A CN2012100516232 A CN 2012100516232A CN 201210051623 A CN201210051623 A CN 201210051623A CN 103289222 A CN103289222 A CN 103289222A
Authority
CN
China
Prior art keywords
parts
pvc
high workability
sheath material
pvc sheath
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100516232A
Other languages
English (en)
Inventor
田维生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Far East Cable Co Ltd
New Far East Cable Co Ltd
Far East Composite Technology Co Ltd
Original Assignee
Far East Cable Co Ltd
New Far East Cable Co Ltd
Far East Composite Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Far East Cable Co Ltd, New Far East Cable Co Ltd, Far East Composite Technology Co Ltd filed Critical Far East Cable Co Ltd
Priority to CN2012100516232A priority Critical patent/CN103289222A/zh
Publication of CN103289222A publication Critical patent/CN103289222A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高流动性PVC护套料，其组成及配比为：PVC树脂100份；钙锌复合稳定剂5～10份；增塑剂45～55份；填充剂30～60份；润滑剂1.5～3份；加工助剂1.5～2.5份；颜料3.5～4.5份。本发明采用钙锌复合稳定剂来保证环保性能、采用功能型改质剂CA-08与ACR 401共用来提高加工流动性能、采用低成本的环氧大豆油和对苯二甲酸二辛酯共增塑来降低配方成本。该PVC护套料的环保性能满足ROHS标准要求、常规性能满足标准《电线电缆用软聚氯乙烯塑料》GB/T 8815-2008中H I-90型的指标要求。

Description

高流动性PVC护套料
技术领域
本发明涉及一种电缆用的护套级软PVC塑料，特别涉及高流动性PVC护套料。
背景技术
在电线电缆的绝缘和护套材料中，PVC比较便宜，机械性能优良，加工方便，使得它长久以来成为电线电缆行业使用数量最多的材料。20世纪末以来，PVC材料的环境问题被广泛认识，一些发达国家已提出了限制或全面禁止使用PVC电缆的法令建议。有数据表明，西欧国家在线缆领域PVC的用量，1994年为441kt，占线缆所用树脂的58％，而2000年，PVC在西欧线缆业总的用量是398kt，占线缆所用树脂的48％，总量和所占比例均呈下降趋势。近年来，控制和禁止使用PVC材料已形成了强有力的趋势。
虽然用无卤料取代PVC材料的呼声越来越高，但是PVC本身具有短期内还无法取代的优势(如价格低廉，阻燃性好，加工设备、工艺简单，硬度可调范围广，电绝缘性好，耐油、耐化学试剂等)，所以短期内在世界范围完全禁止PVC的使用并不现实。
在我国，PVC电缆料发展较早，品种、型号较多。近期，由于国内环保要求的提高，我国PVC电缆料的发展也逐渐呈下降趋势。但由于PVC电缆料价格低廉，加之机械性能优异等多种优势，使得我国PVC电缆料近期仍有一定的发展前途。目前，虽然国外还不会马上淘汰PVC电线电缆，但这不能不引起国内电线电缆行业的高度重视，国内应该注重研究非含铅的PVC或者开发新型不含卤素的环保型电线电缆。尽管环保型电线电缆在国内大规模代替PVC电缆还要相当长的时间，但这是大势所趋。国内一些高档项目已经对此提出了要求。
发明内容
本发明的目的在于克服已有技术的不足，提供一种能满足ROHS标准的环保要求及《电线电缆用软聚氯乙烯塑料》标准GB/T 8815-2008中H I-90型的性能要求的90℃高流动性PVC护套料。
实现本发明目的技术方案为：一种高流动性PVC护套料，所述护套料的组成及配比质量份计为：
PVC树脂                 100份；
钙锌复合稳定剂          5～10份；
增塑剂                  45～55份；
填充剂                  30～60份；
润滑剂                  1.5～3份；
加工助剂                1.5～2.5份。
上述高流动性PVC护套料，其组成及配比以质量份计为：
PVC树脂                 100份；
钙锌复合稳定剂          5份；
增塑剂                  45份；
填充剂                  34份；
润滑剂                  1.5份；
加工助剂                1.8份。
上述高流动性PVC护套料，其组成及配比以质量份计为：
PVC树脂                 100份；
钙锌复合稳定剂          7.5份；
增塑剂                  48份；
填充剂                  38份；
润滑剂                  1.7份；
加工助剂                2.0份。
上述高流动性PVC护套料，其组成及配比以质量份计为：
PVC树脂                 100份；
钙锌复合稳定剂          10份；
增塑剂                  53份；
填充剂                  56份；
润滑剂                  2.4份；
加工助剂                2.2份。
上述的高流动性PVC护套料，所述PVC树脂为悬浮法通用型PVC树脂。
上述的高流动性PVC护套料，所述增塑剂为对苯二甲酸二辛酯和环氧大豆油的混合物，在配方总组分中，对苯二甲酸二辛酯为15～30质量份，环氧大豆油为20～35质量份。
上述的高流动性PVC护套料，所述填充剂为碳酸钙。
上述的高流动性PVC护套料，所述润滑剂为硬脂酸钡，硬脂酸和石蜡的混合物，在配方总组分中，硬脂酸钡为0.2～1.0质量份，硬脂酸为0.2～1.0质量份，石蜡为0.2～1.0质量份。
上述的高流动性PVC护套料所述加工助剂为丙烯酸酯共聚物和改质剂CA-08的混合物，在配方总组分中，丙烯酸酯共聚物为1.0～2.0质量份，改质剂CA-08为0.3～1.0质量份。
CA-08是功能型改质剂，是用特殊化学结构的高分子链化合物、超分散剂、高品质的润滑剂(内、外)和纳米材料等为原料，高效、高品质、复合PVC加工助剂。
CA-08含有多官能团特殊结构的高分子化合物，该化合物既含带羟基的长柔性链又接枝了带羧基的聚丙烯酸甲酯；因此该高分子化合物一端以化学键与无机填料相结合，另一端可溶解于界面区树脂中，与树脂大分子链发生缠结形成高聚物网络，形成柔性的有利于应力弛豫的弹性界面层，提高制品吸收和分散冲击能的效果，且有很好的老化性能。
CA-08在PVC等塑料加工中直接添加使用，与铅盐体系、钙锌体系、有机锡体系稳定剂都可并用。在电缆料制品的应用中，除了具有偶联、分散、润滑等特点外，更具有增强、增韧效果(能适量减少加工助剂ACR和抗冲改性剂CPE、MBS等的用量，或适量增加碳酸钙的用量)、添加少量该产品就能缩短树脂的塑化时间、降低熔体粘度、提高加工性能和热稳定性能，改善制品表面性能。
技术特性
采用了上述技术方案后，本发明具有以下的有益效果：(1)本发明采用钙锌复合稳定剂保证了PVC护套料的环保性能；(2)本发明采用功能型改质剂CA-08与丙烯酸酯共聚物共用来提高加工流动性能；(3)本发明采用低成本的环氧大豆油和对苯二甲酸二辛酯共增塑来降低配方成本，采用环氧大豆油为主要增塑剂，取代了传统的以TOTM为主增塑剂的工艺；(4)本发明的PVC护套料的环保性能满足ROHS标准要求；(5)本发明的PVC护套料的常规性能满足标准《电线电缆用软聚氯乙烯塑料》GB/T 8815-2008中HI-90型的指标要求。
具体实施方式
(实施例1)
本实施例的高流动性PVC护套料的组成、配比份数及型号见表一：
表一
本实施例中：
粒料压片的性能：
Figure BDA0000139913240000042
(实施例2)
本实施例的高流动性PVC护套料的组成、配比份数及型号见表二：
表二
Figure BDA0000139913240000052
本实施例中：
粒料压片的性能：
Figure BDA0000139913240000053
(实施例3)
本实施例的高流动性PVC护套料的组成、配比份数及型号见表三：
表三
Figure BDA0000139913240000061
本实施例中：
粒料压片的性能：
以上所述的具体实施例，对本发明的目的、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (9)

1.一种高流动性PVC护套料，其特征在于：其组成及配比以质量份计为：
PVC树脂                100份；
钙锌复合稳定剂         5～10份；
增塑剂                 45～55份；
填充剂                 30～60份；
润滑剂                 1.5～3份；
加工助剂               1.5～2.5份。
2.根据权利要求1所述高流动性PVC护套料，其特征在于：其组成及配比以质量份计为：
PVC树脂                100份；
钙锌复合稳定剂         5份；
增塑剂                 45份；
填充剂                 34份；
润滑剂                 1.5份；
加工助剂               1.8份。
3.根据权利要求1所述高流动性PVC护套料，其特征在于：其组成及配比以质量份计为：
PVC树脂                100份；
钙锌复合稳定剂         7.5份；
增塑剂                 48份；
填充剂                 38份；
润滑剂                 1.7份；
加工助剂               2.0份。
4.根据权利要求1所述高流动性PVC护套料，其特征在于：其组成及配比以质量份计为：
PVC树脂                100份；
钙锌复合稳定剂         10份；
增塑剂                 53份；
填充剂                 56份；
润滑剂                 2.4份；
加工助剂            2.2份。
5.根据权利要求1或2或3或4所述的高流动性PVC护套料，其特征在于：所述PVC树脂为悬浮法通用型PVC树脂。
6.根据权利要求1或2或3或4所述的高流动性PVC护套料，其特征在于：所述增塑剂为对苯二甲酸二辛酯和环氧大豆油的混合物，在配方总组分中，对苯二甲酸二辛酯为15～30质量份，环氧大豆油为20～35质量份。
7.根据权利要求1或2或3或4所述的高流动性PVC护套料，其特征在于：所述填充剂为碳酸钙。
8.根据权利要求1或2或3或4所述的高流动性PVC护套料，其特征在于：所述润滑剂为硬脂酸钡，硬脂酸和石蜡的混合物，在配方总组分中，硬脂酸钡为0.2～1.0质量份，硬脂酸为0.2～1.0质量份，石蜡为0.2～1.0质量份。
9.根据权利要求1或2或3或4所述的高流动性PVC护套料，其特征在于：所述加工助剂为丙烯酸酯共聚物和改质剂CA-08的混合物，在配方总组分中，ACR 401为1.0～2.0质量份，改质剂CA-08为0.3～1.0质量份。
CN2012100516232A 2012-03-01 2012-03-01 高流动性pvc护套料 Pending CN103289222A (zh)