CN104096843A - 一种纳米铁粉的制备方法 - Google Patents

一种纳米铁粉的制备方法 Download PDF

Info

Publication number
CN104096843A
CN104096843A CN201410348613.4A CN201410348613A CN104096843A CN 104096843 A CN104096843 A CN 104096843A CN 201410348613 A CN201410348613 A CN 201410348613A CN 104096843 A CN104096843 A CN 104096843A
Authority
CN
China
Prior art keywords
powder
iron powder
preparation
nano
iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410348613.4A
Other languages
English (en)
Inventor
关锦池
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410348613.4A priority Critical patent/CN104096843A/zh
Publication of CN104096843A publication Critical patent/CN104096843A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种纳米铁粉的制备方法，包括以下步骤：(1)将金属铝粉和无机盐铁粉混合，其中金属铝粉和无机盐铁粉的摩尔比为1-2:1；(2)在10℃—15℃的情况下，将高频切割机切割次数设定在5500-6000RPM/min，将无机盐铁粉和铝粉混合物加工成纳米粉体颗粒，分别筛选出D3＝21nm、D25＝42.1nm、D50＝80nm、D75＝113.2nm、D97＝137.3nm的颗粒分布的纳米颗粒材料，(3)将步骤(2)中分别选出的纳米颗粒，分别用2M氢氧化钠溶液和去离子水洗涤两次，离心分离，真空干燥得到本发明纳米铁粉。本发明提供的纳米铁粉的制备方法制备效率高，工艺简单，能有效分离和纯化不同尺寸的纳米铁粉。

Description

一种纳米铁粉的制备方法
技术领域
本发明涉及一种铁粉的制备方法，尤其涉及一种纳米铁粉的制备方法。
背景技术
纳米铁粉广泛应用于食品、信息、环保、生物、医疗及军事领域。在一些领域，例如医疗及军事领域对纳米铁粉的颗粒尺寸有严格的控制，颗粒尺寸不均匀会直接影响纳米铁粉的性能和应用。制作纳米铁粉的现有现有工艺，要么工艺太复杂，要么达不到纯度和颗粒要求。
发明内容
本发明提供一种纳米铁粉的制备方法，该方法效率高，工艺简单，能有效分离和纯化不同尺寸的纳米铁粉。
一种纳米铁粉的制备方法，该方法包括以下步骤：
(1)将金属铝粉和无机盐铁粉混合，其中金属铝粉和无机盐铁粉的摩尔比为1-2:1；
(2)在10℃—15℃的情况下，将高频切割机切割次数设定在5500-6000RPM/min，将无机盐铁粉和铝粉混合物加工成纳米粉体颗粒，分别筛选出D3＝21nm、D25＝42.1nm、D50＝80nm、D75＝113.2nm、D97＝137.3nm的颗粒分布的纳米颗粒材料，
(3)将步骤(2)中分别选出的纳米颗粒，分别用2M氢氧化钠溶液和去离子水洗涤两次，离心分离，真空干燥得到本发明纳米铁粉。
优选的，无机铁盐为硫酸亚铁、氯化铁、硝酸铁中的一种或多种。
本发明提供的纳米铁粉的制备方法制备效率高，工艺简单，能有效分离和纯化不同尺寸的纳米铁粉。
具体实施方式
以下通过具体实施例对本发明进行详细说明，但所描述内容不应视为对本发明的限制，根据本发明思想作出的任何改变和修饰，应视为属于本发明的保护范围。
实施例1
一种纳米铁粉的制备方法，该方法包括以下步骤：
(1)将金属铝粉和无机盐铁粉混合，其中金属铝粉和无机盐铁粉的摩尔比为1：2；
(2)在10℃的情况下，将高频切割机切割次数设定在5500RPM/min，将无机盐铁粉和铝粉混合物加工成纳米粉体颗粒，分别筛选出D3＝21nm、D25＝42.1nm、D50＝80nm、D75＝113.2nm、D97＝137.3nm的颗粒分布的纳米颗粒材料，
(3)将步骤(2)中分别选出的纳米颗粒，分别用2M氢氧化钠溶液和去离子水洗涤两次，离心分离，真空干燥得到本发明纳米铁粉；
其中，无机铁盐为硫酸亚铁。
实施例2
一种纳米铁粉的制备方法，该方法包括以下步骤：
(1)将金属铝粉和无机盐铁粉混合，其中金属铝粉和无机盐铁粉的摩尔比为1：1；
(2)在15℃的情况下，将高频切割机切割次数设定在6000RPM/min，将无机盐铁粉和铝粉混合物加工成纳米粉体颗粒，分别筛选出D3＝21nm、D25＝42.1nm、D50＝80nm、D75＝113.2nm、D97＝137.3nm的颗粒分布的纳米颗粒材料，
(3)将步骤(2)中分别选出的纳米颗粒，分别用2M氢氧化钠溶液和去离子水洗涤两次，离心分离，真空干燥得到本发明纳米铁粉；
其中，无机铁盐为氯化铁。
实施例3
一种纳米铁粉的制备方法，该方法包括以下步骤：
(1)将金属铝粉和无机盐铁粉混合，其中金属铝粉和无机盐铁粉的摩尔比为1：2；
(2)在10℃—15℃的情况下，将高频切割机切割次数设定在5500-6000RPM/min，将无机盐铁粉和铝粉混合物加工成纳米粉体颗粒，分别筛选出D3＝21nm、D25＝42.1nm、D50＝80nm、D75＝113.2nm、D97＝137.3nm的颗粒分布的纳米颗粒材料，
(3)将步骤(2)中分别选出的纳米颗粒，分别用2M氢氧化钠溶液和去离子水洗涤两次，离心分离，真空干燥得到本发明纳米铁粉；
其中，无机铁盐为硝酸铁。
实施例4
一种纳米铁粉的制备方法，该方法包括以下步骤：
(1)将金属铝粉和无机盐铁粉混合，其中金属铝粉和无机盐铁粉的摩尔比为1：2；
(2)在12℃的情况下，将高频切割机切割次数设定在6000RPM/min，将无机盐铁粉和铝粉混合物加工成纳米粉体颗粒，分别筛选出D3＝21nm、D25＝42.1nm、D50＝80nm、D75＝113.2nm、D97＝137.3nm的颗粒分布的纳米颗粒材料，
(3)将步骤(2)中分别选出的纳米颗粒，分别用2M氢氧化钠溶液和去离子水洗涤两次，离心分离，真空干燥得到本发明纳米铁粉；
其中，无机铁盐为硝酸铁。
实施例5
一种纳米铁粉的制备方法，该方法包括以下步骤：
(1)将金属铝粉和无机盐铁粉混合，其中金属铝粉和无机盐铁粉的摩尔比为1：2；
(2)在12℃的情况下，将高频切割机切割次数设定在6000RPM/min，将无机盐铁粉和铝粉混合物加工成纳米粉体颗粒，分别筛选出D3＝21nm、D25＝42.1nm、D50＝80nm、D75＝113.2nm、D97＝137.3nm的颗粒分布的纳米颗粒材料，
(3)将步骤(2)中分别选出的纳米颗粒，分别用2M氢氧化钠溶液和去离子水洗涤两次，离心分离，真空干燥得到本发明纳米铁粉；
其中，无机铁盐为硫酸亚铁。

Claims (2)

1.一种纳米铁粉的制备方法，其特征是，该方法包括以下步骤：
(1)将金属铝粉和无机盐铁粉混合，其中金属铝粉和无机盐铁粉的摩尔比为1-2:1；
(2)在10℃—15℃的情况下，将高频切割机切割次数设定在5500-6000RPM/min，将无机盐铁粉和铝粉混合物加工成纳米粉体颗粒，分别筛选出D3＝21nm、D25＝42.1nm、D50＝80nm、D75＝113.2nm、D97＝137.3nm的颗粒分布的纳米颗粒材料，
(3)将步骤(2)中分别选出的纳米颗粒，分别用2M氢氧化钠溶液和去离子水洗涤两次，离心分离，真空干燥得到本发明纳米铁粉。
2.根据权利要求1所述的方法，其特征在于，所述无机铁盐为硫酸亚铁、氯化铁、硝酸铁中的一种或多种。
CN201410348613.4A 2014-07-21 2014-07-21 一种纳米铁粉的制备方法 Pending CN104096843A (zh)