CN104088424A - Method for manufacturing wide-width digital printing Dacron wall cloth - Google Patents
Method for manufacturing wide-width digital printing Dacron wall cloth Download PDFInfo
- Publication number
- CN104088424A CN104088424A CN201410367777.1A CN201410367777A CN104088424A CN 104088424 A CN104088424 A CN 104088424A CN 201410367777 A CN201410367777 A CN 201410367777A CN 104088424 A CN104088424 A CN 104088424A
- Authority
- CN
- China
- Prior art keywords
- cloth
- temperature
- wall paper
- terylene
- conducting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of home decoration and textile printing, in particular to a method for manufacturing wide-width digital printing Dacron wall cloth. According to the technical scheme, the method for manufacturing the wide-width digital printing Dacron wall cloth includes the following steps: knitting cloth, conducting padding in a water-proofing agent, conducting front-face three-proofing processing, conducting back-face PU glue layer processing, conducting sticky rice glue preparation, conducting low-temperature preheating, conducting direct-spraying printing, conducting medium temperature color fixing, conducting air drying and cooling and conducting high-temperature color development. By means of the method for manufacturing the wide-width digital printing Dacron wall cloth, the good oil proofing, fouling proofing and water proofing functions are achieved after the Dacron wall cloth is manufactured, and the Dacron wall cloth is easy to tidy and favorable for cleaning; the original waterproof digital printing part of the wall cloth wall cloth can absorb ink, the color development is good through the three temperature control programs, personalized customization patterns are provided for a user, and the color formation effect is good.
Description
Technical field
The present invention relates to house fitting-up and field of printing and dyeing, be specifically related to a kind of making processing method to wide cut digit printing terylene wall paper.
Background technology
Wall paper is as a kind of ornament materials that is laid on metope, and fashion is attractive in appearance, and class sense is strong, is generally applicable on house fitting-up or hotel, coffee house's metope, as the use of decoration.Existing common wall paper is divided into two kinds, a kind of with knitted jacquard, such wall paper has stereo concave-convex sense, exquisite unsurpassed, but being knitted jacquard, shortcoming is subject to the restriction of modern crafts and itself characteristic, cannot make chromatic colour and complicated pattern, another kind of mode is to use digit printing, digital printing technology is generally used in apparel industry, bright-coloured patterns as various in stamp on T-shirt, use digital printing technology on wall paper, advantage is that pattern is bright-coloured attractive in appearance, ornamental strong, and the various patterns of energy personalized customization, shortcoming is that the wall paper of wide cut is often used in hotel lobby, conference room, the medium-to-high grade place such as large-scale restaurant, for waterproof, grease proofing, mildew-resistant has very high requirement, so wide cut wall paper is often through three anti-processing, and through the wall paper of waterproofing work how can in digit printing process, fully absorb and fixedly ink formed a new difficult problem, a kind of waterproof wall paper that the patent document that for example number of patent application is 201210567415.8 is announced, tow sides at wall paper are respectively established one deck waterproof composite layer, process applicant repeatedly processing experiment records, so structure can play certain waterproof oil-proof result really, but there are two drawbacks: one, two-layer waterproof composite layer can hinder the absorption of wall paper to printing ink in the link of dyeing and printing process, color development effect is bad, two, such waterproofing design also can make gas permeability bad simultaneously, for wall paper, can not breathe freely and easily grow mould, mouldy.
Summary of the invention
The object of this invention is to provide a kind of making processing method to wide cut digit printing terylene wall paper, terylene wall paper has good grease proofing antifouling water-proof function after making, easily arrange be beneficial to clean, the part of digit printing originally the wall paper of waterproof but can absorb ink, through three channel temp control programs, color development is good, to user, provides personalized customization pattern, and quality is effective.
Above-mentioned technical purpose of the present invention is achieved by the following technical programs: a kind of making processing method to wide cut digit printing terylene wall paper, and this making processing method comprises the following steps:
1) cloth braiding step: this terylene wall paper comprises terylene layer of cloth, and described terylene layer of cloth is 2.6 meters-3.2 meters in the distance of width, is formed by warp and parallel 1 to 1 braiding, and described warp and described parallel are chemical-fibres filaments.
The mechanism of graticule one to makes this kind of terylene wall paper vertical direction and horizontal direction after putting up all possess certain tension force, on market, portioned product can also add part cotton thread except chemical-fibres filaments, the difficulty of the color development of heating when but cotton thread can make postorder digit printing link increases, so only need to use chemical-fibres filaments, this kind of terylene wall paper is because applicable object is more the spacious place such as hotel, hall, must possess certain width, between 2.6 meters-3.2 meters, in practical operation, this width distance is usually 3.2 meters.
2) waterproof agent pads step: the terylene layer of cloth that braiding is formed pads fast in waterproof agent, and 3-8 seconds, described waterproof agent comprised polyether ester and dimethyl hydrogen containing siloxane.
Described terylene layer of cloth padded fast in described waterproof agent, made described terylene layer of cloth itself also possess preliminary water-proof function.
3) positive three anti-treatment steps: the positive adhesion of the terylene layer of cloth padding in waterproof agent is had to three anti-coatings, described three anti-coatings comprise polytetrafluoroethylene (PTFE) and titania powder, described three anti-coatings are provided with pore, and the aperture of described pore is 0.8 micron-3 microns.
The diameter of liquid water molecules is 100 microns of left and right, hydrone diameter under gaseous state is below 0.1 micron, the bore of described pore can be breathed freely, but enough block aqueous water, titanium dioxide is nontoxic, healthy, and can purify air, increase to pollutants in air as nitrogen oxide, the decomposition of aromatic hydrocarbons and aldehydes, tetrafluoroethene has powerful waterproof oil-proof result, three anti-coatings have the antifouling ability of certain waterproof and oilproof, in hotel or during exclusive restaurant box, the edible various certain oil smoke generations that have while waiting hot gas food such as iron plate barbecue of guest, if adsorbed by wall paper, easy cleaning impact is not attractive in appearance, described three anti-coatings can be kept off large oil molecule and the hydrone of molecular structure outside, only need wiping to remove, described three anti-coatings do not rely on described gluing adhesion, described three anti-coatings become the membranaceous described terylene layer of cloth that sticks in, thereby can not affect pattern and the gloss in described terylene layer of cloth front.
4) reverse side PU glue-line treatment step: rely on the adhesion of painting glue glued adhesion to have PU white glue waterproofing course described terylene layer of cloth reverse side, described gluing includes PUR, described PU white glue waterproofing course comprises polyurethane resin, DMF solvent, MH208 catalyst, plasticizing agent, curing compound, filler, fixed generation after stoichiometric number hour after stirring, each composition is respectively described polyurethane resin 67%-72% by weight percentage, DMF solvent 25%-31%, MH208 catalyst is 8-9%, on described PU white glue waterproofing course, be also provided with pore, the aperture of described pore is 0.8 micron-3 microns.
Described PU white glue waterproofing course comprises polyurethane resin, density is large, described PU white glue waterproofing course has on the one hand need to smear at the wall paper back side a large amount of glue in construction, avoid glue to enter described terylene layer of cloth, can increase on the other hand hardness and the thickness of wall paper, because this kind of wall paper size is large, width distance is long, if this kind of wall paper too soft being unfavorable for puts up.
5) described glutinous rice glue preliminary step: described PU white glue waterproofing course is also provided with glutinous rice glue glued adhesion layer towards the one side of metope.
When the modern times, fitted up in medium-to-high grade place, for environmental protection, tend to use the glutinous rice glue that is called as " eatable glue ", on described glutinous rice glue glued adhesion layer, can directly smear described glutinous rice glue, be convenient to contact and adhesion, the wall paper of processing through above five processes, this kind of terylene wall paper tow sides can waterproof, positive all right grease proofing antifouling, be beneficial to and put up, when digit printing process, be subject to temperatures involved, can change its molecular structure spacing, use the dispersed ink dye in known technology, the molecular volume of this kind of dyestuff can at high temperature enter in described terylene wall paper.
6) low-temperature prewarming step: carry out low-temperature prewarming by firing equipment common in the known technologies such as heating tube and conveyer belt, temperature is controlled at 30 ° of C-40 ° C, heat time is 8-13 seconds, increases pliability and the pliability of wall paper, increases intermolecular spacing in cloth simultaneously.
7) straight printing step: use digit printing printer, pattern is inputted in printer memory by computer, install the print cartridge of some different colours in printer, color is directly sprayed on to corresponding area of cloth by shower nozzle.
8) warm fixation step in: carry out middle temperature fixation by firing equipment common in the known technologies such as heating tube and conveyer belt, temperature is controlled at 55 ° of C-65 ° C, heat time is 8-13 seconds, further increases the intermolecular spacing of cloth, and ink molecules can be entered among cloth top layer.
9) air-dry cooling step: the conveyer belt on equipment is sent to air-dry region by the cloth of warm fixation in passing through, can adopt the equipment such as fan in known technology herein, on the one hand moisture unnecessary in ink is dispelled to evaporation, reduce the mobility of ink, avoid color to dye out, on the other hand the temperature of wall paper is reduced, allow cloth intermolecular distance diminish, pin the ink molecules that has entered cloth top layer.
10) high temperature fixation step: the wall paper of air-dry cooling is sent to high temperature fixation region, by firing equipment common in the known technologies such as heating tube and conveyer belt, carry out high temperature fixation, temperature is controlled at 180 ° of C-220 ° C, and the heat time is 50-75 seconds.High temperature makes ink enter cloth tissue, moisture content evaporate to dryness completely, and colorant is fixed in cloth, thereby improves ink-jet printed color fastness; Cloth is after high-temperature shaping, and physical property and chemical property have all been subject to fixing, have kept the stability of product, and there is no the remnants of volatile materials.
Above step 1 is to step 5, produce the terylene wall paper of all ventilative and waterproof of positive and negative, front, without PUR, does not hide color pattern and the texture of wall paper itself, and reverse side possesses certain thickness and hardness, be beneficial to and put up and fix, from step 6 to step 10, through three temperature steps different with effect, ink molecules is firmly fixed among cloth, unfading, color development is effective.
As of the present invention preferred, in described gluing, according to weight package, contain PUR 40%-70%, silver nitrate anti-bacterial powder 6%-13%.
Silver nitrate possesses certain oxidation capacity, possesses certain sterilizing ability simultaneously, adds described silver nitrate anti-bacterial powder that described ratio is not high can improve anti-soil and the sterilizing ability of this wall paper in described gluing.
As of the present invention preferred, described woven dacron layer thickness is 0.32mm-0.37mm, and described PU white glue waterproofing layer thickness is 0.08-0.13mm.
As of the present invention preferred, the equipment that the equipment that described low-temperature prewarming step is used and described middle temperature fixation step are used can be integration apparatus, the equipment that the equipment that the equipment that described high temperature fixation step is used and described low-temperature prewarming step are used and described middle temperature fixation step are used is split type equipment, and centre exists thermal insulation to process.
If process without thermal insulation, the temperature of the equipment that described high temperature fixation step is used can improve by heat radiation described in low-temperature prewarming step or the wall paper cloth temperature in described middle temperature fixation step, thereby affects processing effect.
As of the present invention preferred, described low-temperature prewarming step heating-up temperature is 35 ° of C, and the heat time is 10 seconds.
As of the present invention preferred, described middle temperature fixation step heating-up temperature is 60 ° of C, and the heat time is 10 seconds.
As of the present invention preferred, described high temperature fixation step heating-up temperature is 200 ° of C, and the heat time is 60 seconds.
In sum, the present invention has following beneficial effect:
1, this terylene wall paper, at usual state energy ventilating mildew-resistant, can block greasy dirt and moisture simultaneously, and cleaning is convenient, practical.
2, this terylene wall paper back is also provided with glutinous rice glue glued adhesion layer, and glutinous rice glue that can coordinative construction side is realized and being puted up better.
3, this terylene wall paper size is large, but because uprise hardness adding of PU white glue waterproofing course, is beneficial to and puts up.
4, the chemical composition of this terylene wall paper makes at high temperature can react, and intermolecular distance increases, and makes special-purpose dispersed ink dye can enter wall paper, realizes color development.
5, the some chemical properties energy sterilization in this terylene wall paper and decomposition dirt, increase spatter property and the safety of wall paper.
6, use three kinds of color development color fixing process of heating, rationally control temperature and heat time, at utmost widen wall paper cloth intermolecular distance, fully absorb ink, can pin ink molecules again, do not allow ink run look.
7, increase described air-dry cooling step, moisture unnecessary in ink is dispelled to evaporation, reduce the mobility of ink, avoid color to dye out.
Accompanying drawing explanation
Fig. 1 is the schematic flow sheet of embodiment 1;
Fig. 2 is the wall paper layering schematic diagram of embodiment 1.
In figure:
1, three anti-coatings, 2, terylene layer of cloth, 3, PU white glue waterproofing course, 4, glutinous rice glue glued adhesion layer.
The specific embodiment
Below in conjunction with accompanying drawing, the present invention is described in further detail.
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; those skilled in the art can make to the present embodiment the modification that there is no creative contribution as required after reading this manual, but as long as within the scope of claim of the present invention, are all subject to the protection of Patent Law.
Embodiment 1, as depicted in figs. 1 and 2, a kind of making processing method to wide cut digit printing terylene wall paper, this making processing method comprises the following steps:
1 cloth braiding step: this terylene wall paper comprises terylene layer of cloth 2, and terylene layer of cloth 2 is 2.6 meters-3.2 meters in the distance of width, is formed by warp and parallel 1 to 1 braiding, and warp and parallel are chemical-fibres filaments.
The mechanism of graticule one to makes this kind of terylene wall paper vertical direction and horizontal direction after putting up all possess certain tension force, on market, portioned product can also add part cotton thread except chemical-fibres filaments, the difficulty of the color development of heating when but cotton thread can make postorder digit printing link increases, so only need to use chemical-fibres filaments, this kind of terylene wall paper is because applicable object is more the spacious place such as hotel, hall, must possess certain width, between 2.6 meters-3.2 meters, in practical operation, this width distance is usually 3.2 meters.
2 waterproof agents pad step: the terylene layer of cloth 2 that braiding is formed pads fast in waterproof agent, and 3-8 seconds, waterproof agent comprised polyether ester and dimethyl hydrogen containing siloxane.
Terylene layer of cloth padded fast in waterproof agent, made terylene layer of cloth itself also possess preliminary water-proof function.
3 positive three anti-treatment steps: have the anti-coating 1 of three anti-coatings 1, three to comprise polytetrafluoroethylene (PTFE) and titania powder the positive adhesion of terylene layer of cloth 2 of padding in waterproof agent, three anti-coatings 1 are provided with pore 6, and the aperture of pore is 0.8 micron-3 microns.
The diameter of liquid water molecules is 100 microns of left and right, hydrone diameter under gaseous state is below 0.1 micron, the bore of pore can be breathed freely, but enough block aqueous water, titanium dioxide is nontoxic, healthy, and can purify air, increase to pollutants in air as nitrogen oxide, the decomposition of aromatic hydrocarbons and aldehydes, tetrafluoroethene has powerful waterproof oil-proof result, three anti-coatings have the antifouling ability of certain waterproof and oilproof, in hotel or during exclusive restaurant box, the edible various certain oil smoke generations that have while waiting hot gas food such as iron plate barbecue of guest, if adsorbed by wall paper, easy cleaning impact is not attractive in appearance, three anti-coatings can be kept off large oil molecule and the hydrone of molecular structure outside, only need wiping to remove, three anti-coatings do not rely on gluing adhesion, three anti-coatings become the membranaceous terylene layer of cloth that sticks in, thereby can not affect pattern and the gloss in terylene layer of cloth front.
4 reverse side PU glue-line treatment steps: terylene layer of cloth 2 reverse side are relied in gluing 5(figure and do not marked) gummed adhesion has PU white glue waterproofing course 3, in gluing 5, according to weight package, contain PUR 40%-70%, silver nitrate anti-bacterial powder 6%-13%, silver nitrate possesses certain oxidation capacity, possess certain sterilizing ability, the silver nitrate anti-bacterial powder that additional proportion is not high in gluing can improve anti-soil and the sterilizing ability of this wall paper simultaneously; PU white glue waterproofing course 3 comprises polyurethane resin, DMF solvent, MH208 catalyst, plasticizing agent, curing compound, filler, fixed generation after stoichiometric number hour after stirring, each composition is respectively polyurethane resin 67%-72% by weight percentage, DMF solvent 25%-31%, MH208 catalyst is to be also provided with in pore 6(figure and not mark on 8-9%, PU white glue waterproofing course), the aperture of pore is 0.8 micron-3 microns; Terylene layer of cloth 2 thickness are 0.32mm-0.37mm, and PU white glue waterproofing course 3 thickness are 0.08-0.13mm.
PU white glue waterproofing course comprises polyurethane resin, density is large, PU white glue waterproofing course has on the one hand need to smear at the wall paper back side a large amount of glue in construction, avoid glue to enter terylene layer of cloth, can increase on the other hand hardness and the thickness of wall paper, because this kind of wall paper size is large, width distance is long, if this kind of wall paper too soft being unfavorable for puts up.
5 glutinous rice glue preliminary steps: PU white glue waterproofing course 3 is also provided with glutinous rice glue glued adhesion layer 4 towards the one side of metope.
When the modern times, fitted up in medium-to-high grade place, for environmental protection, tend to use the glutinous rice glue that is called as " eatable glue ", on glutinous rice glue glued adhesion layer, can directly smear glutinous rice glue, be convenient to contact and adhesion, the wall paper of processing through above five processes, this kind of terylene wall paper tow sides can waterproof, positive all right grease proofing antifouling, be beneficial to and put up, when digit printing process, be subject to temperatures involved, can change its molecular structure spacing, use the dispersed ink dye in known technology, the molecular volume of this kind of dyestuff can at high temperature enter in terylene wall paper.
6 low-temperature prewarming steps: carry out low-temperature prewarming by firing equipment common in the known technologies such as heating tube and conveyer belt, temperature is controlled at 30 ° of C-40 ° C, take 35 ℃ as good, heat time is 8-13 seconds, take 10 seconds as good, the pliability and the pliability that increase wall paper increase intermolecular spacing in cloth simultaneously.
7 straight printing steps: use digit printing printer, pattern is inputted in printer memory by computer, install the print cartridge of some different colours in printer, color is directly sprayed on to corresponding area of cloth by shower nozzle.
Warm fixation step in 8: carry out middle temperature fixation by firing equipment common in the known technologies such as heating tube and conveyer belt, temperature is controlled at 55 ° of C-65 ° C, take 60 ℃ as good, heat time is 8-13 seconds, take 10 seconds as good, further increase the intermolecular spacing of cloth, ink molecules can be entered among cloth top layer.
9 air-dry cooling steps: the conveyer belt on equipment is sent to air-dry region by the cloth of warm fixation in passing through, can adopt the equipment such as fan in known technology herein, on the one hand moisture unnecessary in ink is dispelled to evaporation, reduce the mobility of ink, avoid color to dye out, on the other hand the temperature of wall paper is reduced, allow cloth intermolecular distance diminish, pin the ink molecules that has entered cloth top layer.
10 high temperature fixation steps: the wall paper of air-dry cooling is sent to high temperature fixation region, by firing equipment common in the known technologies such as heating tube and conveyer belt, carry out high temperature fixation, temperature is controlled at 180 ° of C-220 ° C, take 200 ℃ as good, heat time is 50-75 seconds, take 60 seconds as good.High temperature makes ink enter cloth tissue, moisture content evaporate to dryness completely, and colorant is fixed in cloth, thereby improves ink-jet printed color fastness, cloth is after high-temperature shaping, physical property and chemical property have all been subject to fixing, the stability that has kept product, and the remnants that there is no volatile materials, the equipment that the equipment that low-temperature prewarming step is used and middle temperature fixation step are used can be integration apparatus, the equipment that the equipment that the equipment that high temperature fixation step is used and low-temperature prewarming step are used and middle temperature fixation step are used is split type equipment, and centre exists thermal insulation to process, if process without thermal insulation, the temperature of the equipment that high temperature fixation step is used can improve in low-temperature prewarming step or the wall paper cloth temperature in middle temperature fixation step by heat radiation, thereby affect processing effect.
Above step 1 is to step 5, produce the terylene wall paper of all ventilative and waterproof of positive and negative, front, without PUR, does not hide color pattern and the texture of wall paper itself, and reverse side possesses certain thickness and hardness, be beneficial to and put up and fix, from step 6 to step 10, through three temperature steps different with effect, ink molecules is firmly fixed among cloth, unfading, color development is effective.
Claims (7)
1. the making processing method to wide cut digit printing terylene wall paper, is characterized in that: this making processing method comprises the following steps:
1) cloth braiding step: this terylene wall paper comprises terylene layer of cloth (2), and described terylene layer of cloth (2) is 2.6 meters-3.2 meters in the distance of width, is formed by warp and parallel 1 to 1 braiding, and described warp and described parallel are chemical-fibres filaments.
2) waterproof agent pads step: the terylene layer of cloth (2) that braiding is formed pads fast in waterproof agent, and 3-8 seconds, described waterproof agent comprised polyether ester and dimethyl hydrogen containing siloxane.
3) positive three anti-treatment steps: the positive adhesion of terylene layer of cloth (2) of padding in waterproof agent is had to three anti-coatings (1), described three anti-coatings (1) comprise polytetrafluoroethylene (PTFE) and titania powder, described three anti-coatings (1) are provided with pore (6), and the aperture of described pore is 0.8 micron-3 microns.
4) reverse side PU glue-line treatment step: rely on the adhesion of gluing (5) gummed to have PU white glue waterproofing course (3) described terylene layer of cloth (2) reverse side, described gluing (5) includes PUR, described PU white glue waterproofing course (3) comprises polyurethane resin, DMF solvent, MH208 catalyst, plasticizing agent, curing compound, filler, fixed generation after stoichiometric number hour after stirring, each composition is respectively described polyurethane resin 67%-72% by weight percentage, DMF solvent 25%-31%, MH208 catalyst is 8-9%, on described PU white glue waterproofing course, be also provided with pore (6), the aperture of described pore is 0.8 micron-3 microns.
5) described glutinous rice glue preliminary step: described PU white glue waterproofing course (3) is also provided with glutinous rice glue glued adhesion layer (4) towards the one side of metope.
6) low-temperature prewarming step: carry out low-temperature prewarming by firing equipment common in the known technologies such as heating tube and conveyer belt, temperature is controlled at 30 ° of C-40 ° C, heat time is 8-13 seconds, increases pliability and the pliability of wall paper, increases intermolecular spacing in cloth simultaneously.
7) straight printing step: use digit printing printer, pattern is inputted in printer memory by computer, install the magic box of some different colours in printer, color is directly sprayed on to corresponding area of cloth by shower nozzle.
8) warm fixation step in: carry out middle temperature fixation by firing equipment common in the known technologies such as heating tube and conveyer belt, temperature is controlled at 55 ° of C-65 ° C, heat time is 8-13 seconds, further increases the intermolecular spacing of cloth, and ink molecules can be entered among cloth top layer.
9) air-dry cooling step: the conveyer belt on equipment is sent to air-dry region by the cloth of warm fixation in passing through, can adopt the equipment such as fan in known technology herein, on the one hand moisture unnecessary in ink is dispelled to evaporation, reduce the mobility of ink, avoid color to dye out, on the other hand the temperature of wall paper is reduced, allow cloth intermolecular distance diminish, pin the ink molecules that has entered cloth top layer.
10) high temperature fixation step: the wall paper of air-dry cooling is sent to high temperature fixation region, by firing equipment common in the known technologies such as heating tube and conveyer belt, carry out high temperature fixation, temperature is controlled at 180 ° of C-220 ° C, and the heat time is 50-75 seconds.
2. a kind of making processing method to wide cut digit printing terylene wall paper according to claim 1, is characterized in that: in described gluing (5), according to weight package, contain PUR 40%-70%, silver nitrate anti-bacterial powder 6%-13%.
3. a kind of making processing method to wide cut digit printing terylene wall paper according to claim 1, is characterized in that: described terylene layer of cloth (2) thickness is 0.32mm-0.37mm, and described PU white glue waterproofing course (3) thickness is 0.08-0.13mm.
4. a kind of making processing method to wide cut digit printing terylene wall paper according to claim 1, it is characterized in that: the equipment that the equipment that described low-temperature prewarming step is used and described middle temperature fixation step are used can be integration apparatus, the equipment that the equipment that the equipment that described high temperature fixation step is used and described low-temperature prewarming step are used and described middle temperature fixation step are used is split type equipment, and centre exists thermal insulation to process.
5. a kind of making processing method to wide cut digit printing terylene wall paper according to claim 1, is characterized in that: described low-temperature prewarming step heating-up temperature is 35 ° of C, and the heat time is 10 seconds.
6. a kind of making processing method to wide cut digit printing terylene wall paper according to claim 1, is characterized in that: described middle temperature fixation step heating-up temperature is 60 ° of C, and the heat time is 10 seconds.
7. a kind of making processing method to wide cut digit printing terylene wall paper according to claim 1, is characterized in that: described high temperature fixation step heating-up temperature is 200 ° of C, and the heat time is 60 seconds.