CN104087954A - Derusting/rust-prevention treating agent for steel surfaces - Google Patents
Derusting/rust-prevention treating agent for steel surfaces Download PDFInfo
- Publication number
- CN104087954A CN104087954A CN201410336456.5A CN201410336456A CN104087954A CN 104087954 A CN104087954 A CN 104087954A CN 201410336456 A CN201410336456 A CN 201410336456A CN 104087954 A CN104087954 A CN 104087954A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- rust
- chromium
- derusting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a derusting/rust-prevention treating agent for steel surfaces, which is prepared from the following raw materials: 50-60 parts of phosphoric acid, 15-20 parts of metaphosphoric acid, 5-10 parts of hypochlorous acid, 8-10 parts of hypophosphorous acid, 3-5 parts of potassium permanganate, 10-15 parts of ferric oxide, 10-12 parts of titanium oxide, 3-5 parts of chromic oxide, 10-15 parts of chromic hydroxide, 5-8 parts of chalcanthite, 10-12 parts of potassium chloride, 5-8 parts of alcohol, 5-10 parts of glycerol, 3-5 parts of fatty alcohol polyethenoxy ether, 3-5 parts of cetyl trimethylammonium bromide, 5-10 parts of ethyl orthosilicate and 50-80 parts of deionized water. The derusting/rust-prevention treating agent for steel surfaces has higher anticorrosive capacity. The treating agent can remove trace oil stains on the steel surface, remove the oxide skin and rust on the treated part and form a film without flushing; the film is an excellent anticorrosive protective coating which has favorable adhesive force with the paint and spraying plastics; and the treated workpiece can not be rusted for a long time, and can not change the mechanical properties of the material.
Description
Technical field
The present invention relates to the technical field of derusting rust-proofing treatment agent, relate in particular to a kind of derusting rust-proofing treatment agent for steel surface.
Background technology
At present, having occurred the steel surface processing agent of many new formulas both at home and abroad, although it has many good qualities, introduced a large amount of " salt ", contained a large amount of metallic cations and negatively charged ion is mixed in rete in these " salt ", is disadvantageous to corrosionproof protection.
Summary of the invention
The object of the invention is the shortcoming in order to overcome above-mentioned prior art; a kind of derusting rust-proofing treatment agent for steel surface is provided; this derusting rust-proofing treatment agent that is used for steel surface can improve antiseptic power; slough with the micro-greasy dirt on this treatment agent energy steel surface; remove subsequently oxide skin and the iron rust of processing part; form a kind of film without rinsing; this film is exactly a kind of good corrosionproof protection coating; japanning and plastic-blasting are had to good sticking power; workpiece after treatment can corrosion in long-time, can not change the mechanical property of material.
The technical solution adopted for the present invention to solve the technical problems is: a kind of derusting rust-proofing treatment agent for steel surface, composition of raw materials component by following umber forms: 50-60 part phosphoric acid, 15-20 part metaphosphoric acid, 5-10 part hypochlorous acid, 8-10 part Hypophosporous Acid, 50, 3-5 part potassium permanganate, 10-15 part ferric oxide, 10-12 part titanium oxide, 3-5 part chromium sesquioxide, 10-15 part chromium hydroxide, 5-8 part cupric sulfate pentahydrate, 10-12 part Repone K, 5-8 part alcohol, 5-10 part glycerine, 3-5 part fatty alcohol-polyoxyethylene ether, 3-5 part cetyl trimethylammonium bromide, 5-10 part tetraethoxy, 50-80 part deionized water.
Further, each composition of raw materials component is: 50 parts of phosphoric acid, 15 parts of metaphosphoric acids, 5 parts of hypochlorous acid, 8 parts of Hypophosporous Acid, 50,3 parts of potassium permanganate, 10 parts of ferric oxide, 10 parts of titanium oxide, 3 parts of chromium sesquioxides, 10 parts of chromium hydroxides, 5 parts of cupric sulfate pentahydrates, 10 parts of Repone K, 5 parts of alcohol, 5 parts of glycerine, 3 parts of fatty alcohol-polyoxyethylene ether, 3 parts of cetyl trimethylammonium bromides, 5 parts of tetraethoxys, 50 parts of deionized waters.
Or each composition of raw materials component is: 60 parts of phosphoric acid, 20 parts of metaphosphoric acids, 10 parts of hypochlorous acid, 10 parts of Hypophosporous Acid, 50,5 parts of potassium permanganate, 15 parts of ferric oxide, 12 parts of titanium oxide, 5 parts of chromium sesquioxides, 15 parts of chromium hydroxides, 8 parts of cupric sulfate pentahydrates, 12 parts of Repone K, 8 parts of alcohol, 10 parts of glycerine, 5 parts of fatty alcohol-polyoxyethylene ether, 5 parts of cetyl trimethylammonium bromides, 10 parts of tetraethoxys, 80 parts of deionized waters.
In sum; the invention has the beneficial effects as follows: the derusting rust-proofing treatment agent for steel surface of the present invention can improve antiseptic power; slough with the micro-greasy dirt on this treatment agent energy steel surface; remove subsequently oxide skin and the iron rust of processing part; form a kind of film without rinsing, this film is exactly a kind of good corrosionproof protection coating, and japanning and plastic-blasting are had to good sticking power; workpiece after treatment can corrosion in long-time, can not change the mechanical property of material.
Embodiment
Embodiment 1
The described a kind of derusting rust-proofing treatment agent for steel surface of the present embodiment 1, is made up of the composition of raw materials component of following umber: 50 parts of phosphoric acid, 15 parts of metaphosphoric acids, 5 parts of hypochlorous acid, 8 parts of Hypophosporous Acid, 50,3 parts of potassium permanganate, 10 parts of ferric oxide, 10 parts of titanium oxide, 3 parts of chromium sesquioxides, 10 parts of chromium hydroxides, 5 parts of cupric sulfate pentahydrates, 10 parts of Repone K, 5 parts of alcohol, 5 parts of glycerine, 3 parts of fatty alcohol-polyoxyethylene ether, 3 parts of cetyl trimethylammonium bromides, 5 parts of tetraethoxys, 50 parts of deionized waters.
Embodiment 2
The described a kind of derusting rust-proofing treatment agent for steel surface of the present embodiment 2, is made up of the composition of raw materials component of following umber: 60 parts of phosphoric acid, 20 parts of metaphosphoric acids, 10 parts of hypochlorous acid, 10 parts of Hypophosporous Acid, 50,5 parts of potassium permanganate, 15 parts of ferric oxide, 12 parts of titanium oxide, 5 parts of chromium sesquioxides, 15 parts of chromium hydroxides, 8 parts of cupric sulfate pentahydrates, 12 parts of Repone K, 8 parts of alcohol, 10 parts of glycerine, 5 parts of fatty alcohol-polyoxyethylene ether, 5 parts of cetyl trimethylammonium bromides, 10 parts of tetraethoxys, 80 parts of deionized waters.
The above, be only preferred embodiment of the present invention, not principle of the present invention done to any pro forma restriction.Any simple modification, equivalent variations and modification that every foundation technical spirit of the present invention is done above embodiment, all still belong in the scope of technical scheme of the present invention.
Claims (3)
1. the derusting rust-proofing treatment agent for steel surface, it is characterized in that, composition of raw materials component by following umber forms: 50-60 part phosphoric acid, 15-20 part metaphosphoric acid, 5-10 part hypochlorous acid, 8-10 part Hypophosporous Acid, 50, 3-5 part potassium permanganate, 10-15 part ferric oxide, 10-12 part titanium oxide, 3-5 part chromium sesquioxide, 10-15 part chromium hydroxide, 5-8 part cupric sulfate pentahydrate, 10-12 part Repone K, 5-8 part alcohol, 5-10 part glycerine, 3-5 part fatty alcohol-polyoxyethylene ether, 3-5 part cetyl trimethylammonium bromide, 5-10 part tetraethoxy, 50-80 part deionized water.
2. a kind of derusting rust-proofing treatment agent for steel surface according to claim 1, it is characterized in that, each composition of raw materials component is: 50 parts of phosphoric acid, 15 parts of metaphosphoric acids, 5 parts of hypochlorous acid, 8 parts of Hypophosporous Acid, 50,3 parts of potassium permanganate, 10 parts of ferric oxide, 10 parts of titanium oxide, 3 parts of chromium sesquioxides, 10 parts of chromium hydroxides, 5 parts of cupric sulfate pentahydrates, 10 parts of Repone K, 5 parts of alcohol, 5 parts of glycerine, 3 parts of fatty alcohol-polyoxyethylene ether, 3 parts of cetyl trimethylammonium bromides, 5 parts of tetraethoxys, 50 parts of deionized waters.
3. a kind of derusting rust-proofing treatment agent for steel surface according to claim 1, it is characterized in that, each composition of raw materials component is: 60 parts of phosphoric acid, 20 parts of metaphosphoric acids, 10 parts of hypochlorous acid, 10 parts of Hypophosporous Acid, 50,5 parts of potassium permanganate, 15 parts of ferric oxide, 12 parts of titanium oxide, 5 parts of chromium sesquioxides, 15 parts of chromium hydroxides, 8 parts of cupric sulfate pentahydrates, 12 parts of Repone K, 8 parts of alcohol, 10 parts of glycerine, 5 parts of fatty alcohol-polyoxyethylene ether, 5 parts of cetyl trimethylammonium bromides, 10 parts of tetraethoxys, 80 parts of deionized waters.