CN104087795B - 一种led用防潮防裂铝基复合散热材料 - Google Patents
一种led用防潮防裂铝基复合散热材料 Download PDFInfo
- Publication number
- CN104087795B CN104087795B CN201410322200.9A CN201410322200A CN104087795B CN 104087795 B CN104087795 B CN 104087795B CN 201410322200 A CN201410322200 A CN 201410322200A CN 104087795 B CN104087795 B CN 104087795B
- Authority
- CN
- China
- Prior art keywords
- heat sink
- sink material
- powder
- led
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及灯具散热材料,具体涉及一种LED用防潮防裂铝基复合散热材料及其生产方法,该散热材料由以下重量份的原料制成:铝82-85、氮化铝12-14、六铝酸钙4-5、硼砂1-2、霞石粉2-3、黑晶粉1-2、硅溶胶3-5、膨胀玻化微珠8-10、可再分散乳胶粉6-8、助剂4-5;本发明的散热材料综合了铝、氮化铝、膨胀玻化微珠、助剂等成分的优点,兼具良好的导热和绝缘性能,硅溶胶和可再分散乳胶粉的加入可以促进原料成型,改善烧结效果,制得的散热材料结构致密,表面光洁度高,极具装饰效果,同时还有优良的防水阻潮能力,耐温性能好,不易开裂,更为经久耐用,其良好的散热能力有效的保护LED灯具,大大延长灯具的使用寿命。
Description
技术领域
本发明涉及灯具散热材料,具体涉及一种LED用防潮防裂铝基复合散热材料及其生产方法。
背景技术
LED被称为第四代光源,具有节能、环保、安全、低能耗、高亮度等优点,在日常生活中被广泛使用,LED灯体本身的散热性能至关重要,直接影响到灯具的使用寿命和照明效果。现有的LED散热材料主要是由铝、铜等金属材料制成,在实际使用中存在成本限制、绝缘性能不够等缺点,因此很有必要改进材料的配方,使材料达到更为良好的散热效果,改善灯具的使用性能,延长使用寿命。
发明内容
本发明的目的在于,提供一种LED用防潮防裂铝基复合散热材料,使得材料不仅具有良好散热能力,还具有良好的使用性能,更为经久耐用,为了实现上述目的,本发明采用的技术方案如下:
一种LED用防潮防裂铝基复合散热材料,其特征在于,本发明材料由以下重量份的原料制成:铝82-85、氮化铝12-14、六铝酸钙4-5、硼砂1-2、霞石粉2-3、黑晶粉1-2、硅溶胶3-5、膨胀玻化微珠8-10、可再分散乳胶粉6-8、助剂4-5。
所述的助剂由以下重量份的原料制成:聚合硫酸铝4-5、动物骨8-10、钠砂1-3、聚酰亚胺4-5、银包铜粉8-10、氧化镁12-14、轻质碳酸镁5-8,制备方法为:先将动物骨在800-900℃温度下煅烧10-12h后冷却备用,再将聚合硫酸铝溶于适量水中配制成浓度为4-6%的水溶液,并将煅烧后的动物骨与其它剩余成分投入溶液中,混合搅拌分散2-3h后浓缩干燥,研磨成300-400目细粉,即得。
所述的一种LED用防潮防裂铝基复合散热材料,其制作工艺包含以下步骤:
(1)先将可再分散乳胶粉投入10倍于其重量份的水中,搅拌分散均匀后,加入其它剩余成分,搅拌分散1-2h,将所得物料投入球磨机中球磨处理,使所得物料的万孔筛余量≤0.05%;
(2)将步骤(1)所得的物料在80-100℃下干燥,保持物料的含水率≤0.02%,随后将粉体研磨分散40-50min后送入模具中压制成型,在氮气氛围下以650-700℃的温度烧结4-6h后,经自然冷却至室温即得。
本发明的优点在于:较传统铝质散热材料在原料上综合了铝、氮化铝、六铝酸钙、膨胀玻化微珠、助剂等成分的优点,兼具良好的导热和绝缘性能,硅溶胶和可再分散乳胶粉的加入可以促进原料成型,改善烧结效果,最后烧结制得的散热材料结构致密,表面光洁度高,极具装饰效果,同时还有优良的防水阻潮能力,耐温性能好,不易开裂,更为经久耐用,其良好的散热能力有效的保护LED灯具,大大延长灯具的使用寿命。
具体实施方式
实施例
本实施例LED散热材料由以下重量份原料制成:铝85、氮化铝14、六铝酸钙5、硼砂2、霞石粉3、黑晶粉2、硅溶胶5、膨胀玻化微珠10、可再分散乳胶粉8、助剂5。
所述的助剂由以下重量份的原料制成:聚合硫酸铝5、动物骨10、钠砂3、聚酰亚胺5、银包铜粉10、氧化镁14、轻质碳酸镁5,制备方法为:先将动物骨在800-900℃温度下煅烧10-12h后冷却备用,再将聚合硫酸铝溶于适量水中配制成浓度为6%的水溶液,并将煅烧后的动物骨与其它剩余成分投入溶液中,混合搅拌分散3h后浓缩干燥,研磨成400目细粉,即得。
所述的一种LED用防潮防裂铝基复合散热材料,其制作工艺包含以下步骤:
(1)先将可再分散乳胶粉投入10倍于其重量份的水中,搅拌分散均匀后,加入其它剩余成分,搅拌分散2h,将所得物料投入球磨机中球磨处理,使所得物料的万孔筛余量≤0.05%;
(2)将步骤(1)所得的物料在80-100℃下干燥,保持物料的含水率≤0.02%,随后将粉体研磨分散40min后送入模具中压制成型,在氮气氛围下以650-700℃的温度烧结6h后,经自然冷却至室温即得。
本实施例所制得的散热材料较常规LED用散热材料的导热系数较常规铝基散热材料提高24.8%,热扩散率提高25.4%,热平衡时间平均缩短152min,灯具使用寿命提高28.2%。
Claims (2)
1.一种LED用防潮防裂铝基复合散热材料,其特征在于,该散热材料由以下重量份的原料制成:铝82-85、氮化铝12-14、六铝酸钙4-5、硼砂1-2、霞石粉2-3、黑晶粉1-2、硅溶胶3-5、膨胀玻化微珠8-10、可再分散乳胶粉6-8、助剂4-5;所述的助剂由以下重量份的原料制成:聚合硫酸铝4-5、动物骨8-10、钠砂1-3、聚酰亚胺4-5、银包铜粉8-10、氧化镁12-14、轻质碳酸镁5-8,制备方法为:先将动物骨在800-900℃温度下煅烧10-12h后冷却备用,再将聚合硫酸铝溶于适量水中配制成浓度为4-6%的水溶液,并将煅烧后的动物骨与其它剩余成分投入溶液中,混合搅拌分散2-3h后浓缩干燥,研磨成300-400目细粉,即得。
2.如权利要求1所述的一种LED用防潮防裂铝基复合散热材料,其生产方法如下:
(1)先将可再分散乳胶粉投入10倍于其重量份的水中,搅拌分散均匀后,加入其它剩余成分,搅拌分散1-2h,将所得物料投入球磨机中球磨处理,使所得物料的万孔筛余量≤0.05%;
(2)将步骤(1)所得的物料在80-100℃下干燥,保持物料的含水率≤0.02%,随后将粉体研磨分散40-50min后送入模具中压制成型,在氮气氛围下以650-700℃的温度烧结4-6h后,经自然冷却至室温即得。