CN104087795A - 一种led用防潮防裂铝基复合散热材料 - Google Patents

一种led用防潮防裂铝基复合散热材料 Download PDF

Info

Publication number
CN104087795A
CN104087795A CN201410322200.9A CN201410322200A CN104087795A CN 104087795 A CN104087795 A CN 104087795A CN 201410322200 A CN201410322200 A CN 201410322200A CN 104087795 A CN104087795 A CN 104087795A
Authority
CN
China
Prior art keywords
parts
heat dissipation
aluminum
powder
led
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410322200.9A
Other languages
English (en)
Other versions
CN104087795B (zh
Inventor
施凯
周仁林
张军
朱忠平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Sunny Electric Group Co Ltd
Original Assignee
Anhui Sunny Electric Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Sunny Electric Group Co Ltd filed Critical Anhui Sunny Electric Group Co Ltd
Priority to CN201410322200.9A priority Critical patent/CN104087795B/zh
Publication of CN104087795A publication Critical patent/CN104087795A/zh
Application granted granted Critical
Publication of CN104087795B publication Critical patent/CN104087795B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及灯具散热材料，具体涉及一种LED用防潮防裂铝基复合散热材料及其生产方法，该散热材料由以下重量份的原料制成：铝82-85、氮化铝12-14、六铝酸钙4-5、硼砂1-2、霞石粉2-3、黑晶粉1-2、硅溶胶3-5、膨胀玻化微珠8-10、可再分散乳胶粉6-8、助剂4-5；本发明的散热材料综合了铝、氮化铝、膨胀玻化微珠、助剂等成分的优点，兼具良好的导热和绝缘性能，硅溶胶和可再分散乳胶粉的加入可以促进原料成型，改善烧结效果，制得的散热材料结构致密，表面光洁度高，极具装饰效果，同时还有优良的防水阻潮能力，耐温性能好，不易开裂，更为经久耐用，其良好的散热能力有效的保护LED灯具，大大延长灯具的使用寿命。

Description

一种LED用防潮防裂铝基复合散热材料
技术领域
本发明涉及灯具散热材料，具体涉及一种LED用防潮防裂铝基复合散热材料及其生产方法。
背景技术
LED被称为第四代光源，具有节能、环保、安全、低能耗、高亮度等优点，在日常生活中被广泛使用，LED灯体本身的散热性能至关重要，直接影响到灯具的使用寿命和照明效果。现有的LED散热材料主要是由铝、铜等金属材料制成，在实际使用中存在成本限制、绝缘性能不够等缺点，因此很有必要改进材料的配方，使材料达到更为良好的散热效果，改善灯具的使用性能，延长使用寿命。
发明内容
本发明的目的在于，提供一种LED用防潮防裂铝基复合散热材料，使得材料不仅具有良好散热能力，还具有良好的使用性能，更为经久耐用，为了实现上述目的，本发明采用的技术方案如下：
一种LED用防潮防裂铝基复合散热材料，其特征在于，本发明材料由以下重量份的原料制成：铝82-85、氮化铝12-14、六铝酸钙4-5、硼砂1-2、霞石粉2-3、黑晶粉1-2、硅溶胶3-5、膨胀玻化微珠8-10、可再分散乳胶粉6-8、助剂4-5。
所述的助剂由以下重量份的原料制成：聚合硫酸铝4-5、动物骨8-10、钠砂1-3、聚酰亚胺4-5、银包铜粉8-10、氧化镁12-14、轻质碳酸镁5-8，制备方法为：先将动物骨在800-900℃温度下煅烧10-12h后冷却备用，再将聚合硫酸铝溶于适量水中配制成浓度为4-6%的水溶液，并将煅烧后的动物骨与其它剩余成分投入溶液中，混合搅拌分散2-3h后浓缩干燥，研磨成300-400目细粉，即得。
所述的一种LED用防潮防裂铝基复合散热材料，其制作工艺包含以下步骤：
（1）先将可再分散乳胶粉投入10倍于其重量份的水中，搅拌分散均匀后，加入其它剩余成分，搅拌分散1-2h，将所得物料投入球磨机中球磨处理，使所得物料的万孔筛余量≤0.05%；
（2）将步骤（1）所得的物料在80-100℃下干燥，保持物料的含水率≤0.02%，随后将粉体研磨分散40-50min后送入模具中压制成型，在氮气氛围下以650-700℃的温度烧结4-6h后，经自然冷却至室温即得。
本发明的优点在于：较传统铝质散热材料在原料上综合了铝、氮化铝、六铝酸钙、膨胀玻化微珠、助剂等成分的优点，兼具良好的导热和绝缘性能，硅溶胶和可再分散乳胶粉的加入可以促进原料成型，改善烧结效果，最后烧结制得的散热材料结构致密，表面光洁度高，极具装饰效果，同时还有优良的防水阻潮能力，耐温性能好，不易开裂，更为经久耐用，其良好的散热能力有效的保护LED灯具，大大延长灯具的使用寿命。
具体实施方式
实施例
本实施例LED散热材料由以下重量份原料制成：铝85、氮化铝14、六铝酸钙5、硼砂2、霞石粉3、黑晶粉2、硅溶胶5、膨胀玻化微珠10、可再分散乳胶粉8、助剂5。
所述的助剂由以下重量份的原料制成：聚合硫酸铝5、动物骨10、钠砂3、聚酰亚胺5、银包铜粉10、氧化镁14、轻质碳酸镁5，制备方法为：先将动物骨在800-900℃温度下煅烧10-12h后冷却备用，再将聚合硫酸铝溶于适量水中配制成浓度为6%的水溶液，并将煅烧后的动物骨与其它剩余成分投入溶液中，混合搅拌分散3h后浓缩干燥，研磨成400目细粉，即得。
所述的一种LED用防潮防裂铝基复合散热材料，其制作工艺包含以下步骤：
（1）先将可再分散乳胶粉投入10倍于其重量份的水中，搅拌分散均匀后，加入其它剩余成分，搅拌分散2h，将所得物料投入球磨机中球磨处理，使所得物料的万孔筛余量≤0.05%；
（2）将步骤（1）所得的物料在80-100℃下干燥，保持物料的含水率≤0.02%，随后将粉体研磨分散40min后送入模具中压制成型，在氮气氛围下以650-700℃的温度烧结6h后，经自然冷却至室温即得。
本实施例所制得的散热材料较常规LED用散热材料的导热系数较常规铝基散热材料提高24.8%，热扩散率提高25.4%，热平衡时间平均缩短152min，灯具使用寿命提高28.2%。

Claims (2)

1.一种LED用防潮防裂铝基复合散热材料，其特征在于，该散热由以下重量份的原料制成：铝82-85、氮化铝12-14、六铝酸钙4-5、硼砂1-2、霞石粉2-3、黑晶粉1-2、硅溶胶3-5、膨胀玻化微珠8-10、可再分散乳胶粉6-8、助剂4-5；
所述的助剂由以下重量份的原料制成：聚合硫酸铝4-5、动物骨8-10、钠砂1-3、聚酰亚胺4-5、银包铜粉8-10、氧化镁12-14、轻质碳酸镁5-8，制备方法为：先将动物骨在800-900℃温度下煅烧10-12h后冷却备用，再将聚合硫酸铝溶于适量水中配制成浓度为4-6%的水溶液，并将煅烧后的动物骨与其它剩余成分投入溶液中，混合搅拌分散2-3h后浓缩干燥，研磨成300-400目细粉，即得。
2.如权利要求1所述的一种LED用防潮防裂铝基复合散热材料，其生产方法如下：
（1）先将可再分散乳胶粉投入10倍于其重量份的水中，搅拌分散均匀后，加入其它剩余成分，搅拌分散1-2h，将所得物料投入球磨机中球磨处理，使所得物料的万孔筛余量≤0.05%；
（2）将步骤（1）所得的物料在80-100℃下干燥，保持物料的含水率≤0.02%，随后将粉体研磨分散40-50min后送入模具中压制成型，在氮气氛围下以650-700℃的温度烧结4-6h后，经自然冷却至室温即得。
CN201410322200.9A 2014-07-08 2014-07-08 一种led用防潮防裂铝基复合散热材料 Active CN104087795B (zh)