CN104087129B - Bicycle use paint base composition - Google Patents
Bicycle use paint base composition Download PDFInfo
- Publication number
- CN104087129B CN104087129B CN201410358850.9A CN201410358850A CN104087129B CN 104087129 B CN104087129 B CN 104087129B CN 201410358850 A CN201410358850 A CN 201410358850A CN 104087129 B CN104087129 B CN 104087129B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- base composition
- paint base
- dispersions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Disclosure one bicycle use paint base composition, belongs to technical field of coatings。The present invention counts by weight, with water-based epoxy acrylic resin 55 parts～65 parts, aqueous pu dispersions 20 parts～30 parts, water soluble amino resin 8 parts～12 parts, hexamethylene diisocyanate 10 parts～15 parts, ethanol 5 parts～8 parts, glycerol 0.1 part～1 part, propandiol butyl ether 1 part～2 parts, sodium carboxymethyl cellulose 0.01 part～0.1 part, pigment 5 parts～30 parts, silicone oil 0.2 part～0.5 part and deionized water 50 parts～65 parts are prepared from for raw material。The present invention is the paint base composition of a kind of environment-friendly type。
Description
Technical field
The invention belongs to technical field of coatings, particularly relate to a kind of bicycle use paint base composition。
Background technology
Priming paint is the ground floor of paint system, for improving the adhesive force of finish paint, increasing the richness of finish paint, offer alkali resistance, offer anti-corrosion function etc., can ensure that the uniform pickup of finish paint simultaneously, is that paint system plays optimum efficiency。
Traditional bicycle use priming paint is usually solvent bottom paint, and containing substantial amounts of hazardous solvent, workmen and contactee, in construction and use procedure, can be caused certain injury by these solvents。
Summary of the invention
Present invention solves the technical problem that the bicycle use paint base composition being to provide a kind of environment-friendly type。
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is:
It is made up of the raw material of following parts by weight:
Water-based epoxy acrylic resin 55 parts～65 parts, aqueous pu dispersions 20 parts～30 parts, water soluble amino resin 8 parts～12 parts, hexamethylene diisocyanate 10 parts～15 parts, ethanol 5 parts～8 parts, glycerol 0.1 part～1 part, propandiol butyl ether 1 part～2 parts, sodium carboxymethyl cellulose 0.01 part～0.1 part, pigment 5 parts～30 parts, silicone oil 0.2 part～0.5 part and deionized water 50 parts～65 parts；
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put in reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, standby；
B, by above-mentioned water-based epoxy acrylic resin, aqueous pu dispersions, water soluble amino resin, glycerol, propandiol butyl ether, sodium carboxymethyl cellulose, pigment, silicone oil, the intermediate product I that deionized water and step A prepare is put in high speed dispersor, disperses 4 hours～6 hours with the rotating speeds of 900 revs/min～1000 revs/min, prepares。
Owing to adopting technique scheme, the present invention obtains providing the benefit that:
1, combination property of the present invention is good。
2, the present invention is the bicycle use paint base composition of a kind of environment-friendly type, does not all have the volatilization of hazardous solvent in work progress and use procedure。
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described, and protection scope of the present invention is not intended to be limited to following example。
Embodiment 1
The raw material of preparing of this bicycle use paint base composition is: water-based epoxy acrylic resin 5.5kg, aqueous pu dispersions 2.0kg, water soluble amino resin 1.2kg, hexamethylene diisocyanate 1.5kg, ethanol 0.8kg, glycerol 0.1kg, propandiol butyl ether 0.2kg, sodium carboxymethyl cellulose 0.01kg, pigment 3.0kg, silicone oil 0.05kg and deionized water 6.5kg；
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put in reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, standby；
B, by above-mentioned water-based epoxy acrylic resin, aqueous pu dispersions, water soluble amino resin, glycerol, propandiol butyl ether, sodium carboxymethyl cellulose, pigment, silicone oil, the intermediate product I that deionized water and step A prepare is put in high speed dispersor, disperses 6 hours with the rotating speeds of 900 revs/min, prepares。
Embodiment 2
The raw material of preparing of this bicycle use paint base composition is: water-based epoxy acrylic resin 6.0kg, aqueous pu dispersions 2.5kg, water soluble amino resin 1.0kg, hexamethylene diisocyanate 1.2kg, ethanol 0.7kg, glycerol 0.05kg, propandiol butyl ether 0.15kg, sodium carboxymethyl cellulose 0.005kg, pigment 2.0kg, silicone oil 0.04kg and deionized water 6.0kg；
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put in reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, standby；
B, by above-mentioned water-based epoxy acrylic resin, aqueous pu dispersions, water soluble amino resin, glycerol, propandiol butyl ether, sodium carboxymethyl cellulose, pigment, silicone oil, the intermediate product I that deionized water and step A prepare is put in high speed dispersor, disperses 4 hours with the rotating speeds of 1000 revs/min, prepares。
Embodiment 3
The raw material of preparing of this bicycle use paint base composition is: water-based epoxy acrylic resin 6.5kg, aqueous pu dispersions 3.0kg, water soluble amino resin 0.8kg, hexamethylene diisocyanate 1.0kg, ethanol 0.5kg, glycerol 0.01kg, propandiol butyl ether 0.1kg, sodium carboxymethyl cellulose 0.001kg, pigment 0.5kg, silicone oil 0.02kg and deionized water 5.0kg；
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put in reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, standby；
B, by above-mentioned water-based epoxy acrylic resin, aqueous pu dispersions, water soluble amino resin, glycerol, propandiol butyl ether, sodium carboxymethyl cellulose, pigment, silicone oil, the intermediate product I that deionized water and step A prepare is put in high speed dispersor, disperses 5 hours with the rotating speeds of 950 revs/min, prepares。
The bicycle use paint base composition that embodiment 1～3 prepares is carried out performance detection, and its result is as shown in table 1。
Table 1
Claims (1)
1. a bicycle use paint base composition, it is characterised in that be made up of the raw material of following parts by weight:
Water-based epoxy acrylic resin 55 parts～65 parts, aqueous pu dispersions 20 parts～30 parts, water soluble amino resin 8 parts～12 parts, hexamethylene diisocyanate 10 parts～15 parts, ethanol 5 parts～8 parts, glycerol 0.1 part～1 part, propandiol butyl ether 1 part～2 parts, sodium carboxymethyl cellulose 0.01 part～0.1 part, pigment 5 parts～30 parts, silicone oil 0.2 part～0.5 part and deionized water 50 parts～65 parts；
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put in reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, standby；
B, by above-mentioned water-based epoxy acrylic resin, aqueous pu dispersions, water soluble amino resin, glycerol, propandiol butyl ether, sodium carboxymethyl cellulose, the intermediate product I that pigment, silicone oil, deionized water and step A prepare is put in high speed dispersor, disperse 4 hours～6 hours with the rotating speeds of 900 revs/min～1000 revs/min, prepare。