CN104087095B - 一种环保型高弹性纯丙外墙涂料及其制备方法 - Google Patents
一种环保型高弹性纯丙外墙涂料及其制备方法 Download PDFInfo
- Publication number
- CN104087095B CN104087095B CN201410321632.8A CN201410321632A CN104087095B CN 104087095 B CN104087095 B CN 104087095B CN 201410321632 A CN201410321632 A CN 201410321632A CN 104087095 B CN104087095 B CN 104087095B
- Authority
- CN
- China
- Prior art keywords
- pure
- environment
- friendly type
- wall paint
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种环保型高弹性纯丙外墙涂料及其制备方法，所述涂料的各组分和质量百分含量分别是：水8‑12％，KT‑02纯丙弹性乳液40‑49％，ZT‑6500高档硅丙乳液3‑8％，金红石型钛白粉10‑16％，煅烧高岭土5‑12％，方解石粉4‑10％，云母粉4～10％，高效成膜助剂JS‑PPH(302)1‑5％，3％羟丙基甲基纤维素溶液1～3％，强力杀菌防腐剂981为0.1～1％，润湿剂405为0.1‑1％，强力分散剂0.1‑0.5％，增稠剂AR－2为0.1‑0.5％，消泡剂OS‑5201为0.1～0.5％。本发明的涂料具有持久的柔韧性和优良的伸长性、惊人的回弹性、耐高温性、耐候性、高耐水、高耐碱、耐酸、耐人工老化性、耐紫外线、耐化学品性，疏水、抗污染、附着力极强的优点。
Description
技术领域
本发明属于涂料技术领域，涉及一种建筑涂料，更具体地说是涉及一种环保型高弹性纯丙外墙涂料及其制备方法，主要应用于建筑外墙涂料领域。
背景技术
目前，建筑外墙墙体伸缩裂纹80％以上的机率发生在寒冷的冬季，随着时间的延长裂缝会逐渐加大，对建筑物产生不利影响甚至危害，可能引起混凝土内部钢筋锈蚀，影响建筑物的使用功能和使用寿命。为了防止建筑外墙墙体伸缩裂纹的发生，尽快解决建筑外墙墙体伸缩裂纹这个难题，本申请的发明人通过研究试验发现并充分证实，在建筑外墙涂料中采用KT-02纯丙弹性乳液，具有抗污染能力强，韧性好的特点，KT-02纯丙弹性乳液与一般弹性乳液相比，具备更高的抗拉强度和延伸率，能有效抵御水泥墙体的微小裂纹；在建筑外墙涂料中使用ZT-6500高档硅丙乳液，能有机地结合了有机硅耐高温性、耐候性、耐化学品性、疏水、表面能低不易污染和丙烯酸类树脂的高保色性、柔韧性、附着性好的特点，使其具有高耐候、耐水、耐酸、耐碱、抗沾污、涂膜不泛黄、耐紫外线、抗老化、硬度高的优异性能。本发明通过使用上述两种乳液复合和填料以及各种助剂互配，实现了性能互补，从而达到了所发明的环保型高弹性纯丙外墙涂料具有惊人的回弹性、持久的柔韧性和优良的伸长率，以及适应建筑物表面的“活”裂纹产生的运动，能遮盖墙体的毛细裂缝，使刷涂的建筑表面具有优异的效果。
发明内容
本发明的一种环保型高弹性纯丙外墙涂料，各组分和质量百分含量分别是：水为8-12％，KT-02纯丙弹性乳液为40-49％，ZT-6500高档硅丙乳液为3-8％，金红石型钛白粉为10-16％，煅烧高岭土为5-12％，方解石粉为4-10％，云母粉为4～10％，高效成膜助剂JS-PPH(302)为1-5％，3％羟丙基甲基纤维素溶液为1～3％，强力杀菌防腐剂981为0.1～1％，润湿剂405为0.1-1％，强力分散剂为0.1-0.5％，增稠剂AR－2为0.1-0.5％，消泡剂OS-5201为0.1～0.5％。
其中所述3％羟丙基甲基纤维素溶液是指羟丙基甲基纤维素3斤加97斤水，室温浸泡12小时备用。
所述的金红石型钛白粉、煅烧高岭土的粒径均为1205目。
所述的方解石粉、云母粉的粒径均为1000目。
本发明的一种环保型高弹性纯丙外墙涂料的制备方法，具体步骤是：
在1000-2800r/min高速搅拌的条件下，先将配方中的水，KT-02纯丙弹性乳液，ZT-6500高档硅丙乳液分别加入搅拌容器中搅拌20-25分钟，再分别加入金红石型钛白粉、煅烧高岭土、方解石粉、云母粉搅拌30-40分钟；再分别加入3％羟丙基甲基纤维素溶液、高效成膜助剂JS-PPH(302)搅拌30-35分钟，最后分别加入强力杀菌防腐剂981、润湿剂405、强力分散剂，增稠剂AR－2，消泡剂OS-5201继续搅拌30-35分钟，即得到环保型高弹性纯丙外墙涂料。
本发明中使用KT-02纯丙弹性乳液和ZT-6500高档硅丙乳液制备得到的环保型高弹性纯丙外墙涂料，具有持久的柔韧性和优良的伸长性、惊人的回弹性、耐高温性、耐候性、高耐水、高耐碱、耐酸、耐人工老化性、耐紫外线、耐化学品性，疏水、抗污染、附着力好等优点。
本发明中使用KT-02纯丙弹性乳液，具有抗污染能力强，韧性好，与一般弹性乳液相比，具备更高的抗拉强度和延伸率，能有效抵御水泥墙体的微小裂纹；使用ZT-6500高档硅丙乳液，有机地结合了有机硅耐高温性、耐候性、耐化学品性，疏水、表面能低不易污染性和丙烯酸类树脂的高保色性、柔韧性、附着性，具有高耐候、耐水、耐酸、耐碱、抗沾污、涂膜不泛黄、耐紫外线、抗老化，胶膜致密、坚韧、硬度高极好的优点；使用羟丙基甲基纤维素具有增稠、粘合、分散、乳化、成膜、悬浮、保持水分和保护胶体等性能；使用润湿剂X-405对改善乳液稳定和乳胶涂料体系的冻融稳定性十分有效；使用水性涂料增稠剂AR－2能使乳胶涂料体系粘度增大，具有防沉效果，兼有分散乳化作用，稳定性好，不霉变，流变性佳，使用简便，安全性高；使用金红石型钛白粉，光泽好，遮盖力和流动性强，具有极佳的耐候性和抗粉化性能，防止裂纹，防止紫外线等；使用超细煅烧高岭土具有良好的遮盖力，能替代部分钛白粉用量，降低涂料成本，并改善涂料的存储稳定性，增强耐刷性、耐候性，提高涂层的抗冲击性能；使用超细方解石粉提高遮盖率，改善填充材料的性能以及具有增强和补强等功能，能增强附着力、抗氧化、增加填量、降低成本等优点；使用超细云母粉可以减少紫外线或其它光和热对涂膜的损坏，增加涂层的耐酸碱和电绝缘性能，提高涂层的耐久性，抗冻性，抗腐蚀性，抗透水性，增强涂膜与基质附着力，提高涂膜强度，光亮度，坚韧性和密实性，降低涂层的透气性，防止斑点和龟裂，还可以防止涂料沉淀。使用强力分散剂具有卓越的分散能力，极佳的去污能力，良好的吸附，湿润性能。
本发明的一种环保型高弹性纯丙外墙涂料所具有的优点和有益效果：
本发明的涂料绿色环保，具有持久的柔韧性和优良的伸长性、惊人的回弹性、耐高温性、耐候性、高耐水、高耐碱、耐酸、耐人工老化性、耐紫外线、耐化学品性，疏水、抗污染、附着力极强等优点。有很好的推广价值和发展前景。
具体实施方式
下面结合具体实施例对本发明的技术方案作进一步的详细说明：
一、本发明各组分的来源：
水(本地)，KT-02纯丙弹性乳液(青岛古道化学材料有限公司工业级产品)，ZT-6500高档硅丙乳液(合肥明月化工建材有限公司工业级产品)，高效成膜助剂JS-PPH(302)(上海锦山化工有限公司工业级产品)，金红石型钛白粉1205目(廊坊蓝科化工有限公司工业级产品)，煅烧高岭土1250目(扬州帝蓝化工原料有限公司工业级产品)，方解石粉1000目(淄博玲斐工贸有限公司工业级产品),云母粉1000目(河北石家庄灵寿县云母化有限公司工业级产品),3％羟丙基甲基纤维素溶液(上海齐硕实业有限公司工业级产品),强力杀菌防腐剂981(上海集益化工有限公司工业级产品),润湿剂405(广州通济贸易工业级产品)，强力分散剂(北京工达伟业科学技术研究中心工业级产品)，增稠剂AR－2(南通市晗泰化工有限公司工业级产品)，消泡剂OS-5201(广州冠志化工有限公司工业级产品)。
二、按质量百分含量实施例1—6配方表：
三、实施例1-6的制备方法
在1000-2800r/min高速搅拌的条件下，先将配方中的水，KT-02纯丙弹性乳液，ZT-6500高档硅丙乳液分别加入搅拌容器中搅拌20-25分钟，再分别加入金红石型钛白粉、煅烧高岭土、方解石粉、云母粉搅拌30-40分钟；再分别加入3％羟丙基甲基纤维素溶液、高效成膜助剂JS-PPH(302)搅拌30-35分钟，最后分别加入强力杀菌防腐剂981、润湿剂405、强力分散剂，增稠剂AR－2，消泡剂OS-5201继续搅拌30-35分钟，即得到环保型高弹性纯丙外墙涂料。
四、实施例1—6所得产品性能检测结果如下表所示：
Claims (5)
1.一种环保型高弹性纯丙外墙涂料，其特征在于：所述涂料按质量百分含量由：水为8-12％，KT-02纯丙弹性乳液为40-49％，ZT-6500高档硅丙乳液为3-8％，金红石型钛白粉为10-16％，煅烧高岭土为5-12％，方解石粉为4-10％，云母粉为4～10％，高效成膜助剂JS-PPH(302)为1-5％，3％羟丙基甲基纤维素溶液为1～3％，强力杀菌防腐剂981为0.1～1％，润湿剂405为0.1-1％，强力分散剂为0.1-0.5％，增稠剂AR－2为0.1-0.5％，消泡剂OS-5201为0.1～0.5％组成。
2.根据权利要求1所述的环保型高弹性纯丙外墙涂料，其特征在于：所述的3％羟丙基甲基纤维素溶液是指羟丙基甲基纤维素为3斤加97斤水，室温浸泡12小时备用。
3.根据权利要求1所述的环保型高弹性纯丙外墙涂料，其特征在于：所述的金红石型钛白粉、煅烧高岭土的粒径均为1205目。
4.根据权利要求1所述的环保型高弹性纯丙外墙涂料，其特征在于：所述的方解石粉、云母粉的粒径均为1000目。
5.一种根据权利要求1所述的环保型高弹性纯丙外墙涂料的制备方法，其特征在于：具体步骤是：在1000-2800r/min高速搅拌的条件下，先将配方中的水，KT-02纯丙弹性乳液，ZT-6500高档硅丙乳液分别加入搅拌容器中搅拌20-25分钟，再分别加入金红石型钛白粉、煅烧高岭土、方解石粉、云母粉搅拌30-40分钟；再分别加入3％羟丙基甲基纤维素溶液、高效成膜助剂JS-PPH(302)搅拌30-35分钟，最后分别加入强力杀菌防腐剂981、润湿剂405、强力分散剂、增稠剂AR－2、消泡剂OS-5201，继续搅拌30-35分钟，即得到环保型高弹性纯丙外墙涂料。