CN104087078B - 环保型封闭建筑外墙漆及其制备方法 - Google Patents

环保型封闭建筑外墙漆及其制备方法 Download PDF

Info

Publication number
CN104087078B
CN104087078B CN201410321619.2A CN201410321619A CN104087078B CN 104087078 B CN104087078 B CN 104087078B CN 201410321619 A CN201410321619 A CN 201410321619A CN 104087078 B CN104087078 B CN 104087078B
Authority
CN
China
Prior art keywords
back cover
wall paint
external wall
friendly type
environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410321619.2A
Other languages
English (en)
Other versions
CN104087078A (zh
Inventor
郭文录
张秀荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Shuangshan Energy Saving Technology Co.,Ltd.
Original Assignee
Jiangsu University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu University of Science and Technology filed Critical Jiangsu University of Science and Technology
Priority to CN201410321619.2A priority Critical patent/CN104087078B/zh
Publication of CN104087078A publication Critical patent/CN104087078A/zh
Application granted granted Critical
Publication of CN104087078B publication Critical patent/CN104087078B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保型封闭建筑外墙漆及其制备方法，所述的外墙漆按质量百分含量由组分：水为25‑30％，ZS‑6501封底乳液为28‑35％，A‑90抗碱封底乳液为28‑35％，高效成膜助剂JS‑PPH(302)为1‑4％，超细云母粉为4‑9％，防霉防腐剂SPM为0.2‑1％，GHP‑102增稠剂为0.2～1.2％，有机硅消泡剂JS‑2010S为0.2‑1％组成。本发明的外墙漆绿色环保，渗透力强，具有超长的防水性、极强的抗碱性、优异的粘结力，封闭作用好等优点，能长久保持建筑物靓丽外观。

Description

环保型封闭建筑外墙漆及其制备方法
技术领域
本发明属于涂料技术领域，涉及一种建筑涂料，更具体地说是涉及一种环保型封闭建筑外墙漆及其制备方法，主要应用于建筑外墙涂料领域。
背景技术
随着环保要求的逐步提高，各国对VOC含量的限制日益严格，现有的溶剂型外墙漆的使用日益受到一定的限制。目前，封闭建筑外墙漆已正在开始向环境友好型，VOC含量低的方向发展。普通封闭外墙乳液，由于耐水性、耐碱性较差，不能有效防止墙体的盐碱析出而使面漆发花、发白、变色等缺陷的产生。为了能有效防止墙体的盐碱析出而使面漆发花、发白、变色等缺陷的产生，本申请的发明人通过研究试验发现并充分证实，在建筑外墙涂料中采用ZS—6501封底乳液和A-90抗碱封底乳液形成复合体系，用复合乳液、填料及各种助剂配置的耐碱性封闭建筑外墙漆，由于性能互补，协同效应，粒径小，渗透力强，能对盐碱毛细孔进行有效封闭，同时与基材有适度交联形成极佳封闭性,阻断盐碱从混凝土毛细孔中渗出.防止涂料泛碱起霜，用它配制成的封闭建筑外墙底漆具有突出的防水性，抗碱性，优异的粘结力，以确保外墙涂层的装饰效果。
发明内容
本发明为解决现有技术问题和缺陷，所采取的技术方案是：
一种环保型封闭建筑外墙漆，按质量百分含量由组分：水为25-30％，ZS-6501封底乳液为28-35％，A-90抗碱封底乳液为28-35％，高效成膜助剂JS-PPH(302)为1-4％，超细云母粉为4-9％，防霉防腐剂SPM为0.2-1％，GHP-102增稠剂为0.2～1.2％，有机硅消泡剂JS-2010S为0.2-1％组成。
其中所述的超细云母粉的粒径为1250目。
本发明的一种环保型封闭建筑外墙漆的制备方法，包括下列步骤：
1.按配方计量将水加入搅拌容器中，以800-900r/min的转速启动搅拌器，加入超细云母粉搅拌20-25min；
2.在1000-2800r/min高速搅拌下，分别将配方ZS-6501封底乳液、A-90抗碱封底乳液、高效成膜助剂JS-PPH加入搅拌容器中搅拌15-20min，然后再分别加入GHP-102增稠剂、防霉防腐剂SPM、有机硅消泡剂JS-2010S继续搅拌30-35min，即得到环保型封闭建筑外墙漆。
本发明中使用ZS—6501封底乳液是为专门解决混凝土、水泥砂浆所存在的泛碱、泛盐的缺陷，提高内外墙乳胶漆装饰效果，使其具有极强的附着力抗碱性；使用A-90抗碱封底乳液是为专门解决混凝土泛碱而影响涂层的一种苯丙乳液,适用于混凝土表面，具有突出的抗碱功能,并有较好的透气性，用它也可配置耐碱性乳胶漆，其耐碱、耐水已达到非常令人满意的效果；使用超细云母粉可以减少紫外线或其它光和热对涂膜的损坏，增加涂层的耐酸碱和电绝缘性能，提高涂层的耐久性，抗冻性，抗腐蚀性，抗透水性，增强涂膜与基质附着力，提高涂膜强度，光亮度，坚韧性和密实性，降低涂层的透气性，防止斑点和龟裂，还可以防止涂料沉淀。
本发明中采用ZS—6501封底乳液和A-90抗碱封底乳液形成复合体系，使用复合乳液、填料及各种助剂配置的耐碱性封闭建筑外墙漆，由于性能互补，协同效应，粒径小，渗透力强，能对盐碱毛细孔进行有效封闭，同时与基材有适度交联形成极佳封闭性,阻断盐碱从混凝土毛细孔中渗出.防止涂料泛碱起霜，用它配制成的封闭建筑外墙底漆具有突出的防水性，抗碱性，并具有优异的粘结力，以确保外墙涂层的装饰效果。该外墙漆绿色环保，渗透力强，具有超长的防水性、极强的抗碱性、优异的粘结力、封闭作用好等优点，长久保持建筑物靓丽外观，具有广阔的市场前景。
具体实施方式
下面结合具体实施例对本发明的技术方案作进一步的详细说明：
一、本发明各组分的来源：
水(本地)，ZS-6501封底乳液(江苏紫石化工科技有限公司工业级产品)，A-90抗碱封底乳液(上海振洲化工涂料有限公司工业级产品)，高效成膜助剂JS-PPH(302)(上海锦山化工有限公司工业级产品)，超细云母粉(河北石家庄灵寿县云母化有限公司工业级产品)，防霉防腐剂SPM(广州市卓洲贸易有限公司工业级产品)，GHP-102增稠剂(深圳市吉田化工 有限公司工业级产品)，有机硅消泡剂JS-2010S(上海锦山化工有限公司工业级产品)。
二、按质量百分含量实施例1—5配方表：
各组分含量(质量百分数) 实施例1 实施例2 实施例3 实施例4 实施例5
水 28 26 25 30 27
ZS-6501封底乳液 30 35 28 30 29
A-90抗碱封底乳液 30 28 35 33 32
高效成膜助剂JS-PPH(302) 4 3.5 3 2 1
超细云母粉(1250目) 5 6 8 4 9
防霉防腐剂SPM 1 0.3 0.2 0.4 0.3
GHP-102增稠剂 1 1 0.5 0.2 1.2
有机硅消泡剂JS-2010S 1 0.2 0.3 0.4 0.5
三、实施例1-5的制备方法
1.按配方计量将水加入搅拌容器中，以800-900r/min的转速启动搅拌器，加入超细云母粉搅拌20-25min；
2.在1000-2800r/min高速搅拌下，分别将配方ZS-6501封底乳液、A-90抗碱封底乳液、高效成膜助剂JS-PPH加入搅拌容器中搅拌15-20min，然后再分别加入GHP-102增稠剂、防霉防腐剂SPM、有机硅消泡剂JS-2010S继续搅拌30-35min，即得到环保型封闭建筑外墙漆。
四、实施例1—5所得产品性能检测结果如下表所示：

Claims (2)

1.一种环保型封闭建筑外墙漆，其特征在于，按质量百分含量由组分：水为25-30％，ZS-6501封底乳液为28-35％，A-90抗碱封底乳液为28-35％，高效成膜助剂JS-PPH(302)为1-4％，超细云母粉为4-9％，防霉防腐剂SPM为0.2-1％，GHP-102增稠剂为0.2～1.2％，有机硅消泡剂JS-2010S为0.2-1％组成；其中，所述的超细云母粉的粒径为1250目。
2.一种根据权利要求1所述的环保型封闭建筑外墙漆的制备方法，其特征在于，包括下列步骤：
(1).按配方计量将水加入搅拌容器中，以800-900r/min的转速启动搅拌器，加入超细云母粉搅拌20-25min；
(2).在1000-2800r/min高速搅拌下，分别将配方ZS-6501封底乳液、A-90抗碱封底乳液、高效成膜助剂JS-PPH加入搅拌容器中搅拌15-20min，然后再分别加入GHP-102增稠剂、防霉防腐剂SPM、有机硅消泡剂JS-2010S继续搅拌30-35min，即得到环保型封闭建筑外墙漆。
CN201410321619.2A 2014-07-07 2014-07-07 环保型封闭建筑外墙漆及其制备方法 Active CN104087078B (zh)