CN104087019A - Navy blue or black disperse dye composition - Google Patents

Navy blue or black disperse dye composition Download PDF

Info

Publication number
CN104087019A
CN104087019A CN201310729233.0A CN201310729233A CN104087019A CN 104087019 A CN104087019 A CN 104087019A CN 201310729233 A CN201310729233 A CN 201310729233A CN 104087019 A CN104087019 A CN 104087019A
Authority
CN
China
Prior art keywords
work
formula
dyestuff
time
suc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310729233.0A
Other languages
Chinese (zh)
Other versions
CN104087019B (en
Inventor
赵敏
燕美芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai ANOKY Textile Chemicals Co Ltd
Original Assignee
Shanghai ANOKY Textile Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai ANOKY Textile Chemicals Co Ltd filed Critical Shanghai ANOKY Textile Chemicals Co Ltd
Priority to CN201310729233.0A priority Critical patent/CN104087019B/en
Publication of CN104087019A publication Critical patent/CN104087019A/en
Application granted granted Critical
Publication of CN104087019B publication Critical patent/CN104087019B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a navy blue or black disperse dye composition. The navy blue or black disperse dye composition contains one or more of dye A shown as formula (I), one or more of dye B shown as formula (II), one or more of dye C shown as formula (III) and one or more of dye D shown as formula (IV). The navy blue or black disperse dye composition provided by the invention has the characteristics of high chromogenic intensity, excellent lifting power and excellent color fastness when applied in textile dyeing, can reach the dyeing depth consistent with conventional fastness dyes, and does not contain 24 kinds of forbidden aromatic amines or forbidden carcinogenic and allergenic dyes, etc. and meets the requirements of environmental protection. (formula (I), formula (II), formula (III), formula (IV)).

Description

A kind of navy or black disperse dye composition
Technical field
The present invention relates to field of fine chemical, be specifically related to a kind of navy or black disperse dye disperse dye composition.
Background technology
Monoazo type dispersed dye so that its synthesis technique is simple, cheap, chromatogram is complete, application and the reason such as fastness ability is good, particularly in the dyeing of trevira goods and stamp, occupy critical role at hydrophobic fibre, be widely used dispersed dye.
In recent years, along with the enhancing of people's environmental consciousness and health perception, human consumer is also more and more higher for the requirement of the aspect such as dyefastness grade and ecological performance of textiles.For dispersed dye, the product that is still conventional fastness requirement of widely applying in the market, as the disperse navy blue EXN-SF that combines with C.I. EX-SF DISPERSE BLUE EX-SF 300 291: 1, C.I. 63 ,DIS,PER,SE ,Vio,let, 63 93, DISPERSE ORANGE 30 200 288 and disperse black EXN-SF, these dyestuffs shortcoming to some extent still aspect its washing fastness and sublimation fastness in the time of dyeing and printing process.Along with people are more and more higher to the requirement of textile product, can predict and have compared with the dispersed dye product of high washing fastness and sublimation fastness and will there is very large market potential.
Summary of the invention
Technical problem solved by the invention is, a kind of navy or black disperse dye composition are provided.When disperse dye composition of the present invention is applied to textile dyeing, there is very high coloring intensity, good lifting force and good dyefastness, can reach the dye level consistent with conventional fastness dyestuff, and do not contain 24 kinds of forbidding aromatic amines, the carcinogenic sensitization dye etc. that does not contain forbidding meets environmental requirement.
The invention provides a kind of navy or black disperse dye composition, its comprise one or more suc as formula the dyestuff A shown in (I), one or more suc as formula the dyestuff B shown in (II), one or more are suc as formula the dyestuff C shown in (III), and one or more are suc as formula the dyestuff D shown in (IV); Described one or more weight contents suc as formula the dyestuff A shown in (I) are 2～30%; Described one or more weight contents suc as formula the dyestuff B shown in (II) are 20～90%; Described one or more weight contents suc as formula the dyestuff C shown in (III) are 2～50%; Described one or more weight contents suc as formula the dyestuff D shown in (IV) are 2～30%; Described weight content refers to that this component accounts for the massfraction of described disperse dye composition gross weight;
Wherein, R 1, R 2and R 3in have a H or halogen atom at least, R 4and R 5in have a H or halogen atom at least;
R 1for H, C 1～C 4alkyl, c 1～C 4the formamido group, benzamido that replace of alkyl, or halogen;
R 7for C 1～C 4alkyl, phenyl or benzyl;
R 2, R 3be H, C independently of one another 1～C 4the formamido group, benzamido that replace of alkyl, or halogen;
R 4, R 5be independently of one another H, halogen,
R 6for H, C 1～C 4alkyl, cyclohexyl, C 1～C 4alkoxyl group replace C 1～C 4alkyl;
R 8, R 9be H ,-NO independently of one another 2,-CN, halogen or C 1～C 4alkoxyl group, and R 8, R 9when different, be-NO 2;
R 10for H, hydroxyl or C 1～C 4alkyl;
R 11for H or C 1～C 4alkoxyl group;
R 12, R 13be H, C independently of one another 1～C 4alkyl, allyl group, benzyl, wherein n is 1 or 2, R 22for methyl, ethyl, phenyl or benzyl, but R 12, R 13when different, be H or benzyl; And for dyestuff B, work as R 8for-NO 2, R 9during for halogen, or R 9for-NO 2, R 8during for halogen, R 12, R 13in have at most one for C 1～C 4alkyl, allyl group, benzyl or
Described R 1in, described C 1～C 4alkyl preferable methyl or ethyl.Described C 1～C 4alkyl replace the preferred kharophen of formamido group.The preferred chlorine or bromine of described halogen.Described R 1r 7in, described C 1～C 4alkyl preferable methyl or ethyl.
Described R 2, R 3in, described C 1～C 4alkyl replace the preferred kharophen of formamido group.The preferred chlorine or bromine of described halogen.Described R 2, R 3r 7in, described C 1～C 4alkyl preferable methyl or ethyl.
Described R 4, R 5in, the preferred chlorine or bromine of described halogen.
Described R 8, R 9in, the preferred chlorine or bromine of described halogen.Described C 1～C 4the preferred methoxy or ethoxy of alkoxyl group.
Described R 10in, described in preferably kharophen, propionamido or benzamido.Described C 1～C 4alkyl preferable methyl.
Described R 11in, described C 1～C 4the preferred methoxy or ethoxy of alkoxyl group.
Described R 12, R 13in, described C 1～C 4the preferred ethyl of alkyl.Described preferably described preferably or described preferably described preferably or
Described is preferably following arbitrary compound suc as formula the dyestuff A shown in (I):
Work as R 1during for Cl, R 2for Cl, R 3for H, R 4for H, R 5for H, R 6for C 2h 5;
Work as R 1during for H, R 2for H, R 3for Cl, R 4for Cl, R 5for H, R 6for H;
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for r 4for H, R 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1during for Cl, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1during for H, R 2for r 3for r 4for H, R 5for H, R 6for cyclohexyl;
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for CF 3, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for Cl, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for CN, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for NO 2, R 5for Br, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for r 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for r 4for r 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for H, R 4for H, R 5for r 6for
Work as R 1during for H, R 2for H, R 3for H, R 4for H, R 5for r 6for
Work as R 1during for H, R 2for H, R 3for r 4for H, R 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for r 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Described is preferably following arbitrary compound suc as formula the dyestuff B shown in (II):
Described is preferably following arbitrary compound suc as formula the dyestuff C shown in (III):
Described is preferably following arbitrary compound suc as formula the dyestuff D shown in (IV):
In described navy or black disperse dye composition, described one or more weight contents suc as formula the dyestuff A shown in (I) are preferably 5～25%, and more preferably 5～20%.
In described navy or black disperse dye composition, described one or more weight contents suc as formula the dyestuff B shown in (II) are preferably 25～85%, and more preferably 40～75%.
In described navy or black disperse dye composition, described one or more weight contents suc as formula the dyestuff C shown in (III) are preferably 4～35%, and more preferably 6～25%.
In described navy or black disperse dye composition, described one or more weight contents suc as formula the dyestuff D shown in (IV) are preferably 4～20%, and more preferably 5～15%.
In described navy or black disperse dye composition, dyestuff A, dyestuff B, dyestuff C and dyestuff D all can be prepared by methods such as diazotization well known to those skilled in the art, couplings, and its preparation condition and step all can be selected with reference to this type of reaction of this area routine.
The invention provides a kind of navy or black disperse dye, it comprises above-mentioned navy or black disperse dye composition and auxiliary agent.
Described auxiliary agent all can adopt commercially available prod, is generally dispersion agent and/or diffusant that dispersed dye are conventional.Described dispersion agent and/or diffusant can be dispersion agent and/or the diffusant of this area routine, preferably include one of following or its mixture: dispersion agent NNO (naphthalenesulfonic acid-formaldehyde condensate), sulfonated lignin, Dispersant MF (methyl naphthalene sulfonate formaldehyde condensate), dispersing agent C NF (benzyl naphthalenesulfonic acid-formaldehyde condensate), more preferably Dispersant MF and/or sodium lignosulfonate.
In described navy or black disperse dye, the weight ratio of described navy or black disperse dye composition and auxiliary agent preferably 1: (0.6～5), more preferably 1: (0.6～3).
The present invention also provides the preparation method of above-mentioned navy or black disperse dye, and it is following either method:
Method one comprises the steps: one or more suc as formula the described dyestuff A shown in (I), one or more are suc as formula the described dyestuff B shown in (II), after one or more mix suc as formula the described dyestuff D shown in (IV) suc as formula the described dyestuff C shown in (III) and one or more, under the existence of described auxiliary agent and water, grinding distribution, then spraying is dry;
Method two comprise the steps: by one or more suc as formula the described dyestuff A shown in (I), one or more suc as formula the described dyestuff B shown in (II), one or more suc as formula the described dyestuff C shown in (III) and one or more suc as formula the described dyestuff D shown in (IV) respectively under the existence of described auxiliary agent and water, after grinding distribution, spraying are dry, mix.
Described grinding distribution can use the pulverizer of this area routine.Described pulverizer can be sand mill or shredder.
The present invention also provides the application in printed fabrics of described navy or black disperse dye.
Described application preferably comprises following steps: described navy or black disperse dye are mixed with water, under acidic conditions, be warming up to 50～70 DEG C (preferably 60～70 DEG C), put into fabric, in 20～50 minutes (preferably 30～40 minutes), temperature is risen to 120～135 DEG C (preferably 125～130 DEG C), be incubated 30～60 minutes (preferably 40～50 minutes), be cooled to 70～90 DEG C (preferably 80～90 DEG C).
Described fabric refers generally to hydrophobic fibre goods, preferably contains the goods of trevira.
Described acidic conditions preferably regulates by acetic acid, pH value preferably 4～5.
In described application, described cooling after, also can comprise reduction clearing step.Described reduction clearing step preferably includes: fabric is put into the aqueous solution that contains 1 grams per liter caustic soda and 3 grams per liter vat powders, clean at 60～90 DEG C (preferably 70～80 DEG C), the time is 10～30 minutes (preferably 15～20 minutes).
Described vat powder refers to V-Brite B.
Without prejudice to the field on the basis of common sense, above-mentioned each optimum condition, can arbitrary combination, obtains the preferred embodiments of the invention.
Agents useful for same of the present invention and raw material be commercially available obtaining all.
Positive progressive effect of the present invention is: disperse dye composition of the present invention, meet environmental protection and the ecological requirement of Oeko-Tex Standard100, and can be applied to the dyeing that hydrophobic fibre goods particularly contain trevira goods.The dyeing articles obtaining has the features such as dye uptake is high, depth good, lifting force is excellent, dyefastness is excellent, good level-dyeing property.
Embodiment
Mode below by embodiment further illustrates the present invention, but does not therefore limit the present invention among described scope of embodiments.The experimental technique of unreceipted actual conditions in the following example, according to ordinary method and condition, or selects according to catalogue.
Embodiment 1
Former dyestuff A1 shown in formula (I) is got to 2 grams, A18 and get 8 grams, former dyestuff B1 shown in formula (II) gets 5 grams, B30 and gets 7.5 grams, former dyestuff C6 shown in formula (III) gets 12.5 grams, former dyestuff D3 shown in formula (IV) gets 15 grams, add again 153 gram one of 67 grams of Dispersant MF, 8 grams of sodium lignosulfonates, water to reinstate sand mill and carry out dispersion treatment, spraying is dry again, obtains dye composite of the present invention.
Embodiment 2～27
According to the preparation method of embodiment 1, press the data shown in table 5 respectively by least one dyestuff A, at least one dyestuff B, at least one dyestuff C, at least one dyestuff D and Dispersant MF, sodium lignosulfonate and water blending, sand milling disperses, the dry finished product dispersed dye that obtain of spraying.Wherein, dyestuff A, B, C, D by the defined structural formula of each substituting group in table 1～table 4.
Embodiment 28
Respectively getting dispersed dye that 2.5 grams of embodiment 1～27 make is dispersed in 500 ml waters and becomes dye suspensions, drawing respectively 20 milliliters mixes with the water of 80 milliliters, adjusting dye bath pH with acetic acid is 4～5, being warming up to 70 DEG C puts into 5 grams of polyester fiber cloths simultaneously and dyes, in 30 minutes, be warming up to 130 DEG C by 70 DEG C, be incubated 50 minutes, be cooled to 90 DEG C of following drainings and clean.Cloth specimen is put into 100 milliliters of reduction clearing liquid containing 1 grams per liter caustic soda and 3 grams per liter vat powders again and cleaned in 80 DEG C, the time is 20 minutes.Measure embodiment 1～27 by GB GB/T2397-2003 and make the lifting force of dispersed dye, adopt that GB GB/T3921-2008, GB/T3920-2008, GB/T8427-2008, GB/T5718-1997 test respectively that it is water-fastness, rub resistance, colour fastness to light and sub limation fastness.Test result is in table 6.
Comparative example 1
The dyestuff of getting 2.5 grams of black EXN-SF300% of commercial dispersion repeats the performance test methods of embodiment 28.Test result is in table 6.
Comparative example 2
The dyestuff of getting 2.5 grams of commercial disperse navy blue EXN-SF300% repeats the performance test methods of embodiment 28.Test result is in table 6.
Table 6
From result in table 6, dye composite of the present invention has better dyefastness than the black EXN-SF300% of the dispersion being most widely used in the market and disperse navy blue EXN-SF300%.

Claims (10)

1. a navy or black disperse dye composition, it is characterized in that: comprise one or more suc as formula the dyestuff A shown in (I), one or more suc as formula the dyestuff B shown in (II), one or more are suc as formula the dyestuff C shown in (III), and one or more are suc as formula the dyestuff D shown in (IV); Described one or more weight contents suc as formula the dyestuff A shown in (I) are 2～30%; Described one or more weight contents suc as formula the dyestuff B shown in (II) are 20～90%; Described one or more weight contents suc as formula the dyestuff C shown in (III) are 2～50%; Described one or more weight contents suc as formula the dyestuff D shown in (IV) are 2～30%; Described weight content refers to that this component accounts for the massfraction of described disperse dye composition gross weight;
Wherein, R 1, R 2and R 3in have a H or halogen atom at least, R 4and R 5in have a H or halogen atom at least;
R 1for H, C 1～C 4alkyl, c 1～C 4the formamido group, benzamido that replace of alkyl, or halogen;
R 7for C 1～C 4alkyl, phenyl or benzyl;
R 2, R 3be H, C independently of one another 1～C 4the formamido group, benzamido that replace of alkyl, or halogen;
R 4, R 5be independently of one another H, halogen,
R 6for H, C 1～C 4alkyl, cyclohexyl, C 1～C 4alkoxyl group replace C 1～C 4alkyl;
R 8, R 9be H ,-NO independently of one another 2,-CN, halogen or C 1～C 4alkoxyl group, and R 8, R 9when different, be-NO 2;
R 10for H, hydroxyl or C 1～C 4alkyl;
R 11for H or C 1～C 4alkoxyl group;
R 12, R 13be H, C independently of one another 1～C 4alkyl, allyl group, benzyl, wherein n is 1 or 2, R 22for methyl, ethyl, phenyl or benzyl, but R 12, R 13when different, be H or benzyl; And for dyestuff B, work as R 8for-NO 2, R 9during for halogen, or R 9for-NO 2, R 8during for halogen, R 12, R 13in have at most one for C 1～C 4alkyl, allyl group, benzyl or
2. navy as claimed in claim 1 or black disperse dye composition, is characterized in that: described R 1in, described C 1～C 4alkyl be methyl or ethyl; Described C 1～C 4alkyl replace formamido group be kharophen; Described halogen is chlorine or bromine; Described R 1r 7in, described C 1～C 4alkyl be methyl or ethyl.
3. navy as claimed in claim 1 or black disperse dye composition, is characterized in that: described R 2, R 3in, described C 1～C 4alkyl replace formamido group be kharophen; Described halogen is chlorine or bromine; Described R 2, R 3r 7in, described C 1～C 4alkyl be methyl or ethyl;
Described R 4, R 5in, described halogen is chlorine or bromine;
Described R 8, R 9in, described halogen is chlorine or bromine; Described R 8, R 9in, described C 1～C 4alkoxyl group be methoxy or ethoxy.
4. navy as claimed in claim 1 or black disperse dye composition, is characterized in that: described R 10in, described in for kharophen, propionamido or benzamido; Described C 1～C 4alkyl be methyl;
Described R 11in, described C 1～C 4alkoxyl group be methoxy or ethoxy;
Described R 12, R 13in, described C 1～C 4alkyl be ethyl; Described for described for or described for described for or
5. navy as claimed in claim 1 or black disperse dye composition, is characterized in that: described is following arbitrary compound suc as formula the dyestuff A shown in (I):
Work as R 1during for Cl, R 2for Cl, R 3for H, R 4for H, R 5for H, R 6for C 2h 5;
Work as R 1during for H, R 2for H, R 3for Cl, R 4for Cl, R 5for H, R 6for H;
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for r 4for H, R 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1during for Cl, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for NO 2, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1during for H, R 2for r 3for r 4for H, R 5for H, R 6for cyclohexyl;
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for CF 3, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for Cl, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for CN, R 5for H, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for NO 2, R 5for Br, R 6for
Work as R 1for NO 2time, R 2for H, R 3for H, R 4for r 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for r 4for r 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for H, R 4for H, R 5for r 6for
Work as R 1during for H, R 2for H, R 3for H, R 4for H, R 5for r 6for
Work as R 1during for H, R 2for H, R 3for r 4for H, R 5for H, R 6for
Work as R 1during for H, R 2for H, R 3for r 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
Work as R 1for time, R 2for H, R 3for H, R 4for H, R 5for H, R 6for
6. navy as claimed in claim 1 or black disperse dye composition, is characterized in that: described is the arbitrary compound of following B1～B40 suc as formula the dyestuff B shown in (II):
。
7. navy as claimed in claim 1 or black disperse dye composition, is characterized in that: described is the arbitrary compound of following C1～C15 suc as formula the dyestuff C shown in (III):
。
8. navy as claimed in claim 1 or black disperse dye composition, is characterized in that: described is the arbitrary compound of following D1～D16 suc as formula the dyestuff D shown in (IV):
。
9. navy as claimed in claim 1 or black disperse dye composition, is characterized in that: in described navy or black disperse dye composition, described one or more weight contents suc as formula the dyestuff A shown in (I) are 5～25%; Described one or more weight contents suc as formula the dyestuff B shown in (II) are 25～85%; Described one or more weight contents suc as formula the dyestuff C shown in (III) are 4～35%; Described one or more weight contents suc as formula the dyestuff D shown in (IV) are 4～20%.
10. navy as claimed in claim 9 or black disperse dye composition, is characterized in that: in described navy or black disperse dye composition, described one or more weight contents suc as formula the dyestuff A shown in (I) are 5～20%; Described one or more weight contents suc as formula the dyestuff B shown in (II) are 40～75%; Described one or more weight contents suc as formula the dyestuff C shown in (III) are 6～25%; Described one or more weight contents suc as formula the dyestuff D shown in (IV) are 5～15%.
CN201310729233.0A 2013-12-25 2013-12-25 A kind of navy or black disperse dye composition Active CN104087019B (en)