CN104072844B - 一种漫射农膜 - Google Patents

一种漫射农膜 Download PDF

Info

Publication number
CN104072844B
CN104072844B CN201410271127.7A CN201410271127A CN104072844B CN 104072844 B CN104072844 B CN 104072844B CN 201410271127 A CN201410271127 A CN 201410271127A CN 104072844 B CN104072844 B CN 104072844B
Authority
CN
China
Prior art keywords
plastic sheeting
farm use
diffusion
matrix resin
masterbatch
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410271127.7A
Other languages
English (en)
Other versions
CN104072844A (zh
Inventor
徐刚
梁溥森
熊斌
李育坚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Institute of Energy Conversion of CAS
Original Assignee
Guangzhou Institute of Energy Conversion of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Institute of Energy Conversion of CAS filed Critical Guangzhou Institute of Energy Conversion of CAS
Priority to CN201410271127.7A priority Critical patent/CN104072844B/zh
Publication of CN104072844A publication Critical patent/CN104072844A/zh
Application granted granted Critical
Publication of CN104072844B publication Critical patent/CN104072844B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种漫射农膜，由漫射母料与基体树脂混合均匀后通过吹塑成型而制备，以LDPE作为基体树脂，其特征在于，所述漫射母料中含有氧化锌或氧化镁中的至少一种。氧化锌、氧化镁均与基体树脂LDPE的折射率存在较大差异，且对红外光具有一定屏蔽作用。本发明制备出的漫射农膜，具有实现光线在棚内照射的均匀度、减少光线直射造成的阴影面积及和对农作物的伤害，同时氧化锌和氧化镁均对红外光具有较好的屏蔽性能，故该农膜还有较好的保温性能，与传统农膜相比，可提高棚内温度2-3℃，这在一定程度上实现的温室效应，从而达到提高农作物产量的效果。

Description

一种漫射农膜
技术领域
本发明涉及一种农用薄膜的配方，尤其是可实现光线透过薄膜后以散射或漫射的形式照射到农作物上的农膜。
背景技术
传统的透明农膜，阳光直射透过为主，在背阳面的农作物就无法接受阳光而实现光合作用。且农作物自身的上部也会对下部造成遮挡，造成对农作物的阳光照射不均匀，部分在接受阳光照射，另一部分却因为遮挡阴影的出现而无法进行光合作用。而在夏天时候，在阳光直射下的农作物则会局部的高温，引起植物细胞、生物膜的半透性丧失、蛋白质的钝化和变形，严重时可引起植物的死亡。传统的农膜，对大棚内不同位置的农作物或同株农作物出现生长不均一现象，难以起到改善作用，农作物的产量会由于照射光线不均匀的因素而受到影响。
公开号为CN102186333A的中国专利，公开了一种通过辊压使薄膜的单面呈现凹凸状的光散射农用薄膜。该方法生散光农膜，需要对现有设备进行升级改造，并且由于农膜的基体材料为PE，很薄且较软，极易在使用过程中对辊压形成的散光作用的凹凸部位造成伤害。故需要新的、在不增加设备投入的前提下，快速高效的生产出可实现光线透过薄膜后产生高比例散射或漫射的农膜，对于农业应用领域具有重大的意义。
发明内容
本发明提供一种漫射农膜，无需辊压凹凸面，通过改良制造农膜的配方直接生产可得。
本发明漫射农膜，由漫射母料与基体树脂混合均匀后通过吹塑成型而制备，以LDPE(低密度聚乙烯)作为基体树脂，其特征在于，所述漫射母料中含有氧化锌或氧化镁中的至少一种。
进一步的，所述漫射母料按照重量的配比如下：
LDPE：6-10份
LLDPE(线性低密度聚乙烯)：1-4份
氧化锌或氧化镁中的至少一种：共0.8-1.5份
滑石粉：0.8-1.5份
硬脂酸镁：0.4-1份
聚乙烯蜡：0.2-0.4份
将配比好的漫射母料搅拌均匀，与基体树脂LDPE按照重量比1:10-40的比例加热挤出吹塑成型得到漫射农膜。
本发明在农膜的母料成份中引入了与基体树脂LDPE折射率差异较大的氧化锌或氧化镁作为主要添加剂，实现了薄膜对入射光线的有效散射，改变透过农膜的光线的传递方向，使得农作物的各个部位均能接受到合适的阳光照射，保证生长的进行，从而提高农作物的产量。尤其在夏天高温时，阳光以漫射形式照射到农作物表面，可有效减弱强辐射中的直射光对作物局部的伤害。其次，因为氧化锌和氧化镁均对红外光具有较好的屏蔽性能，故该农膜还有较好的保温性能，与传统农膜相比，可提高棚内温度2-3℃，这在一定程度上实现的温室效应。
所述母料中还添加有润滑剂滑石粉、硬脂酸镁和聚乙烯蜡。它们的配合可大大改善母粒的造粒加工工艺，因为氧化锌或氧化镁的摩擦系数较大，直接与LDPE共混制备母粒加工有难度，故添加滑石粉、硬脂酸镁和聚乙烯蜡作为润滑剂来改善母料的加工性能。
较佳地，在吹塑成型阶段，选择性添加颜料、流滴剂、抗氧化剂、抗紫外剂的一种或多种以实现漫射农膜的多功能化，并有利于提高农膜的使用寿命。
本发明制备出的漫射农膜，具有实现光线在棚内照射的均匀度、减少光线直射造成的阴影面积及和对农作物的伤害，同时氧化锌和氧化镁均对红外光具有较好的屏蔽性能，故该农膜还有较好的保温性能，与传统农膜相比，可提高棚内温度2-3℃，这在一定程度上实现的温室效应，从而达到提高农作物产量的效果。
附图说明
图1为实施例1的漫射农膜与传统农膜的光线总透射率曲线。
图2为实施例1的漫射农膜与传统农膜的漫射光线透过率曲线。
其中N表示市场购买的传统农膜；S表示实施例1所制备的漫射农膜。
具体实施方式
下面结合附图对本发明作进一步的说明，本发明不限于以下实施例。
实施例1
漫射母料以重量比按如下的配方制备：
LDPE：7.5份；LLDPE：2.5份；氧化锌：1份；滑石粉：1份；硬脂酸镁：0.5份；聚乙烯蜡：0.3份。
农膜制备方法：将配比好的母料搅拌均匀，使所有的添加料均匀的粘附在塑料的表面，上挤出机，挤出造粒。以LDPE作为基体树脂，按照母料:基体树脂＝1:20的比例进行吹塑成膜，制备薄膜的厚度为0.03mm。在吹塑之前，加入酞菁蓝染料、流滴剂和抗紫外剂，使得制备的农膜在具备散射透过阳光的同时具备蓝色、抗流滴性和抗老化性能的高性能农膜。
如附图所示，其中N表示市场购买的传统农膜；S表示实施例1所制备的漫射农膜。按照本发明制备的农膜与市场上购买的传统农膜的整体透光性能基本一致，但其散射透过光所占的比例大大高于市场购买农膜，这使得太阳光在透过农膜后主要以散射光的形式照射到农作物表面，可有效的减少阴影的比例，从而提高光合作用面积。
实施例2
漫射母料以重量比按如下的配方制备：
LDPE：10份；LLDPE：1份；氧化镁：1.5份；滑石粉：1份；硬脂酸镁：0.8份；聚乙烯蜡：0.2份。
农膜制备方法：将配比好的母料搅拌均匀，使所有的添加料均匀的粘附在塑料的表面，上挤出机，挤出造粒。以LDPE作为基体树脂，按照母料:基体树脂＝1:10的比例进行吹塑成膜，制备薄膜的厚度为0.1mm。在吹塑之前，加入流滴剂和抗紫外剂，使得制备的农膜在具备散射透过阳光的同时具备抗流滴性和抗老化性能的乳白色高性能、长寿命散射农膜。
实施例3
漫射母料以重量比按如下的配方制备：
LDPE：9份；LLDPE：2份；氧化锌：0.6份；氧化镁：0.7份；滑石粉：0.8份；硬脂酸镁：1份；聚乙烯蜡：0.4份。
农膜制备方法：将配比好的母料搅拌均匀，使所有的添加料均匀的粘附在塑料的表面，上挤出机，挤出造粒。以LDPE作为基体树脂，按照母料:基体树脂＝1:40的比例进行吹塑成膜，制备薄膜的厚度为0.02mm。在吹塑之前，加入从市场购买流滴剂和抗紫外剂，使得制备的农膜在具备散射透过阳光的同时具备抗流滴性和抗老化性能的乳白色高性能、长寿命散射农膜。
实施例4
漫射母料以重量比按如下的配方制备：
LDPE：6份；LLDPE：4份；氧化锌：0.8份；滑石粉：1.5份；硬脂酸镁：0.4份；聚乙烯蜡：0.3份。
农膜制备方法：将配比好的母料搅拌均匀，使所有的添加料均匀的粘附在塑料的表面，上挤出机，挤出造粒。以LDPE作为基体树脂，按照母料:基体树脂＝1:35的比例进行吹塑成膜，制备薄膜的厚度为0.03mm。在吹塑之前，加入从市场购买流滴剂和抗紫外剂，使得制备的农膜在具备散射透过阳光的同时具备抗流滴性和抗老化性能的乳白色高性能、长寿命散射农膜。
实施例5
漫射母料以重量比按如下的配方制备：
LDPE：10份；LLDPE：2份；氧化镁：0.8份；滑石粉：1份；硬脂酸镁：1份；聚乙烯蜡：0.4份。
农膜制备方法：将配比好的母料搅拌均匀，使所有的添加料均匀的粘附在塑料的表面，上挤出机，挤出造粒。以LDPE作为基体树脂，按照母料:基体树脂＝1:40的比例进行吹塑成膜，制备薄膜的厚度为0.03mm。在吹塑之前，加入从市场购买流滴剂和抗紫外剂，使得制备的农膜在具备散射透过阳光的同时具备抗流滴性和抗老化性能的乳白色高性能、长寿命散射农膜。

Claims (2)

1.一种漫射农膜，由漫射母料与基体树脂混合均匀后通过吹塑成型而制备，以LDPE作为基体树脂，所述漫射母料中含有氧化锌或氧化镁中的至少一种；其特征在于，所述漫射母料按照重量的配比如下：
LDPE：6-10份
LLDPE：1-4份
氧化锌或氧化镁中的至少一种：共0.8-1.5份
滑石粉：0.8-1.5份
硬脂酸镁：0.4-1份
聚乙烯蜡：0.2-0.4份
将配比好的漫射母料搅拌均匀，与基体树脂LDPE按照重量比1:10-40的比例加热挤出吹塑成型得到漫射农膜。
2.如权利要求1所述的漫射农膜，其特征在于：在吹塑成型阶段，选择性添加颜料、流滴剂、抗氧化剂、抗紫外剂的一种或多种以实现漫射农膜的多功能化。
CN201410271127.7A 2014-06-17 2014-06-17 一种漫射农膜 Active CN104072844B (zh)