CN104059457A - 一种水性防腐涂料 - Google Patents
一种水性防腐涂料 Download PDFInfo
- Publication number
- CN104059457A CN104059457A CN201410303897.5A CN201410303897A CN104059457A CN 104059457 A CN104059457 A CN 104059457A CN 201410303897 A CN201410303897 A CN 201410303897A CN 104059457 A CN104059457 A CN 104059457A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- agent
- anticorrosive paint
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种水性防腐涂料，由以下重量份的组分构成：钛白粉22-25份、滑石粉10-25份、轻质碳酸钙10-15份、重质碳酸钙5-10份、云母粉5-8份、增稠剂溶液8-10份、分散剂1.0-1.4份、丙烯酸弹性树脂乳液35-40份、防霉剂0.1-0.2份、消泡剂0.05-0.2份、正丁醇2-4份、纯净水7-11份、芳烃混合溶剂30-40份、硫酸钡8-10份、膨润土2-5份、流平剂0.6-1份、改性氨类固化剂5-10份。
Description
技术领域
本发明涉及建筑涂料领域，具体涉及一种水性防腐涂料。
背景技术
传统的溶剂型防腐涂料会排放大量的VOC，对生活环境及人们的身体健康都有潜在的威胁。水性防腐涂料主要是以水为溶剂和分散剂，与溶剂型防腐涂料相比生产和运输过程更加安全，不含或含有少量溶剂，VOC释放量极低，适用于室内及室外环境。目前，水性防腐涂料几乎已达到溶剂型防腐涂料的性能。但是，水性丙烯酸防腐涂料成膜机理复杂，附着力较水性环氧稍欠缺；水性无机硅酸锌防腐涂料对基面处理要求过高，而且不使用面漆时易形成高浓度锌盐；水性聚氨酯性能很好，但成本较高。
发明内容
本发明的目的是解决现有的技术缺陷，提供一种新型耐高温绝缘涂料。
本发明所采用的技术方案是：一种水性防腐涂料，由以下重量份的组分构成 ：钛白粉22-25 份、滑石粉10-25份、轻质碳酸钙10-15份、重质碳酸钙5-10份、云母粉5-8份、增稠剂溶液8-10份、分散剂1.0-1.4份、丙烯酸弹性树脂乳液35-40份、防霉剂0.1-0.2份、消泡剂0.05-0.2 份、正丁醇2-4份、纯净水7-11 份、芳烃混合溶剂30-40 份、硫酸钡8-10份、膨润土2-5份、流平剂0.6-1 份、改性氨类固化剂5-10 份。
上述的流平剂为经过聚醚改性的聚硅氧烷。
本发明的有益效果是：涂料的防腐性能好，不会挥发出VOC等有毒物质。采用聚硅氧烷作为流平剂，可以促使涂料在干燥成膜过程中形成一个平整、光滑、均匀的涂膜。
具体实施方式
下面结合具体实施例来对本发明作进一步的描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例1
一种水性防腐涂料，由以下重量份的组分构成 ：钛白粉22份、滑石粉10份、轻质碳酸钙10份、重质碳酸钙5份、云母粉5份、增稠剂溶液8份、分散剂1.0份、丙烯酸弹性树脂乳液35份、防霉剂0.1份、消泡剂0.05份、正丁醇2份、纯净水7份、芳烃混合溶剂30份、硫酸钡8份、膨润土2份、流平剂0.6份、改性氨类固化剂5份。流平剂为经过聚醚改性的聚硅氧烷。
实施例2
一种水性防腐涂料，由以下重量份的组分构成 ：钛白粉23份、滑石粉20份、轻质碳酸钙13份、重质碳酸钙8份、云母粉7份、增稠剂溶液9份、分散剂1.2份、丙烯酸弹性树脂乳液38份、防霉剂0.15份、消泡剂0.1份、正丁醇3份、纯净水9份、芳烃混合溶剂35份、硫酸钡9份、膨润土4份、流平剂0.8份、改性氨类固化剂8份。流平剂为经过聚醚改性的聚硅氧烷。
实施例3
一种水性防腐涂料，由以下重量份的组分构成 ：钛白粉25份、滑石粉25份、轻质碳酸钙15份、重质碳酸钙10份、云母粉8份、增稠剂溶液10份、分散剂1.4份、丙烯酸弹性树脂乳液40份、防霉剂0.2份、消泡剂0.2 份、正丁醇4份、纯净水11 份、芳烃混合溶剂40份、硫酸钡10份、膨润土5份、流平剂1份、改性氨类固化剂10 份。流平剂为经过聚醚改性的聚硅氧烷。
上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进，这些改进也应视为本发明的保护范围。
Claims (2)
1.一种水性防腐涂料，其特征在于，由以下重量份的组分构成 ：钛白粉22-25 份、滑石粉10-25 份、轻质碳酸钙10-15份、重质碳酸钙5-10份、云母粉5 -8 份、增稠剂溶液8-10份、分散剂1.0-1.4份、丙烯酸弹性树脂乳液35-40份、防霉剂0.1-0.2 份、消泡剂0.05-0.2 份、正丁醇2-4份、纯净水7-11 份、芳烃混合溶剂40 份、硫酸钡8-10份、膨润土2-5份、流平剂0.6 份、改性氨类固化剂25份。
2.根据权利要求1所述的一种水性防腐涂料，其特征在于：所述的流平剂为经过聚醚改性的聚硅氧烷。