CN104046307A - High-temperature-resistant sealant - Google Patents
High-temperature-resistant sealant Download PDFInfo
- Publication number
- CN104046307A CN104046307A CN201410236754.7A CN201410236754A CN104046307A CN 104046307 A CN104046307 A CN 104046307A CN 201410236754 A CN201410236754 A CN 201410236754A CN 104046307 A CN104046307 A CN 104046307A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- kerosene
- ethanol
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A disclosed high-temperature-resistant sealant is prepared from the following raw materials in parts by weight: 6-10 parts of bamboo charcoal fiber, 4-8 parts of hollow bead, 8-14 parts of nitrile butadiene rubber, 10-20 parts of EVA thermoplastic elastomer, 6-12 parts of paraffin oil, 3-8 parts of graphene, 4-9 parts of isocyanate, 5-8 parts of aluminium hydroxide, 2-6 parts of terpene resin, 4-8 parts of gas-phase white carbon black, 7-11 parts of diaryl secondary amine, 7-14 parts of polysulfide rubber, 5-10 parts of zinc oxide, 10-20 parts of epoxy resin, 20-30 parts of acrylate emulsion, 8-16 parts of chitin, 7-9 parts of ethanol, 5-11 parts of kerosene, 5-8 parts of illite powder and 4-8 parts of attapulgite. The provided high-temperature-resistant sealant is excellent in waterproof performance and good in high-temperature resistance and flame resistance.
Description
Technical field
The present invention relates to fire-retardant material technical field, be specifically related to a kind of refractory seals glue.
Background technology
Seal gum is mainly used in various thing thing bondings or gap filling, and its function is mainly reflected in bonding and seals this two aspect.Due to the high speed development of every profession and trade, the Application Areas of seal gum constantly expands, and in some occasion, requires seal gum not only will possess the function of bonding and sealing, but also will possess the functions such as fire protection flame retarding.The fire prevention isolation of the various openings that fireproof elastic sealant forms while being mainly used in cable, airduct, oil pipe, tracheae etc. through wall, floor and cable testing bridge.Because of the requirement of particular surroundings, fireproof seal gum must have resistance to ray, resistance to ozone, cold-resistant, ageing-resistant, high temperature resistant, fire-retardant contour performance.That existing seal gum can not possess is simultaneously fire-retardant, radiation hardness, resistance to ozone, the property such as water-fast.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is that a kind of refractory seals glue with excellent water tolerance, resistance to elevated temperatures and good flame resistance is provided.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of refractory seals glue, raw material by following parts by weight is made: bamboo-carbon fibre 6-10 part, cenosphere 4-8 part, paracril 8-14 part, EVA thermoplastic elastomer 10-20 part, paraffin oil 6-12 part, Graphene 3-8 part, isocyanic ester 4-9 part, aluminium hydroxide 5-8 part, terpine resin 2-6 part, gas-phase silica 4-8 part, secondary diarylamine 7-11 part, thiorubber 7-14 part, zinc oxide 5-10 part, epoxy resin 10-20 part, acrylic ester emulsion 20-30 part, chitin 8-16 part, ethanol 7-9 part, kerosene 5-11 part, the stone flour 5-8 of Erie part, attapulgite 4-8 part.
Above-mentioned refractory seals glue, is made by the raw material of following parts by weight: 8 parts of bamboo-carbon fibres, 6 parts of cenospheres, 11 parts of paracrils, 15 parts of EVA thermoplastic elastomers, 10 parts of paraffin oils, 5 parts of Graphenes, 7 parts of isocyanic ester, 7 parts, aluminium hydroxide, 4 parts of terpine resins, 6 parts of gas-phase silicas, 9 parts of secondary diarylamine, 11 parts of thiorubber, 8 parts, zinc oxide, 15 parts of epoxy resin, 25 parts of acrylic ester emulsions, 12 parts of chitins, 8 parts of ethanol, 8 parts of kerosene, 6 parts of Erie's stone flours, 6 parts of attapulgites.
Refractory seals glue advantage of the present invention is:
1, refractory seals glue of the present invention, has excellent water tolerance, resistance to elevated temperatures and good flame resistance; The effectively effect of dust adsorption and objectionable impurities, decomposition peculiar smell and smelly eliminating.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1, and a kind of refractory seals glue is made by the raw material of following parts by weight: 6 parts of bamboo-carbon fibres, 4 parts of cenospheres, 8 parts of paracrils, 10 parts of EVA thermoplastic elastomers, 6 parts of paraffin oils, 3 parts of Graphenes, 4 parts of isocyanic ester, 5 parts, aluminium hydroxide, 2 parts of terpine resins, 4 parts of gas-phase silicas, 7 parts of secondary diarylamine, 7 parts of thiorubber, 5 parts, zinc oxide, 10 parts of epoxy resin, 20 parts of acrylic ester emulsions, 8 parts of chitins, 7 parts of ethanol, 5 parts of kerosene, 5 parts of Erie's stone flours, 4 parts of attapulgites.
Embodiment 2, and a kind of refractory seals glue is made by the raw material of following parts by weight: 8 parts of bamboo-carbon fibres, 6 parts of cenospheres, 11 parts of paracrils, 15 parts of EVA thermoplastic elastomers, 10 parts of paraffin oils, 5 parts of Graphenes, 7 parts of isocyanic ester, 7 parts, aluminium hydroxide, 4 parts of terpine resins, 6 parts of gas-phase silicas, 9 parts of secondary diarylamine, 11 parts of thiorubber, 8 parts, zinc oxide, 15 parts of epoxy resin, 25 parts of acrylic ester emulsions, 12 parts of chitins, 8 parts of ethanol, 8 parts of kerosene, 6 parts of Erie's stone flours, 6 parts of attapulgites.
Embodiment 3, and a kind of refractory seals glue is made by the raw material of following parts by weight: 10 parts of bamboo-carbon fibres, 8 parts of cenospheres, 14 parts of paracrils, 20 parts of EVA thermoplastic elastomers, 12 parts of paraffin oils, 8 parts of Graphenes, 9 parts of isocyanic ester, 8 parts, aluminium hydroxide, 6 parts of terpine resins, 8 parts of gas-phase silicas, 11 parts of secondary diarylamine, 14 parts of thiorubber, 10 parts, zinc oxide, 20 parts of epoxy resin, 30 parts of acrylic ester emulsions, 16 parts of chitins, 9 parts of ethanol, 11 parts of kerosene, 8 parts of Erie's stone flours, 8 parts of attapulgites.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, change, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (2)
1. a refractory seals glue, it is characterized in that: the raw material by following parts by weight is made: bamboo-carbon fibre 6-10 part, cenosphere 4-8 part, paracril 8-14 part, EVA thermoplastic elastomer 10-20 part, paraffin oil 6-12 part, Graphene 3-8 part, isocyanic ester 4-9 part, aluminium hydroxide 5-8 part, terpine resin 2-6 part, gas-phase silica 4-8 part, secondary diarylamine 7-11 part, thiorubber 7-14 part, zinc oxide 5-10 part, epoxy resin 10-20 part, acrylic ester emulsion 20-30 part, chitin 8-16 part, ethanol 7-9 part, kerosene 5-11 part, the stone flour 5-8 of Erie part, attapulgite 4-8 part.
2. refractory seals glue according to claim 1, is characterized in that: the raw material by following parts by weight is made: 8 parts of bamboo-carbon fibres, 6 parts of cenospheres, 11 parts of paracrils, 15 parts of EVA thermoplastic elastomers, 10 parts of paraffin oils, 5 parts of Graphenes, 7 parts of isocyanic ester, 7 parts, aluminium hydroxide, 4 parts of terpine resins, 6 parts of gas-phase silicas, 9 parts of secondary diarylamine, 11 parts of thiorubber, 8 parts, zinc oxide, 15 parts of epoxy resin, 25 parts of acrylic ester emulsions, 12 parts of chitins, 8 parts of ethanol, 8 parts of kerosene, 6 parts of Erie's stone flours, 6 parts of attapulgites.