CN104046188A - High-polymer biological composite coating material - Google Patents
High-polymer biological composite coating material Download PDFInfo
- Publication number
- CN104046188A CN104046188A CN201410297493.XA CN201410297493A CN104046188A CN 104046188 A CN104046188 A CN 104046188A CN 201410297493 A CN201410297493 A CN 201410297493A CN 104046188 A CN104046188 A CN 104046188A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- coating material
- composite coating
- biological composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-polymer biological composite coating material which is composed of the following components in parts by weight: 50-60 parts of silicone-acrylic emulsion, 15-20 parts of Pachystachys lutea cutting powder, 25-30 parts of rose cutting powder, 15-30 parts of peanut straw powder, 11-19 parts of carbamate, 20-25 parts of melamine resin, 11-16 parts of ash calcium powder, 60-75 parts of calcium carbonate, 6-9 parts of silicic acid cellucotton, 15-20 parts of kaolin, 10-15 parts of expanded perlite and 9-14 parts of magnesium hydroxide. The high-polymer biological composite coating material has the advantages of excellent high-temperature stability, high strength, wear resistance, high toughness, environment friendliness, flame retardancy, self-cleaning performance and thermal insulation, is convenient for construction and saves the cost.
Description
Technical field
The present invention relates to a kind of polymeric coating material.
Background technology
Modern society's energy consumption increases day by day, has consumed electric power resource and the coal resources of a large amount of preciousnesses.Along with people recognize the finiteness of resource and the ecocrisis that energy consumption causes gradually, energy-conservationly become environment protection and one of the important content that economizes on resources, thermal insulation technology is widely applied in each field, as various lagging materials, reflective insulation coating etc.Yet, tradition heat preserving and insulating material is to reduce thermal conductivity and transmissibility factor is main, fiber-like lagging material will be given full play to the effect of transmission of heat by convection and radiative transfer in environment for use, must use thick and heavy coating, and section bar class lagging material assembling construction is loaded down with trivial details, seam affect more attractive in appearance, work-ing life is shorter.At present, there is function singleness, effect is limited and validity period is short problem in the domestic thermal insulating coating on market, is difficult to widespread use, and import composite coating material is effective, purposes is wide, but price is higher, has increased production cost.Now oneself is through being penetrated into the industry-by-industry department of national economy for polymeric coating material, and it has the superior physicochemical properties such as good visible ray and infrared reflectivity, higher thermal infrared emittance, high-temperature stability.Therefore, a kind of energy-conserving and environment-protective, high strength are developed in design, the low-cost environment-friendly high polymer composite coating material that high temperature resistant, thermal insulation separation temp effect is good is technical problem urgently to be resolved hurrily.
Summary of the invention
Technical problem to be solved by this invention is: a kind of environmentally friendly high polymer composite coating material is provided, there is superior high-temperature stability, and high strength, wear-resisting, high tenacity, environmental protection, fire-retardant, self-cleaning, insulation, easy construction simultaneously, cost-saving.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A high-molecular biologic composite coating material, is comprised of the composition of following parts by weight: organosilicon crylic acid latex 50-60 part, Jinbaohua wood chip powder 15-20 part, rosewood crumbs powder 25-30 part, peanut stalk powder 15-30 part, carbamate 11-19 part, melmac 20-25 part, ash calcium powder 11-16 part, calcium carbonate 60-75 part, the cotton 6-9 part of silicate fiber, kaolin 15-20 part, pearlstone 10-15 part, magnesium hydroxide 9-14 part.
The invention has the beneficial effects as follows: there is superior high-temperature stability, high strength, wear-resisting, high tenacity, environmental protection, fire-retardant, self-cleaning, insulation, easy construction simultaneously, cost-saving.
Embodiment
Embodiment 1
A high-molecular biologic composite coating material, is comprised of the composition of following parts by weight: organosilicon crylic acid latex 50-60 part, Jinbaohua wood chip powder 15-20 part, rosewood crumbs powder 25-30 part, peanut stalk powder 15-30 part, carbamate 11-19 part, melmac 20-25 part, ash calcium powder 11-16 part, calcium carbonate 60-75 part, the cotton 6-9 part of silicate fiber, kaolin 15-20 part, pearlstone 10-15 part, magnesium hydroxide 9-14 part.
Claims (1)
1. a high-molecular biologic composite coating material, is comprised of the composition of following parts by weight: organosilicon crylic acid latex 50-60 part, Jinbaohua wood chip powder 15-20 part, rosewood crumbs powder 25-30 part, peanut stalk powder 15-30 part, carbamate 11-19 part, melmac 20-25 part, ash calcium powder 11-16 part, calcium carbonate 60-75 part, the cotton 6-9 part of silicate fiber, kaolin 15-20 part, pearlstone 10-15 part, magnesium hydroxide 9-14 part.