CN106673572A - Environment-friendly building material - Google Patents
Environment-friendly building material Download PDFInfo
- Publication number
- CN106673572A CN106673572A CN201510759422.1A CN201510759422A CN106673572A CN 106673572 A CN106673572 A CN 106673572A CN 201510759422 A CN201510759422 A CN 201510759422A CN 106673572 A CN106673572 A CN 106673572A
- Authority
- CN
- China
- Prior art keywords
- parts
- mesh
- environment
- building material
- hollow glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an environment-friendly building material. The environment-friendly building material is mainly used in building materials, and is prepared from the following components: calcium carbonate, kieselguhr, hollow glass microspheres, graphite powder, kaolin and the like. The environment-friendly building material has good heat insulation property, is long in service life and free from aging, has a function of corrosion prevention, and is good in non-combustion performance, thus having high social benefits and economic benefits.
Description
Technical field
The present invention relates to building material field, more particularly to a kind of building environment-friendly materials.
Background technology
In recent years, as national economic development enters the stage of high speed development, the industry such as domestic chemical industry, oil, electric power, metallurgy, light industry, food, medicine, traffic, national defence, to the annual requirement of insulation material up to 1,500,000,000 cubes.Wherein, to silicic acid read insulation material the market demand oneself reach 500,000,000 cubes, average annual demand amplification is up to more than 25%.Particularly country forces using the policy of high-quality insulation material to building industry, further expands the domestic demand for reading silicic acid insulation material.And the market demand for facing to grow at top speed and extensively application, silicic acid insulation material is put forward higher requirement, not only want thermal conductivity factor it is lower, using temperature is wider, bonding force is higher, and require that heat impact strength is good, do not ftracture, it is nontoxic dustless pollution-free.Existing silicic acid steamed bun insulation material can't reach the requirement of many applications.
The content of the invention
The technical problem to be solved is to provide a kind of building environment-friendly materials.
To solve above-mentioned technical problem, the technical solution used in the present invention is：
One kind building environment-friendly materials, including the material of following parts by weight：Calcium carbonate 30-50 parts, diatomite 10-11 parts, hollow glass micropearl 2-9 parts, graphite powder 1-9 parts, kaolin 3-7 parts, wood fibre（80-100 mesh）4-9 parts, diatomite（80-100 mesh）6-9 parts, perforate expanded perlite（20-120 mesh）7-8 parts, hollow glass micropearl（120-200 mesh）5-8 parts, lime 6-9 parts, gypsum 14-28 parts, nucleator 1-5 parts, talcum powder 2-4 parts, the nano combined environmental protection fire retarding agent 3-8 parts of antimony base, three fulminuric acid fat 5-9 part.
The invention has the beneficial effects as follows：It is long service life, not aging with good heat-insulating property, with anti-corrosion function, do not have good burning performance, Social benefit and economic benefit is high.
Specific embodiment
Presently preferred embodiments of the present invention is described in detail below, so that advantages and features of the invention can be easier to be readily appreciated by one skilled in the art, apparent is clearly defined so as to make to protection scope of the present invention.
Embodiment 1.
One kind building environment-friendly materials, including the material of following parts by weight：30 parts of calcium carbonate, 10 parts of diatomite, 2 parts of hollow glass micropearl, 1 part of graphite powder, 3 parts of kaolin, wood fibre（80 mesh）4 parts, diatomite（80 mesh）6 parts, perforate expanded perlite（20 mesh）7 parts, hollow glass micropearl（120 mesh）5 parts, 6 parts of lime, 14 parts of gypsum, 1 part of nucleator, 2 parts of talcum powder, 3 parts of the nano combined environmental protection fire retarding agent of antimony base, 5 parts of three fulminuric acid fat.
Embodiment 2.
One kind building environment-friendly materials, including the material of following parts by weight：40 parts of calcium carbonate, 10 parts of diatomite, 5 parts of hollow glass micropearl, 5 parts of graphite powder, 5 parts of kaolin, wood fibre（80 mesh）7 parts, diatomite（100 mesh）7 parts, perforate expanded perlite（80 mesh）7 parts, hollow glass micropearl（150 mesh）6 parts, 7 parts of lime, 19 parts of gypsum, 3 parts of nucleator, 3 parts of talcum powder, 5 parts of the nano combined environmental protection fire retarding agent of antimony base, 7 parts of three fulminuric acid fat.
Embodiment 3.
One kind building environment-friendly materials, including the material of following parts by weight：50 parts of calcium carbonate, 11 parts of diatomite, 9 parts of hollow glass micropearl, 9 parts of graphite powder, 7 parts of kaolin, wood fibre（100 mesh）9 parts, diatomite（100 mesh）9 parts, perforate expanded perlite（120 mesh）8 parts, hollow glass micropearl（200 mesh）8 parts, 9 parts of lime, 28 parts of gypsum, 5 parts of nucleator, 4 parts of talcum powder, 8 parts of the nano combined environmental protection fire retarding agent of antimony base, 9 parts of three fulminuric acid fat.
Claims (1)
1. it is a kind of to build environment-friendly materials, it is characterised in that including the material of following parts by weight：Calcium carbonate 30-50 parts, diatomite 10-11 parts, hollow glass micropearl 2-9 parts, graphite powder 1-9 parts, kaolin 3-7 parts, wood fibre（80-100 mesh）4-9 parts, diatomite（80-100 mesh）6-9 parts, perforate expanded perlite（20-120 mesh）7-8 parts, hollow glass micropearl（120-200 mesh）5-8 parts, lime 6-9 parts, gypsum 14-28 parts, nucleator 1-5 parts, talcum powder 2-4 parts, the nano combined environmental protection fire retarding agent 3-8 parts of antimony base, three fulminuric acid fat 5-9 part.