CN104032617A - 一种造纸用高岭土 - Google Patents
一种造纸用高岭土 Download PDFInfo
- Publication number
- CN104032617A CN104032617A CN201410206679.XA CN201410206679A CN104032617A CN 104032617 A CN104032617 A CN 104032617A CN 201410206679 A CN201410206679 A CN 201410206679A CN 104032617 A CN104032617 A CN 104032617A
- Authority
- CN
- China
- Prior art keywords
- kaolin
- ore pulp
- stock
- paper grade
- bleaching
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种造纸用高岭土,其制备包括了开采粗矿、初沉降结合离心分离制备初级矿浆、矿浆初料制备、漂白制备矿浆精料、洗涤、脱水、干燥、再分散、喷雾干燥的制备过程。本发明在漂白过程先加入过氧化氢,可让高岭土中着色杂质反应完全,然后再加入Na2S2O4漂白,其最终漂白白度可提高到85.0%以上;在漂白之后,添加磷酸盐可以阻止泛黄;加入分散剂调节粘度使粘度达到68%以上,满足涂布要求,同时获得良好流动性;本发明的高岭土具有片状六边形晶形发育完好,纯度高、粘浓度高、粒度细、成浆流动性能好等优点,尤其适用于高级铜版纸、高档白卡纸的生产。
Description
技术领域
本发明涉及一种高岭土,具体是一种造纸用高岭土。
背景技术
高岭土是一种以高岭石族粘土矿物为主的粘土和粘土岩,其矿物成分主要由高岭石、埃洛石、水云母、伊利石、蒙脱石以及石英、长石等矿物组成,质纯的高岭土呈洁白细腻、松软土状,具有良好的可塑性和耐火性等理化性质。高岭土用途十分广泛,主要用于造纸、陶瓷和耐火材料,其次用于涂料、橡胶填料、搪瓷釉料和白水泥原料,少量用于塑料、油漆、颜料、砂轮、铅笔、日用化妆品、肥皂、农药、医药、纺织、石油、化工、建材、国防等工业部门。国内有五大高岭土矿产地:(1)茂名地区高岭土(2)龙岩高岭土(3)苏州阳山高岭土(4)合浦高岭土(5)北方煤系高岭土。高岭土矿分布的地域不同,不同的产地,高岭土的成分、结构、理化性能等差异很大。
在造纸生产上用作颜料、填料和涂料的高岭土,其白度和亮度的高低直接影响其价值的高低,因此,在高岭土的制备过程中,需要通过化学漂白工序除去一些牢固覆盖在高岭土颗粒表面的氧化铁等有色杂质。常用的化学漂白方法有:氧化还原法、酸溶法、氯化法等。
粘度是另一个评价高岭土在用于造纸工业中质量优劣的重要因素。粘度值越大表面高岭土粘度越低,流动性越好。目前造纸刮刀涂布要求高岭土粘度值大于68%。影响高岭土粘度的主要因素有:高岭石的结构有序度、晶体形态、晶体大小分布情况等。
发明内容
本发明目的是提供一种结合茂名地区高岭土的理化特征,制备得到的用于造纸生产特别是适合于高级铜版纸、高档白卡纸生产的具有纯度高、粘浓度高、粒度细、成浆流动性能好等优点的一种造纸用高岭土。
本发明所采用的技术方案如下:一种造纸用高岭土,其制备方法包括如下步骤:
(1)开采高岭土矿料,初步分离去掉粘土、杂物后,获得基料,将基料与水混合制成原矿浆,进行初沉降,除去大块砂砾,然后再进行离心分离,制得初级矿浆;
(2)将初级矿浆与分散剂混合进行制浆,获得固含量为12~15%的高岭土矿浆初料;
边搅拌边向高岭土矿浆初料中加入浓度30%的过氧化氢溶液反应20~40min,加入连二亚硫酸钠溶液反应30~50min,再加入磷酸盐,制得高岭土矿浆精料;
(3)将高岭土矿浆精料在pH4~6条件下进行酸性水洗涤,经过真空过滤脱水,获得滤饼,将滤饼粉碎后重新分散成固含量为50~60%的矿浆,再经过喷雾干燥,即得成品;
其中,所述磷酸盐用量为高岭土矿浆初料的0.01~0.05%;所述分散剂用量为高岭土矿浆初料的0.5~3%。
所述原矿浆固含量优选为50~70%。
所述离心分离转速优选为200~500转/min,离心分离时间为5~10min。
所述分散剂优选为阴离子聚丙烯酸盐、阴离子聚磷酸盐、无机高分子分散剂中的一种或几种的复合。
所述磷酸盐优选为偏磷酸钠。
所述步骤(3)的搅拌转速优选为200转/min。
所述离心分离转速优选为300转/分,离心分离时间为5min。
所述加入过氧化氢的反应时间优选为30min。
本发明的方法与现有技术相比,在矿浆中先加入过氧化氢,可让高岭土中着色杂质反应完全,然后再加入Na2S2O4漂白,其最终漂白白度可提高到85.0%以上;在漂白之后,添加磷酸盐可以阻止泛黄;加入分散剂调节粘度使粘度达到68%以上,满足涂布要求,同时获得良好流动性能;本发明的高岭土具有片状六边形晶形发育完好,纯度高、粘浓度高、粒度细、成浆流动性能好等优点,尤其适用于高级铜版纸、高档白卡纸的生产。
具体实施方式
下面通过实施例对本发明做进一步详细说明,这些实施例仅用来说明本发明,并不限制本发明的范围。
实施例1:采用以下步骤实现本发明:
(1)开采高岭土矿料,初步分离去掉粘土、杂物后,获得基料,将基料与水混合制成原矿浆,调整原矿浆固含量为60%进行初沉降,除去大块砂砾,然后再以转速200转/min,离心分离5min,制得初级矿浆;
(2)将初级矿浆与分散剂阴离子聚丙烯酰胺、水混合进行制浆,获得固含量为12%的高岭土矿浆初料;分散剂用量为高岭土矿浆初料的0.8%;边搅拌边向高岭土矿浆初料中加入浓度30%的过氧化氢溶液反应30min,加入连二亚硫酸钠溶液反应30min,再加入高岭土矿浆初料0.01%的偏磷酸钠,制得高岭土矿浆精料;
(3)将高岭土矿浆精料在pH5条件下进行酸性水洗涤,经过真空过滤脱水,获得滤饼,将滤饼粉碎后重新分散成固含量为55%的矿浆,再经过喷雾干燥,即得成品。
实施例2:采用以下步骤实现本发明:
(1)开采高岭土矿料,初步分离去掉粘土、杂物后,获得基料,将基料与水混合制成原矿浆,调整原矿浆固含量为70%进行初沉降,除去大块砂砾,然后再以转速450转/min,离心分离10min,制得初级矿浆;
(2)将初级矿浆与分散剂阴离子聚磷酸盐、水混合进行制浆,获得固含量为15%的高岭土矿浆初料;分散剂用量为高岭土矿浆初料的1.5%;边搅拌边向高岭土矿浆初料中加入浓度30%的过氧化氢溶液反应20min,加入连二亚硫酸钠溶液反应30min,再加入高岭土矿浆初料0.05%的偏磷酸钠,制得高岭土矿浆精料;
(3)将高岭土矿浆精料在pH4条件下进行酸性水洗涤,经过真空过滤脱水,获得滤饼,将滤饼粉碎后重新分散成固含量为50%的矿浆,再经过喷雾干燥,即得成品。
实施例3:采用以下步骤实现本发明:
(1)开采高岭土矿料,初步分离去掉粘土、杂物后,获得基料,将基料与水混合制成原矿浆,调整原矿浆固含量为50%进行初沉降,除去大块砂砾,然后再以转速300转/min,离心分离8min,制得初级矿浆;
(2)将初级矿浆与无机高分子分散剂、水混合进行制浆,获得固含量为12%的高岭土矿浆初料;分散剂用量为高岭土矿浆初料的2.5%;边搅拌边向高岭土矿浆初料中加入浓度30%的过氧化氢溶液反应40min,加入连二亚硫酸钠溶液反应30min,再加入高岭土矿浆初料0.02%的偏磷酸钠,制得高岭土矿浆精料;
(3)将高岭土矿浆精料在pH6条件下进行酸性水洗涤,经过真空过滤脱水,获得滤饼,将滤饼粉碎后重新分散成固含量为60%的矿浆,再经过喷雾干燥,即得成品。
Claims (8)
1.一种造纸用高岭土,其特征在于:其制备方法包括如下步骤:
开采高岭土矿料,初步分离去掉粘土、杂物后,获得基料,将基料与水混合制成原矿浆,进行初沉降,除去大块砂砾,然后再进行离心分离,制得初级矿浆;
将初级矿浆与分散剂混合进行制浆,获得固含量为12~15%的高岭土矿浆初料;
边搅拌边向高岭土矿浆初料中加入浓度30%的过氧化氢溶液反应20~40min,加入连二亚硫酸钠溶液反应30~50min,再加入磷酸盐,制得高岭土矿浆精料;
将高岭土矿浆精料在pH4~6条件下进行酸性水洗涤,经过真空过滤脱水,获得滤饼,将滤饼粉碎后重新分散成固含量为50~60%的矿浆,再经过喷雾干燥,即得成品;
其中,所述磷酸盐用量为高岭土矿浆初料的0.01~0.05%;所述分散剂用量为高岭土矿浆初料的0.5~3%。
2.根据权利要求1所述的造纸用高岭土,其特征在于:所述原矿浆固含量为50~70%。
3.根据权利要求1所述的造纸用高岭土,其特征在于:所述离心分离转速为200~500转/min,离心分离时间为5~10min。
4.根据权利要求1所述的造纸用高岭土,其特征在于:所述分散剂为:阴离子聚丙烯酸盐、阴离子聚磷酸盐、无机高分子分散剂中的一种或几种的复合。
5.根据权利要求1所述的造纸用高岭土,其特征在于:所述磷酸盐为偏磷酸钠。
6.根据权利要求1所述的造纸用高岭土,其特征在于:所述步骤(3)的搅拌转速为200转/min。
7.根据权利要求3所述的造纸用高岭土,其特征在于:所述离心分离转速为300转/分,离心分离时间为5min。
8.根据权利要求1所述的造纸用高岭土,其特征在于:所述加入过氧化氢的反应时间为30min。