CN104031506B - 一种硬膜乳胶漆 - Google Patents
一种硬膜乳胶漆 Download PDFInfo
- Publication number
- CN104031506B CN104031506B CN201410218648.6A CN201410218648A CN104031506B CN 104031506 B CN104031506 B CN 104031506B CN 201410218648 A CN201410218648 A CN 201410218648A CN 104031506 B CN104031506 B CN 104031506B
- Authority
- CN
- China
- Prior art keywords
- stirring
- minutes
- emulsion
- dispersed
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种硬膜乳胶漆，它是由下述重量份的原料组成的：纯丙乳液34-40、灰钙粉2-3、煅烧高岭土20-27、醇酯十二成膜助剂3-5、羟乙基纤维素1-2、二亚乙基三胺0.2-0.3、偏钨酸铵0.1-0.3、钛白粉8-11、2,4,7,9-四甲基-5-癸炔-4,7-二醇2-3、复合助剂5-7、去离子水20-40；本发明的乳胶漆漆膜硬度好，遮盖力强，耐擦洗性好，使用寿命长，不会发生鼓起脱落现象，稳定性高，耐水性、耐酸碱性好，综合性能优越。
Description
技术领域
本发明主要涉及涂料领域，尤其涉及一种硬膜乳胶漆。
背景技术
以丙烯酸酯共聚乳液为代表的一大类合成树脂乳液涂料。乳胶漆是水分散性涂料，它是以合成树脂乳液为基料，填料经过研磨分散后加入各种助剂精制而成的涂料。乳胶漆具备了与传统墙面涂料不同的众多优点，如易于涂刷、干燥迅速、漆膜耐水、耐擦洗性好等；
乳胶漆是水性涂料，它们的漆膜性能比溶剂型涂料要好得多，占溶剂型涂料一半的有机溶剂在这里被水代替了，因此有机溶剂的毒性问题，基本上被乳胶漆彻底的解决了。
发明内容
本发明目的就是提供一种硬膜乳胶漆。
本发明是通过以下技术方案实现的：
一种硬膜乳胶漆，它是由下述重量份的原料组成的：
纯丙乳液34-40、灰钙粉2-3、煅烧高岭土20-27、醇酯十二成膜助剂3-5、羟乙基纤维素1-2、二亚乙基三胺0.2-0.3、偏钨酸铵0.1-0.3、钛白粉8-11、2,4,7,9-四甲基-5-癸炔-4,7-二醇2-3、复合助剂5-7、去离子水20-40；
所述的复合助剂是由下述重量份的原料组成的：
VAE乳液15-20、铝溶胶5-7、吡咯烷酮羟酸钠1-2、氨基酸螯合锌0.2-1、羟丙基甲基纤维素2-3、卡拉胶0.2-1、富马酸二甲酯1-2；
将上述富马酸二甲酯加入到铝溶胶中，在70-80℃下搅拌混合2-3分钟，加入氨基酸螯合锌，100-200转/分搅拌分散3-5分钟；
将羟丙基甲基纤维素与卡拉胶混合，搅拌均匀后加入到VAE乳液中，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，200-300转/分搅拌分散10-20分钟，即得所述复合助剂。
一种硬膜乳胶漆的制备方法，包括以下步骤：
将灰钙粉、煅烧高岭土、钛白粉混合加入到去离子水中，加入羟乙基纤维素，500-600转/分搅拌分散10-13分钟，加入二亚乙基三胺、2,4,7,9-四甲基-5-癸炔-4,7-二醇，1200-1400转/分搅拌分散30-50分钟，测得上述物料混合物的细度为50μm以下，加入剩余各原料，1000-1200转/分搅拌分散30-40分钟，即得所述硬膜乳胶漆。
本发明的优点是：
本发明的乳胶漆漆膜硬度好，遮盖力强，耐擦洗性好，使用寿命长，不会发生鼓起脱落现象，稳定性高，耐水性、耐酸碱性好，综合性能优越。
具体实施方式
实施例1
一种硬膜乳胶漆，它是由下述重量份（公斤）的原料组成的：
纯丙乳液40、灰钙粉3、煅烧高岭土27、醇酯十二成膜助剂5、羟乙基纤维素1、二亚乙基三胺0.3、偏钨酸铵0.3、钛白粉11、2,4,7,9-四甲基-5-癸炔-4,7-二醇2-3、复合助剂7、去离子水40；
所述的复合助剂是由下述重量份的原料组成的：
VAE乳液20、铝溶胶7、吡咯烷酮羟酸钠1、氨基酸螯合锌0.2、羟丙基甲基纤维素2、卡拉胶0.2、富马酸二甲酯1；
将上述富马酸二甲酯加入到铝溶胶中，在80℃下搅拌混合2分钟，加入氨基酸螯合锌，200转/分搅拌分散3分钟；
将羟丙基甲基纤维素与卡拉胶混合，搅拌均匀后加入到VAE乳液中，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，300转/分搅拌分散20分钟，即得所述复合助剂。
一种硬膜乳胶漆的制备方法，包括以下步骤：
将灰钙粉、煅烧高岭土、钛白粉混合加入到去离子水中，加入羟乙基纤维素，600转/分搅拌分散13分钟，加入二亚乙基三胺、2,4,7,9-四甲基-5-癸炔-4,7-二醇，1200-1400转/分搅拌分散50分钟，测得上述物料混合物的细度为50μm以下，加入剩余各原料，1200转/分搅拌分散40分钟，即得所述硬膜乳胶漆。
性能测试：
漆膜外观平整、无硬块、手感好、光泽度好；
耐洗刷性试验：5000次通过，漆膜无破损；
耐人工老化性试验：2000小时不起泡、不剥落、无裂纹；
耐水性：140h漆膜无破损；
耐碱性：120h漆膜无破损。
Claims (1)
1.一种硬膜乳胶漆，它是由下述重量份的原料制成的：
纯丙乳液40、灰钙粉3、煅烧高岭土27、醇酯十二成膜助剂5、羟乙基纤维素1、二亚乙基三胺0.3、偏钨酸铵0.3、钛白粉11、2,4,7,9-四甲基-5-癸炔-4,7-二醇2-3、复合助剂7、去离子水40；
所述的复合助剂是由下述重量份的原料制成的：
VAE乳液20、铝溶胶7、吡咯烷酮羟酸钠1、氨基酸螯合锌0.2、羟丙基甲基纤维素2、卡拉胶0.2、富马酸二甲酯1；
将上述富马酸二甲酯加入到铝溶胶中，在80℃下搅拌混合2分钟，加入氨基酸螯合锌，200转/分搅拌分散3分钟；
将羟丙基甲基纤维素与卡拉胶混合，搅拌均匀后加入到VAE乳液中，搅拌均匀；
将上述处理后的各原料与吡咯烷酮羟酸钠混合，300转/分搅拌分散20分钟，即得所述复合助剂；
所述的一种硬膜乳胶漆的制备方法，包括以下步骤：
将灰钙粉、煅烧高岭土、钛白粉混合加入到去离子水中，加入羟乙基纤维素，600转/分搅拌分散13分钟，加入二亚乙基三胺、2,4,7,9-四甲基-5-癸炔-4,7-二醇，1200-1400转/分搅拌分散50分钟，测得上述物料混合物的细度为50μm以下，加入剩余各原料，1200转/分搅拌分散40分钟，即得所述硬膜乳胶漆。