CN104046161A - 一种清香型乳胶漆 - Google Patents
一种清香型乳胶漆 Download PDFInfo
- Publication number
- CN104046161A CN104046161A CN201410218656.0A CN201410218656A CN104046161A CN 104046161 A CN104046161 A CN 104046161A CN 201410218656 A CN201410218656 A CN 201410218656A CN 104046161 A CN104046161 A CN 104046161A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- minute
- stirring
- dispersed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种清香型乳胶漆，它是由下述重量份的原料组成的：醋丙乳液34-40、甲基环戊烯醇酮2-3、檀香油0.5-1、轻质碳酸钙10-15、十二烷基磺酸钠1-2、2-甲基-1,3-丙二醇1-2、聚氧丙烯甘油醚0.5-1、钼酸铵2-3、长石粉10-16、纳米膨润土10-15、复合助剂5-8、去离子水25-40；本发明的乳胶漆具有淡淡的清香，改善了传统乳胶漆的味道，漆膜稳定，还具有很好的抗菌效果，安全环保，耐水性、耐酸碱性好，耐人工老化试验合格，使用寿命长。
Description
技术领域
本发明主要涉及涂料领域，尤其涉及一种清香型乳胶漆。
背景技术
以丙烯酸酯共聚乳液为代表的一大类合成树脂乳液涂料。乳胶漆是水分散性涂料，它是以合成树脂乳液为基料，填料经过研磨分散后加入各种助剂精制而成的涂料。乳胶漆具备了与传统墙面涂料不同的众多优点，如易于涂刷、干燥迅速、漆膜耐水、耐擦洗性好等；
乳胶漆是水性涂料，它们的漆膜性能比溶剂型涂料要好得多，占溶剂型涂料一半的有机溶剂在这里被水代替了，因此有机溶剂的毒性问题，基本上被乳胶漆彻底的解决了。
发明内容
本发明目的就是提供一种清香型乳胶漆。
本发明是通过以下技术方案实现的：
一种清香型乳胶漆，它是由下述重量份的原料组成的：
醋丙乳液34-40、甲基环戊烯醇酮2-3、檀香油0.5-1、轻质碳酸钙10-15、十二烷基磺酸钠1-2、2-甲基-1,3-丙二醇1-2、聚氧丙烯甘油醚0.5-1、钼酸铵2-3、长石粉10-16、纳米膨润土10-15、复合助剂5-8、去离子水25-40；
所述的复合助剂是由下述重量份的原料组成的：
VAE乳液15-20、铝溶胶5-7、吡咯烷酮羟酸钠1-2、氨基酸螯合锌0.2-1、羟丙基甲基纤维素2-3、卡拉胶0.2-1、富马酸二甲酯1-2；
将上述富马酸二甲酯加入到铝溶胶中，在70-80℃下搅拌混合2-3分钟，加入氨基酸螯合锌，100-200转/分搅拌分散3-5分钟；
将羟丙基甲基纤维素与卡拉胶混合，搅拌均匀后加入到VAE乳液中，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，200-300转/分搅拌分散10-20分钟，即得所述复合助剂。
一种清香型乳胶漆的制备方法，包括以下步骤：
（1）将上述去离子水加热至沸，加入甲基环戊烯醇酮，保温搅拌2-4分钟，降低温度为50-60℃，加入十二烷基磺酸钠，充分搅拌，加入檀香油、钼酸铵，500-600转/分搅拌分散10-15分钟；
（2）将上述处理后的各原料与剩余各原料混合，1600-2000转/分搅拌分散30-40分钟，即得所述清香型乳胶漆。
本发明的优点是：
本发明的乳胶漆具有淡淡的清香，改善了传统乳胶漆的味道，漆膜稳定，还具有很好的抗菌效果，安全环保，耐水性、耐酸碱性好，耐人工老化试验合格，使用寿命长。
具体实施方式
实施例1
一种清香型乳胶漆，它是由下述重量份（公斤）的原料组成的：
醋丙乳液40、甲基环戊烯醇酮2、檀香油0.5、轻质碳酸钙15、十二烷基磺酸钠2、2-甲基-1,3-丙二醇1、聚氧丙烯甘油醚0.5、钼酸铵3、长石粉16、纳米膨润土15、复合助剂8、去离子水40；
所述的复合助剂是由下述重量份的原料组成的：
VAE乳液20、铝溶胶5、吡咯烷酮羟酸钠1、氨基酸螯合锌0.2、羟丙基甲基纤维素2、卡拉胶0.2、富马酸二甲酯1；
将上述富马酸二甲酯加入到铝溶胶中，在80℃下搅拌混合3分钟，加入氨基酸螯合锌，200转/分搅拌分散5分钟；
将羟丙基甲基纤维素与卡拉胶混合，搅拌均匀后加入到VAE乳液中，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，300转/分搅拌分散20分钟，即得所述复合助剂。
一种清香型乳胶漆的制备方法，包括以下步骤：
（1）将上述去离子水加热至沸，加入甲基环戊烯醇酮，保温搅拌4分钟，降低温度为60℃，加入十二烷基磺酸钠，充分搅拌，加入檀香油、钼酸铵，600转/分搅拌分散15分钟；
（2）将上述处理后的各原料与剩余各原料混合，2000转/分搅拌分散40分钟，即得所述清香型乳胶漆。
性能测试：
漆膜外观平整、无硬块、手感好、光泽度好；
耐洗刷性试验：5000 次通过，漆膜无破损；
耐人工老化性试验：2000小时不起泡、不剥落、无裂纹；
耐水性：140h漆膜无破损；
耐碱性：120h漆膜无破损。
Claims (2)
1.一种清香型乳胶漆，其特征在于它是由下述重量份的原料组成的：
醋丙乳液34-40、甲基环戊烯醇酮2-3、檀香油0.5-1、轻质碳酸钙10-15、十二烷基磺酸钠1-2、2-甲基-1,3-丙二醇1-2、聚氧丙烯甘油醚0.5-1、钼酸铵2-3、长石粉10-16、纳米膨润土10-15、复合助剂5-8、去离子水25-40；
所述的复合助剂是由下述重量份的原料组成的：
VAE乳液15-20、铝溶胶5-7、吡咯烷酮羟酸钠1-2、氨基酸螯合锌0.2-1、羟丙基甲基纤维素2-3、卡拉胶0.2-1、富马酸二甲酯1-2；
将上述富马酸二甲酯加入到铝溶胶中，在70-80℃下搅拌混合2-3分钟，加入氨基酸螯合锌，100-200转/分搅拌分散3-5分钟；
将羟丙基甲基纤维素与卡拉胶混合，搅拌均匀后加入到VAE乳液中，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，200-300转/分搅拌分散10-20分钟，即得所述复合助剂。
2.一种如权利要求1所述的清香型乳胶漆的制备方法，其特征在于包括以下步骤：
（1）将上述去离子水加热至沸，加入甲基环戊烯醇酮，保温搅拌2-4分钟，降低温度为50-60℃，加入十二烷基磺酸钠，充分搅拌，加入檀香油、钼酸铵，500-600转/分搅拌分散10-15分钟；
（2）将上述处理后的各原料与剩余各原料混合，1600-2000转/分搅拌分散30-40分钟，即得所述清香型乳胶漆。