CN104031480A - 一种抗菌防腐乳胶漆 - Google Patents
一种抗菌防腐乳胶漆 Download PDFInfo
- Publication number
- CN104031480A CN104031480A CN201410218647.1A CN201410218647A CN104031480A CN 104031480 A CN104031480 A CN 104031480A CN 201410218647 A CN201410218647 A CN 201410218647A CN 104031480 A CN104031480 A CN 104031480A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion
- stirring
- antibacterial
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗菌防腐乳胶漆,它是由下述重量份的原料组成的:VAE乳液42-50、氧化聚乙烯蜡乳液5-8、聚氧乙烯聚氧丙醇胺醚0.1-0.2、乙二醇2-3、双乙酸钠1-2、丙二醇苯醚1-2、山梨酸钾1-2、N-乙酰基乙二胺2-3、沉淀硫酸钡20-25、硅灰石粉20-25、复合助剂5-8、去离子水30-50;本发明的乳胶漆加入的抗菌防腐乳液具有很好的抗菌防腐效果,可以有效的延长漆膜的使用寿命,增强漆膜的耐候性和稳定性,本发明的乳胶漆遮盖力强,附着力好,环保性能佳,综合性能优越。
Description
技术领域
本发明主要涉及涂料领域,尤其涉及一种抗菌防腐乳胶漆。
背景技术
以丙烯酸酯共聚乳液为代表的一大类合成树脂乳液涂料。乳胶漆是水分散性涂料,它是以合成树脂乳液为基料,填料经过研磨分散后加入各种助剂精制而成的涂料。乳胶漆具备了与传统墙面涂料不同的众多优点,如易于涂刷、干燥迅速、漆膜耐水、耐擦洗性好等;
乳胶漆是水性涂料,它们的漆膜性能比溶剂型涂料要好得多,占溶剂型涂料一半的有机溶剂在这里被水代替了,因此有机溶剂的毒性问题,基本上被乳胶漆彻底的解决了。
发明内容
本发明目的就是提供一种抗菌防腐乳胶漆。
本发明是通过以下技术方案实现的:
一种抗菌防腐乳胶漆,它是由下述重量份的原料组成的:
VAE乳液42-50、氧化聚乙烯蜡乳液5-8、聚氧乙烯聚氧丙醇胺醚0.1-0.2、乙二醇2-3、双乙酸钠1-2、丙二醇苯醚1-2、山梨酸钾1-2、N-乙酰基乙二胺2-3、沉淀硫酸钡20-25、硅灰石粉20-25、复合助剂5-8、去离子水30-50;
所述的复合助剂是由下述重量份的原料组成的:
VAE乳液15-20、铝溶胶5-7、吡咯烷酮羟酸钠1-2、氨基酸螯合锌0.2-1、羟丙基甲基纤维素2-3、卡拉胶0.2-1、富马酸二甲酯1-2;
将上述富马酸二甲酯加入到铝溶胶中,在70-80℃下搅拌混合2-3分钟,加入氨基酸螯合锌,100-200转/分搅拌分散3-5分钟;
将羟丙基甲基纤维素与卡拉胶混合,搅拌均匀后加入到VAE乳液中,搅拌均匀;
将上述处理后的各原料与剩余各原料混合,200-300转/分搅拌分散10-20分钟,即得所述复合助剂。
一种抗菌防腐乳胶漆的制备方法,包括以下步骤:
(1)将双乙酸钠、山梨酸钾混合,加入氧化聚乙烯蜡乳液,加热到30-40℃,100-200转/分搅拌分散3-5分钟,冷却至常温,加入N-乙酰基乙二胺,搅拌均匀,即得抗菌防腐乳液;
(2)将聚氧乙烯聚氧丙醇胺醚与乙二醇、去离子水混合,搅拌均匀后加入沉淀硫酸钡、硅灰石粉,200-300转/分搅拌分散10-15分钟;
(3)将上述处理后的各原料与剩余各原料混合,1500-1600转/分搅拌分散30-40分钟,即得所述抗菌防腐乳胶漆。
本发明的优点是:
本发明的乳胶漆加入的抗菌防腐乳液具有很好的抗菌防腐效果,可以有效的延长漆膜的使用寿命,增强漆膜的耐候性和稳定性,本发明的乳胶漆遮盖力强,附着力好,环保性能佳,综合性能优越。
具体实施方式
实施例1
一种抗菌防腐乳胶漆,它是由下述重量份(公斤)的原料组成的:
VAE乳液50、氧化聚乙烯蜡乳液8、聚氧乙烯聚氧丙醇胺醚0.2、乙二醇2、双乙酸钠1、丙二醇苯醚2、山梨酸钾2、N-乙酰基乙二胺3、沉淀硫酸钡25、硅灰石粉25、复合助剂8、去离子水50;
所述的复合助剂是由下述重量份的原料组成的:
VAE乳液20、铝溶胶5、吡咯烷酮羟酸钠1、氨基酸螯合锌0.2、羟丙基甲基纤维素2、卡拉胶0.2、富马酸二甲酯2;
将上述富马酸二甲酯加入到铝溶胶中,在80℃下搅拌混合3分钟,加入氨基酸螯合锌,200转/分搅拌分散3分钟;
将羟丙基甲基纤维素与卡拉胶混合,搅拌均匀后加入到VAE乳液中,搅拌均匀;
将上述处理后的各原料与剩余各原料混合,300转/分搅拌分散20分钟,即得所述复合助剂。
一种抗菌防腐乳胶漆的制备方法,包括以下步骤:
(1)将双乙酸钠、山梨酸钾混合,加入氧化聚乙烯蜡乳液,加热到40℃,200转/分搅拌分散3分钟,冷却至常温,加入N-乙酰基乙二胺,搅拌均匀,即得抗菌防腐乳液;
(2)将聚氧乙烯聚氧丙醇胺醚与乙二醇、去离子水混合,搅拌均匀后加入沉淀硫酸钡、硅灰石粉,300转/分搅拌分散15分钟;
(3)将上述处理后的各原料与剩余各原料混合,1600转/分搅拌分散30分钟,即得所述抗菌防腐乳胶漆。
性能测试:
漆膜外观平整、无硬块、手感好、光泽度好;
耐洗刷性试验:5000 次通过,漆膜无破损;
耐人工老化性试验:2000小时不起泡、不剥落、无裂纹;
耐水性:140h漆膜无破损;
耐碱性:120h漆膜无破损。
Claims (2)
1.一种抗菌防腐乳胶漆,其特征在于它是由下述重量份的原料组成的:
VAE乳液42-50、氧化聚乙烯蜡乳液5-8、聚氧乙烯聚氧丙醇胺醚0.1-0.2、乙二醇2-3、双乙酸钠1-2、丙二醇苯醚1-2、山梨酸钾1-2、N-乙酰基乙二胺2-3、沉淀硫酸钡20-25、硅灰石粉20-25、复合助剂5-8、去离子水30-50;
所述的复合助剂是由下述重量份的原料组成的:
VAE乳液15-20、铝溶胶5-7、吡咯烷酮羟酸钠1-2、氨基酸螯合锌0.2-1、羟丙基甲基纤维素2-3、卡拉胶0.2-1、富马酸二甲酯1-2;
将上述富马酸二甲酯加入到铝溶胶中,在70-80℃下搅拌混合2-3分钟,加入氨基酸螯合锌,100-200转/分搅拌分散3-5分钟;
将羟丙基甲基纤维素与卡拉胶混合,搅拌均匀后加入到VAE乳液中,搅拌均匀;
将上述处理后的各原料与剩余各原料混合,200-300转/分搅拌分散10-20分钟,即得所述复合助剂。
2.一种如权利要求1所述的抗菌防腐乳胶漆的制备方法,其特征在于包括以下步骤:
(1)将双乙酸钠、山梨酸钾混合,加入氧化聚乙烯蜡乳液,加热到30-40℃,100-200转/分搅拌分散3-5分钟,冷却至常温,加入N-乙酰基乙二胺,搅拌均匀,即得抗菌防腐乳液;
(2)将聚氧乙烯聚氧丙醇胺醚与乙二醇、去离子水混合,搅拌均匀后加入沉淀硫酸钡、硅灰石粉,200-300转/分搅拌分散10-15分钟;
(3)将上述处理后的各原料与剩余各原料混合,1500-1600转/分搅拌分散30-40分钟,即得所述抗菌防腐乳胶漆。