CN104109436A - 一种自清洁涂料 - Google Patents

一种自清洁涂料 Download PDF

Info

Publication number
CN104109436A
CN104109436A CN201410280466.1A CN201410280466A CN104109436A CN 104109436 A CN104109436 A CN 104109436A CN 201410280466 A CN201410280466 A CN 201410280466A CN 104109436 A CN104109436 A CN 104109436A
Authority
CN
China
Prior art keywords
mixed
parts
self
raw material
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410280466.1A
Other languages
English (en)
Inventor
王金波
梁威
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Lang Run Novel Material Co Ltd
Original Assignee
Wuhu Lang Run Novel Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Lang Run Novel Material Co Ltd filed Critical Wuhu Lang Run Novel Material Co Ltd
Priority to CN201410280466.1A priority Critical patent/CN104109436A/zh
Publication of CN104109436A publication Critical patent/CN104109436A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种自清洁涂料，其特征在它是由下述重量份的原料组成的：丙烯酸酯乳液52.1-60、2,4-二甲基苯乙酮0.1-0.2、脲丙基三乙氧基硅烷0.6-1、氧化锌0.4-1、对羟基苯甲酸甲酯0.4-1、伊利石粉4-6、钛白粉14-18、聚丙烯酸丁酯2-3、2-氨基-2-甲基-1-丙醇1.3-2、乙撑双硬脂酰胺1.3-2、成膜助剂5-7、去离子水26-40，本发明的涂料耐沾污性持久，可以通过雨水的冲刷达到自清洁的效果，特别适合做建筑外墙涂料，涂层稳定性强，抗菌防腐性好，综合品质高。

Description

一种自清洁涂料
技术领域
    本发明主要涉及涂料领域，尤其涉及一种自清洁涂料。
背景技术
墙用丙烯酸有光乳胶漆，都是薄质涂料，它以有机高分子材料为主要成膜物质，加上不同的颜料、填料和骨料而制成的薄涂料，具有耐水、耐酸、耐碱、抗冻融等特点，目前市面上的涂料具有的功能不完善，存在缺陷，这种涂料的主要缺点是涂膜弹性容易老化、导致拉伸率下降、不能有效保护墙面粉刷底层的强度，从而产生墙面开裂、脱落，不仅影响建筑物美观，而且墙面开裂，导致墙面漏水。
发明内容
本发明目的就是提供一种自清洁涂料。
本发明是通过以下技术方案实现的：
一种自清洁涂料，其特征在于它是由下述重量份的原料组成的：
丙烯酸酯乳液52.1-60、2,4-二甲基苯乙酮0.1-0.2、脲丙基三乙氧基硅烷0.6-1、氧化锌0.4-1、对羟基苯甲酸甲酯0.4-1、伊利石粉4-6、钛白粉14-18、聚丙烯酸丁酯2-3、2- 氨基-2- 甲基-1- 丙醇1.3-2、乙撑双硬脂酰胺1.3-2、成膜助剂5-7、去离子水26-40；
所述的成膜助剂是由下述重量份的原料组成的：
丙烯酸酯12-20、氨基三甲叉膦酸1-2、乙二胺四乙酸二钠2-3、氨丙基三乙氧基硅烷0.1-1、沙棘油1-2、过硫酸钾0.7-2、水50-60；
将丙烯酸酯与氨丙基三乙氧基硅烷混合，50-60℃下搅拌混合4-7分钟，加入到上述水中，搅拌条件下加入过硫酸钾，搅拌均匀；
将乙二胺四乙酸二钠与氨基三甲叉膦酸混合，搅拌均匀后加入沙棘油，在50-60℃下搅拌混合3-5分钟，冷却至常温；
将上述处理后的各原料与剩余各原料混合，800-1000转/分搅拌分散20-30分钟，即得所述成膜助剂。
一种自清洁涂料的制备方法，包括以下步骤：
（1）将钛白粉与伊利石粉混合，球磨均匀后加入到去离子水中，加入脲丙基三乙氧基硅烷，50-60℃下搅拌混合20-30分钟；
（2）将氧化锌与对羟基苯甲酸甲酯混合，搅拌均匀后加入乙撑双硬脂酰胺，混合均匀；
（3）将丙烯酸酯乳液与聚丙烯酸丁酯混合，50-60℃下搅拌混合2-4分钟；
（4）将上述处理后的各原料与剩余各原料混合，700-800转/分搅拌分散30-40分钟，经砂磨机研磨至细度10-15μm，过滤，即得所述自清洁涂料。
本发明的优点是：
    本发明的涂料耐沾污性持久，可以通过雨水的冲刷达到自清洁的效果，特别适合做建筑外墙涂料，涂层稳定性强，抗菌防腐性好，综合品质高。
具体实施方式
实施例1
一种自清洁涂料，它是由下述重量份的原料组成的：
丙烯酸酯乳液52.1、2,4-二甲基苯乙酮0.2、脲丙基三乙氧基硅烷0.6、氧化锌0.4、对羟基苯甲酸甲酯0.4、伊利石粉6、钛白粉18、聚丙烯酸丁酯2、2- 氨基-2- 甲基-1- 丙醇1.3、乙撑双硬脂酰胺1.3、成膜助剂5、去离子水40；
所述的成膜助剂是由下述重量份的原料组成的：
丙烯酸酯20、氨基三甲叉膦酸1、乙二胺四乙酸二钠3、氨丙基三乙氧基硅烷0.1、沙棘油2、过硫酸钾0.7、水60；
将丙烯酸酯与氨丙基三乙氧基硅烷混合，60℃下搅拌混合7分钟，加入到上述水中，搅拌条件下加入过硫酸钾，搅拌均匀；
将乙二胺四乙酸二钠与氨基三甲叉膦酸混合，搅拌均匀后加入沙棘油，在60℃下搅拌混合5分钟，冷却至常温；
将上述处理后的各原料与剩余各原料混合，1000转/分搅拌分散30分钟，即得所述成膜助剂。
一种自清洁涂料的制备方法，包括以下步骤：
（1）将钛白粉与伊利石粉混合，球磨均匀后加入到去离子水中，加入脲丙基三乙氧基硅烷，60℃下搅拌混合30分钟；
（2）将氧化锌与对羟基苯甲酸甲酯混合，搅拌均匀后加入乙撑双硬脂酰胺，混合均匀；
（3）将丙烯酸酯乳液与聚丙烯酸丁酯混合，56℃下搅拌混合4分钟；
（4）将上述处理后的各原料与剩余各原料混合，800转/分搅拌分散40分钟，经砂磨机研磨至细度15μm，过滤，即得所述自清洁涂料。
使用方法：
本发明的涂料在施工时，要求建筑墙面要预先用水泥腻子批平，干燥，涂刷封底涂料1-2 道，干燥，然后，喷涂本发明涂料，厚度为2-3毫米左右为宜，然后立刻用压花辊进行辊压；
性能测试：
漆膜外观饱满、平整、无硬块、光泽度好；
耐水性：200h无异常；
耐酸性：240h无异常；
耐碱性：200h无异常；
低温稳定性：3次循环不变质；
耐人工老化性试验：1000小时不起泡、不剥落、无裂纹。

Claims (2)

1.一种自清洁涂料，其特征在于它是由下述重量份的原料组成的：
丙烯酸酯乳液52.1-60、2,4-二甲基苯乙酮0.1-0.2、脲丙基三乙氧基硅烷0.6-1、氧化锌0.4-1、对羟基苯甲酸甲酯0.4-1、伊利石粉4-6、钛白粉14-18、聚丙烯酸丁酯2-3、2- 氨基-2- 甲基-1- 丙醇1.3-2、乙撑双硬脂酰胺1.3-2、成膜助剂5-7、去离子水26-40；
所述的成膜助剂是由下述重量份的原料组成的：
丙烯酸酯12-20、氨基三甲叉膦酸1-2、乙二胺四乙酸二钠2-3、氨丙基三乙氧基硅烷0.1-1、沙棘油1-2、过硫酸钾0.7-2、水50-60；
将丙烯酸酯与氨丙基三乙氧基硅烷混合，50-60℃下搅拌混合4-7分钟，加入到上述水中，搅拌条件下加入过硫酸钾，搅拌均匀；
将乙二胺四乙酸二钠与氨基三甲叉膦酸混合，搅拌均匀后加入沙棘油，在50-60℃下搅拌混合3-5分钟，冷却至常温；
将上述处理后的各原料与剩余各原料混合，800-1000转/分搅拌分散20-30分钟，即得所述成膜助剂。
2.一种如权利要求1所述的自清洁涂料的制备方法，其特征在于包括以下步骤：
（1）将钛白粉与伊利石粉混合，球磨均匀后加入到去离子水中，加入脲丙基三乙氧基硅烷，50-60℃下搅拌混合20-30分钟；
（2）将氧化锌与对羟基苯甲酸甲酯混合，搅拌均匀后加入乙撑双硬脂酰胺，混合均匀；
（3）将丙烯酸酯乳液与聚丙烯酸丁酯混合，50-60℃下搅拌混合2-4分钟；
（4）将上述处理后的各原料与剩余各原料混合，700-800转/分搅拌分散30-40分钟，经砂磨机研磨至细度10-15μm，过滤，即得所述自清洁涂料。
CN201410280466.1A 2014-06-21 2014-06-21 一种自清洁涂料 Pending CN104109436A (zh)