CN104031498A - 一种用于易拉罐表面的水性涂料及其制备方法 - Google Patents
一种用于易拉罐表面的水性涂料及其制备方法 Download PDFInfo
- Publication number
- CN104031498A CN104031498A CN201410232103.0A CN201410232103A CN104031498A CN 104031498 A CN104031498 A CN 104031498A CN 201410232103 A CN201410232103 A CN 201410232103A CN 104031498 A CN104031498 A CN 104031498A
- Authority
- CN
- China
- Prior art keywords
- water
- pop
- borne coatings
- aminoresin
- flow agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于易拉罐表面的水性涂料及其制备方法，属于涂料技术领域。该涂料由水性改性树脂、氨基树脂、流平剂、增稠剂、乙醚和去离子水混合后搅拌均匀制备得到。制备得到的水性涂料附着在易拉罐表面具有较好的RCA耐磨性(175g力，300圈以上不露底)和较强的硬度(≥5H)，此外，该易拉罐还具有优异的耐蒸煮性，在温度为130℃条件下蒸煮1小时后，易拉罐表面的涂料不失光，不起泡，不剥落。
Description
技术领域
本发明属于涂料技术领域，具体涉及一种用于易拉罐表面的水性涂料及其制备方法。
背景技术
易拉罐具有重量轻、体积小、不易破碎、便于携带的优点，所以备受人们青睐。随着人们环保意识的增强以及环境保护的客观要求，传统涂料在涂装过程中会造成大量有机溶剂的挥发，不仅会影响涂膜的性能，还会损害作业人员的健康并导致环境污染，据报道涂料涂装过程挥发的有机溶剂是美国空气污染的主要来源之一。因此，环保型涂料成为当前以及今后涂料的重点研究方向之一。
目前，水性涂料在金属涂装领域的应用集中在食品、饮料包装罐涂装，但是现有的水性涂料在耐蒸煮性和耐磨性方面存在不足。因此，急需开发一种新的适于金属表面的水性涂料。
发明内容
本发明的目的是针对上述问题提供一种用于易拉罐表面的水性涂料，该涂料具有优异的耐蒸煮性能、耐磨性能以及较强的硬度。此外，本发明还有一个目的是提供上述水性涂料的制备方法。
本发明的目的可以通过以下技术方案实现：
一种用于易拉罐表面的水性涂料，其特征在于：该涂料由以下重量百分比的原料混合而成：
上述各组分之和为100wt％。
优选：所述的用于易拉罐表面的水性涂料由以下重量百分比的原料混合而成：水性改性树脂53～63wt％，氨基树脂21～31wt％，流平剂0.1～1wt％，增稠剂1～4wt％，乙醚1～8wt％和去离子水5～10wt％。前述各组分之和为100wt％。
进一步优选：所述的用于易拉罐表面的水性涂料由以下重量百分比的原料混合而成：水性改性树脂58wt％，氨基树脂26wt％，流平剂0.5wt％，增稠剂1.5wt％，乙醚5wt％和去离子水9wt％。
所述的水性改性树脂为AC769RG水溶性有机硅改性丙烯酸树脂。
所述的流平剂为迪高流平剂2100。
所述的氨基树脂为氨基树脂717。
所述的增稠剂为增稠剂TT935。
一种上述用于易拉罐表面的水性涂料的制备方法，该制备方法是将水性改性树脂、氨基树脂、流平剂、增稠剂、乙醚和去离子水混合后搅拌30～50min制得。
本发明的有益效果：
本发明技术方案用于易拉罐表面的水性涂料，该涂料附着在易拉罐表面具有较好的RCA耐磨性(175g力，300圈以上不露底)和较强的硬度(≥5H)，此外，该易拉罐还具有优异的耐蒸煮性，在温度为130℃条件下蒸煮1小时后，易拉罐表面的涂料不失光，不起泡，不剥落。
具体实施方式
下面结合实施例对本发明作进一步说明，但本发明的保护范围不限于此：
1.实施例1～3
2.水性涂料的制备：将水性改性树脂(AC769RG水溶性有机硅改性丙烯酸树脂)、氨基树脂(氨基树脂717)、流平剂(迪高流平剂2100)、增稠剂(增稠剂TT935)、乙醚和去离子水混合后搅拌30～50min制得。
3.施工工序：首先将制备好的涂料搅拌30分钟，静置20分钟待气泡完全消掉；然后将准备好的样板放置好，启动涂料滚涂装置，进行涂膜，经过烘道150～160℃，30～45分钟的烘烤后，即得到所需成品。
4.将实施例1～3制备得到的成品进行如下的测试，测试技术指标见表.
实验研究发现，缺少水性改性树脂(AC769RG水溶性有机硅改性丙烯酸树脂)和氨基树脂(氨基树脂717)中的任意一种，制备得到的涂料硬度均≤3B，此外，RCA耐磨性能也降低，120圈左右就出现剥落的现象。
Claims (8)
1.一种用于易拉罐表面的水性涂料，其特征在于：该涂料由以下重量百分比的原料混合而成：
2.根据权利要求1所述的用于易拉罐表面的水性涂料，其特征在于：该涂料由以下重量百分比的原料混合而成：水性改性树脂53～63wt％，氨基树脂21～31wt％，流平剂0.1～1wt％，增稠剂1～4wt％，乙醚1～8wt％和去离子水5～10wt％。
3.根据权利要求2所述的用于易拉罐表面的水性涂料，其特征在于：该涂料由以下重量百分比的原料混合而成：水性改性树脂58wt％，氨基树脂26wt％，流平剂0.5wt％，增稠剂1.5wt％，乙醚5wt％和去离子水9wt％。
4.根据权利要求1-3任一项所述的用于易拉罐表面的水性涂料，其特征在于：所述的水性改性树脂为AC769RG水溶性有机硅改性丙烯酸树脂。
5.根据权利要求1-3任一项所述的用于易拉罐表面的水性涂料，其特征在于：所述的流平剂为迪高流平剂2100。
6.根据权利要求1-3任一项所述的用于易拉罐表面的水性涂料，其特征在于：所述的氨基树脂为氨基树脂717。
7.根据权利要求1-3任一项所述的用于易拉罐表面的水性涂料，其特征在于：所述的增稠剂为增稠剂TT935。
8.一种权利要求1-3任一项所述的用于易拉罐表面的水性涂料的制备方法，其特征在于：该方法是将水性改性树脂、氨基树脂、流平剂、有机溶剂、增稠剂和去离子水混合后搅拌30～50min制得。