CN104030616B - 一种耐腐蚀高强度混凝土及其制备方法 - Google Patents
一种耐腐蚀高强度混凝土及其制备方法 Download PDFInfo
- Publication number
- CN104030616B CN104030616B CN201410178399.2A CN201410178399A CN104030616B CN 104030616 B CN104030616 B CN 104030616B CN 201410178399 A CN201410178399 A CN 201410178399A CN 104030616 B CN104030616 B CN 104030616B
- Authority
- CN
- China
- Prior art keywords
- concrete
- water
- powder
- plant ash
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种耐腐蚀高强度混凝土,由下列重量份的原料制成：水泥320‑340、石子900‑920、砂240‑260、水120‑130、改性草木灰80‑100、二甲基硅油3‑5、抗坏血酸1‑1.3、霞石粉40‑60、磷酸铜1‑2、石英尾砂80‑100、水镁石纤维20‑25、羧基丙烯酸树脂粉末4‑6、聚羧酸高效减水剂6‑7、氰脲酸三缩水甘油酯2‑3、吡啶硫酮锌1‑1.6、废旧微晶玻璃粉20‑25、超细矿粉30‑40；本发明混凝土具有优异的抗菌防腐蚀性能，通过添加霞石粉，减小了混凝土的干收缩率，防止裂纹产生；通过添加水镁石纤维，增加了混凝土的强度、耐热性、保温性能。
Description
技术领域
本发明属于建筑材料领域，特别涉及一种耐腐蚀高强度混凝土及其制备方法。
背景技术
混凝土作为建筑材料已有一百多年历史，具有很多无法比拟的优点，例如抗压强度高，取材容易，易成型，价格低廉，可与其他材料结合制成各种沉重固件。
随着混凝土组成材料的不断发展，人们对混凝土的性能要求不仅仅局限于抗压强度，而是在立足强度的基础上，更加注重混凝土的耐久性、变形性能、防火抗爆性能、防渗水性能、韧性、耐腐蚀性、保温性、健康环保性以及降低成本等等综合指标的平衡和协调。混凝土各项性能指标的要求比以前更明确、细化和具体。同时，建筑设备水平的提升，新型施工工艺的不断涌现和推广，使混凝土技术适应了不同的设计、施工和使用要求，发展很快。因此，研制性能更加优异、功能更加强大、更适应新工艺的混凝土就显得尤为重要。
发明内容
本发明的目的在于提供一种耐腐蚀高强度混凝土及其制备方法，该混凝土具有优异的抗菌防腐蚀性能，干收缩率低，耐水性好，强度高、耐热性好、保温性能好。
本发明的技术方案如下：
一种耐腐蚀高强度混凝土,其特征在于由下列重量份的原料制成：水泥320-340、石子900-920、砂240-260、水120-130、改性草木灰80-100、二甲基硅油3-5、抗坏血酸1-1.3、霞石粉40-60、磷酸铜1-2、石英尾砂80-100、水镁石纤维20-25、羧基丙烯酸树脂粉末4-6、聚羧酸高效减水剂6-7、氰脲酸三缩水甘油酯2-3、吡啶硫酮锌1-1.6、废旧微晶玻璃粉20-25、超细矿粉30-40；
所述改性草木灰由下列重量份的原料制成：草木灰80-90、十三氟辛基三甲氧基硅烷5-7、聚葡萄糖1-2、木钙1-2、玻璃粉10-20、微孔硅酸钙8-10、丙烯酸甲酯3-4、石蜡乳液3-4、超细矿粉10-15、环氧丙烯酸酯6-7、碳酸钙3-4、过硫酸铵0.4-0.5、羟丙基淀粉0.7-1、磷酸酯0.6-0.9、水40-50；制作方法为：将草木灰与石蜡乳液、十三氟辛基三甲氧基硅烷混合均匀，放置1-2天，再与微孔硅酸钙、丙烯酸甲酯、超细矿粉、环氧丙烯酸酯、过硫酸铵、水混合，搅拌成泥状，加热至80-90℃，搅拌30-40分钟，搅拌烘干粉碎成100-200目颗粒，再与其他剩余成分混合，分散研磨10-15分钟，即得。
所述的耐腐蚀高强度混凝土的制备方法，其特征在于包括以下步骤：
（1）将霞石粉、磷酸铜、羧基丙烯酸树脂粉末、吡啶硫酮锌混合，分散研磨20-30分钟，得到混合物；
（2）将氰脲酸三缩水甘油酯、聚羧酸高效减水剂、抗坏血酸与水混合，搅拌均匀，得到混合物；
（3）将其他剩余成分与第一步和第二步得到的混合物混合，搅拌2-6分钟，然后浇注；
（4）浇筑后在 5-25℃的潮湿环境中进行养护，养护时间不少于 7d。
本发明的有益效果
本发明混凝土使用了磷酸铜、吡啶硫酮锌，使得混凝土具有优异的抗菌防腐蚀性能，通过添加霞石粉，减小了混凝土的干收缩率，防止裂纹产生；通过使用使用石英尾砂和废旧微晶玻璃粉，增加了混凝土的耐水性和耐腐蚀性；通过添加水镁石纤维，增加了混凝土的强度、耐热性、保温性能；通过使用改性草木灰，增加了混凝土的密实性、防水性，可塑性和可泵送效果好。
具体实施方式
一种耐腐蚀高强度混凝土,由下列重量份（公斤）的原料制成：水泥330、石子910、砂250、水125、改性草木灰90、二甲基硅油4、抗坏血酸1.2、霞石粉50、磷酸铜1.5、石英尾砂90、水镁石纤维23、羧基丙烯酸树脂粉末5、聚羧酸高效减水剂6.5、氰脲酸三缩水甘油酯2.5、吡啶硫酮锌1.4、废旧微晶玻璃粉24、超细矿粉35；
所述改性草木灰由下列重量份（公斤）的原料制成：草木灰85、十三氟辛基三甲氧基硅烷6、聚葡萄糖1.5、木钙1.5、玻璃粉15、微孔硅酸钙9、丙烯酸甲酯3.5、石蜡乳液3.5、超细矿粉13、环氧丙烯酸酯6.5、碳酸钙3.5、过硫酸铵0.5、羟丙基淀粉0.8、磷酸酯0.7、水45；制作方法为：将草木灰与石蜡乳液、十三氟辛基三甲氧基硅烷混合均匀，放置1天，再与微孔硅酸钙、丙烯酸甲酯、超细矿粉、环氧丙烯酸酯、过硫酸铵、水混合，搅拌成泥状，加热至85℃，搅拌35分钟，搅拌烘干粉碎成160目颗粒，再与其他剩余成分混合，分散研磨14分钟，即得。
所述的耐腐蚀高强度混凝土的制备方法，包括以下步骤：
（1）将霞石粉、磷酸铜、羧基丙烯酸树脂粉末、吡啶硫酮锌混合，分散研磨25分钟，得到混合物；
（2）将氰脲酸三缩水甘油酯、聚羧酸高效减水剂、抗坏血酸与水混合，搅拌均匀，得到混合物；
（3）将其他剩余成分与第一步和第二步得到的混合物混合，搅拌4分钟，然后浇注；
（4）浇筑后在 12-21℃的潮湿环境中进行养护9d。
实验数据：
该实施例的混凝土坍落度为13cm,强度等级为C45，抗压强度 52MPa，抗折强度 19.4Mpa。
Claims (2)
1.一种耐腐蚀高强度混凝土,其特征在于由下列重量份的原料制成：水泥320-340、石子900-920、砂240-260、水120-130、改性草木灰80-100、二甲基硅油3-5、抗坏血酸1-1.3、霞石粉40-60、磷酸铜1-2、石英尾砂80-100、水镁石纤维20-25、羧基丙烯酸树脂粉末4-6、聚羧酸高效减水剂6-7、氰脲酸三缩水甘油酯2-3、吡啶硫酮锌1-1.6、废旧微晶玻璃粉20-25、超细矿粉30-40； 所述改性草木灰由下列重量份的原料制成：草木灰80-90、十三氟辛基三甲氧基硅烷5-7、聚葡萄糖1-2、木钙1-2、玻璃粉10-20、微孔硅酸钙8-10、丙烯酸甲酯3-4、石蜡乳液3-4、超细矿粉10-15、环氧丙烯酸酯6-7、碳酸钙3-4、过硫酸铵0.4-0.5、羟丙基淀粉0.7-1、磷酸酯0.6-0.9、水40-50；制作方法为：将草木灰与石蜡乳液、十三氟辛基三甲氧基硅烷混合均匀，放置1-2天，再与微孔硅酸钙、丙烯酸甲酯、超细矿粉、环氧丙烯酸酯、过硫酸铵、水混合，搅拌成泥状，加热至80-90℃，搅拌30-40分钟，搅拌烘干粉碎成100-200目颗粒，再与其他剩余成分混合，分散研磨10-15分钟，即得。
2.根据权利要求1所述的耐腐蚀高强度混凝土的制备方法，其特征在于包括以下步骤：
（1）将霞石粉、磷酸铜、羧基丙烯酸树脂粉末、吡啶硫酮锌混合，分散研磨20-30分钟，得到混合物；
（2）将氰脲酸三缩水甘油酯、聚羧酸高效减水剂、抗坏血酸与水混合，搅拌均匀，得到混合物；
（3）将其他剩余成分与第一步和第二步得到的混合物混合，搅拌2-6分钟，然后浇注；
（4）浇注后在 5-25℃的潮湿环境中进行养护，养护时间不少于7d。