CN104016620A - 一种抗菌混凝土及其制备方法 - Google Patents

一种抗菌混凝土及其制备方法 Download PDF

Info

Publication number
CN104016620A
CN104016620A CN201410178392.0A CN201410178392A CN104016620A CN 104016620 A CN104016620 A CN 104016620A CN 201410178392 A CN201410178392 A CN 201410178392A CN 104016620 A CN104016620 A CN 104016620A
Authority
CN
China
Prior art keywords
parts
performance
concrete
stir
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410178392.0A
Other languages
English (en)
Inventor
方明珠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zongyang County Tian Zhu New Building Materials Co Ltd
Original Assignee
Zongyang County Tian Zhu New Building Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zongyang County Tian Zhu New Building Materials Co Ltd filed Critical Zongyang County Tian Zhu New Building Materials Co Ltd
Priority to CN201410178392.0A priority Critical patent/CN104016620A/zh
Publication of CN104016620A publication Critical patent/CN104016620A/zh
Pending legal-status Critical Current

Abstract

一种抗菌混凝土,由下列重量份的原料制成：水泥280-310、矿粉50-60、粉煤灰60-70、石子970-1000、砂450-470、水150-170、温伦胶2.5-2.8、聚丙烯酸0.8-1.4、石墨14-17、熟石膏20-25、三氧化二锑4-6、四针状氧化锌晶须4-6、聚葡萄糖1-2、明矾石粉80-100、聚羧酸高效减水剂7-7.5、甲基纤维素2-3、透明质酸钠1-2、改性草木灰60-80、硅烷偶联剂KH-5501-1.5；本发明混凝土密实性能和抗渗性能好，耐腐蚀性好；耐磨、降噪、吸波、抗老化、抗静电、抗菌等性能好；同时本发明混凝土抗压抗折强度、抗裂性能、抗冲击能力比一般混凝土大大提高。

Description

一种抗菌混凝土及其制备方法
技术领域
本发明属于建筑材料领域，特别涉及一种抗菌混凝土及其制备方法。 
背景技术
混凝土作为建筑材料已有一百多年历史，具有很多无法比拟的优点，例如抗压强度高，取材容易，易成型，价格低廉，可与其他材料结合制成各种沉重固件。 
随着混凝土组成材料的不断发展，人们对混凝土的性能要求不仅仅局限于抗压强度，而是在立足强度的基础上，更加注重混凝土的耐久性、变形性能、防火抗爆性能、防渗水性能、韧性、耐腐蚀性、保温性、健康环保性以及降低成本等等综合指标的平衡和协调。混凝土各项性能指标的要求比以前更明确、细化和具体。同时，建筑设备水平的提升，新型施工工艺的不断涌现和推广，使混凝土技术适应了不同的设计、施工和使用要求，发展很快。因此，研制性能更加优异、功能更加强大、更适应新工艺的混凝土就显得尤为重要。 
发明内容
本发明的目的在于提供一种抗菌混凝土及其制备方法，该混凝土密实性能和抗渗性能好，耐腐蚀性好，耐磨、降噪、吸波、抗老化、抗静电、抗菌等性能好，同时本发明混凝土抗压抗折强度、抗裂性能、抗冲击能力比一般混凝土大大提高。 
本发明的技术方案如下： 
一种抗菌混凝土,其特征在于由下列重量份的原料制成：水泥280-310、矿粉50-60、粉煤灰60-70、石子970-1000、砂450-470、水150-170、温伦胶2.5-2.8、聚丙烯酸0.8-1.4、石墨14-17、熟石膏20-25、三氧化二锑4-6、四针状氧化锌晶须4-6、聚葡萄糖1-2、明矾石粉80-100、聚羧酸高效减水剂7-7.5、甲基纤维素2-3、透明质酸钠1-2、改性草木灰60-80、硅烷偶联剂KH-550 1-1.5；
所述改性草木灰由下列重量份的原料制成：草木灰80-90、十三氟辛基三甲氧基硅烷5-7、聚葡萄糖1-2、木钙1-2、玻璃粉10-20、微孔硅酸钙8-10、丙烯酸甲酯3-4、石蜡乳液3-4、超细矿粉10-15、环氧丙烯酸酯6-7、碳酸钙3-4、过硫酸铵0.4-0.5、羟丙基淀粉0.7-1、磷酸酯0.6-0.9、水40-50；制作方法为：将草木灰与石蜡乳液、十三氟辛基三甲氧基硅烷混合均匀，放置1-2天，再与微孔硅酸钙、丙烯酸甲酯、超细矿粉、环氧丙烯酸酯、过硫酸铵、水混合，搅拌成泥状，加热至80-90℃，搅拌30-40分钟，搅拌烘干粉碎成100-200目颗粒，再与其他剩余成分混合，分散研磨10-15分钟，即得。
所述的抗菌混凝土的制备方法，其特征在于包括以下步骤： 
（1）将粉煤灰、石墨、三氧化二锑、四针状氧化锌晶须混合，加入温伦胶、硅烷偶联剂KH-550搅拌均匀，分散研磨20-30分钟，得到混合物；
（2）将聚丙烯酸、聚葡萄糖、聚羧酸高效减水剂、甲基纤维素、透明质酸钠与水混合，搅拌均匀，得到混合物；
（3）将其他剩余成分与第一步和第二步得到的混合物混合，搅拌2-6分钟，然后浇注；
（4）浇筑后在 10-27℃的潮湿环境中进行养护，养护时间不少于 7d。
本发明的有益效果 
本发明混凝土密实性能和抗渗性能好，通过使用明矾石粉，具有热电效应，能够抗菌从而提高了耐腐蚀性；通过添加四针状氧化锌晶须，提高了混凝土的耐磨、降噪、吸波、抗老化、抗静电、抗菌等性能；同时本发明混凝土抗压抗折强度、抗裂性能、抗冲击能力比一般混凝土大大提高 ；通过使用改性草木灰，增加了混凝土的密实性、防水性，可塑性和可泵送效果好。
具体实施方式
一种抗菌混凝土,由下列重量份(公斤)的原料制成：水泥290、矿粉55、粉煤灰65、石子990、砂460、水160、温伦胶2.6、聚丙烯酸1.2、石墨16、熟石膏23、三氧化二锑5、四针状氧化锌晶须5、聚葡萄糖1.5、明矾石粉90、聚羧酸高效减水剂7.3、甲基纤维素2.5、透明质酸钠1.5、改性草木灰70、硅烷偶联剂KH-550 1.3； 
所述改性草木灰由下列重量份（公斤）的原料制成：草木灰85、十三氟辛基三甲氧基硅烷6、聚葡萄糖1.5、木钙1.5、玻璃粉15、微孔硅酸钙9、丙烯酸甲酯3.5、石蜡乳液3.5、超细矿粉13、环氧丙烯酸酯6.5、碳酸钙3.5、过硫酸铵0.5、羟丙基淀粉0.8、磷酸酯0.7、水45；制作方法为：将草木灰与石蜡乳液、十三氟辛基三甲氧基硅烷混合均匀，放置1天，再与微孔硅酸钙、丙烯酸甲酯、超细矿粉、环氧丙烯酸酯、过硫酸铵、水混合，搅拌成泥状，加热至85℃，搅拌35分钟，搅拌烘干粉碎成160目颗粒，再与其他剩余成分混合，分散研磨14分钟，即得。
所述的抗菌混凝土的制备方法，包括以下步骤： 
（1）将粉煤灰、石墨、三氧化二锑、四针状氧化锌晶须混合，加入温伦胶、硅烷偶联剂KH-550搅拌均匀，分散研磨25分钟，得到混合物；
（2）将聚丙烯酸、聚葡萄糖、聚羧酸高效减水剂、甲基纤维素、透明质酸钠与水混合，搅拌均匀，得到混合物；
（3）将其他剩余成分与第一步和第二步得到的混合物混合，搅拌4分钟，然后浇注；
（4）浇筑后在 10-18℃的潮湿环境中进行养护，养护时间7d。
实验数据： 
该实施例的混凝土坍落度为14cm,强度等级为C40，抗压强度41MPa，抗折强度 18.2Mpa。

Claims (2)

1.一种抗菌混凝土,其特征在于由下列重量份的原料制成：水泥280-310、矿粉50-60、粉煤灰60-70、石子970-1000、砂450-470、水150-170、温伦胶2.5-2.8、聚丙烯酸0.8-1.4、石墨14-17、熟石膏20-25、三氧化二锑4-6、四针状氧化锌晶须4-6、聚葡萄糖1-2、明矾石粉80-100、聚羧酸高效减水剂7-7.5、甲基纤维素2-3、透明质酸钠1-2、改性草木灰60-80、硅烷偶联剂KH-550 1-1.5；
所述改性草木灰由下列重量份的原料制成：草木灰80-90、十三氟辛基三甲氧基硅烷5-7、聚葡萄糖1-2、木钙1-2、玻璃粉10-20、微孔硅酸钙8-10、丙烯酸甲酯3-4、石蜡乳液3-4、超细矿粉10-15、环氧丙烯酸酯6-7、碳酸钙3-4、过硫酸铵0.4-0.5、羟丙基淀粉0.7-1、磷酸酯0.6-0.9、水40-50；制作方法为：将草木灰与石蜡乳液、十三氟辛基三甲氧基硅烷混合均匀，放置1-2天，再与微孔硅酸钙、丙烯酸甲酯、超细矿粉、环氧丙烯酸酯、过硫酸铵、水混合，搅拌成泥状，加热至80-90℃，搅拌30-40分钟，搅拌烘干粉碎成100-200目颗粒，再与其他剩余成分混合，分散研磨10-15分钟，即得。
2.根据权利要求1所述的抗菌混凝土的制备方法，其特征在于包括以下步骤：
（1）将粉煤灰、石墨、三氧化二锑、四针状氧化锌晶须混合，加入温伦胶、硅烷偶联剂KH-550搅拌均匀，分散研磨20-30分钟，得到混合物；
（2）将聚丙烯酸、聚葡萄糖、聚羧酸高效减水剂、甲基纤维素、透明质酸钠与水混合，搅拌均匀，得到混合物；
（3）将其他剩余成分与第一步和第二步得到的混合物混合，搅拌2-6分钟，然后浇注；
（4）浇筑后在 10-27℃的潮湿环境中进行养护，养护时间不少于 7d。
CN201410178392.0A 2014-04-30 2014-04-30 一种抗菌混凝土及其制备方法 Pending CN104016620A (zh)