CN104016714A - 水泥密封固化剂及其施工工艺 - Google Patents

水泥密封固化剂及其施工工艺 Download PDF

Info

Publication number
CN104016714A
CN104016714A CN201410185988.3A CN201410185988A CN104016714A CN 104016714 A CN104016714 A CN 104016714A CN 201410185988 A CN201410185988 A CN 201410185988A CN 104016714 A CN104016714 A CN 104016714A
Authority
CN
China
Prior art keywords
solidifying agent
ground
parts
polishing
cement seal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410185988.3A
Other languages
English (en)
Inventor
李东平
蒋少雄
赵广杰
孙腾远
李艳蓉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin University of Science and Technology
Original Assignee
Harbin University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin University of Science and Technology filed Critical Harbin University of Science and Technology
Priority to CN201410185988.3A priority Critical patent/CN104016714A/zh
Publication of CN104016714A publication Critical patent/CN104016714A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种建筑涂料，具体为一种锂基渗透结晶型水泥密封固化剂。水泥密封固化剂配方为：硅酸钠15～20份、硅酸锂8～15份、氟硅酸镁3～5份、磷酸二氢钠2～4份、涂料用水性色浆0～6份、水50～70份。采用本发明的水泥密封固化剂施工工艺步骤为：新地面：新地面抹光作业-初步硬化-涂覆固化剂-完全干燥固化-清水冲洗地面-自然干燥-打磨机打磨抛光。旧地面：打磨清洗旧地面-涂覆固化剂-自然干燥-清洗地面-自然干燥-打磨抛光（或追加固化剂-清洗地面-自然干燥-打磨抛光）。施用本固化剂及施工工艺后，混凝土的强度、硬度、密实度都得到了很大提升，有效提高了混凝土的耐久性和混凝土抗风化能力。

Description

水泥密封固化剂及其施工工艺
技术领域
本发明涉及一种水泥地面改善涂料及其施工工艺，具体为一种锂基渗透结晶型水泥密封固化剂及其施工工艺。 
背景技术
混凝土固化剂是碱激活的化学渗透混凝土的无机硅防水剂，组份内的催化剂能和混凝土的游离碱发生缩合反应，形成枝蔓状的微细颗粒晶体，封闭混凝土的毛细孔和微细裂缝，构成一道内在屏障的防水保护，提高混凝土表层的抗压强度和密实程度，能有效阻止外界水分和腐蚀性气体的渗入。 
使用混凝土密封固化剂后，混凝土内部生成了很多硅凝胶晶体，这些硅凝胶经水化变成坚固、透气、簇状的物质充满混凝土表面下的所有毛细孔隙，使混凝土的强度、硬度、密实度都得到了很大提升，能有效提高混凝土的耐久性和防止混凝土风化。 
水泥密封固化剂现中国市场有三代产品 
第一代,钠基产品
有限提高混凝土强度和耐磨性,缺点控制不好容易泛碱发白,这种产品的市场由最初的进口产品为主,变成如今的与国内产品平分天下.另外由 于国内产品大多数为仿制品,在材料助剂方面它无法去完全照搬进口产品,性能方面有很大区别。
第二代,钾基产品 
这种产品在大陆市场不是很常见,其性能比钠基的稍微有所改进,但不是很明显,替换的可能性很小。
第三代锂基产品 
锂基的产品在性能上与前两代产品相比,具有无比的优越性,它可以很大程度上降低或避免混凝土和耐磨地面的发丝状裂纹,它可以更大程度上提高混凝土和耐磨地面的抗压强度和耐磨性,它可以避免前两代产品出现的泛碱发白的通病,在施工方面减少了清水冲洗基面的繁琐工序,等等事实说明了第三代锂基产品的优越性和理想性。
本发明属于第三代锂基水泥密封固化剂，并在此基础上引入氟硅酸镁、磷酸二氢钠等成分。使用本发明固化剂后，混凝土内部生成了很多硅凝胶晶体，这些硅凝胶经水化变成坚固、透气、簇状的物质充满混凝土表面下的所有毛细孔隙，可以更有效地提高混凝土地面的硬度及耐磨性。本发明组分成本低廉，加工工艺简单具有很强的市场竞争力。 
发明内容
本发明以硅酸钠和硅酸锂为主成分，以水为溶剂，另引入辅助成分：氟硅酸镁，磷酸二氢钠。 
具体配方为： 
硅酸钠15～20份
硅酸锂8～15份
氟硅酸镁3～5份
磷酸二氢钠2～4份
涂料用水性色浆0～6份
水50～70份
配制方法：将固体成分混合均匀后加入水与水性色浆，强烈搅拌60分钟形成均匀稳定的透明溶液 ，长期存放不析出、不反应 ，外观无变化。
本发明水泥密封固化剂所用硅酸钠与硅酸锂，要求其模数均小于2。 
采用本发明的水泥密封固化剂施工工艺步骤为：新地面：新地面抹光作业-初步硬化-涂覆固化剂-完全干燥固化-清水冲洗地面-自然干燥-打磨机打磨抛光；旧地面：打磨清洗旧地面-涂覆固化剂-自然干燥-清洗地面-自然干燥-打磨抛光（或追加固化剂-清洗地面-自然干燥-打磨抛光）。 
施工温度：1.7～57℃。当低于4℃时混凝土应用塑料膜完全覆盖。
本发明的水泥密封固化剂优点如下：
渗透力强。可渗透到5-8mm的混凝土里层；有效密封，硬化剂将混凝土密封成一个坚固的实体，并能渗透到混凝土里层，从内部封堵混凝土毛细孔，混凝土将变得坚固密实，有效的抑制外界污染物进入混凝土中，从而提高、延长了混凝土的寿命。
处理后的水泥地面坚硬耐磨。固化剂与混凝土中的物质发生反应形成硬性物质，堵塞混凝土中的结构空隙，大大提高混凝土表层的硬化耐磨程度，形成长久类似大理石般的保护层。最佳可达莫氏硬度8-9度。 
抗化学侵蚀。凝胶状的化学结构与材料独具的特性，让使用后的混凝土表面变得坚密光滑，更有效的抑制和抵抗外界化学物质进入混凝土中，防止化学物品侵蚀破坏混凝土。抗老化性好，不会变黄，抗白化现象。 
彻底防尘。混凝土风化产生的灰尘会停留空间内的货物、货架与设备上。渗透型密封固化材料与混凝土中的盐结合，成为混凝土不可分割的一部分。因而能有效防止混凝土表面产生灰尘，保护设备、货物、货架不受尘土等的侵扰。 
呼吸功能。在阻止大部分的杂质进入混凝土内部的同时，允许气体和水自由流通，让混凝土得以呼吸，从而避免起鼓、脱皮、微裂纹等混凝土的特点。 
光亮防滑。经处理，基层好的地面会出现迷人的光亮防滑。且经时间的延缓，外观会更好看，使清洁工作变得简单，不需要重复维护。 
环保，产品无色、无味、不会挥发有毒气体，可边生产边施工，可快速投入使用。
具体实施方式：
新地面：紧跟在抹光作业后，人在上面行走而不会产生脚印时，即施用本固化剂。具体步骤为：新地面抹光作业-初步硬化-涂覆固化剂-完全干燥固化-清水冲洗地面-自然干燥-打磨机打磨抛光。
旧地面：任何时间都可以，具体步骤为：打磨清洗旧地面-涂覆固化剂-干燥-清洗-干燥-打磨抛光。当一次涂覆固化剂效果不理想时可以追加固化剂-清洗地面-自然干燥-打磨抛光 
施工温度：1.7～57℃。当低于4℃时混凝土应用塑料膜完全覆盖；固化剂施工用量：机磨竣光地坪覆盖率为5M2/L；
施工工具：低压喷嘴、滚筒、毛刷或精良柔软的硬毛刷；
在产品地面涂抹油漆或环氧涂料前，至少应干燥7天。
实例1：
首先进行水泥密封固化剂的配制：用模数为1.5的硅酸锂与硅酸钠。按配方称取硅酸钠20 g，硅酸锂12 g，氟硅酸镁4 g，磷酸二氢钠4 g。将所称取组分混匀，室温下加入60 g水匀速搅拌60分钟，配制完的水泥密封固化剂溶液均匀稳定透明，完成待用。
然后进行地面的处理及固化剂的施工（旧地面）：用打磨机打磨地面使地面尽可能平整，除去浮尘，用浸水的拖把反复拖洗除去污物，自然晾干地面。在室温下用低压喷嘴将水泥密封固化剂喷涂在准备好的地面上，不留死角，用量为0.25kg/m2,自然晾干24小时。用清水冲洗地面除去残留固化剂及固化剂与地面的反应产物。自然晾干。观察地面硬度理想无需追涂固化剂，打磨机再次打磨使地面平整光滑避免小坑出现，除去浮尘抛光，施工完毕。 
所发明的水泥密封固化剂施工后地面性能测试结果如下：
吸水率降低程度 89%
水渗透率CRD-C48-73 7.5厘米/秒
完全硬度 86
莫式硬度 8.0
抗弯强度ASTMC78-94 635psi
pH值 12
高光 次日见效，30天内日益明显
地面泛潮 无膨胀凝胶不吸收水，也不会引起泛潮
龟裂 不会出现表面细纹或发丝状裂纹
施工后清洁 基本不产生浮灰，易清洗

Claims (5)

1.一种水泥密封固化剂，其特征在于，按重量份计，所述水泥密封固化剂配方为： 硅酸钠15～20份、硅酸锂8～15份、氟硅酸镁3～5份、磷酸二氢钠2～4份、涂料用水性色浆0～6份、水50～70份。
2.如权利要求1所述的水泥密封固化剂，其特征在于，所述的水泥密封固化剂以硅酸钠和硅酸锂为主成份。
3.如权利要求1所述的水泥密封固化剂，其特征在于，所述的水泥密封固化剂以氟硅酸镁、磷酸二氢钠和涂料用水性色浆为辅助成分。
4.如权利要求1所述的水泥密封固化剂，其特征在于，所述水泥密封固化剂所用硅酸钠与硅酸锂要求模数均小于2。
5.一种采用权利要求1所述水泥密封固化剂的施工工艺步骤为：
新地面：新地面抹光作业-初步硬化-涂覆固化剂-完全干燥固化-清水冲洗地面-自然干燥-打磨机打磨抛光，旧地面：打磨清洗旧地面-涂覆固化剂-自然干燥-清洗地面-自然干燥-打磨抛光（或追加固化剂-清洗地面-自然干燥-打磨抛光）。
CN201410185988.3A 2014-05-05 2014-05-05 水泥密封固化剂及其施工工艺 Pending CN104016714A (zh)