CN104005272A - Glass fiber-containing highly waterproof air filter paper and making method thereof - Google Patents
Glass fiber-containing highly waterproof air filter paper and making method thereof Download PDFInfo
- Publication number
- CN104005272A CN104005272A CN201410168741.0A CN201410168741A CN104005272A CN 104005272 A CN104005272 A CN 104005272A CN 201410168741 A CN201410168741 A CN 201410168741A CN 104005272 A CN104005272 A CN 104005272A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass fiber
- filter paper
- water
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass fiber-containing highly waterproof air filter paper. The glass fiber-containing highly waterproof air filter paper is made by using the following raw materials, by weight, 46-48 parts of a Bambusa textilis pulp, 52-54 parts of a mulberry bark pulp, 1-2 parts of dried oleander leaf, 0.7-0.9 parts of oleic acid, 0.4-0.5 parts of flaxseed gum, 0.3-0.5 parts of starch wheat, 3-4 parts of montmorillonite, 1-2 parts of cerium oxide, 1-2 parts of chopped glass fiber, 1-2 parts of molybdenum dioxide, 5-7 parts of polyamine epichlorohydrin resin, 3-5 parts of a vinyl acetate-acrylic emulsion, 0.3-0.4 parts of polyvinyl alcohol, 0.2-0.4 parts of a paraffin emulsion, 1-2 parts of an assistant and a proper amount of water. Cerium oxide added in the invention has a catalysis performance and can purify air; the addition of the chopped glass fiber improves the waterproof performance; and the assistant added in the invention is safe and environmentally-friendly, and forms tiny apertures on the surface of filter paper, so the adsorptivity is increased, and the filter paper has a waterproof property. The filter paper has the advantages of small filtering resistance, high efficiency, waterproof property, moisture resistance, and high wet stiffness.
Description
Technical field
The present invention relates to automobile filter field, particularly a kind of high water resistant air paper that contains glass fibre and preparation method thereof.
Background technology
Automobile air filter paper is the core material of manufacturing air cleaner of vehicle engine; because air filter is arranged in the gas handling system of engine; and engine when work conventionally can amplification quantity heat, therefore conventionally wish that this air filtration media possesses good strainability and higher filtering efficiency and certain heat-resisting quantity, WATER RESISTANCE and bursting strength.Existing Adsorption of Filter Paper is poor, and strainability is low, thereby causes filtering efficiency low, can only filtering machine oil in the impurity of 50-60%; When air paper uses in the high area of rainy humidity in addition, rise and can there is profit after the papery filter course moisture absorption, cause aperture and the porosity of filter paper to reduce, cause the problem that cleaner resistance increases and power of vehicle reduces, the heat-resisting quantity of also having is poor, the shortcomings such as tensile strength is low, bursting strength is poor, the service life of having limited filter paper.
Summary of the invention
The object of this invention is to provide a kind of high water resistant air paper that contains glass fibre and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A high water resistant air paper that contains glass fibre, is made up of the raw material of following weight portion: rascal bamboo pulp 46-48, mulberry root bark pulp 52-54, dry sweetscented oleander leaf 1-2, oleic acid 0.7-0.9, flax gum 0.4-0.5, wheaten starch 0.3-0.5, montmorillonite 3-4, cerium oxide 1-2, short glass fiber 1-2, molybdenum dioxide 1-2, polyamine epichlorohydrin resin 5-7, acrylate and vinyl acetate emulsion 3-5, polyvinyl alcohol 0.3-0.4, paraffin wax emulsions 0.2-0.4, auxiliary agent 1-2, water are appropriate;
Described auxiliary agent is made up of the raw material of following weight portion: diatomite 3-4, reed 1-2, aluminum sulfate 3-4, polyethylene glycol 3-4, liquid silica gel 2-3, titanium dioxide 3-5, lithium soap stone flour 2-3, gelatin 3-5, molecular sieve 1-2, water 50-60; Preparation method be first by diatomite, reed, molecular sieve, putting into pulverizer together, to be ground into 120-140 object mixed-powder stand-by; Then gelatin, liquid silica gel, chitin are mixed, add appropriate water to stir, be heated to 30-35 DEG C of continuation stirring and add polyethylene glycol, titanium dioxide, lithium soap stone flour after 10-15 minute, continue insulation 20-25 minute, finally add mixed-powder to stir, form turbid liquid.
A kind of high water resistant air paper that contains glass fibre of the present invention, made by following concrete steps:
(1) montmorillonite, dry sweetscented oleander leaf, cerium oxide, short glass fiber are mixed, grind to form 50-100 object powder, add wheaten starch, with the speed of 850-950 rev/min, stir 25-30 minute, then 60-70 DEG C dry 1.5-2.5 hour stand-by;
(2) rascal bamboo pulp, mulberry root bark pulp are put into hydrabrusher size degradation, then through beater, beating consistency is controlled at 5.3-6.3%, makes slurry;
(3) compound of step (1) is added in slurry, add polyvinyl alcohol, paraffin wax emulsions, be heated to 65-75 DEG C, stir, add appropriate water size mixing to solid content be 2.0-3.0%, the slurry mixing up, after forming web moulding, aspirates dehydration to the l Water Paper after moulding under the vacuum condition of 0.05-0.08Mpa;
(4) by all the other the residual components mixing and stirring except auxiliary agent, the water that adds 2-3 doubly to measure, then heating, temperature is controlled at 60-70 DEG C, boils 50-60 minute, insulation 25-30 minute, be warming up to 70-75 DEG C, stir and make maceration extract and put into dipping tank;
(5) body paper after step (3) dehydration is passed through to dipping tank with the speed of 3-3.5m/s, maceration extract is uniformly coated on body paper, in electric drying oven with forced convection, dries 4-5min, then auxiliary agent is coated on the body paper of oven dry, dry 6-10min on last ray machine, after taking-up and get final product.
The invention has the beneficial effects as follows: the present invention adds cerium oxide, there is catalytic performance, can purify air, add short glass fiber and improved water repelling property; Add auxiliary agent, safety and environmental protection, the small hole forming on filter paper surface, has increased adsorptivity, has a water resisting property, and filter paper filtering resistance of the present invention is little, and efficiency is high, water resistant protection against the tide, wet deflection is high.
Specific embodiments
Below by instantiation, the present invention is described in detail.
A high water resistant air paper that contains glass fibre, by following weight portion (kilogram) raw material make: rascal bamboo pulp 46, mulberry root bark pulp 52, dry sweetscented oleander leaf 1, oleic acid 0.7, flax gum 0.4, wheaten starch 0.3, montmorillonite 3, cerium oxide 1, short glass fiber 1, molybdenum dioxide 1, polyamine epichlorohydrin resin 5, acrylate and vinyl acetate emulsion 3, polyvinyl alcohol 0.3, paraffin wax emulsions 0.2, auxiliary agent 1, water are appropriate;
Described auxiliary agent by following weight portion (kilogram) raw material make: diatomite 3, reed 1, aluminum sulfate 3, polyethylene glycol 3, liquid silica gel 2, titanium dioxide 3, lithium soap stone flour 2, gelatin 3, molecular sieve 1, water 50; Preparation method be first by diatomite, reed, molecular sieve, putting into pulverizer together, to be ground into 120-140 object mixed-powder stand-by; Then gelatin, liquid silica gel, chitin are mixed, add appropriate water to stir, be heated to 30-35 DEG C of continuation stirring and add polyethylene glycol, titanium dioxide, lithium soap stone flour after 10-15 minute, continue insulation 20-25 minute, finally add mixed-powder to stir, form turbid liquid.
A kind of high water resistant air paper that contains glass fibre of the present invention, made by following concrete steps:
(1) montmorillonite, dry sweetscented oleander leaf, cerium oxide, short glass fiber are mixed, grind to form 50-100 object powder, add wheaten starch, with the speed of 850-950 rev/min, stir 25-30 minute, then 60-70 DEG C dry 1.5-2.5 hour stand-by;
(2) rascal bamboo pulp, mulberry root bark pulp are put into hydrabrusher size degradation, then through beater, beating consistency is controlled at 5.3-6.3%, makes slurry;
(3) compound of step (1) is added in slurry, add polyvinyl alcohol, paraffin wax emulsions, be heated to 65-75 DEG C, stir, add appropriate water size mixing to solid content be 2.0-3.0%, the slurry mixing up, after forming web moulding, aspirates dehydration to the l Water Paper after moulding under the vacuum condition of 0.05-0.08Mpa;
(4) by all the other the residual components mixing and stirring except auxiliary agent, the water that adds 2-3 doubly to measure, then heating, temperature is controlled at 60-70 DEG C, boils 50-60 minute, insulation 25-30 minute, be warming up to 70-75 DEG C, stir and make maceration extract and put into dipping tank;
(5) body paper after step (3) dehydration is passed through to dipping tank with the speed of 3-3.5m/s, maceration extract is uniformly coated on body paper, in electric drying oven with forced convection, dries 4-5min, then auxiliary agent is coated on the body paper of oven dry, dry 6-10min on last ray machine, after taking-up and get final product.
After testing, the filter efficiency of the filter paper that the present invention makes is 99.7%, bursting strength 260KPa, Air permenbility 425L/m
2s.
Claims (2)
1. a high water resistant air paper that contains glass fibre, it is characterized in that, made by the raw material of following weight portion: rascal bamboo pulp 46-48, mulberry root bark pulp 52-54, dry sweetscented oleander leaf 1-2, oleic acid 0.7-0.9, flax gum 0.4-0.5, wheaten starch 0.3-0.5, montmorillonite 3-4, cerium oxide 1-2, short glass fiber 1-2, molybdenum dioxide 1-2, polyamine epichlorohydrin resin 5-7, acrylate and vinyl acetate emulsion 3-5, polyvinyl alcohol 0.3-0.4, paraffin wax emulsions 0.2-0.4, auxiliary agent 1-2, water are appropriate;
Described auxiliary agent is made up of the raw material of following weight portion: diatomite 3-4, reed 1-2, aluminum sulfate 3-4, polyethylene glycol 3-4, liquid silica gel 2-3, titanium dioxide 3-5, lithium soap stone flour 2-3, gelatin 3-5, molecular sieve 1-2, water 50-60; Preparation method be first by diatomite, reed, molecular sieve, putting into pulverizer together, to be ground into 120-140 object mixed-powder stand-by; Then gelatin, liquid silica gel, chitin are mixed, add appropriate water to stir, be heated to 30-35 DEG C of continuation stirring and add polyethylene glycol, titanium dioxide, lithium soap stone flour after 10-15 minute, continue insulation 20-25 minute, finally add mixed-powder to stir, form turbid liquid.
2. a kind of high water resistant air paper that contains glass fibre according to claim 1, is characterized in that, is made up of following concrete steps:
(1) montmorillonite, dry sweetscented oleander leaf, cerium oxide, short glass fiber are mixed, grind to form 50-100 object powder, add wheaten starch, with the speed of 850-950 rev/min, stir 25-30 minute, then 60-70 DEG C dry 1.5-2.5 hour stand-by;
(2) rascal bamboo pulp, mulberry root bark pulp are put into hydrabrusher size degradation, then through beater, beating consistency is controlled at 5.3-6.3%, makes slurry;
(3) compound of step (1) is added in slurry, add polyvinyl alcohol, paraffin wax emulsions, be heated to 65-75 DEG C, stir, add appropriate water size mixing to solid content be 2.0-3.0%, the slurry mixing up, after forming web moulding, aspirates dehydration to the l Water Paper after moulding under the vacuum condition of 0.05-0.08Mpa;
(4) by all the other the residual components mixing and stirring except auxiliary agent, the water that adds 2-3 doubly to measure, then heating, temperature is controlled at 60-70 DEG C, boils 50-60 minute, insulation 25-30 minute, be warming up to 70-75 DEG C, stir and make maceration extract and put into dipping tank;
(5) body paper after step (3) dehydration is passed through to dipping tank with the speed of 3-3.5m/s, maceration extract is uniformly coated on body paper, in electric drying oven with forced convection, dries 4-5min, then auxiliary agent is coated on the body paper of oven dry, dry 6-10min on last ray machine, after taking-up and get final product.