CN103993521A - Ventilating oxygen-enriching energy-saving filter paper for fuel filter and preparation method thereof - Google Patents
Ventilating oxygen-enriching energy-saving filter paper for fuel filter and preparation method thereof Download PDFInfo
- Publication number
- CN103993521A CN103993521A CN201410170012.9A CN201410170012A CN103993521A CN 103993521 A CN103993521 A CN 103993521A CN 201410170012 A CN201410170012 A CN 201410170012A CN 103993521 A CN103993521 A CN 103993521A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- filter paper
- stir
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a ventilating oxygen-enriching energy-saving filter paper for a fuel filter. The filter paper is characterized by being prepared from the following raw materials by weight: 49 to 52 parts of cotton pulp, 46 to 49 parts of Manila hemp pulp, 0.5 to 0.8 part of a silane coupling agent kh560, 3 to 4 parts of nacrite, 2 to 3 parts of copperas, 2 to 3 parts of zirconia, 1 to 2 parts of antimony trioxide, 1 to 2 parts of calcium peroxide, 0.4 to 0.6 part of carragheenan, 0.3 to 0.5 part of rosin size, 9 to 10 parts of poly(dimethyldiallylammonium chloride), 0.4 to 0.6 part of polyacrylamide, 0.3 to 0.5 part of petroleum ether, 1 to 2 parts of an auxiliary agent and a proper amount of water. According to the invention, ceramic materials like nacrite and zirconia are added and organically combined with the filter paper, so the filter paper is ventilating, water-resistant and pollution-resistant; calcium peroxide is added into a prepared impregnation liquid and slowly releases oxygen in water, so pores in the surface of the filter paper are increased, and filtered fuel oil can be fully combusted, thereby achieving effects of energy conservation and emission reduction.
Description
Technical field
The present invention relates to automobile filter field, particularly a kind of ventilative bleeding and energy saving fuel filter filter paper and preparation method thereof.
Background technology
The loss of the speed of the cleaner of automobile to running car, engine, energy-conservation and environmental protection is extremely important.Therefore, people have proposed a lot of technology and products about improving automobile air, fuel filter for a long time, mainly comprise the several types such as oxygenation combustion technology, ion combustion technology, ray activating technology.As the fuel filter paper of one of automobile three filter paper, Main Function is filter fuel, and the impurity in clean fuel oil prevents that them from entering injection valve and cold start-up device, reduces mechanical wear, guarantees engine stable operation, improves reliability.In order to ensure that internal combustion engine carries out and Lixing energy-conserving and environment-protective safely and effectively, supporting filter material must possess good mechanical property and certain strainability and the effect of energy-conserving and environment-protective with it.
Summary of the invention
The object of this invention is to provide a kind of ventilative bleeding and energy saving fuel filter filter paper and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A kind of ventilative bleeding and energy saving fuel filter filter paper, is made up of the raw material of following weight portion: cotton pulp 49-52, manila pulp 46-49, silane coupler kh560 0.5-0.8, nacrite 3-4, green vitriol 2-3, zirconia 2-3, antimonous oxide 1-2, calper calcium peroxide 1-2, carragheen 0.4-0.6, gum rosin 0.3-0.5, PDDA 9-10, polyacrylamide 0.4-0.6, benzinum 0.3-0.5, auxiliary agent 1-2, water are appropriate;
Described auxiliary agent is made up of the raw material of following weight portion: fruit of glossy privet 2-3, castor bean shell 1-2, carboxymethyl cellulose 1-2, zirconium English powder 3-5, nano titanium oxide 2-3, xanthans 3-5, Ludox 2-3, sodium alginate 1-2, water 50-60; First preparation method puts into the fruit of glossy privet pulverizer to be ground into 120-140 object mixed-powder stand-by together with castor bean shell; Then xanthans, Ludox, sodium alginate are mixed, add appropriate water to stir, be heated to 30-35 DEG C of continuation stirring and add carboxymethyl cellulose, zirconium English powder, nano titanium oxide after 10-15 minute, continue insulation 24-29 minute, finally add mixed-powder to stir, form turbid liquid.
The one of the present invention bleeding and energy saving fuel filter filter paper of breathing freely, made by following concrete steps:
(1) nacrite, green vitriol, zirconia, antimonous oxide are mixed, grind to form 50-100 object powder, add silane coupler kh560, with the speed of 850-950 rev/min, stir 25-30 minute, then 50-60 DEG C dry 1.5-2.5 hour stand-by;
(2) cotton pulp, manila pulp are put into hydrabrusher size degradation, then through beater, beating consistency is controlled at 5.5-6.2%, makes slurry;
(3) compound of step (1) is added in slurry, add benzinum, carragheen, be heated to 65-75 DEG C, stir, add appropriate water size mixing to solid content be 2.0-3.5%, the slurry mixing up, after forming web moulding, aspirates dehydration to the l Water Paper after moulding under the vacuum condition of 0.05-0.08Mpa;
(4) by all the other the residual components mixing and stirring except auxiliary agent, the water that adds 2-3 doubly to measure, then heating, temperature is controlled at 60-70 DEG C, boils 50-60 minute, insulation 25-30 minute, be warming up to 70-75 DEG C, stir and make maceration extract and put into dipping tank;
(5) body paper after step (3) dehydration is passed through to dipping tank with the speed of 3-3.5m/s, maceration extract is uniformly coated on body paper, in electric drying oven with forced convection, dries 4-5min, then auxiliary agent is coated on the body paper of oven dry, dry 6-10min on last ray machine, after taking-up and get final product.
The invention has the beneficial effects as follows: the present invention adds the ceramic material such as nacrite, zirconia and filter paper organically combines, ventilative, water resistant, anti-soil; In the maceration extract of making, add calper calcium peroxide, meet the slow releasing oxygen of water, not only increased the hole on filter paper surface, and be that the fuel oil filtering can fully burn, reach the effect of energy-saving and emission-reduction.
Specific embodiments
Below by instantiation, the present invention is described in detail.
A kind of ventilative bleeding and energy saving fuel filter filter paper, by following weight portion (kilogram) raw material make: cotton pulp 49, manila pulp 46, silane coupler kh560 0.5, nacrite 3, green vitriol 2, zirconia 2, antimonous oxide 1, calper calcium peroxide 1, carragheen 0.4, gum rosin 0.3, PDDA 9, polyacrylamide 0.4, benzinum 0.3, auxiliary agent 1, water are appropriate;
Described auxiliary agent by following weight portion (kilogram) raw material make: the fruit of glossy privet 2, castor bean shell 1, carboxymethyl cellulose 1, zirconium English powder 3, nano titanium oxide 2, xanthans 3, Ludox 2, sodium alginate 1, water 50; First preparation method puts into the fruit of glossy privet pulverizer to be ground into 120-140 object mixed-powder stand-by together with castor bean shell; Then xanthans, Ludox, sodium alginate are mixed, add appropriate water to stir, be heated to 30-35 DEG C of continuation stirring and add carboxymethyl cellulose, zirconium English powder, nano titanium oxide after 10-15 minute, continue insulation 24-29 minute, finally add mixed-powder to stir, form turbid liquid.
The one of the present invention bleeding and energy saving fuel filter filter paper of breathing freely, made by following concrete steps:
(1) nacrite, green vitriol, zirconia, antimonous oxide are mixed, grind to form 50-100 object powder, add silane coupler kh560, with the speed of 850-950 rev/min, stir 25-30 minute, then 50-60 DEG C dry 1.5-2.5 hour stand-by;
(2) cotton pulp, manila pulp are put into hydrabrusher size degradation, then through beater, beating consistency is controlled at 5.5-6.2%, makes slurry;
(3) compound of step (1) is added in slurry, add benzinum, carragheen, be heated to 65-75 DEG C, stir, add appropriate water size mixing to solid content be 2.0-3.5%, the slurry mixing up, after forming web moulding, aspirates dehydration to the l Water Paper after moulding under the vacuum condition of 0.05-0.08Mpa;
(4) by all the other the residual components mixing and stirring except auxiliary agent, the water that adds 2-3 doubly to measure, then heating, temperature is controlled at 60-70 DEG C, boils 50-60 minute, insulation 25-30 minute, be warming up to 70-75 DEG C, stir and make maceration extract and put into dipping tank;
(5) body paper after step (3) dehydration is passed through to dipping tank with the speed of 3-3.5m/s, maceration extract is uniformly coated on body paper, in electric drying oven with forced convection, dries 4-5min, then auxiliary agent is coated on the body paper of oven dry, dry 6-10min on last ray machine, after taking-up and get final product.
The Air permenbility 87-89L/m of the filter paper that after testing, the present invention makes
2between s, maximum diameter of hole is 54-56 μ m, and average pore size is 45 μ m.
Claims (2)
1. a ventilative bleeding and energy saving fuel filter filter paper, it is characterized in that, made by the raw material of following weight portion: cotton pulp 49-52, manila pulp 46-49, silane coupler kh560 0.5-0.8, nacrite 3-4, green vitriol 2-3, zirconia 2-3, antimonous oxide 1-2, calper calcium peroxide 1-2, carragheen 0.4-0.6, gum rosin 0.3-0.5, PDDA 9-10, polyacrylamide 0.4-0.6, benzinum 0.3-0.5, auxiliary agent 1-2, water are appropriate;
Described auxiliary agent is made up of the raw material of following weight portion: fruit of glossy privet 2-3, castor bean shell 1-2, carboxymethyl cellulose 1-2, zirconium English powder 3-5, nano titanium oxide 2-3, xanthans 3-5, Ludox 2-3, sodium alginate 1-2, water 50-60; First preparation method puts into the fruit of glossy privet pulverizer to be ground into 120-140 object mixed-powder stand-by together with castor bean shell; Then xanthans, Ludox, sodium alginate are mixed, add appropriate water to stir, be heated to 30-35 DEG C of continuation stirring and add carboxymethyl cellulose, zirconium English powder, nano titanium oxide after 10-15 minute, continue insulation 24-29 minute, finally add mixed-powder to stir, form turbid liquid.
2. a kind of ventilative bleeding and energy saving fuel filter filter paper according to claim 1, is characterized in that, is made up of following concrete steps:
(1) nacrite, green vitriol, zirconia, antimonous oxide are mixed, grind to form 50-100 object powder, add silane coupler kh560, with the speed of 850-950 rev/min, stir 25-30 minute, then 50-60 DEG C dry 1.5-2.5 hour stand-by;
(2) cotton pulp, manila pulp are put into hydrabrusher size degradation, then through beater, beating consistency is controlled at 5.5-6.2%, makes slurry;
(3) compound of step (1) is added in slurry, add benzinum, carragheen, be heated to 65-75 DEG C, stir, add appropriate water size mixing to solid content be 2.0-3.5%, the slurry mixing up, after forming web moulding, aspirates dehydration to the l Water Paper after moulding under the vacuum condition of 0.05-0.08Mpa;
(4) by all the other the residual components mixing and stirring except auxiliary agent, the water that adds 2-3 doubly to measure, then heating, temperature is controlled at 60-70 DEG C, boils 50-60 minute, insulation 25-30 minute, be warming up to 70-75 DEG C, stir and make maceration extract and put into dipping tank;
(5) body paper after step (3) dehydration is passed through to dipping tank with the speed of 3-3.5m/s, maceration extract is uniformly coated on body paper, in electric drying oven with forced convection, dries 4-5min, then auxiliary agent is coated on the body paper of oven dry, dry 6-10min on last ray machine, after taking-up and get final product.