CN104004570A - 一种无腐蚀性防老化拉丝油 - Google Patents

一种无腐蚀性防老化拉丝油 Download PDF

Info

Publication number
CN104004570A
CN104004570A CN201410170151.1A CN201410170151A CN104004570A CN 104004570 A CN104004570 A CN 104004570A CN 201410170151 A CN201410170151 A CN 201410170151A CN 104004570 A CN104004570 A CN 104004570A
Authority
CN
China
Prior art keywords
oil
wire drawing
parts
drawing oil
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410170151.1A
Other languages
English (en)
Inventor
朱兴堂
朱亮亮
陈军彦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU TIMES ELECTRONICS Co Ltd
Original Assignee
BENGBU TIMES ELECTRONICS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU TIMES ELECTRONICS Co Ltd filed Critical BENGBU TIMES ELECTRONICS Co Ltd
Priority to CN201410170151.1A priority Critical patent/CN104004570A/zh
Publication of CN104004570A publication Critical patent/CN104004570A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种拉丝油，具体涉及一种无腐蚀性防老化拉丝油，本发明拉丝油由以下重量份的原料制成：聚异丁烯40-50、磺化油10-12、米糠油80-100、十六醇1-2、三异丙醇胺环硼酸酯1-2、没食子酸丙酯1-2、聚甘油脂肪酸酯12-15、二烷基二硫代磷酸锌1-2、防老剂ODA 1-2、助剂2-3；本发明拉丝油以聚异丁烯与米糠油混合作为基础油，同时添加了多种低毒高效的抗氧化剂以及防老剂等成分，本发明制备的拉丝油润滑性能极为优良，耐热耐储存，制备的乳化液能长时间保持良好的润滑性能，不易腐败变质，且对各种材质的线材均无腐蚀作用，能够满足多种金属材质的拉丝、拉拔工艺需求。

Description

一种无腐蚀性防老化拉丝油
技术领域
本发明涉及一种拉丝油，具体涉及一种无腐蚀性防老化拉丝油及其制备工艺。
背景技术
拉丝油是一类重要的工业助剂，在金属线拉丝、拉拔工艺过程中做高效润滑油用，具有润滑、清洗、冷却、防锈等功效，协助金属流动，避免模具拖花拉线，提高成品率，降低生产损耗。现有的拉丝油主要分为油性拉丝油和水性拉丝油，这两类拉丝油在实际使用时各有利弊，如油性拉丝油存在散热性能差，清洗排屑困难，废液难降解等问题，而水性的拉丝油虽然散热性能较油性拉丝油优良，但是润滑效果却不尽如人意，难以满足多种金属线的拉丝拉拨工艺要求，因此为了提高企业的机加工水平、降低生产成本，需要对拉丝油配方及工艺进行改进，使其达到良好的使用性能。
发明内容
本发明的目的在于，提供一种无腐蚀性防老化拉丝油，为了实现上述目的，本发明采用的技术方案如下：
一种无腐蚀性防老化拉丝油，其特征在于，本发明材料由以下重量份的原料制成：聚异丁烯40-50、磺化油10-12、米糠油80-100、十六醇1-2、三异丙醇胺环硼酸酯1-2、没食子酸丙酯1-2、聚甘油脂肪酸酯12-15、二烷基二硫代磷酸锌1-2、防老剂ODA 1-2、助剂2-3；所述的助剂由以下重量份的原料制成：石墨烯1-2、硅烷偶联剂KH560 0.1-0.2、异硬脂酸15-18、黄原胶10-12、司盘80 4-5、去离子水适量；制备方法为：先将石墨烯与硅烷偶联剂混合研磨10-15min，得到的粉体与异硬脂酸、司盘80混合，在1000-1500转/分钟的转速下搅拌20-30min，制成乳化液备用，再将黄原胶与适量的去离子水混合，配制成质量浓度为60-70%的黄原胶水溶液，最后将水溶液、乳化液混合，继续以1000-1500转/分钟转速搅拌15-20min，搅拌结束后静置2-4h，即得。
所述的一种无腐蚀性防老化拉丝油，其制备工艺为：先将聚异丁烯、米糠油混合，加热至60-70℃，先加入聚甘油脂肪酸酯、磺化油，混合搅拌20-30min，随后再加入其它剩余成分，继续搅拌40-50min，搅拌结束后经自然冷却至室温，即得成品。
本发明制备得到的拉丝油优点在于：以聚异丁烯与米糠油混合作为基础油，这类基础油更为环保安全，热稳定性良好，同时添加了多种低毒高效的抗氧化剂以及防老剂等成分，使得本发明制备的拉丝油润滑性能极为优良，更耐储存，制备的乳化液能长时间保持良好的润滑性能，不易腐败变质，且对各种材质的线材均无腐蚀作用，能够满足多种金属材质的拉丝、拉拔工艺需求。
具体实施方式
实施例
本实施例拉丝油由以下重量份（公斤）的原料制成：聚异丁烯50、磺化油10、米糠油100、十六醇1、三异丙醇胺环硼酸酯2、没食子酸丙酯2、聚甘油脂肪酸酯15、二烷基二硫代磷酸锌1、防老剂ODA 2、助剂3；所述的助剂由以下重量份的原料制成：石墨烯1、硅烷偶联剂KH560 0.2、异硬脂酸15、黄原胶10、司盘80 4、去离子水适量；制备方法为：先将石墨烯与硅烷偶联剂混合研磨15min，得到的粉体与异硬脂酸、司盘80混合，在1500转/分钟的转速下搅拌20min，制成乳化液备用，再将黄原胶与适量的去离子水混合，配制成质量浓度为60%的黄原胶水溶液，最后将水溶液、乳化液混合，继续以1500转/分钟转速搅拌15min，搅拌结束后静置2h，即得。
所述的一种无腐蚀性防老化拉丝油，其制备工艺为：先将聚异丁烯、米糠油混合，加热至60-70℃，先加入聚甘油脂肪酸酯、磺化油，混合搅拌30min，随后再加入其它剩余成分，继续搅拌50min，搅拌结束后经自然冷却至室温，即得成品。
本发明拉丝油能在室温条件下稳定存放至少一年，期间无沉淀、分层现象；具体各性能指标如下：
项目 指标
运动粘度（100℃） 16-20mm2/s
凝点 ≤-4℃
闪点（开口） ≥230℃
5%乳化液pH值 7.2
5%乳化液腐蚀（55±2）℃，全浸铜片24h 无腐蚀
防锈性（35±2）℃，铜屑2h 合格
5%乳化液稳定性（15-35℃）4h 无分层，无沉淀，无皂、油析出
PB值/N 593

Claims (2)

1.一种无腐蚀性防老化拉丝油，其特征在于，该拉丝油由以下重量份的原料制成：聚异丁烯40-50、磺化油10-12、米糠油80-100、十六醇1-2、三异丙醇胺环硼酸酯1-2、没食子酸丙酯1-2、聚甘油脂肪酸酯12-15、二烷基二硫代磷酸锌1-2、防老剂ODA 1-2、助剂2-3；所述的助剂由以下重量份的原料制成：石墨烯1-2、硅烷偶联剂KH560 0.1-0.2、异硬脂酸15-18、黄原胶10-12、司盘80 4-5、去离子水适量；制备方法为：先将石墨烯与硅烷偶联剂混合研磨10-15min，得到的粉体与异硬脂酸、司盘80混合，在1000-1500转/分钟的转速下搅拌20-30min，制成乳化液备用，再将黄原胶与适量的去离子水混合，配制成质量浓度为60-70%的黄原胶水溶液，最后将水溶液、乳化液混合，继续以1000-1500转/分钟转速搅拌15-20min，搅拌结束后静置2-4h，即得。
2.如权利要求1所述的一种无腐蚀性防老化拉丝油，其制备工艺为：先将聚异丁烯、米糠油混合，加热至60-70℃，先加入聚甘油脂肪酸酯、磺化油，混合搅拌20-30min，随后再加入其它剩余成分，继续搅拌40-50min，搅拌结束后经自然冷却至室温，即得成品。
CN201410170151.1A 2014-04-25 2014-04-25 一种无腐蚀性防老化拉丝油 Pending CN104004570A (zh)