CN104004315B - 一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料 - Google Patents
一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料 Download PDFInfo
- Publication number
- CN104004315B CN104004315B CN201410257745.6A CN201410257745A CN104004315B CN 104004315 B CN104004315 B CN 104004315B CN 201410257745 A CN201410257745 A CN 201410257745A CN 104004315 B CN104004315 B CN 104004315B
- Authority
- CN
- China
- Prior art keywords
- butadiene
- acrylonitrile
- regeneration
- parts
- styrene copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了属于高分子塑料制品再生利用技术领域的一种再生丙烯腈‑丁二烯‑苯乙烯共聚物增韧改性材料。它由以下重量份数的物质组成：再生丙烯腈‑丁二烯‑苯乙烯共聚物55‑65份，增韧剂5‑10份，胶黏剂3‑6份，玉石粉1‑3份，硬脂酸铝1‑4份，抗氧剂1‑2份，颜料0.1‑1份。本发明以废弃丙烯腈‑丁二烯‑苯乙烯共聚物为原料，制备增韧改性材料，提高了材料的性能，又解决了废弃丙烯腈‑丁二烯‑苯乙烯共聚物环境污染的问题，制备的材料可以用于汽车塑料配件及零件的生产。
Description
技术领域
本发明属于高分子塑料制品再生利用技术领域，具体涉及一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料。
背景技术
丙烯腈-丁二烯-苯乙烯共聚物是一种强度高、韧性好、易于加工成型的热塑型高分子材料，是丙烯腈(ACRYLONITRILE)、1，3-丁二烯(BUTADIENE)、苯乙烯(STYRENE)三种单体的接枝共聚物，适于制作一般机械零件、减磨耐磨零件、传动零件和电讯零件。
随着石油化工及塑料工业的迅速发展，丙烯腈-丁二烯-苯乙烯共聚物在建材、家用电器等方面得到广泛应用，但同时也造成了比较严重的白色污染，其回收利用率不高。废弃的丙烯腈-丁二烯-苯乙烯共聚物如果深埋，因其不易老化和难以降解，会破坏土壤结构，污染地下水源，使粮食等作物减产，如果简单焚烧处理，则会严重污染空气及大气环境。如能再生循环利用，将是符合国家经济发展和环境保护的统一，符合资源节约和可持续发展之路的。
丙烯腈-丁二烯-苯乙烯共聚物再生后，其性能比再生之前大打折扣，丙烯腈-丁二烯-苯乙烯共聚物本身具有的高抗冲、高耐热、阻燃、增强、透明等优良特征不复存在，影响再生丙烯腈-丁二烯-苯乙烯共聚物的应用。
发明内容
本发明的目的在于提供一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，充分利用废弃丙烯腈-丁二烯-苯乙烯共聚物，生产高性能汽车用部件。
一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，由以下重量份数的物质组成：再生丙烯腈-丁二烯-苯乙烯共聚物55-65份，增韧剂5-10份，胶黏剂3-6份，玉石粉1-3份，硬脂酸铝1-4份，抗氧剂1-2份，颜料0.1-1份。
所述增韧剂为环氧树脂，酚醛树脂，快固丙烯酸酯，α-氰基丙烯酸酯，脲醛树脂中的一种或一种以上。
所述胶黏剂为聚乙酸乙烯酯，聚乙烯醇，过氯乙烯，聚异丁烯，聚酰胺，聚丙烯酸酯，a-氰基丙烯酸酯，聚乙烯醇缩醛，乙烯-乙酸乙烯酯共聚物，酚醛-聚乙烯醇缩醛，酚醛-聚酰胺，酚醛-环氧树脂，环氧-聚酰胺，氯丁橡胶，丁苯橡胶，丁基橡胶，丁钠橡胶，异戊橡胶，聚硫橡胶，聚氨酯橡胶，氯磺化聚乙烯弹性体，硅橡胶，酚醛-丁腈胶，酚醛-氯丁胶，酚醛-聚氨酯胶，环氧-丁腈胶，环氧-聚硫胶中的一种或一种以上。
所述抗氧剂为二异辛基二苯胺，苯基-α-萘胺，三(2，4-二叔丁基苯基)亚磷酸酯，双(2.4-二叔丁基苯基)季戊四醇二亚磷酸酯，N，N’-二仲丁基对苯二胺中的一种或一种以上。
所述颜料为朱砂，红土，雄黄，孔雀绿，重质碳酸钙，硅灰石，重晶石粉，滑石粉，云母粉，高岭土，胭脂虫红，天然鱼鳞粉，藤黄，茜素红，靛青，钛白，锌钡白，铅铬黄，铁蓝，大红粉，偶淡黄，酞菁蓝，喹吖啶酮中的一种或一种以上。
所述再生丙烯腈-丁二烯-苯乙烯共聚物为废弃丙烯腈-丁二烯-苯乙烯共聚物经过破碎，清洗，烘干，均化后得到的片材。
所述改性材料中还包含1-5重量份数的刺苋提取物。
所述刺苋提取物的提取方法为：将刺苋晒干，磨成粉末，采用70％乙醇溶液回流提取3次，合并滤液，蒸干，制成。
上述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料的制备方法，其特征在于，按照如下步骤进行：
(1)取再生丙烯腈-丁二烯-苯乙烯共聚物55-65份，增韧剂5-10份，硬脂酸铝1-4份，混合，熔融；
(2)加入玉石粉1-3份，抗氧剂1-2份，搅拌均匀；
(3)加入胶黏剂3-6份，颜料0.1-1份，搅拌均匀，共挤出，入造粒机造粒。
本发明的有益效果：本发明以废弃丙烯腈-丁二烯-苯乙烯共聚物为原料，制备增韧改性材料，提高了材料的性能，又解决了废弃丙烯腈-丁二烯-苯乙烯共聚物环境污染的问题，制备的材料可以用于汽车塑料配件及零件的生产。
具体实施方式
下面结合具体实施例对本发明做进一步说明。
实施例1
一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，由以下重量份数的物质组成：再生丙烯腈-丁二烯-苯乙烯共聚物55份，酚醛树脂5份，聚乙烯醇3份，玉石粉1份，硬脂酸铝1份，二异辛基二苯胺1份，靛青0.1份。
所述再生丙烯腈-丁二烯-苯乙烯共聚物为废弃丙烯腈-丁二烯-苯乙烯共聚物经过破碎，清洗，烘干，均化后得到的片材。
上述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料的制备方法，其特征在于，按照如下步骤进行：
(1)取再生丙烯腈-丁二烯-苯乙烯共聚物55份，酚醛树脂5份，硬脂酸铝1份，混合，熔融；
(2)加入玉石粉1份，二异辛基二苯胺1份，搅拌均匀；
(3)加入聚乙烯醇3份，靛青0.1份，搅拌均匀，共挤出，入造粒机造粒。
本实施例产品的拉伸强度为46MPa，弯曲强度为66MPa，简支梁缺口冲击强度为11kJ/m2。
实施例2
一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，由以下重量份数的物质组成：再生丙烯腈-丁二烯-苯乙烯共聚物60份，α-氰基丙烯酸酯7份，a-氰基丙烯酸酯5份，玉石粉2份，硬脂酸铝3份，双(2.4-二叔丁基苯基)季戊四醇二亚磷酸酯1.5份，酞菁蓝0.5份。
所述再生丙烯腈-丁二烯-苯乙烯共聚物为废弃丙烯腈-丁二烯-苯乙烯共聚物经过破碎，清洗，烘干，均化后得到的片材。
上述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料的制备方法，其特征在于，按照如下步骤进行：
(1)取再生丙烯腈-丁二烯-苯乙烯共聚物60份，α-氰基丙烯酸酯7份，硬脂酸铝3份，混合，熔融；
(2)加入玉石粉2份，双(2.4-二叔丁基苯基)季戊四醇二亚磷酸酯1.5份，搅拌均匀；
(3)加入a-氰基丙烯酸酯5份，酞菁蓝0.5份，搅拌均匀，共挤出，入造粒机造粒。
本实施例产品的拉伸强度为44MPa，弯曲强度为67MPa，简支梁缺口冲击强度为12kJ/m2。
实施例3
一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，由以下重量份数的物质组成：再生丙烯腈-丁二烯-苯乙烯共聚物65份，脲醛树脂10份，丁苯橡胶6份，玉石粉3份，硬脂酸铝4份，三(2，4-二叔丁基苯基)亚磷酸酯2份，茜素红1份。
所述再生丙烯腈-丁二烯-苯乙烯共聚物为废弃丙烯腈-丁二烯-苯乙烯共聚物经过破碎，清洗，烘干，均化后得到的片材。
上述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料的制备方法，其特征在于，按照如下步骤进行：
(1)取再生丙烯腈-丁二烯-苯乙烯共聚物55-65份，脲醛树脂10份，硬脂酸铝4份，混合，熔融；
(2)加入玉石粉3份，三(2，4-二叔丁基苯基)亚磷酸酯2份，搅拌均匀；
(3)加入丁苯橡胶6份，茜素红1份，搅拌均匀，共挤出，入造粒机造粒。
本实施例产品的拉伸强度为46MPa，弯曲强度为66MPa，简支梁缺口冲击强度为11kJ/m2。
实施例4
一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，由以下重量份数的物质组成：再生丙烯腈-丁二烯-苯乙烯共聚物65份，脲醛树脂10份，丁苯橡胶6份，玉石粉3份，硬脂酸铝4份，三(2，4-二叔丁基苯基)亚磷酸酯2份，茜素红1份，刺苋提取物2份。
所述刺苋提取物的提取方法为：将刺苋晒干，磨成粉末，采用70％乙醇溶液回流提取3次，合并滤液，蒸干，制成。
所述再生丙烯腈-丁二烯-苯乙烯共聚物为废弃丙烯腈-丁二烯-苯乙烯共聚物经过破碎，清洗，烘干，均化后得到的片材。
上述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料的制备方法，其特征在于，按照如下步骤进行：
(1)取再生丙烯腈-丁二烯-苯乙烯共聚物55-65份，脲醛树脂10份，硬脂酸铝4份，混合，熔融；
(2)加入玉石粉3份，三(2，4-二叔丁基苯基)亚磷酸酯2份，刺苋提取物2份，搅拌均匀；
(3)加入丁苯橡胶6份，茜素红1份，搅拌均匀，共挤出，入造粒机造粒。
本实施例产品的拉伸强度为66MPa，弯曲强度为86MPa，简支梁缺口冲击强度为15kJ/m2。
实施例5
一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，由以下重量份数的物质组成：再生丙烯腈-丁二烯-苯乙烯共聚物65份，脲醛树脂10份，丁苯橡胶6份，硬脂酸铝4份，三(2，4-二叔丁基苯基)亚磷酸酯2份，茜素红1份，刺苋提取物2份。
所述刺苋提取物的提取方法为：将刺苋晒干，磨成粉末，采用70％乙醇溶液回流提取3次，合并滤液，蒸干，制成。
所述再生丙烯腈-丁二烯-苯乙烯共聚物为废弃丙烯腈-丁二烯-苯乙烯共聚物经过破碎，清洗，烘干，均化后得到的片材。
上述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料的制备方法，其特征在于，按照如下步骤进行：
(1)取再生丙烯腈-丁二烯-苯乙烯共聚物55-65份，脲醛树脂10份，硬脂酸铝4份，混合，熔融；
(2)加入三(2，4-二叔丁基苯基)亚磷酸酯2份，刺苋提取物2份，搅拌均匀；
(3)加入丁苯橡胶6份，茜素红1份，搅拌均匀，共挤出，入造粒机造粒。
本实施例产品的拉伸强度为56MPa，弯曲强度为76MPa，简支梁缺口冲击强度为14kJ/m2，与前述实施例相比，材料表面不光滑，略显粗糙。
实施例6
一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，由以下重量份数的物质组成：再生丙烯腈-丁二烯-苯乙烯共聚物65份，脲醛树脂10份，丁苯橡胶6份，玉石粉3份，三(2，4-二叔丁基苯基)亚磷酸酯2份，茜素红1份，刺苋提取物2份。
所述刺苋提取物的提取方法为：将刺苋晒干，磨成粉末，采用70％乙醇溶液回流提取3次，合并滤液，蒸干，制成。
所述再生丙烯腈-丁二烯-苯乙烯共聚物为废弃丙烯腈-丁二烯-苯乙烯共聚物经过破碎，清洗，烘干，均化后得到的片材。
上述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料的制备方法，其特征在于，按照如下步骤进行：
(1)取再生丙烯腈-丁二烯-苯乙烯共聚物55-65份，脲醛树脂10份，混合，熔融；
(2)加入玉石粉3份，三(2，4-二叔丁基苯基)亚磷酸酯2份，刺苋提取物2份，搅拌均匀；
(3)加入丁苯橡胶6份，茜素红1份，搅拌均匀，共挤出，入造粒机造粒。
本实施例产品的拉伸强度为34MPa，弯曲强度为55MPa，简支梁缺口冲击强度为13kJ/m2。
Claims (8)
1.一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，其特征在于，由以下重量份数的物质组成：再生丙烯腈-丁二烯-苯乙烯共聚物55-65份，增韧剂5-10份，胶黏剂3-6份，玉石粉1-3份，硬脂酸铝1-4份，抗氧剂1-2份，颜料0.1-1份，刺苋提取物1-5份；
所述刺苋提取物的提取方法为：将刺苋晒干，磨成粉末，采用70％乙醇溶液回流提取3次，合并滤液，蒸干，制成。
2.根据权利要求1所述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，其特征在于，所述增韧剂为环氧树脂，酚醛树脂，快固丙烯酸酯，脲醛树脂中的一种或一种以上。
3.根据权利要求2所述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，其特征在于，所述快固丙烯酸酯为α-氰基丙烯酸酯。
4.根据权利要求1所述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，其特征在于，所述胶黏剂为聚乙酸乙烯酯，聚乙烯醇，过氯乙烯，聚异丁烯，聚酰胺，聚丙烯酸酯，a-氰基丙烯酸酯，聚乙烯醇缩醛，乙烯-乙酸乙烯酯共聚物，酚醛-聚乙烯醇缩醛，酚醛-聚酰胺，酚醛-环氧树脂，环氧-聚酰胺，氯丁橡胶，丁苯橡胶，丁基橡胶，丁钠橡胶，异戊橡胶，聚硫橡胶，聚氨酯橡胶，氯磺化聚乙烯弹性体，硅橡胶，酚醛-丁腈胶，酚醛-氯丁胶，酚醛-聚氨酯胶，环氧-丁腈胶，环氧-聚硫胶中的一种或一种以上。
5.根据权利要求1所述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，其特征在于，所述抗氧剂为二异辛基二苯胺，苯基-α-萘胺，三(2，4-二叔丁基苯基)亚磷酸酯，双(2，4-二叔丁基苯基)季戊四醇二亚磷酸酯，N，N’-二仲丁基对苯二胺中的一种或一种以上。
6.根据权利要求1所述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，其特征在于，所述颜料为朱砂，红土，雄黄，孔雀绿，重质碳酸钙，硅灰石，重晶石粉，滑石粉，云母粉，高岭土，胭脂虫红，天然鱼鳞粉，藤黄，茜素红，靛青，钛白，锌钡白，铅铬黄，铁蓝，大红粉，偶淡黄，酞菁蓝，喹吖啶酮中的一种或一种以上。
7.根据权利要求1所述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料，其特征在于，所述再生丙烯腈-丁二烯-苯乙烯共聚物为废弃丙烯腈-丁二烯-苯乙烯共聚物经过破碎，清洗，烘干，均化后得到的片材。
8.权利要求1所述一种再生丙烯腈-丁二烯-苯乙烯共聚物增韧改性材料的制备方法，其特征在于，按照如下步骤进行：
(1)取再生丙烯腈-丁二烯-苯乙烯共聚物55-65份，增韧剂5-10份，硬脂酸铝1-4份，混合，熔融；
(2)加入玉石粉1-3份，抗氧剂1-2份，刺苋提取物1-5份，搅拌均匀；
所述刺苋提取物的提取方法为：将刺苋晒干，磨成粉末，采用70％乙醇溶液回流提取3次，合并滤液，蒸干，制成；
(3)加入胶黏剂3-6份，颜料0.1-1份，搅拌均匀，共挤出，入造粒机造粒。