CN104003695B - A kind of glaze spraying ceramic tile and preparation method thereof - Google Patents
A kind of glaze spraying ceramic tile and preparation method thereof Download PDFInfo
- Publication number
- CN104003695B CN104003695B CN201410227320.0A CN201410227320A CN104003695B CN 104003695 B CN104003695 B CN 104003695B CN 201410227320 A CN201410227320 A CN 201410227320A CN 104003695 B CN104003695 B CN 104003695B
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic tile
- brick body
- body layer
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of ceramic tile, the glaze spraying ceramic tile of a kind of brick body layer and glaze layer solid colour is provided, comprise brick body layer and be located at the glaze layer of brick body layer outside surface, it is characterized in that, described brick body layer comprises the raw material thing of following weight part: black talc 2 ~ 4 parts, diopside 3 ~ 5 parts, 4 ~ 6 parts, white Guangxi soil, 13 ~ 15 parts, washing soil, elongated stone flour 35 ~ 40 parts, 10 ~ 15 parts, Longyan feldspar sand, husky 12 ~ 16 parts of washing, 10 ~ 18 parts, the cured stone of Shou Shan, yellow point 7 ~ 8 parts, material.A kind of preparation method of described glaze spraying ceramic tile is provided simultaneously, comprises stock tank color matching treatment process.
Description
Technical field
The present invention relates to a kind of ceramic tile, particularly relate to a kind of glaze spraying ceramic tile and preparation method thereof.
Background technology
The preparation method of tradition glaze spraying ceramic tile, generally first prepare brick body, glaze spraying on brick body again, finished product obtained like this, there is glaze layer with brick body layer, because brick body layer material is comparatively common, add glaze layer very thin, brick body layer directly will be exposed after glaze layer is scratched, brick body layer and glaze layer have two kinds of different colours, like this, when after use certain hour, brick body layer comes out, cause product very unsightly, and in order to change this situation, usual needs are reprocessed the glaze spraying ceramic tile after use certain hour, glaze layer just can be made again to be added up, and processing needs drop into manpower and material resources, not only consume data, also take unnecessary energy simultaneously.
Summary of the invention
Therefore, for above content, the invention provides the glaze spraying ceramic tile of a kind of brick body layer and glaze layer solid colour, a kind of preparation method of described glaze spraying ceramic tile is provided simultaneously.
For achieving the above object, the present invention is achieved by the following technical solutions: a kind of glaze spraying ceramic tile, and comprise brick body layer and be located at the glaze layer of brick body layer outside surface, described brick body layer comprises the raw material thing of following weight part:
Black talc 2 ~ 4 parts
Diopside 3 ~ 5 parts
4 ~ 6 parts, Bai Guangxi soil
13 ~ 15 parts, washing soil
Elongated stone flour 35 ~ 40 parts
10 ~ 15 parts, Longyan feldspar sand
Husky 12 ~ 16 parts of washing
10 ~ 18 parts, the cured stone of Shou Shan
Yellow point 7 ~ 8 parts, material.
Further improvement is: described elongated talc particles diameter is less than 0.841mm.
Further improvement is: the raw material thing of described brick body layer also includes zirconium silicate 1.0 ~ 2.0 parts.
Further improvement is: described Huang point material is made up of colorant and bed material, and the mass ratio of described colorant and bed material is 20:1.
Further improvement is: described bed material comprises each raw material of following weight part:
Silicon-dioxide: 68.39 parts
Alchlor: 18.07 parts
Indian red: 0.85 part
Titanium oxide: 0.29 part
Calcium oxide: 0.88 part
Magnesium oxide: 4.2 parts
Sodium oxide: 2.20 parts
Further improvement is: the burning vector of described bed material is 4.58%.
A preparation method for glaze spraying ceramic tile, comprises the following steps: the raw material thing except colorant of the layer of turning described in claim 1 or 2 is dropped in tank body carry out mixing, ball milling, filtration treatment, then color matching process in stock tank.
Further improvement is: the concrete steps of described stock tank color matching process are: the mixture after filtration treatment is put into stock tank, and the colorant pouring 7 ~ 8 weight parts into carries out toning and processes.
Further improvement is: in stock tank, also carry out spray tower drying treatment after color matching process.
By adopting preceding solution, the invention has the beneficial effects as follows: glaze spraying ceramic tile of the present invention, comprise brick body layer and be located at the glaze layer of brick body layer outside surface, described brick body layer comprises the raw material thing of following weight part: black talc 2 ~ 4 parts, diopside 3 ~ 5 parts, 4 ~ 6 parts, Bai Guangxi soil, 13 ~ 15 parts, washing soil, elongated stone flour 35 ~ 40 parts, 10 ~ 15 parts, Longyan feldspar sand, husky 12 ~ 16 parts of washing, 10 ~ 18 parts, the cured stone of Shou Shan, yellow point 7 ~ 8 parts, material.The obtained brick body layer of above integral formula and glaze layer is selected to form same color, after using certain hour, brick body layer and glaze layer are still same colors, so after glaze layer is by part wears, the brick body layer come out due to glaze layer solid colour, inaesthetic problem can not be produced, also do not need to supplement glaze layer again, use manpower and material resources sparingly, saving resource.In preparation process, add this step of color matching process in stock tank, make brick body layer have the color the same with glaze layer.
Embodiment
Describe embodiments of the present invention in detail below with reference to specific embodiment, to the present invention, how utilisation technology means solve technical problem whereby, and the implementation procedure reaching technique effect can fully understand and implement according to this.
If do not specialize, the conventional means that the technique means adopted in embodiment is well known to those skilled in the art, the reagent adopted and product be also can business obtain.Source, the trade(brand)name of agents useful for same and be necessary to list its moiety person, all indicate when occurring first.
Embodiment one
A kind of glaze spraying ceramic tile, comprise brick body layer and be located at the glaze layer of brick body layer outside surface, described brick body layer comprises the raw material thing of following weight part:
Black talc 2kg
Diopside 3kg
Bai Guangxi soil 4kg
Wash native 14kg
Elongated stone flour 38kg
The husky 12kg of Longyan feldspar
Wash husky 13kg
The cured stone 14kg of Shou Shan
Colorant 7.5kg
Bed material 0.35kg.
Described bed material comprises each raw material of following weight part:
Silicon-dioxide: 68.39 parts
Alchlor: 18.07 parts
Indian red: 0.85 part
Titanium oxide: 0.29 part
Calcium oxide: 0.88 part
Magnesium oxide: 4.2 parts
Sodium oxide: 2.20 parts
Wherein, the burning vector of bed material is 4.58%, and described elongated talc particles diameter is less than 0.841mm.
Its preparation method is: throw tank: will mix in above-mentioned each component (colorant and bed material except) input tank body, then ball-milling processing is carried out, again in the process of stock tank inner filtration: the bed material of 7.5kg colorant and 0.35kg is dropped in stock tank and matches colors, then spray tower is sent into dry, feeding warehouse → sink-float 24h → entrance pressure machine → oven dry → glaze spraying → spraying decoration → pouring glaze → burn till → polishing, obtains glaze spraying ceramic tile.
Embodiment two
A kind of glaze spraying ceramic tile, comprise brick body layer and be located at the glaze layer of brick body layer outside surface, described brick body layer comprises the raw material thing of following weight part:
Black talc 3kg
Diopside 4kg
Bai Guangxi soil 5kg
Wash native 14kg
Elongated stone flour 37kg
The husky 13kg of Longyan feldspar
Wash husky 14kg
The cured stone 14kg of Shou Shan
Zirconium silicate 1.5kg
Colorant 7.5kg
Bed material 0.35kg.
Described bed material comprises each raw material of following weight part:
Silicon-dioxide: 68.39 parts
Alchlor: 18.07 parts
Indian red: 0.85 part
Titanium oxide: 0.29 part
Calcium oxide: 0.88 part
Magnesium oxide: 4.2 parts
Sodium oxide: 2.20 parts
Wherein, the burning vector of bed material is 4.58%, and described elongated talc particles diameter is less than 0.841mm.
Its preparation method is: throw tank: will mix in above-mentioned each component (colorant and bed material except) input tank body, then ball-milling processing is carried out, again in the process of stock tank inner filtration: the bed material of 7.5kg colorant and 0.35kg is dropped in stock tank and matches colors, then spray tower is sent into dry, feeding warehouse → sink-float 24h → entrance pressure machine → oven dry → glaze spraying → spraying decoration → pouring glaze → burn till → polishing, obtains glaze spraying ceramic tile.
Embodiment three
A kind of glaze spraying ceramic tile, comprise brick body layer and be located at the glaze layer of brick body layer outside surface, described brick body layer comprises the raw material thing of following weight part:
Black talc 4kg
Diopside 5kg
Bai Guangxi soil 6kg
Wash native 15kg
Elongated stone flour 40kg
The husky 15kg of Longyan feldspar
Wash husky 16kg
The cured stone 18kg of Shou Shan
Colorant 7.5kg
Bed material 0.35kg.
Described bed material comprises each raw material of following weight part:
Silicon-dioxide: 68.39 parts
Alchlor: 18.07 parts
Indian red: 0.85 part
Titanium oxide: 0.29 part
Calcium oxide: 0.88 part
Magnesium oxide: 4.2 parts
Sodium oxide: 2.20 parts
Wherein, the burning vector of bed material is 4.58%, and described elongated talc particles diameter is less than 0.841mm.
Its preparation method is: throw tank: will mix in above-mentioned each component (colorant and bed material except) input tank body, then ball-milling processing is carried out, again in the process of stock tank inner filtration: the bed material of 7.5kg colorant and 0.35kg is dropped in stock tank and matches colors, then spray tower is sent into dry, feeding warehouse → sink-float 24h → entrance pressure machine → oven dry → glaze spraying → spraying decoration → pouring glaze → burn till → polishing, obtains glaze spraying ceramic tile.
Black talc of the present invention, diopside, white Guangxi soil, washing soil, elongated stone flour, Longyan feldspar sand, washing sand, the cured stone of Shou Shan, zirconium silicate, colorant, silicon-dioxide, alchlor, Indian red, titanium oxide, calcium oxide, magnesium oxide, sodium oxide all can buy from existing market.Glaze layer of the present invention glaze used is bought in island, Foshan City ten thousand glaze company limited, and wherein, the glaze of cover-coat enamel is for being selected from: ten thousand island glaze numbering 355 consumptions are 6%, ten thousand island glaze numbering 358 materials is 80%, zirconium silicate: 14%; Throw glaze: ten thousand island glaze numbering 9210 materials 100%.
Glaze spraying ceramic tile of the present invention, comprise brick body layer and be located at the glaze layer of brick body layer outside surface, described brick body layer comprises the raw material thing of following weight part: black talc 2 ~ 4 parts, diopside 3 ~ 5 parts, 4 ~ 6 parts, white Guangxi soil, 13 ~ 15 parts, washing soil, elongated stone flour 35 ~ 40 parts, 10 ~ 15 parts, Longyan feldspar sand, husky 12 ~ 16 parts of washing, 10 ~ 18 parts, the cured stone of Shou Shan, yellow point 7 ~ 8 parts, material.The obtained brick body layer of above integral formula and glaze layer is selected to form same color, after using certain hour, brick body layer and glaze layer are still same colors, so after glaze layer is by part wears, the brick body layer come out due to glaze layer solid colour, inaesthetic problem can not be produced, also do not need to supplement glaze layer again, use manpower and material resources sparingly, saving resource.In preparation process, add this step of color matching process in stock tank, make brick body layer have the color the same with glaze layer.
Above, be only the embodiment utilizing this origination techniques content, the modification that any those skilled in the art use this creation to do, change, all belong to the scope of the claims that this creation is advocated, and be not limited to those disclosed embodiments.
Claims (8)
1. a glaze spraying ceramic tile, comprise brick body layer and be located at the glaze layer of brick body layer outside surface, it is characterized in that, described brick body layer comprises the raw material thing of following weight part:
Black talc 2 ~ 4 parts
Diopside 3 ~ 5 parts
4 ~ 6 parts, Bai Guangxi soil
13 ~ 15 parts, washing soil
Elongated stone flour 35 ~ 40 parts
10 ~ 15 parts, Longyan feldspar sand
Husky 12 ~ 16 parts of washing
10 ~ 18 parts, the cured stone of Shou Shan
Yellow point 7 ~ 8 parts, material;
Described Huang point material is made up of colorant and bed material, and the mass ratio of described colorant and bed material is 20:1.
2. glaze spraying ceramic tile according to claim 1, is characterized in that: described elongated talc particles diameter is less than 0.841mm.
3. glaze spraying ceramic tile according to claim 1, is characterized in that: the raw material thing of described brick body layer also includes zirconium silicate 1.0 ~ 2.0 parts.
4. glaze spraying ceramic tile according to claim 1, is characterized in that, described bed material comprises each raw material of following weight part:
Silicon-dioxide: 68.39 parts
Alchlor: 18.07 parts
Indian red: 0.85 part
Titanium oxide: 0.29 part
Calcium oxide: 0.88 part
Magnesium oxide: 4.2 parts
Sodium oxide: 2.20 parts.
5. glaze spraying ceramic tile according to claim 4, is characterized in that: the burning vector of described bed material is 4.58%.
6. a preparation method for glaze spraying ceramic tile, is characterized in that, comprises the following steps: the raw material thing except colorant and bed material of the brick body layer described in claim 1 or 2 is dropped in tank body carry out mixing, ball milling, filtration treatment, then color matching process in stock tank.
7. the preparation method of glaze spraying ceramic tile according to claim 6, is characterized in that, the concrete steps of described stock tank color matching process are: the mixture after filtration treatment is put into stock tank, pours the colorant of 7 ~ 8 weight parts and bed material into and carries out toning and process.
8. the preparation method of glaze spraying ceramic tile according to claim 6, is characterized in that: in stock tank, also carry out spray tower drying treatment after color matching process.