CN104001929B - 一种用机械合金化制造铜钨合金粉末的方法 - Google Patents

一种用机械合金化制造铜钨合金粉末的方法 Download PDF

Info

Publication number
CN104001929B
CN104001929B CN201410278010.1A CN201410278010A CN104001929B CN 104001929 B CN104001929 B CN 104001929B CN 201410278010 A CN201410278010 A CN 201410278010A CN 104001929 B CN104001929 B CN 104001929B
Authority
CN
China
Prior art keywords
ball
copper
powder
tungsten
milling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410278010.1A
Other languages
English (en)
Other versions
CN104001929A (zh
Inventor
阮秀仕
吴鹏
曹大力
赵清海
赵勇胜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Guofu TRW Electric Technology Co Ltd
Original Assignee
Fujian Guofu Trw Electric Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujian Guofu Trw Electric Technology Co Ltd filed Critical Fujian Guofu Trw Electric Technology Co Ltd
Priority to CN201410278010.1A priority Critical patent/CN104001929B/zh
Publication of CN104001929A publication Critical patent/CN104001929A/zh
Application granted granted Critical
Publication of CN104001929B publication Critical patent/CN104001929B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开涉及一种用机械合金化制造铜钨合金粉末的方法，该方法是将铜粉、钨粉配制好，放入球磨罐中，加入球磨介质和磨球，在有气氛保护或真空的球磨罐中球磨50‑100小时，球磨结束，静置，以使粉料和磨球充分冷却后取出粉末，即得到铜钨合金粉末。用这种制造方法获得的铜钨合金粉末晶粒细小、成分均匀、易于分散，并且工艺简单，易于操作。

Description

一种用机械合金化制造铜钨合金粉末的方法
技术领域
本发明涉及粉末技术冶金领域，尤其涉及一种用机械合金化制造铜钨合金粉末的方法。
背景技术
通过粉末冶金技术制造的钨铜电工触头是由具有高熔点、低线膨胀系数、高强度的钨和具有很好的导热性能和导电性能的铜复合而成的，其兼具钨、铜两种金属的优点，因而广泛用作电接触材料和电极材料。
但钨、铜两种金属互不相溶，熔点相差很大，所以用传统的方法制造全致密的钨铜复合材料会遇到许多困难。
发明内容
本发明的目的在于提供一种用机械合金化制造铜钨合金粉末的方法，通过该方法可以制备的铜钨合金粉末晶粒细小、成分均匀和易于分散。
为实现上述目的，本发明采用以下技术方案：
一种用机械合金化制造铜钨合金粉末的方法，所述方法具体包括以下步骤：
1）将钨粉、铜粉按比例配制成铜钨复合粉，放入球磨罐中；所述铜钨复合粉中，钨粉和铜粉按质量比的含量分别为：钨粉70-80%，其余为铜粉；
2）在球磨罐中，加入球磨介质和磨球，所述球磨介质占铜钨复合粉质量的5-7%，球磨介质为易挥发性有机溶剂；所述磨球与铜钨复合粉的质量比为20-50：1；
3）在球磨罐中充入保护气体或抽真空，打开球磨罐的循环冷却水，开始球磨，球磨时间为50-100小时，球磨结束，静置，待粉料和磨球充分冷却后取出粉末，得到铜钨合金粉末。
所述步骤1）中，钨粉和铜粉的纯度均大于99.5%。
所述球磨介质为无水乙醇。
所述磨球为不同大小的硬质合金磨球、玛瑙磨球、不锈钢磨球中的一种或两种以上任意比例的混合。
所述球磨罐的材质为尼龙或不锈钢。
在步骤3）中，在球磨罐中充入的保护气体为氮气或氢气。
在步骤3）球磨过程中，球磨罐外壁始终采用循环水冷却。
本发明采用以上技术方案，采用高球料比的机械合金化法，使铜在常温下完全溶入钨颗粒中，形成过饱和固溶体合金粉末。该方法得到的钨铜合金粉末具有晶粒细小、成份均匀、易于分散的优点，制造工艺简单，适用成分范围广，易于控制。
具体实施方式
本发明一种用机械合金化制造铜钨合金粉末的方法，所述方法具体包括以下步骤：
1）将钨粉、铜粉按比例配制成铜钨复合粉，放入球磨罐中；所述铜钨复合粉中，钨粉和铜粉按质量比的含量分别为：钨粉70-80%，其余为铜粉；
2）在球磨罐中，加入球磨介质和磨球，所述球磨介质占铜钨复合粉质量的5-7%，球磨介质为易挥发性有机溶剂；所述磨球与铜钨复合粉的质量比为20-50：1；
3）在球磨罐中充入保护气体或抽真空，打开球磨罐的循环冷却水，开始球磨，球磨时间为50-100小时，球磨结束，静置，待粉料和磨球充分冷却后取出粉末，得到铜钨合金粉末。
所述步骤1）中，钨粉和铜粉的纯度均大于99.5%。
所述球磨介质为无水乙醇。
所述磨球为不同大小的硬质合金磨球、玛瑙磨球、不锈钢磨球中的一种或两种以上任意比例的混合。
所述球磨罐的材质为尼龙或不锈钢。
在步骤3）中，在球磨罐中充入的保护气体为氮气或氢气。
在步骤3）球磨过程中，球磨罐外壁始终采用循环水冷却。
实施例1：将质量比含量为70%的钨粉、30%的铜粉配制成铜钨复合粉，放入尼龙材质的球磨罐中。在球磨罐中，加入无水乙醇和硬质合金磨球，无水乙醇占铜钨复合粉质量的5%，硬质合金磨球与铜钨复合粉的质量比为50：1。充入氮气将球磨罐中的空气排除，进行保护，并将球磨罐密封，打开球磨罐的循环冷却水，开始球磨，球磨100小时，球磨结束，静置，待粉料和硬质合金磨球充分冷却后取出粉末，得到铜钨合金粉末。
实施例2：将质量比含量为75%的钨粉、25%的铜粉配制成铜钨复合粉，放入尼龙材质的球磨罐中。在球磨罐中，加入无水乙醇和玛瑙磨球，无水乙醇占铜钨复合粉质量的6%，玛瑙磨球与铜钨复合粉的质量比为40：1。用氢气将球磨罐中的空气排除，进行保护，并将球磨罐密封，打开球磨罐的循环冷却水，开始球磨，球磨80小时，球磨结束，静置，待粉料和玛瑙磨球充分冷却后取出粉末，得到铜钨合金粉末。
实施例3：将质量比含量为80%的钨粉、20%的铜粉配制成铜钨复合粉，放入不锈钢材质的球磨罐中。在球磨罐中，加入无水乙醇和不锈钢磨球，无水乙醇占铜钨复合粉质量的7%，不锈钢磨球与铜钨复合粉的质量比为20：1。将球磨罐中缓慢抽真空至小于或等于10-1Pa，打开球磨罐的循环冷却水，开始球磨，球磨50小时，球磨结束，静置，待粉料和不锈钢磨球充分冷却后取出粉末，得到铜钨合金粉末。

Claims (7)

1.一种用机械合金化制造铜钨合金粉末的方法，其特征在于：所述方法具体包括以下步骤：
1）将钨粉、铜粉按比例配制成铜钨复合粉，放入球磨罐中；所述铜钨复合粉中，钨粉和铜粉按质量比的含量分别为：钨粉70-80%，其余为铜粉；
2）在球磨罐中，加入球磨介质和磨球，所述球磨介质占铜钨复合粉质量的5-7%，球磨介质为易挥发性有机溶剂；所述磨球与铜钨复合粉的质量比为20-50：1；
3）在球磨罐中充入保护气体或抽真空，打开球磨罐的循环冷却水，开始球磨，球磨时间为50-100小时，球磨结束，静置，待粉料和磨球充分冷却后取出粉末，得到铜钨合金粉末。
2.根据权利要求1所述的一种用机械合金化制造铜钨合金粉末的方法，其特征在于：所述步骤1）中，钨粉和铜粉的纯度均大于99.5%。
3.根据权利要求1所述的一种用机械合金化制造铜钨合金粉末的方法，其特征在于：所述球磨介质为无水乙醇。
4.根据权利要求1所述的一种用机械合金化制造铜钨合金粉末的方法，其特征在于：所述磨球为不同大小的硬质合金磨球、玛瑙磨球、不锈钢磨球中的一种或两种以上任意比例的混合。
5.根据权利要求1所述的一种用机械合金化制造铜钨合金粉末的方法，其特征在于：所述球磨罐的材质为尼龙或不锈钢。
6.根据权利要求1所述的一种用机械合金化制造铜钨合金粉末的方法，其特征在于：在步骤3）中，在球磨罐中充入的保护气体为氮气或氢气。
7.根据权利要求1所述的一种用机械合金化制造铜钨合金粉末的方法，其特征在于：在步骤3）球磨过程中，球磨罐外壁始终采用循环水冷却。
CN201410278010.1A 2014-06-20 2014-06-20 一种用机械合金化制造铜钨合金粉末的方法 Active CN104001929B (zh)