CN103979905A - 一种掺钛白粉的混凝土及其制作方法 - Google Patents

一种掺钛白粉的混凝土及其制作方法 Download PDF

Info

Publication number
CN103979905A
CN103979905A CN201410125122.3A CN201410125122A CN103979905A CN 103979905 A CN103979905 A CN 103979905A CN 201410125122 A CN201410125122 A CN 201410125122A CN 103979905 A CN103979905 A CN 103979905A
Authority
CN
China
Prior art keywords
parts
concrete
titanium dioxide
waste
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410125122.3A
Other languages
English (en)
Other versions
CN103979905B (zh
Inventor
朱安会
马洪章
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangmen Zhiguang cement products Co., Ltd.
Original Assignee
Anhui Xin Run Type Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Xin Run Type Material Co Ltd filed Critical Anhui Xin Run Type Material Co Ltd
Priority to CN201410125122.3A priority Critical patent/CN103979905B/zh
Publication of CN103979905A publication Critical patent/CN103979905A/zh
Application granted granted Critical
Publication of CN103979905B publication Critical patent/CN103979905B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种掺钛白粉的混凝土，其特征在于，由下列重量份的原料制成：水泥90-120、砂砾80-100、脱硫石膏30-40、橡胶颗粒10-13、环氧树脂9-11、异氰酸酯8-10、钛白粉5-8、氟硅酸钠2-4、废弃混凝土95-125、粉煤灰80-100、硝酸钠2-4、废旧衣服40-50、助剂4-8、适量水；本发明制得的混凝土的骨料中含有废弃混凝土、粉煤灰，减少了天然砂石的用量，提高了废弃混凝土利用率，降低了生产成本，钛白粉及废旧衣服纤维添加到本发明的原料中，增加了混凝土的韧性和防辐射性能，使制得的混凝土不易开裂、和易性好、抗压强度高、耐高温性能优等优点。

Description

一种掺钛白粉的混凝土及其制作方法
 
技术领域
本发明涉及建筑混凝土技术领域，具体涉及一种掺钛白粉的混凝土及其制作方法。
背景技术
混凝土通常是以水泥作胶凝材料，砂、石作集料，与水（可含外加剂和掺合料）按一定比例配合，经搅拌而得的水泥混凝土，也称普通混凝土，它具有易成型、能耗低、耐久性好、价格便宜以及与钢材结合可制成各种承重机构的优点，是当代应用最广泛的建筑材料，对人类社会的发展起着十分重要的作用
作为混凝土必须添加料之一的集料用量很大，天然集料过度开采，使之质量也无法满足现有混凝土生产的需求，目前混凝土还存在强度差、抗冻性低、干燥收缩大，易发生开裂等不足。因此，研制各种人造集料和寻找合适的代用材料，从而开发出一种高强度、耐冻性好、干燥收缩性小、不易开裂、抗菌耐热等功能的新型混凝土，以满足高质量建设工程的需要成为本领域急需解决的技术难题。
近年来，随着生活水平的提高和社会进步，人们日常生活和工业生产过程产生的各种固废以及城市建设拆迁重造带来的固废等一直困扰着居民的生活环境，特别是一些不能继续穿的废旧衣服的处理一直是一道难题。本发明将固废作为原材料添加到混凝土中，实现了废物的循环利用，减少了对环境的污染，符合可持续发展战略要求。
发明内容
本发明的目的就是提供一种掺钛白粉的混凝土及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种掺钛白粉的混凝土，其特征在于，由下列重量份的原料制成：水泥90-120、砂砾80-100、脱硫石膏30-40、橡胶颗粒10-13、环氧树脂9-11、异氰酸酯8-10、钛白粉5-8、氟硅酸钠2-4、废弃混凝土95-125、粉煤灰80-100、硝酸钠2-4、废旧衣服40-50、助剂4-8、适量水。
所述的助剂由下列重量份原料制成：高岭土7-12、桐油2-4、尿素10-13、苦楝皮9-11、氢氧化铝9-13、废旧玻璃4-7、十二烷基苯磺酸钠0.03-0.07、镁粉0.02-0.04、超微蜡粉0.3-0.6、沥青2-5、玫瑰精油0.03-0.07，其制备方法是将各物料粉碎混匀，加适量水搅拌30-40分钟，造粒，成球粒径在2-5mm，烘干即得。
所述的一种掺钛白粉的混凝土的制备方法，其特征在于包括以下步骤：
（1）将废旧衣服清洗干净拆除纽扣、拉链等配饰后，撕扯使大块的纠结纤维松解变成棉絮状，制成5-10mm左右长的纤维备用；
（2）将脱硫石膏、粉煤灰一起于610-815℃下煅烧3-6小时后取出粉碎，加入橡胶颗粒、环氧树脂、钛白粉和适量水搅拌30-40分钟，混匀，造粒，成球粒径在5-8mm；
（3）将废弃混凝土放入1‰氯化铁和0.5‰氯化钙复合溶液中浸渍10-12小时，取出自然晾干粉碎；
（4）将步骤（1）（2）、（3）反应物料及其他剩余物料加适量水搅拌5-8分钟混匀即得。
本发明有以下有益效果：本发明制得的混凝土的骨料中含有废弃混凝土、粉煤灰，减少了天然砂石的用量，提高了废弃混凝土利用率，降低了生产成本，钛白粉及废旧衣服纤维添加到本发明的原料中，增加了混凝土的韧性和防辐射性能，使制得的混凝土不易开裂、和易性好、抗压强度高、耐高温性能优等优点。
具体实施方式
所述的一种掺钛白粉的混凝土，其特征在于，由下列重量份的原料制成：水泥97、砂砾85、脱硫石膏36、橡胶颗粒12、环氧树脂9、异氰酸酯10、钛白粉5、氟硅酸钠2、废弃混凝土98、粉煤灰100、硝酸钠4、废旧衣服45、助剂8、适量水。
所述的助剂由下列重量份原料制成：高岭土8、桐油3、尿素11、苦楝皮9、氢氧化铝13、废旧玻璃7、十二烷基苯磺酸钠0.06、镁粉0.02、超微蜡粉0.3、沥青2、玫瑰精油0.03，其制备方法是将各物料粉碎混匀，加适量水搅拌30-40分钟，造粒，成球粒径在2-5mm，烘干即得。
制作方法包括以下步骤：
（1）将废旧衣服清洗干净拆除纽扣、拉链等配饰后，撕扯使大块的纠结纤维松解变成棉絮状，制成5-10mm左右长的纤维备用；
（2）将脱硫石膏、粉煤灰一起于610-815℃下煅烧3-6小时后取出粉碎，加入橡胶颗粒、环氧树脂、钛白粉和适量水搅拌30-40分钟，混匀，造粒，成球粒径在5-8mm；
（3）将废弃混凝土放入1‰氯化铁和0.5‰氯化钙复合溶液中浸渍10-12小时，取出自然晾干粉碎；
（4）将步骤（1）（2）、（3）反应物料及其他剩余物料加适量水搅拌5-8分钟混匀即得。
通过上述实施例加工得到的混凝土的技术指标如下：
（1）导热系数（平均温度25±2℃）：0.081W/(m·k)；
（2）抗压强度（28d）：32.15MPa；
（3）和易性良好，施工性能及强度满足施工要求；
（4）耐高温、和墙面紧密粘结、无缝。

Claims (2)

1.一种掺钛白粉的混凝土，其特征在于，由下列重量份的原料制成：水泥90-120、砂砾80-100、脱硫石膏30-40、橡胶颗粒10-13、环氧树脂9-11、异氰酸酯8-10、钛白粉5-8、氟硅酸钠2-4、废弃混凝土95-125、粉煤灰80-100、硝酸钠2-4、废旧衣服40-50、助剂4-8、适量水；所述的助剂由下列重量份原料制成：高岭土7-12、桐油2-4、尿素10-13、苦楝皮9-11、氢氧化铝9-13、废旧玻璃4-7、十二烷基苯磺酸钠0.03-0.07、镁粉0.02-0.04、超微蜡粉0.3-0.6、沥青2-5、玫瑰精油0.03-0.07，其制备方法是将各物料粉碎混匀，加适量水搅拌30-40分钟，造粒，成球粒径在2-5mm，烘干即得。
2.根据权利要求1所述的一种掺钛白粉的混凝土的制作方法，其特征在于包括以下步骤：
（1）将废旧衣服清洗干净拆除纽扣、拉链等配饰后，撕扯使大块的纠结纤维松解变成棉絮状，制成5-10mm左右长的纤维备用；
（2）将脱硫石膏、粉煤灰一起于610-815℃下煅烧3-6小时后取出粉碎，加入橡胶颗粒、环氧树脂、钛白粉和适量水搅拌30-40分钟，混匀，造粒，成球粒径在5-8mm；
（3）将废弃混凝土放入1‰氯化铁和0.5‰氯化钙复合溶液中浸渍10-12小时，取出自然晾干粉碎；
（4）将步骤（1）（2）、（3）反应物料及其他剩余物料加适量水搅拌5-8分钟混匀即得。
CN201410125122.3A 2014-03-31 2014-03-31 一种掺钛白粉的混凝土及其制作方法 Expired - Fee Related CN103979905B (zh)