CN103979809B - 利用锂云母提锂渣制备少熟料白色硅酸盐水泥的方法 - Google Patents
利用锂云母提锂渣制备少熟料白色硅酸盐水泥的方法 Download PDFInfo
- Publication number
- CN103979809B CN103979809B CN201410151900.6A CN201410151900A CN103979809B CN 103979809 B CN103979809 B CN 103979809B CN 201410151900 A CN201410151900 A CN 201410151900A CN 103979809 B CN103979809 B CN 103979809B
- Authority
- CN
- China
- Prior art keywords
- white
- lithium slag
- portland cement
- extracted lithium
- lepidolite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种利用锂云母提锂渣制备少熟料白色硅酸盐水泥的方法，将锂云母提锂渣与白色硅酸盐水泥熟料、石膏、石灰、白石子等组分材料计量配料后，送入球磨机粉磨至0.08mm方孔筛筛余小于10%即得产品，上述各原料的质量百分比为：锂云母提锂渣30-55%，白色硅酸盐水泥熟料20-40%，白石子5-10%，二水石膏3-6%，石灰5-10%。本发明由于大量利用锂云母提锂渣，可大量节约白水泥熟料，大幅节省能耗和矿物资源，具有节能、环保、资源循环利用等多重意义。
Description
技术领域
本发明涉及一种利用锂云母提锂渣制备少熟料白色硅酸盐水泥的方法，属于特种水泥技术领域。
背景技术
江西宜春钽铌伴生锂云母矿是我国最大的钽铌锂原料基地。氯盐压煮法锂云母提锂是目前国内锂云母提锂成本最低的工艺方法，但是锂云母中的氧化锂只占锂云母矿中的4～5%，提取量只有3%左右，仅提锂后的废渣数量高达95%以上，产渣量极大，因此提锂渣的有效综合利用对该矿物提锂技术的节能减排及清洁生产具有重要意义。
我国白水泥企业生产的白色硅酸盐水泥品种中有一种专用于饰面涂装的低标号白水泥，该品种虽然在国家标准规定的强度等级之外，但因其施工性能好、饰面美观、价格低廉，因而备受用户欢迎。该类产品通常都由生产企业依据自行制订的企业标准进行生产，或由靠近市场的粉磨站购买白水泥厂的熟料进行加工生产，其特点是只有少量白水泥熟料配掺较多的白石子（白度在90亨特度以上的石灰石、方解石、白云石等）和适量石膏磨细制成，其强度等级大多为17.5MPa或22.5MPa，属于少熟料水泥类型。近年来，由于优质白色石灰石、方解石和白云石资源日益紧缺，价格不断上涨，使白色饰面水泥的价格优势逐渐缩小。因此，寻找可替代白色碳酸钙的白水泥混合材已成为白水泥企业的迫切愿望。
少熟料白色硅酸盐水泥具有能耗低、水化热低、安定性好、施工性能好、生产成本低等特点，在建筑装饰领域具有广泛用途，可用于白色墙体饰面材料、制备水磨石、彩色路面材料、彩色地砖、彩色瓦等。当制备彩色水泥制品时，由于掺有大量锂云母提锂渣，可有效克服水泥制品表面泛碱（即白霜）现象。
发明内容
本发明的目的是提供一种利用锂云母提锂渣作混合材，与白色硅酸盐水泥熟料、石膏、白石子等制备少熟料白色硅酸盐水泥的方法。该产品可广泛应用于生产建筑墙体的饰面材料。
本发明的制造工艺为：将锂云母提锂渣与白色硅酸盐水泥熟料、石膏、石灰、白石子等组分材料计量配料后，喂入球磨机粉磨至0.08mm方孔筛筛余小于10%即得产品，上述各原料的质量百分比为：锂云母提锂渣30-55%，白色硅酸盐水泥熟料20-40%，白石子5-10%，二水石膏3-6%，石灰5-10%；
本发明所述的锂云母提锂渣可以是氯盐压煮法锂云母矿提锂后的滤渣；白石子可以是白度在90亨特度以上的白色方解石、白云石和石灰石中的一种。
锂云母提锂渣的组成见表1。锂渣放射性检测结果见表2。
锂渣的放射性强度远低于中华人民共和国国家标准（GB6566—2001）规定的天然放射性核素镭–226、钍–232、钾–40放射性比活度的限量（分别为370、260、4200Bq·kg-1））要求，说明锂渣完全可以用于生产建筑材料。
本发明的有益效果：
（1）氯盐法锂云母提锂渣具有较好的火山灰活性，其掺入白水泥中作为活性混合材比掺加传统的石灰石非活性混合材更有利于水泥强度，而且明显降低生产成本。
（2）锂云母提锂渣中的活性SiO2、Al2O3可吸收白水泥熟料中的游离氧化钙，因此可与游离氧化钙较高的白水泥熟料掺合使用，可放宽白水泥熟料中的游离氧化钙限量，有利于生产和质量控制。
（3）由于大量利用锂云母提锂渣，可大量节约白水泥熟料，大幅节省能耗和矿物资源，具有节能、环保、资源循环利用等多重意义。
具体实施方式
实施例1：
产品配方：锂云母提锂渣45%，白色硅酸盐水泥熟料40%，方解石10%，二水石膏5%，。
将上述各组分材料在球磨机中粉磨至0.08mm方孔筛筛余小于10%即制得产品。
实施例2：
产品配方：锂云母提锂渣55%，白色硅酸盐水泥熟料30%，方解石10%，二水石膏5%。
将上述各组分材料在球磨机中粉磨至0.08mm方孔筛筛余小于10%即制得产品。
实施例3：
产品配方：锂云母提锂渣50%，白色硅酸盐水泥熟料30%，方解石10%，石灰5%，二水石膏5%。。
将上述各组分材料在球磨机中粉磨至0.08mm方孔筛筛余小于10%即制得产品。
依据国家标准GB/T1346检测凝结时间，GB/T1767检测强度，GB/T2015-2005附录A测定白度，实施例1、实施例2、实施例3所制得产品的主要技术性能指标见表3。
注：所用白色硅酸盐水泥熟料的实测28d抗压强度为53.5MPa，白度为85亨特度；所用锂云母提锂渣的白度为78亨特度。
由表3可见，三个实施例所制锂云母提锂渣少熟料白色硅酸盐水泥的28d强度都大于22.5NPa，凝结时间符合国家标准GB/T2015-2005规定的要求，技术性能完全满足白色饰面水泥的要求。
Claims (1)
1.一种利用锂云母提锂渣制备少熟料白色硅酸盐水泥的方法，其特征在于：将锂云母提锂渣与白色硅酸盐水泥熟料、石膏、石灰、白石子组分材料计量配料后，喂入球磨机粉磨至0.08mm方孔筛筛余小于10％即得产品，上述各原料的质量百分比为：锂云母提锂渣30-55％，白色硅酸盐水泥熟料20-40％，白石子5-10％，二水石膏3-6％，石灰5-10％；上述原料的质量百分比之和为100％；
所述锂云母提锂渣是氯盐压煮法锂云母矿提锂后的滤渣；
所述白石子是白度在90亨特度以上的白色方解石、白云石和石灰石中的一种。