CN103967261A - Stain-resistant putty spatula and manufacturing method thereof - Google Patents
Stain-resistant putty spatula and manufacturing method thereof Download PDFInfo
- Publication number
- CN103967261A CN103967261A CN201410139825.1A CN201410139825A CN103967261A CN 103967261 A CN103967261 A CN 103967261A CN 201410139825 A CN201410139825 A CN 201410139825A CN 103967261 A CN103967261 A CN 103967261A
- Authority
- CN
- China
- Prior art keywords
- component
- stain resistant
- resistant material
- cutter
- material coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a stain-resistant putty spatula and a manufacturing method thereof. The spatula comprises a handle and a blade base body, and the surface of the blade base body is coated with a stain-resistant material coating which is mainly made from modified silica sol materials, wherein the thickness of the stain-resistant material coating is 30-60 microns. Materials can not adhere to the putty spatula, the materials can be smeared evenly, material loss is reduced, and work efficiency is improved.
Description
Technical field
The present invention relates to the instrument using in a kind of fitment process, be specially stain resistant putty and criticize cutter and preparation method thereof.
Background technology
In household fitment process, people can criticize cutter with putty and carry out base treatment and wall surface putty processing, but traditional putty is criticized cutter meeting adhered materials, not only can be unfavorable for the coating of material in operating process, reduces operating efficiency, also can improve the loss late of material.
Summary of the invention
In order to solve above-mentioned existing technological deficiency, the object of this invention is to provide a kind of stain resistant putty and criticize cutter and preparation method thereof, efficiently solve in use material and easily on batch cutter, adhesion problem occurs.
For achieving the above object, the present invention adopts following technical scheme:
A kind of stain resistant putty is criticized cutter, comprises handle and blade base, and described blade base surface spraying has one deck stain resistant material coating.
Further, the main component of described stain resistant material coating is modified silicasol, and coating layer thickness is 30-60 μ m.
Further, described stain resistant material coating comprises component A, B component and component C; According to quality than component A: B component: component C is (50 ~ 70): (20 ~ 50): (1 ~ 5), and summation is 100.
Further, described stain resistant material coating component A is a kind of Ludox, is one or more combinations in acidic silicasol, alkaline silica sol and neutral Ludox; Ludox is the colloidal solution that silicon dioxide colloid particulate evenly diffuses to form in water, is a kind of inorganic material of stable chemical nature; Described stain resistant material coating B component includes organic siloxane, silicone oil, auxiliary agent, solvent; Described organosiloxane is one or more combinations in MTMS, γ-(methacryloxypropyl) propyl trimethoxy silicane, γ-glycidyl ether oxygen propyl trimethoxy silicane and gamma-aminopropyl-triethoxy-silane, described auxiliary agent is levelling agent and/or defoamer, and described solvent is isopropyl alcohol; Described stain resistant material coating component C is initator, is one in formic acid, hydrochloric acid and ammoniacal liquor or multiple combination.
Stain resistant putty is criticized a preparation method for cutter, comprises the steps:
1) blade base processing: sandblast, rust cleaning, oil removing, removing oxide layer are carried out in the blade base surface of putty being criticized to cutter;
2) prepare stain resistant material: proportionally component C is joined in component A, regulate the pH of component A to 3-4, mix; B component is added in the component A mixing, under room temperature, stir 14-20 hour, rotating speed is 130-150rpm; By sol-gel process modified silicasol, make the hybrid inorganic-organic materials of stain resistant;
3) spraying stain resistant material coating: on the blade base of processing, spray stain resistant material coating, coating thickness 30-60 μ m, when spraying, the temperature of blade base is controlled at 50-80 DEG C;
4) hot setting: the putty that is coated with stain resistant material coating is criticized to cutter heat treatment 15-30min at 150 DEG C-300 DEG C.
Compared with prior art, the present invention has following outstanding substantive distinguishing features and significant advantage:
It is to be coated with one deck staining-proof coating that the present invention criticizes cutter surface at traditional putty, and this coating is water paint, environmental friendliness.The present invention has used stain resistant material coating, has not only kept putty to criticize the clean of cutter surface, is more conducive to the construction of the larger material of viscosity, has improved operating efficiency, effectively reduces the loss late of material.Stain resistant putty of the present invention is criticized the coating that cutter also can be used for other thickness pulpous state material, comprises the construction of aqueous damping coating.
Brief description of the drawings
Fig. 1 is the structural representation that stain resistant putty is criticized cutter.
Detailed description of the invention
Below in conjunction with accompanying drawing, the specific embodiment of the present invention is further described.
embodiment 1
As shown in Figure 1, a kind of stain resistant putty is criticized cutter, comprises handle 1 and blade base 2, and described blade base 2 surface sprayings have one deck stain resistant material coating 3.
Stain resistant putty is criticized a preparation method for cutter, comprises the steps:
A. blade base processing: sandblast, rust cleaning, oil removing, removing oxide layer are carried out in the blade base surface of putty being criticized to cutter;
B. prepare stain resistant material: proportionally component C is joined in component A, regulate the pH to 4 of component A, mix; B component is added in the component A mixing, stir 14 hours under room temperature, rotating speed is 150rpm; By sol-gel process modified silicasol, make the hybrid inorganic-organic materials of stain resistant; Fill a prescription as follows:
C. spray stain resistant material coating: on the blade base of processing, spray stain resistant material coating, coating thickness 40 μ m, when spraying, the temperature of blade base is controlled at 55 DEG C.
D. hot setting: the putty that is coated with stain resistant material coating is criticized to cutter and put into baker heating cure, temperature is 200 DEG C, and the time is 20min.After coating is solidified completely, come out of the stove, complete whole manufacture process.
embodiment 2
Stain resistant putty is criticized a preparation method for cutter, comprises the steps:
A. blade base processing: sandblast, rust cleaning, oil removing, removing oxide layer are carried out in the blade base surface of putty being criticized to cutter;
B. prepare stain resistant material: proportionally component C is joined in component A, regulate the PH to 3.5 of component A, mix.B component is joined in the component A mixing, stir 20 hours under room temperature, rotating speed is 130rpm, prepares modified silicasol by sol-gel process, makes the organic-inorganic hybridization coating of stain resistant; Fill a prescription as follows:
C. spray stain resistant material coating: on the blade base of processing, spray stain resistant material coating, coating thickness 45 μ m, when spraying, the temperature of blade base is controlled at 55 DEG C.
D. hot setting: the putty that is coated with stain resistant material coating is criticized to cutter and put into baker heating cure, temperature is 200 DEG C, and the time is 20min.After coating is solidified completely, come out of the stove, complete whole manufacture process.
Claims (5)
1. stain resistant putty is criticized a cutter, comprises handle and blade base, it is characterized in that, described blade base surface spraying has one deck stain resistant material coating.
2. stain resistant putty according to claim 1 is criticized cutter, it is characterized in that, the main component of described stain resistant material coating is modified silicasol, and coating layer thickness is 30-60 μ m.
3. stain resistant putty according to claim 1 and 2 is criticized cutter, it is characterized in that, described stain resistant material coating comprises component A, B component and component C; According to quality than component A: B component: component C is (50 ~ 70): (20 ~ 50): (1 ~ 5), and summation is 100.
4. stain resistant putty according to claim 3 is criticized cutter, it is characterized in that, described stain resistant material coating component A is a kind of Ludox, is one or more combinations in acidic silicasol, alkaline silica sol and neutral Ludox; Ludox is the colloidal solution that silicon dioxide colloid particulate evenly diffuses to form in water, is a kind of inorganic material of stable chemical nature; Described stain resistant material coating B component includes organic siloxane, silicone oil, auxiliary agent, solvent; Described organosiloxane is one or more combinations in MTMS, γ-(methacryloxypropyl) propyl trimethoxy silicane, γ-glycidyl ether oxygen propyl trimethoxy silicane and gamma-aminopropyl-triethoxy-silane, described auxiliary agent is levelling agent and/or defoamer, and described solvent is isopropyl alcohol; Described stain resistant material coating component C is initator, is one in formic acid, hydrochloric acid and ammoniacal liquor or multiple combination.
5. stain resistant putty is criticized a preparation method for cutter, it is characterized in that, comprises the steps:
1) blade base processing: sandblast, rust cleaning, oil removing, removing oxide layer are carried out in the blade base surface of putty being criticized to cutter;
2) prepare stain resistant material: proportionally component C is joined in component A, regulate the pH of component A to 3-4, mix; B component is added in the component A mixing, under room temperature, stir 14-20 hour, rotating speed is 130-150rpm; By sol-gel process modified silicasol, make the hybrid inorganic-organic materials of stain resistant;
3) spraying stain resistant material coating: on the blade base of processing, spray stain resistant material coating, coating thickness 30-60 μ m, when spraying, the temperature of blade base is controlled at 50-80 DEG C;
4) hot setting: the putty that is coated with stain resistant material coating is criticized to cutter heat treatment 15-30min at 150 DEG C-300 DEG C.