CN103965808A - 一种利用废聚苯乙烯泡沫塑料制备的防水补漏胶 - Google Patents
一种利用废聚苯乙烯泡沫塑料制备的防水补漏胶 Download PDFInfo
- Publication number
- CN103965808A CN103965808A CN201410190200.8A CN201410190200A CN103965808A CN 103965808 A CN103965808 A CN 103965808A CN 201410190200 A CN201410190200 A CN 201410190200A CN 103965808 A CN103965808 A CN 103965808A
- Authority
- CN
- China
- Prior art keywords
- foam plastic
- percent
- polystyrene foam
- water
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种利用废聚苯乙烯泡沫塑料制备的防水补漏胶,由以下重量百分比的原料组成:45-60%聚苯乙烯泡沫塑料胶液,15-20%酚醛调和漆料,0.5-1%消泡剂,0.5-1.5%松节油,0.5-1%稳定剂,0.5-1%抗氧化剂,0.5-1%催干剂,填料补足100%;聚苯乙烯泡沫塑料胶液利用废聚苯乙烯泡沫塑料制备而成,酚醛调和漆料用酚醛树脂和石灰松香制备而成。本发明主要应用于楼房顶层、外墙、卫生间等渗漏水的处理,也可应用于瓷砖、马赛克或水泥块等材料的粘接,具有粘度高、弹性好、耐晒耐水耐寒、使用方便、成本低、工艺简单、稳定可靠、无二次污染的优点。
Description
技术领域
本发明涉及一种利用废聚苯乙烯泡沫塑料制备的防水补漏胶,主要应用于楼房顶层、外墙、卫生间等渗漏水的处理,也可应用于瓷砖、马赛克或水泥块等材料的粘接。
背景技术
目前,为了防止建筑渗漏水,多采取在混凝土或砂浆中加入化学防水剂增加密实度以达到防水目的,由于化学防水剂属于刚性防水材料,抗老化性能较好,但是其抗裂性较差,易变性,仍然会导致建筑渗漏水的现象发生。
防水补漏胶主要用于建筑装修中的楼房翻新防水、楼顶补漏防水、外墙防水、室内的厨卫防水、管道防渗漏等防水工程施工。防水补漏胶不仅要求防水性能好,同时还需要环保、安全,使用方便。
传统的防水卷材施工复杂,环保性差,抗老化性能较差;而常用的防水涂料中多含有有害物质,人畜使用不安全,且易污染环境,抗老化性能也较差。
发明内容
本发明所要解决的技术问题在于提供一种防水性能好,耐水耐寒耐晒,使用方便,环保安全的防水补漏胶。
本发明解决上述技术问题所采取的技术方案为:一种利用废聚苯乙烯泡沫塑料制备的防水补漏胶,由以下重量百分比的原料组成:45-60%聚苯乙烯泡沫塑料胶液,15-20%酚醛调和漆料,0.5-1%消泡剂,0.5-1.5%松节油,0.5-1%稳定剂,0.5-1%抗氧化剂,0.5-1%催干剂,填料补足100%;
所述的聚苯乙烯泡沫塑料胶液由以下重量百分比的原料组成:10-30%废聚苯乙烯泡沫塑料,0.1-0.5%异氰酸酯交联剂,2-4%邻苯二甲酸二辛酯,有机溶剂补足100%;所述的有机溶剂为乙酸乙酯、聚氨酯稀释剂和丙酮;
所述的酚醛调和漆料由以下重量百分比的原料组成:5-6%松香改性酚醛树脂、5-6%石灰松香、20-30%桐油、10-12%亚桐聚合油、0.2-1%醋酸铅、200号溶剂汽油补足100%。
进一步地,所述的聚苯乙烯泡沫塑料胶液中的有机溶剂,乙酸乙酯、聚氨酯稀释剂和丙酮的质量比为1.2:1:1。
所述的抗氧化剂为抗氧化剂330或抗氧化剂2246,消泡剂为磷酸三丁酯,填料为滑石粉或膨润土,催干剂为环烷酸钴和环烷酸锰,环烷酸钴和环烷酸锰的质量比为1:1。
与现有技术相比,本发明所述的防水补漏胶粘度高、富有弹性、抗晒、耐水、耐寒、使用方便,主要应用于楼房顶层、外墙、卫生间等渗漏水的处理,也可应用于瓷砖、马赛克或水泥块等材料的粘接。同时回收利用废弃泡沫塑料,变废为宝,不仅能消除其引起的环境污染,且原料成本低、工艺简单、稳定可靠,无二次污染,具有较好的经济效益和社会效益。
具体实施方式
下面结合实施例对本发明的技术方案做进一步说明。
一.产品配方
1.表1制备聚苯乙烯泡沫塑料胶液的配方表
原料 | 实施例1 | 实施例2 | 实施例3 |
废聚苯乙烯泡沫塑料 | 10% | 20% | 30% |
异氰酸酯交联剂 | 0.1% | 0.3% | 0.5% |
邻苯二甲酸二辛酯 | 2% | 3% | 4% |
乙酸乙酯 | 33% | 28.5% | 24.5% |
聚氨酯稀释剂 | 27.5% | 24% | 20% |
丙酮 | 补足100% | 补足100% | 补足100% |
2.表2制备酚醛调和漆料的配方表
原料 | 实施例1 | 实施例2 | 实施例3 |
松香改性酚醛树脂 | 5% | 5.5% | 6% |
石灰松香 | 5% | 5.5% | 6% |
桐油 | 20% | 25% | 30% |
亚桐聚合油 | 10% | 10.5% | 12% |
醋酸铅 | 0.2% | 0.5% | 1% |
200号溶剂汽油 | 补足100% | 补足100% | 补足100% |
3.表3产品总配方表
原料 | 实施例1 | 实施例2 | 实施例3 |
聚苯乙烯泡沫塑料胶液 | 45% | 54% | 60% |
酚醛调和漆料 | 15% | 18% | 20% |
磷酸三丁酯(消泡剂) | 0.5% | 0.8% | 1% |
松节油 | 0.5% | 0.8% | 1.5% |
光稳定剂UV-9 | 0.5% | 1% | |
光稳定剂UV-531 | 0.8% | ||
抗氧化剂330 | 0.5% | 1% | |
抗氧化剂2246 | 0.5% |
环烷酸钴 | 0.5% | 0.5% | 0.5% |
环烷酸锰 | 0.5% | 0.5% | 0.5% |
滑石粉 | 补足100% | 补足100% | |
膨润土 | 补足100% |
二.产品制备方法
1.制备聚苯乙烯泡沫塑料胶液
按照表1所述的配方比例计算好各原料所需的量,将废聚苯乙烯泡沫塑料清洗干净后晾干,经粉碎后放入桶内,加入其他原料溶解搅拌,静置20-30h后过滤得聚苯乙烯泡沫塑料胶液,备用;
2.制备酚醛调和漆料
按照表2所述的配方比例计算好各原料所需的量,将松香改性酚醛树脂、石灰松香、桐油和一半亚桐聚合油投入热炼锅混合,升温175-180℃,加入醋酸铅,继续升温270-275℃,保温至粘度为100-200s,降温并加入另一半亚桐聚合油,冷却至155-160℃,加入200号溶剂汽油稀释,过滤得酚醛调和漆料,备用;
所述的粘度的测定采用涂-4杯测定法,在温度为25℃条件下测定;
3.按照表3所述的配方比例计算好各原料所需的量,将上述制备好的聚苯乙烯泡沫塑料胶液和酚醛调和漆料按照质量比为3:1混合,搅拌均匀后再加入剩余原料继续搅拌均匀,最后用胶膜机磨1-2遍即可。
三.产品质量检测
将实施例2所得的产品进行产品质量检测,最终结果如表4所示。
表4产品质量检测表
检测项目 | 指标标准值 | 产品的最终检测值 |
拉伸强度 | ≥1.0Mpa | 3.5Mpa |
无空隙结构粘结强度 | ≥0.6Mpa | 1.6Mpa |
无空隙结构粘结强度 | ≥0.6Mpa | 2.3Mpa |
不透水性28d | 0.8Mpd动水压力,2h | 不透水 |
吸水率/㎡.h | ≤0.2 | 0.08 |
耐水压剪强度 | ≥0.8Mpa | 3.0Mpa |
耐冻压剪强度 | ≥0.8Mpa | 3.2Mpa |
开裂指数 | ≤0.3 | 0.1 |
Claims (3)
1.一种利用废聚苯乙烯泡沫塑料制备的防水补漏胶,其特征在于,由以下重量百分比的原料组成:45-60%聚苯乙烯泡沫塑料胶液,15-20%酚醛调和漆料,0.5-1%消泡剂,0.5-1.5%松节油,0.5-1%稳定剂,0.5-1%抗氧化剂,0.5-1%催干剂,填料补足100%;
所述的聚苯乙烯泡沫塑料胶液由以下重量百分比的原料组成:10-30%废聚苯乙烯泡沫塑料,0.1-0.5%异氰酸酯交联剂,2-4%邻苯二甲酸二辛酯,有机溶剂补足100%;所述的有机溶剂为乙酸乙酯、聚氨酯稀释剂和丙酮;
所述的酚醛调和漆料由以下重量百分比的原料组成:5-6%松香改性酚醛树脂、5-6%石灰松香、20-30%桐油、10-12%亚桐聚合油、0.2-1%醋酸铅、200号溶剂汽油补足100%。
2.根据权利要求1所述的利用废聚苯乙烯泡沫塑料制备的防水补漏胶,其特征在于,所述的聚苯乙烯泡沫塑料胶液中的有机溶剂,乙酸乙酯、聚氨酯稀释剂和丙酮的质量比为1.2:1:1。
3.根据权利要求1或2所述的利用废聚苯乙烯泡沫塑料制备的防水补漏胶,其特征在于,所述的抗氧化剂为抗氧化剂330或抗氧化剂2246,消泡剂为磷酸三丁酯,填料为滑石粉或膨润土,催干剂为环烷酸钴和环烷酸锰,环烷酸钴和环烷酸锰的质量比为1:1。