CN103772958A - 一种水性聚氨酯沥青材料 - Google Patents
一种水性聚氨酯沥青材料 Download PDFInfo
- Publication number
- CN103772958A CN103772958A CN201410023428.8A CN201410023428A CN103772958A CN 103772958 A CN103772958 A CN 103772958A CN 201410023428 A CN201410023428 A CN 201410023428A CN 103772958 A CN103772958 A CN 103772958A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- waterborne polyurethane
- asphalt material
- bituminous material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种水性聚氨酯沥青材料，其组成成份以质量份数表示法为：沥青为80-90份；环氧树脂为20-25份；聚氨酯预聚体90-100份；丙烯酸酯20-30份；甲苯胺红10-15份;碳酸氢钠12-15份；苯丙乳液8-10份；咪唑1.5-2.5份；滑石粉15-20份;重质碳酸钙为5-10份；高岭土5-10份；苯酚5-8份；二乙烯三胺3-5份；产品剪切强度1-2MPa，抗压强度1000-1100MPa；硬度≥0.4，水性，环保；表干1-3h，实干10-15h；产品成本低廉，使用寿命长，不易开裂，可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于沥青材料领域，尤其涉及一种水性聚氨酯沥青材料。
背景技术
石油沥青具有良好的粘结性、抗老化性和防水能力,长期以来被广泛的用作筑路、防水和密封等材料。用于防水工程有原料易得、价格低廉等的优点,是国内外防水防渗工程中应用最为广泛的材料之一；聚氨酯沥青涂料为高分子聚氨酯沥青防腐防水材料，为环氧树脂型高分子防腐防水系列，使用寿命为永久性防腐防水材料。使用寿命长，施工方便，广泛用于地下工程项目砼基础的底部、侧面、背面、基坑、地下室的防腐防水工程；水泥基建筑物，基坑、地基、地面、桥墩、铁路、港口、码头、煤矿、油田钻探的防腐防水工程，地槽、水塔、水池、冷却塔、污水池、食用清水池的防腐防水工程；新旧民用建筑物、屋顶、卫生间、天沟、阳台、外墙、地下室、仓库、隧道的防腐防水及各种桥梁灌缝和各种伸缩缝的浇灌；各种金属管道、钢筋、混凝土防腐工程，能防止钢筋锈蚀、延长混凝土的使用寿命。
聚氨酯沥青具有适用范围广、寿命长，耐候性、抗变形、拉伸强度高、延伸率大，对基层收缩和开裂变形适应性强、抗酸性、抗碱性、防腐防水性能优越、任何复杂部位都容易施工，解决了传统防腐防水材料，如涂料立面下滑、卷材空鼓，以及复杂部份操作难的难题。完全取代于传统防腐防水材料。有着比之更好的防腐、防水、绝缘性能；然而沥青高温流淌、低温冷脆开裂、耐候性不佳,大多采用现场熬制、热施工的方式，随着社会城市化、科技化、人性化的发展，设计一种剪切强度、抗压强度高，硬度高的水性聚氨酯沥青材料以满足市场需求，是非常必要的。
发明内容
解决的技术问题：
本申请针对现有水性聚氨酯沥青材料剪切强度、抗压强度低和硬度低等技术问题，提供一种水性聚氨酯沥青材料。
技术方案：
一种水性聚氨酯沥青材料，由下列原料组成，以质量份数表示法为：沥青为80-90份；环氧树脂为20-25份；聚氨酯预聚体90-100份；丙烯酸酯20-30份；甲苯胺红10-15份;碳酸氢钠12-15份；苯丙乳液8-10份；咪唑1.5-2.5份；滑石粉15-20份;重质碳酸钙为5-10份；高岭土5-10份；苯酚5-8份；二乙烯三胺3-5份。
作为本发明的一种优选技术方案：所述水性聚氨酯沥青材料，其组成成分，以质量份数表示法为：沥青为85份；环氧树脂为22.5份；聚氨酯预聚体95份；丙烯酸酯25份；甲苯胺红12.5份;碳酸氢钠13.5份；苯丙乳液90份；咪唑2份；滑石粉17.5份;重质碳酸钙为7.5份；高岭土7.5份；苯酚6.5份；二乙烯三胺4份。
作为本发明的一种优选技术方案：所述环氧树脂型号为环氧树脂E-44。
有益效果：
本发明所述一种水性聚氨酯沥青材料采用以上技术方案与现有技术相比，具有以下技术效果：1、产品剪切强度1-2MPa，抗压强度1000-1100MPa；2、硬度≥0.4，水性，环保；3、表干1-3h，实干10-15h；4、产品成本低廉，使用寿命长，不易开裂，可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种水性聚氨酯沥青材料，其组成成份以质量份数表示法为：沥青为80份；环氧树脂E-44为20份；聚氨酯预聚体90份；丙烯酸酯20份；甲苯胺红10份;碳酸氢钠12份；苯丙乳液8份；咪唑1.5份；滑石粉15份;重质碳酸钙为5份；高岭土5份；苯酚5份；二乙烯三胺3份。将沥青在反应釜中加热至180℃后，加入其余组分，边加热边搅拌，搅拌30min后，冷却过滤即得成品。
产品剪切强度1MPa，抗压强度1000MPa；硬度0.4，表干3h，实干15h。
实施例2:
一种水性聚氨酯沥青材料，其组成成份以质量份数表示法为：沥青为90份；环氧树脂E-44为25份；聚氨酯预聚体100份；丙烯酸酯30份；甲苯胺红15份;碳酸氢钠15份；苯丙乳液10份；咪唑2.5份；滑石粉20份;重质碳酸钙为10份；高岭土10份；苯酚8份；二乙烯三胺5份。将沥青在反应釜中加热至180℃后，加入其余组分，边加热边搅拌，搅拌30min后，冷却过滤即得成品。
产品剪切强度1.5MPa，抗压强度1050MPa；硬度0.45，表干2h，实干12h。
实施例3:
一种水性聚氨酯沥青材料，其组成成份以质量份数表示法为：沥青为85份；环氧树脂E-44为22.5份；聚氨酯预聚体95份；丙烯酸酯25份；甲苯胺红12.5份;碳酸氢钠13.5份；苯丙乳液90份；咪唑2份；滑石粉17.5份;重质碳酸钙为7.5份；高岭土7.5份；苯酚6.5份；二乙烯三胺4份。将沥青在反应釜中加热至180℃后，加入其余组分，边加热边搅拌，搅拌30min后，冷却过滤即得成品。
产品剪切强度2MPa，抗压强度1100MPa；硬度0.5，表干1h，实干10h。
以上实施例中的所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。
Claims (3)
1.一种水性聚氨酯沥青材料，其特征在于：其组成成份以质量份数表示法为：沥青为80-90份；环氧树脂为20-25份；聚氨酯预聚体90-100份；丙烯酸酯20-30份；甲苯胺红10-15份;碳酸氢钠12-15份；苯丙乳液8-10份；咪唑1.5-2.5份；滑石粉15-20份;重质碳酸钙为5-10份；高岭土5-10份；苯酚5-8份；二乙烯三胺3-5份。
2.根据权利要求1所述的一种水性聚氨酯沥青材料，其特征在于：其组成成份以质量份数表示法为：沥青为85份；环氧树脂为22.5份；聚氨酯预聚体95份；丙烯酸酯25份；甲苯胺红12.5份;碳酸氢钠13.5份；苯丙乳液90份；咪唑2份；滑石粉17.5份;重质碳酸钙为7.5份；高岭土7.5份；苯酚6.5份；二乙烯三胺4份。
3.根据权利要求1所述的一种水性聚氨酯沥青材料，其特征在于：所述环氧树脂型号为环氧树脂E-44。