CN103952075A - 一种建筑用疏水防水涂料 - Google Patents

一种建筑用疏水防水涂料 Download PDF

Info

Publication number
CN103952075A
CN103952075A CN201410214524.0A CN201410214524A CN103952075A CN 103952075 A CN103952075 A CN 103952075A CN 201410214524 A CN201410214524 A CN 201410214524A CN 103952075 A CN103952075 A CN 103952075A
Authority
CN
China
Prior art keywords
parts
sodium
building
formula ratio
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410214524.0A
Other languages
English (en)
Inventor
陆玉珍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410214524.0A priority Critical patent/CN103952075A/zh
Publication of CN103952075A publication Critical patent/CN103952075A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种建筑用疏水防水涂料，其包括如下重量份数的组分：聚丙烯酸钠0.2～1份、十二水硫酸铝钾5～10份、甲基三氯硅烷10～15份、甲基硅酸钠10～15份、乙醇5～8份、氢氧化钠8～15份和水60～80份。通过本发明的配方制备的建筑用疏水防水涂料具有成本低廉、具有疏水防水特性、渗透性强、操作简单的优点，各个组分和用量的相互配合使其各自的作用充分的发挥。

Description

一种建筑用疏水防水涂料
技术领域
本发明属于建筑材料技术领域，具体地涉及一种建筑用疏水防水涂料。
背景技术
三毡四油和防水卷材是目前广泛使用的建筑防水材料，但三毡四油施工复杂，且对环境造成严重污染，成本高，而卷材品种虽然繁多，但限于其属于覆盖式防水，对于一些复杂部位或边角部位不易施工，且不耐老化，渗透性差。
发明内容
发明目的：为解决现有技术中存在的技术问题，本发明提出一种成本低廉、具有疏水防水特性、渗透性强、操作简单的建筑用疏水防水涂料。
技术内容：为实现上述技术目的，本发明提出一种建筑用疏水防水涂料，其包括如下重量份数的组分：聚丙烯酸钠0.2～1份、十二水硫酸铝钾5～10份、甲基三氯硅烷10～15份、甲基硅酸钠10～15份、乙醇5～8份、氢氧化钠8～15份和水60～80份。
优选地，所述建筑用疏水防水涂料包括如下重量份数的组分：聚丙烯酸钠0.6份、十二水硫酸铝钾8份、甲基三氯硅烷12份、甲基硅酸钠13份、乙醇6份、强氧化钠10份和水70份。
本发明还提出了上述建筑用疏水防水涂料的制备方法，包括如下步骤：
(1)将配方量的甲基三氯硅烷、聚丙烯酸钠、十二水硫酸铝钾和甲基硅酸钠加入到1/2配方量的水中，搅拌10～15分钟，得到溶液A；
(2)将配方量的氢氧化钠和1/2配方量的水搅拌混合均匀，加热至50～60℃，向其中加入步骤(1)得到的溶液A，继续加热并搅拌均匀，持续反应10～20min，停止加热，冷却至室温时即得。
其中，步骤(1)中的搅拌速度为800～1000r/min。
步骤(2)中的加热温度为85～90℃。
有益效果：与现有技术相比，通过本发明的配方制备的建筑用疏水防水涂料具有成本低廉、具有疏水防水特性、渗透性强、操作简单的优点，各个组分和用量的相互配合使其各自的作用充分的发挥。
具体实施方式
实施例1
一种建筑用疏水防水涂料，其包括如下重量份数的组分：聚丙烯酸钠0.6份、十二水硫酸铝钾8份、甲基三氯硅烷12份、甲基硅酸钠13份、乙醇6份、强氧化钠10份和水70份。
其制备方法包括如下步骤：
(1)将配方量的甲基三氯硅烷、聚丙烯酸钠、十二水硫酸铝钾和甲基硅酸钠加入到1/2配方量的水中，在900r/min下搅拌12分钟，得到溶液A；
(2)将配方量的氢氧化钠和1/2配方量的水搅拌混合均匀，加热至55℃，向其中加入步骤(1)得到的溶液A，继续加热至85℃并搅拌均匀，持续反应20min，停止加热，冷却至室温时即得。
实施例2
一种建筑用疏水防水涂料，其包括如下重量份数的组分：聚丙烯酸钠0.2份、十二水硫酸铝钾10份、甲基三氯硅烷10份、甲基硅酸钠15份、乙醇5份、氢氧化钠15份和水60份。
其制备方法包括如下步骤：
(1)将配方量的甲基三氯硅烷、聚丙烯酸钠、十二水硫酸铝钾和甲基硅酸钠加入到1/2配方量的水中，在800r/min下搅拌15分钟，得到溶液A；
(2)将配方量的氢氧化钠和1/2配方量的水搅拌混合均匀，加热至60℃，向其中加入步骤(1)得到的溶液A，继续加热至90℃并搅拌均匀，持续反应10min，停止加热，冷却至室温时即得。
实施例3
一种建筑用疏水防水涂料，其包括如下重量份数的组分：聚丙烯酸钠1份、十二水硫酸铝钾5份、甲基三氯硅烷15份、甲基硅酸钠10份、乙醇8份、氢氧化钠8份和水80份。
其制备方法包括如下步骤：
(1)将配方量的甲基三氯硅烷、聚丙烯酸钠、十二水硫酸铝钾和甲基硅酸钠加入到1/2配方量的水中，在000r/min下搅拌10分钟，得到溶液A；
(2)将配方量的氢氧化钠和1/2配方量的水搅拌混合均匀，加热至50℃，向其中加入步骤(1)得到的溶液A，继续加热至85℃并搅拌均匀，持续反应20min，停止加热，冷却至室温时即得。
实施例4
一种建筑用疏水防水涂料，其包括如下重量份数的组分：聚丙烯酸钠0.8份、十二水硫酸铝钾6份、甲基三氯硅烷14份、甲基硅酸钠12份、乙醇7份、氢氧化钠10份和水75份。
其制备方法包括如下步骤：
(1)将配方量的甲基三氯硅烷、聚丙烯酸钠、十二水硫酸铝钾和甲基硅酸钠加入到1/2配方量的水中，在1000r/min下搅拌15分钟，得到溶液A；
(2)将配方量的氢氧化钠和1/2配方量的水搅拌混合均匀，加热至50℃，向其中加入步骤(1)得到的溶液A，继续加热至85℃并搅拌均匀，持续反应20min，停止加热，冷却至室温时即得。
实施例5
一种建筑用疏水防水涂料，其包括如下重量份数的组分：聚丙烯酸钠0.6份、十二水硫酸铝钾7份、甲基三氯硅烷12份、甲基硅酸钠11份、乙醇6份、氢氧化钠12份和水65份。
其制备方法包括如下步骤：
(1)将配方量的甲基三氯硅烷、聚丙烯酸钠、十二水硫酸铝钾和甲基硅酸钠加入到1/2配方量的水中，在800r/min下搅拌15分钟，得到溶液A；
(2)将配方量的氢氧化钠和1/2配方量的水搅拌混合均匀，加热至60℃，向其中加入步骤(1)得到的溶液A，继续加热至90℃并搅拌均匀，持续反应16min，停止加热，冷却至室温时即得。
本发明制备的建筑用疏水防水涂料具有成本低廉、具有疏水防水特性、渗透性强、操作简单的优点，各个组分和用量的相互配合使其各自的作用充分的发挥。

Claims (5)

1.一种建筑用疏水防水涂料，其特征在于，其包括如下重量份数的组分：聚丙烯酸钠0.2～1份、十二水硫酸铝钾5～10份、甲基三氯硅烷10～15份、甲基硅酸钠10～15份、乙醇5～8份、氢氧化钠8～15份和水60～80份。
2.根据权利要求1所述的建筑用疏水防水涂料，其特征在于，其包括如下重量份数的组分：聚丙烯酸钠0.6份、十二水硫酸铝钾8份、甲基三氯硅烷12份、甲基硅酸钠13份、乙醇6份、强氧化钠10份和水70份。
3.权利要求1所述的建筑用疏水防水涂料的制备方法，其特征在于，包括如下步骤：
(1)将配方量的甲基三氯硅烷、聚丙烯酸钠、十二水硫酸铝钾和甲基硅酸钠加入到1/2配方量的水中，搅拌10～15分钟，得到溶液A；
(2)将配方量的氢氧化钠和1/2配方量的水搅拌混合均匀，加热至50～60℃，向其中加入步骤(1)得到的溶液A，继续加热并搅拌均匀，持续反应10～20min，停止加热，冷却至室温时即得。
4.根据权利要求3所述的制备方法，其特征在于，步骤(1)中的搅拌速度为800～1000r/min。
5.根据权利要求3所述的制备方法，其特征在于，步骤(2)中的加热温度为85～90℃。
CN201410214524.0A 2014-05-20 2014-05-20 一种建筑用疏水防水涂料 Pending CN103952075A (zh)