CN103951987B - 一种防水硬质沥青材料及其制备方法 - Google Patents

一种防水硬质沥青材料及其制备方法 Download PDF

Info

Publication number
CN103951987B
CN103951987B CN201410164519.3A CN201410164519A CN103951987B CN 103951987 B CN103951987 B CN 103951987B CN 201410164519 A CN201410164519 A CN 201410164519A CN 103951987 B CN103951987 B CN 103951987B
Authority
CN
China
Prior art keywords
parts
preparation
hard pitch
reactor
waterproof hard
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410164519.3A
Other languages
English (en)
Other versions
CN103951987A (zh
Inventor
戴晓宸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xinnuo Lixing (Huanghua City) Group Co.,Ltd.
Original Assignee
SUZHOU YUFAN NEW MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU YUFAN NEW MATERIAL TECHNOLOGY Co Ltd filed Critical SUZHOU YUFAN NEW MATERIAL TECHNOLOGY Co Ltd
Priority to CN201410164519.3A priority Critical patent/CN103951987B/zh
Publication of CN103951987A publication Critical patent/CN103951987A/zh
Application granted granted Critical
Publication of CN103951987B publication Critical patent/CN103951987B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种防水硬质沥青材料及其制备方法，防水硬质沥青材料由以下成分按照重量比组成：煤焦沥青为26～33份、脲醛树脂为22～29份、1-己烯为12～17份、甲磺酸甲酯为6～9份、硫酸二甲酯为7～11份、异硫氰酸烯丙酯为5～8份、丙酮为6～8份。防水硬质沥青材料的制备方法步骤包括：加热、溶解、搅拌、反应，制备得到的沥青材料不仅具有优良的防水性能，还具有良好的硬度。可以作为沥青材料广泛的用于防水材料等应用中。

Description

一种防水硬质沥青材料及其制备方法
技术领域
本发明涉及一种沥青材料及其制备方法，特别是涉及一种防水硬质沥青材料及其制备方法。
背景技术
沥青材料具有较为广阔的使用空间，如在地面、房屋、涂料等中具有较为深入的应用。沥青材料主要分为煤焦沥青和和石油沥青。沥青材料在应用时，需要具被较为良好的防水特性。防水性能较差，在沥青材料长时间使用后，会有渗水现象产生。渗水后沥青材料的性能也会发生变化，不仅如此，在一些地面及有可能涉及到压力的领域，如果沥青材料的硬度较低，沥青材料会容易发生形变，影响着沥青材料的长期使用。公开号为104151847A的发明专利公开了一种防水沥青材料，其具有一定的防水性能，但是，如果能够更加提高其防水性能，可更好的保证沥青材料的防水稳定性。
常规的沥青材料通常其硬度较低，在受到高温后就会发生较大的形变，这些都降低了沥青材料的相关性能，影响了沥青材料的大规模应用。
发明内容
要解决的技术问题：普通的沥青材料防水性能较差、硬度较低，限制了沥青材料的使用的问题。
技术方案：本发明公开了一种防水硬质沥青材料及其制备方法，防水硬质沥青材料由以下成分按照重量比组成：煤焦沥青为26～33份、脲醛树脂为22～29份、1-己烯为12～17份、甲磺酸甲酯为6～9份、硫酸二甲酯为7～11份、异硫氰酸烯丙酯为5～8份、丙酮为6～8份。
一种防水硬质沥青材料的制备方法，制备方法包括如下步骤：(1)打开恒温反应釜，反应釜温度为145℃，向反应釜中加入煤焦沥青为26～33份、脲醛树脂为22～29份、1-己烯为12～17份、进行机械搅拌，搅拌转速为120～160rpm，搅拌时间为30min；(2)再向反应釜中加入甲磺酸甲酯为6～9份、硫酸二甲酯为7～11份、异硫氰酸烯丙酯为5～8份，再次进行机械搅拌，搅拌转速为100～120rpm，搅拌时间为20min；(3)最后再向反应釜中加入丙酮为6～8份，进行搅拌，搅拌转速为110～120rpm，搅拌时间为1h；(4)保持反应釜温度不变，保温3h，制备得到防水硬质沥青材料。
一种防水硬质沥青材料的制备方法，向反应釜中加入的煤焦沥青优选为33份。
一种防水硬质沥青材料的制备方法，向反应釜中加入的脲醛树脂优选为22份。
一种防水硬质沥青材料的制备方法，向反应釜中加入的异硫氰酸烯丙酯优选为8份。
有益效果：本发明制备得到的沥青材料具有良好的防水功能，将沥青材料加热后刮涂在水泥表面后，将沥青材料室温下放置在水中，放置30天至60天后，沥青材料没有渗透现象产生，具有良好的防水功能。此外，本发明的沥青材料的铅笔硬度在5H至6H，具有较好的硬度，可以抵抗一定的外在压强。
具体实施方式
实施例1
一种防水硬质沥青材料的制备方法，制备方法包括如下步骤：(1)打开恒温反应釜，反应釜温度为145℃，向反应釜中加入煤焦沥青为26kg、脲醛树脂为29kg、1-己烯为12kg、进行机械搅拌，搅拌转速为120rpm，搅拌时间为30min；(2)再向反应釜中加入甲磺酸甲酯为6kg、硫酸二甲酯为11kg、异硫氰酸烯丙酯为5kg，再次进行机械搅拌，搅拌转速为120rpm，搅拌时间为20min；(3)最后再向反应釜中加入丙酮为7kg，进行搅拌，搅拌转速为110rpm，搅拌时间为1h；(4)保持反应釜温度不变，保温3h，制备得到防水硬质沥青材料。
实施例2
一种防水硬质沥青材料的制备方法，制备方法包括如下步骤：(1)打开恒温反应釜，反应釜温度为145℃，向反应釜中加入煤焦沥青为29kg、脲醛树脂为24kg、1-己烯为15kg、进行机械搅拌，搅拌转速为140rpm，搅拌时间为30min；(2)再向反应釜中加入甲磺酸甲酯为7kg、硫酸二甲酯为9kg、异硫氰酸烯丙酯为6kg，再次进行机械搅拌，搅拌转速为100rpm，搅拌时间为20min；(3)最后再向反应釜中加入丙酮为8kg，进行搅拌，搅拌转速为120rpm，搅拌时间为1h；(4)保持反应釜温度不变，保温3h，制备得到防水硬质沥青材料。
实施例3
一种防水硬质沥青材料的制备方法，制备方法包括如下步骤：(1)打开恒温反应釜，反应釜温度为145℃，向反应釜中加入煤焦沥青为33kg、脲醛树脂为22kg、1-己烯为17kg、进行机械搅拌，搅拌转速为160rpm，搅拌时间为30min；(2)再向反应釜中加入甲磺酸甲酯为9kg、硫酸二甲酯为7kg、异硫氰酸烯丙酯为8kg，再次进行机械搅拌，搅拌转速为110rpm，搅拌时间为20min；(3)最后再向反应釜中加入丙酮为6kg，进行搅拌，搅拌转速为110rpm，搅拌时间为1h；(4)保持反应釜温度不变，保温3h，制备得到防水硬质沥青材料。
将实施例1、实施例2、实施例3制备的沥青材料加热后刮涂在水泥表面后，将沥青材料室温下放置在水中，分别放置30天、45天、60天后，观察沥青材料是否有渗透现象产生。另外测定了实施例1、实施例2、实施例3的沥青材料的铅笔硬度。结果如下。
由于本发明的沥青材料具备了较高的铅笔硬度和防水性能，可以较为广泛的应用于路面、房屋等防水材料中，提高材料的硬度和防水性能。

Claims (5)

1.一种防水硬质沥青材料，其特征在于防水硬质沥青材料由以下成分按照重量比组成：煤焦沥青为26～33份、脲醛树脂为22～29份、1-己烯为12～17份、甲磺酸甲酯为6～9份、硫酸二甲酯为7～11份、异硫氰酸烯丙酯为5～8份、丙酮为6～8份。
2.一种防水硬质沥青材料的制备方法，其特征在于制备方法包括如下步骤：(1)打开恒温反应釜，反应釜温度为145℃，向反应釜中加入煤焦沥青为26～33份、脲醛树脂为22～29份、1-己烯为12～17份、进行机械搅拌，搅拌转速为120～160rpm，搅拌时间为30min；(2)再向反应釜中加入甲磺酸甲酯为6～9份、硫酸二甲酯为7～11份、异硫氰酸烯丙酯为5～8份，再次进行机械搅拌，搅拌转速为100～120rpm，搅拌时间为20min；(3)最后再向反应釜中加入丙酮为6～8份，进行搅拌，搅拌转速为110～120rpm，搅拌时间为1h；(4)保持反应釜温度不变，保温3h，制备得到防水硬质沥青材料。
3.根据权利要求2所述的一种防水硬质沥青材料的制备方法，其特征在于向反应釜中加入的煤焦沥青为33份。
4.根据权利要求2所述的一种防水硬质沥青材料的制备方法，其特征在于向反应釜中加入的脲醛树脂为22份。
5.根据权利要求2所述的一种防水硬质沥青材料的制备方法，其特征在于向反应釜中加入的异硫氰酸烯丙酯为8份。
CN201410164519.3A 2014-04-23 2014-04-23 一种防水硬质沥青材料及其制备方法 Active CN103951987B (zh)