CN103938492B - 一种结实耐用的机油滤清器滤纸及其制备方法 - Google Patents

一种结实耐用的机油滤清器滤纸及其制备方法 Download PDF

Info

Publication number
CN103938492B
CN103938492B CN201410099717.6A CN201410099717A CN103938492B CN 103938492 B CN103938492 B CN 103938492B CN 201410099717 A CN201410099717 A CN 201410099717A CN 103938492 B CN103938492 B CN 103938492B
Authority
CN
China
Prior art keywords
paper
auxiliary agent
minute
filter paper
filter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410099717.6A
Other languages
English (en)
Other versions
CN103938492A (zh
Inventor
薛卉慧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu City Music filter Co.
Original Assignee
Bengbu Feng Chi Cleaner Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Feng Chi Cleaner Co Ltd filed Critical Bengbu Feng Chi Cleaner Co Ltd
Priority to CN201410099717.6A priority Critical patent/CN103938492B/zh
Publication of CN103938492A publication Critical patent/CN103938492A/zh
Application granted granted Critical
Publication of CN103938492B publication Critical patent/CN103938492B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种结实耐用的机油滤清器滤纸，其特征在于，由下列重量份的原料制备制成：针叶木浆55-58、芦苇浆39-44、莫来石3-4、氧化锆2-3、活性氧化铝2-3、竹炭1-2、氨丙基三乙氧基硅烷0.6-0.9、氯化钙0.6-0.8、石蜡乳液6-8、聚乙烯醇3-5、脲醛树脂3-5、磷酸三丁酯0.4-0.6、助剂1-2；本发明添加氧化锆、活性氧化铝等增加吸附效果，添加助剂，安全环保，具有良好的耐水性以及耐油性；通过陶瓷材料与滤纸的有机结合，结实耐用，滤过效果好，吸附效果好。

Description

一种结实耐用的机油滤清器滤纸及其制备方法
技术领域
本发明涉及汽车滤清器领域，特别是一种结实耐用的机油滤清器滤纸及其制备方法。
背景技术
机油滤清器是滤清器的一种，能够去除机油中的灰尘、金属颗粒、碳沉淀物和煤烟颗粒等杂质，保护发动机。机油滤纸是机油滤清器中的关键组成部件，决定着机油过滤器的性能，机油滤纸他通常包括用普通木浆为主要成分制成的一种纸质过滤层，由于普通木浆纤维较细、容灰量低、寿命短等缺点，而且纸制的机油滤纸还普遍存在着耐水性和耐油性差，不耐高温不环保等特性，当燃油长时间浸泡容易变形，进而影响过滤效果。
发明内容
本发明的目的是提供一种结实耐用的机油滤清器滤纸及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种结实耐用的机油滤清器滤纸，由下列重量份的原料制备制成：针叶木浆55-58、芦苇浆39-44、莫来石3-4、氧化锆2-3、活性氧化铝2-3、竹炭1-2、氨丙基三乙氧基硅烷0.6-0.9、氯化钙0.6-0.8、石蜡乳液6-8、聚乙烯醇3-5、脲醛树脂3-5、磷酸三丁酯0.4-0.6、助剂1-2；
所述助剂由以下重量份的原料制成：高岭土7-9、粘土5-8、锆英粉4-6、氧化钡2-3、氢氧化铝2-3、尼龙1214-16、柠檬酸三乙酯2-3、乙酸1-2；制备方法是首先将高岭土、粘土、锆英粉、氧化钡、氢氧化铝放入球磨机中，磨成100-140目的粉末，混合均匀；然后将尼龙12加热至软化，加入其余剩余成分搅拌15-25分钟后加入混合粉末，送入双螺杆挤出机造粒，得到颗粒料；最后将颗粒料放入磨粉机中粉碎，即得。
本发明所述一种结实耐用的机油滤清器滤纸，由以下具体步骤制成：
（1）将莫来石、氧化锆、活性氧化铝、竹炭混合均匀，研磨成50-100目的粉末，加入氨丙基三乙氧基硅烷，以850-950转/分的速度，搅拌25-30分钟，然后在110-120℃烘干1.5-2.5小时待用；
（2）将针叶木浆、芦苇浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在5.9-6.5％，制得浆料；
（3）将步骤（1）的混合料加入浆料中，加入磷酸三丁酯，加热至65-75℃，搅拌均匀，加适量的水调浆至固含量为2.4-3.5%，调好的浆料经成型网成型后，在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水；
（4）将其余剩余成分混合均匀，用水稀释，然后加热，温度控制在60-70℃，熬制50-60分钟，保温25-30分钟，升温至70-75℃，搅拌均匀制成浸渍乳液；（5）用涂布器使步骤（3）脱水后的纸均匀浸渍乳液，然后将浸渍好的纸电热鼓风干燥箱内烘干3-5min，最后在上光机上干燥7-10min，取出后即得。
本发明的有益效果是：本发明添加氧化锆、活性氧化铝等增加吸附效果，添加助剂，安全环保，具有良好的耐水性以及耐油性；通过陶瓷材料与滤纸的有机结合，结实耐用，滤过效果好，吸附效果好。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种结实耐用的机油滤清器滤纸，由下列重量份（公斤）的原料制备制成：针叶木浆55、芦苇浆39、莫来石3、氧化锆2、活性氧化铝2、竹炭1、氨丙基三乙氧基硅烷0.6、氯化钙0.6、石蜡乳液6、聚乙烯醇3、脲醛树脂3、磷酸三丁酯0.4、助剂1；
所述助剂由以下重量份（公斤）的原料制成：高岭土7、粘土5、锆英粉4、氧化钡2、氢氧化铝2、尼龙1214、柠檬酸三乙酯2、乙酸1；制备方法是首先将高岭土、粘土、锆英粉、氧化钡、氢氧化铝放入球磨机中，磨成100-140目的粉末，混合均匀；然后将尼龙12加热至软化，加入其余剩余成分搅拌15-25分钟后加入混合粉末，送入双螺杆挤出机造粒，得到颗粒料；最后将颗粒料放入磨粉机中粉碎，即得。
本发明所述一种结实耐用的机油滤清器滤纸，由以下具体步骤制成：
（1）将莫来石、氧化锆、活性氧化铝、竹炭混合均匀，研磨成50-100目的粉末，加入氨丙基三乙氧基硅烷，以850-950转/分的速度，搅拌25-30分钟，然后在110-120℃烘干1.5-2.5小时待用；
（2）将针叶木浆、芦苇浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在5.9-6.5％，制得浆料；
（3）将步骤（1）的混合料加入浆料中，加入磷酸三丁酯，加热至65-75℃，搅拌均匀，加适量的水调浆至固含量为2.4-3.5%，调好的浆料经成型网成型后，在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水；
（4）将其余剩余成分混合均匀，用水稀释，然后加热，温度控制在60-70℃，熬制50-60分钟，保温25-30分钟，升温至70-75℃，搅拌均匀制成浸渍乳液；（5）用涂布器使步骤（3）脱水后的纸均匀浸渍乳液，反复多次，至浸渍乳液用尽，然后将浸渍好的纸电热鼓风干燥箱内烘干3-5min，最后在上光机上干燥7-10min，取出后即得。
经检测，本发明制得的滤纸的耐破度356KPa，透气量85-88L/m2·s之间，最大孔径为75μm，平均孔径为55μm，过滤效率94.2%。

Claims (1)

1.一种结实耐用的机油滤清器滤纸，其特征在于，由下列重量份的原料制备制成：针叶木浆55-58、芦苇浆39-44、莫来石3-4、氧化锆2-3、活性氧化铝2-3、竹炭1-2、氨丙基三乙氧基硅烷0.6-0.9、氯化钙0.6-0.8、石蜡乳液6-8、聚乙烯醇3-5、脲醛树脂3-5、磷酸三丁酯0.4-0.6、助剂1-2；所述助剂由以下重量份的原料制成：高岭土7-9、粘土5-8、锆英粉4-6、氧化钡2-3、氢氧化铝2-3、尼龙1214-16、柠檬酸三乙酯2-3、乙酸1-2；所述助剂的制备方法是首先将高岭土、粘土、锆英粉、氧化钡、氢氧化铝放入球磨机中，磨成100-140目的粉末，混合均匀；然后将尼龙12加热至软化，加入其余剩余成分搅拌15-25分钟后加入混合粉末，送入双螺杆挤出机造粒，得到颗粒料；最后将颗粒料放入磨粉机中粉碎，即得；
所述的结实耐用的机油滤清器滤纸，由以下具体步骤制成：
（1）将莫来石、氧化锆、活性氧化铝、竹炭混合均匀，研磨成50-100目的粉末，加入氨丙基三乙氧基硅烷，以850-950转/分的速度，搅拌25-30分钟，然后在110-120℃烘干1.5-2.5小时待用；
（2）将针叶木浆、芦苇浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在5.9-6.5％，制得浆料；
（3）将步骤（1）的混合料加入浆料中，加入磷酸三丁酯，加热至65-75℃，搅拌均匀，加适量的水调浆至固含量为2.4-3.5%，调好的浆料经成型网成型后，在0.05-0.08MPa的真空条件下对成型后的湿纸进行抽吸脱水；
（4）将其余剩余成分混合均匀，用水稀释，然后加热，温度控制在60-70℃，熬制50-60分钟，保温25-30分钟，升温至70-75℃，搅拌均匀制成浸渍乳液；
（5）用涂布器使步骤（3）脱水后的纸均匀浸渍乳液，然后将浸渍好的纸电热鼓风干燥箱内烘干3-5min，最后在上光机上干燥7-10min，取出后即得。
CN201410099717.6A 2014-03-18 2014-03-18 一种结实耐用的机油滤清器滤纸及其制备方法 Expired - Fee Related CN103938492B (zh)