CN103993514A - 一种安全环保强度大的燃油滤清器复合滤纸及其制备方法 - Google Patents

一种安全环保强度大的燃油滤清器复合滤纸及其制备方法 Download PDF

Info

Publication number
CN103993514A
CN103993514A CN201410169952.6A CN201410169952A CN103993514A CN 103993514 A CN103993514 A CN 103993514A CN 201410169952 A CN201410169952 A CN 201410169952A CN 103993514 A CN103993514 A CN 103993514A
Authority
CN
China
Prior art keywords
parts
water
filter paper
slurry
auxiliary agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410169952.6A
Other languages
English (en)
Inventor
陈登宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu Phoenix International Co Ltd
Original Assignee
Bengbu Phoenix International Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Phoenix International Co Ltd filed Critical Bengbu Phoenix International Co Ltd
Priority to CN201410169952.6A priority Critical patent/CN103993514A/zh
Publication of CN103993514A publication Critical patent/CN103993514A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种安全环保强度大的燃油滤清器复合滤纸，其特征在于，由下列重量份的原料制备制成：玉米杆浆49-52、高粱杆浆43-47、稻壳1-2、大豆卵磷脂0.5-1、海绵铁2-3、天然粘土3-4、棕刚玉2-3、动物胶0.2-0.3、硅溶胶0.5-0.8、聚氧乙烯脂肪醇醚0.4-0.6、阿拉伯胶0.4-0.6、水溶性酚醛树脂胶黏剂9-11、双醛淀粉2-3、助剂1-2、水适量；本发明使用的浸渍液无混分溶剂，安全环保，具有很强的粘结性和成膜性，浸渍后能够增强滤纸的干湿强度，韧性，提高了滤清器滤清效率；添加助剂，安全环保，在滤纸表面形成的微小的孔隙，增加了吸附性，具有抗水性。

Description

一种安全环保强度大的燃油滤清器复合滤纸及其制备方法
技术领域
本发明涉及汽车滤清器领域，特别是一种安全环保强度大的燃油滤清器复合滤纸及其制备方法。
背景技术
汽车的滤清器对汽车行驶的速度、发动机的损耗、节能和环境保护非常重要。因此，长期以来人们提出了很多关于改进汽车空气、燃油滤清器的技术和产品，主要包括增氧燃烧技术、离子燃烧技术、射线活化技术等几种类型。作为汽车三滤纸之一的燃油滤清器滤纸，主要作用是过滤燃油，清洁燃油中的杂质，防止它们进入喷射阀和冷启动器，减少机械磨损，确保发动机稳定运行，提高可靠性。为了保证内燃机安全有效的进行以及力行节能环保，与之配套的滤材必须具备优良的力学性能以及一定的过滤性能以及节能环保的效果。
发明内容
本发明的目的是提供一种安全环保强度大的燃油滤清器复合滤纸及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种安全环保强度大的燃油滤清器复合滤纸，由下列重量份的原料制备制成：玉米杆浆49-52、高粱杆浆43-47、稻壳1-2、大豆卵磷脂0.5-1、海绵铁2-3、天然粘土3-4、棕刚玉2-3、动物胶0.2-0.3、硅溶胶0.5-0.8、聚氧乙烯脂肪醇醚0.4-0.6、阿拉伯胶0.4-0.6、水溶性酚醛树脂胶黏剂9-11、双醛淀粉2-3、助剂1-2、水适量；
所述助剂由以下重量份的原料制成：女贞子2-3、蓖麻子壳1-2、羧甲基纤维素1-2、锆英粉3-5、纳米二氧化钛2-3、黄原胶3-5、硅溶胶2-3、海藻酸钠1-2、水50-60；制备方法是首先将女贞子与蓖麻子壳一起放入粉碎机中粉碎成120-140目的混合粉末待用；然后将黄原胶、硅溶胶、海藻酸钠混合，加入适量的水搅拌均匀，加热至30-35℃继续搅拌10-15分钟后加入羧甲基纤维素、锆英粉、纳米二氧化钛，继续保温24-29分钟，最后加入混合粉末搅拌均匀，形成悬浊液即可。
本发明所述一种安全环保强度大的燃油滤清器复合滤纸，由以下具体步骤制成：
（1）将稻壳、天然粘土、海绵铁、棕刚玉混合均匀，研磨成50-100目的粉末，加入双醛淀粉7，以850-950转/分的速度，搅拌25-30分钟，然后在50-60℃烘干1.5-2.5小时待用；
（2）将玉米杆浆、高粱杆浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在5.5-6.2％，制得浆料；
（3）将步骤（1）的混合料加入浆料中，加入聚氧乙烯脂肪醇醚、动物胶，加热至65-75℃，搅拌均匀，加适量的水调浆至固含量为2.0-3.0%，调好的浆料经成型网成型后，在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水；
（4）将除助剂以外的其余剩余成分混合搅拌均匀，加入2-3倍量的水，然后加热，温度控制在60-70℃，熬制50-60分钟，保温25-30分钟，升温至70-75℃，搅拌均匀制成浸渍液放入浸渍槽中；
（5）将步骤（3）脱水后的原纸以3-3.5m/s的速度通过浸渍槽，使浸渍液均匀涂布在原纸上，电热鼓风干燥箱内烘干4-5min，再将助剂涂布在烘干的原纸上，最后光机上干燥6-10min，取出后即得。
本发明的有益效果是：本发明使用的浸渍液无混分溶剂，安全环保，具有很强的粘结性和成膜性，浸渍后能够增强滤纸的干湿强度，韧性，提高了滤清器滤清效率；添加助剂，安全环保，在滤纸表面形成的微小的孔隙，增加了吸附性，具有抗水性。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种安全环保强度大的燃油滤清器复合滤纸，由下列重量份（公斤）的原料制备制成：玉米杆浆49、高粱杆浆43、稻壳1、大豆卵磷脂0.5、海绵铁2、天然粘土3、棕刚玉2、动物胶0.2、硅溶胶0.5、聚氧乙烯脂肪醇醚0.4、阿拉伯胶0.4、水溶性酚醛树脂胶黏剂9、双醛淀粉2、助剂1、水适量；
所述助剂由以下重量份（公斤）的原料制成：女贞子2、蓖麻子壳1、羧甲基纤维素1、锆英粉3、纳米二氧化钛2、黄原胶3、硅溶胶2、海藻酸钠1、水50；制备方法是首先将女贞子与蓖麻子壳一起放入粉碎机中粉碎成120-140目的混合粉末待用；然后将黄原胶、硅溶胶、海藻酸钠混合，加入适量的水搅拌均匀，加热至30-35℃继续搅拌10-15分钟后加入羧甲基纤维素、锆英粉、纳米二氧化钛，继续保温24-29分钟，最后加入混合粉末搅拌均匀，形成悬浊液即可。
本发明所述一种安全环保强度大的燃油滤清器复合滤纸，由以下具体步骤制成：
（1）将稻壳、天然粘土、海绵铁、棕刚玉混合均匀，研磨成50-100目的粉末，加入双醛淀粉7，以850-950转/分的速度，搅拌25-30分钟，然后在50-60℃烘干1.5-2.5小时待用；
（2）将玉米杆浆、高粱杆浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在5.5-6.2％，制得浆料；
（3）将步骤（1）的混合料加入浆料中，加入聚氧乙烯脂肪醇醚、动物胶，加热至65-75℃，搅拌均匀，加适量的水调浆至固含量为2.0-3.0%，调好的浆料经成型网成型后，在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水；
（4）将除助剂以外的其余剩余成分混合搅拌均匀，加入2-3倍量的水，然后加热，温度控制在60-70℃，熬制50-60分钟，保温25-30分钟，升温至70-75℃，搅拌均匀制成浸渍液放入浸渍槽中；
（5）将步骤（3）脱水后的原纸以3-3.5m/s的速度通过浸渍槽，使浸渍液均匀涂布在原纸上，电热鼓风干燥箱内烘干4-5min，再将助剂涂布在烘干的原纸上，最后光机上干燥6-10min，取出后即得。
经检测，本发明制得的滤纸的透气量85-90 L/m2·s之间，最大孔径为53-55μm，平均孔径为45μm。

Claims (2)

1.一种安全环保强度大的燃油滤清器复合滤纸，其特征在于，由下列重量份的原料制备制成：玉米杆浆49-52、高粱杆浆43-47、稻壳1-2、大豆卵磷脂0.5-1、海绵铁2-3、天然粘土3-4、棕刚玉2-3、动物胶0.2-0.3、硅溶胶0.5-0.8、聚氧乙烯脂肪醇醚0.4-0.6、阿拉伯胶0.4-0.6、水溶性酚醛树脂胶黏剂9-11、双醛淀粉2-3、助剂1-2、水适量；
所述助剂由以下重量份的原料制成：女贞子2-3、蓖麻子壳1-2、羧甲基纤维素1-2、锆英粉3-5、纳米二氧化钛2-3、黄原胶3-5、硅溶胶2-3、海藻酸钠1-2、水50-60；制备方法是首先将女贞子与蓖麻子壳一起放入粉碎机中粉碎成120-140目的混合粉末待用；然后将黄原胶、硅溶胶、海藻酸钠混合，加入适量的水搅拌均匀，加热至30-35℃继续搅拌10-15分钟后加入羧甲基纤维素、锆英粉、纳米二氧化钛，继续保温24-29分钟，最后加入混合粉末搅拌均匀，形成悬浊液即可。
2.根据权利要求1所述一种安全环保强度大的燃油滤清器复合滤纸，其特征在于，由以下具体步骤制成：
（1）将稻壳、天然粘土、海绵铁、棕刚玉混合均匀，研磨成50-100目的粉末，加入双醛淀粉7，以850-950转/分的速度，搅拌25-30分钟，然后在50-60℃烘干1.5-2.5小时待用；
（2）将玉米杆浆、高粱杆浆放入水力碎浆机碎解，再经打浆机，打浆浓度控制在5.5-6.2％，制得浆料；
（3）将步骤（1）的混合料加入浆料中，加入聚氧乙烯脂肪醇醚、动物胶，加热至65-75℃，搅拌均匀，加适量的水调浆至固含量为2.0-3.0%，调好的浆料经成型网成型后，在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水；
（4）将除助剂以外的其余剩余成分混合搅拌均匀，加入2-3倍量的水，然后加热，温度控制在60-70℃，熬制50-60分钟，保温25-30分钟，升温至70-75℃，搅拌均匀制成浸渍液放入浸渍槽中；
（5）将步骤（3）脱水后的原纸以3-3.5m/s的速度通过浸渍槽，使浸渍液均匀涂布在原纸上，电热鼓风干燥箱内烘干4-5min，再将助剂涂布在烘干的原纸上，最后光机上干燥6-10min，取出后即得。
CN201410169952.6A 2014-04-25 2014-04-25 一种安全环保强度大的燃油滤清器复合滤纸及其制备方法 Pending CN103993514A (zh)