CN103936461A - 一种青花瓷轴料配方 - Google Patents

一种青花瓷轴料配方 Download PDF

Info

Publication number
CN103936461A
CN103936461A CN201410135284.5A CN201410135284A CN103936461A CN 103936461 A CN103936461 A CN 103936461A CN 201410135284 A CN201410135284 A CN 201410135284A CN 103936461 A CN103936461 A CN 103936461A
Authority
CN
China
Prior art keywords
parts
blue
white porcelain
white
material formula
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410135284.5A
Other languages
English (en)
Inventor
蔡胜兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Blue And White Fang Ci Industry Limited-Liability Co
Original Assignee
Anhui Blue And White Fang Ci Industry Limited-Liability Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Blue And White Fang Ci Industry Limited-Liability Co filed Critical Anhui Blue And White Fang Ci Industry Limited-Liability Co
Priority to CN201410135284.5A priority Critical patent/CN103936461A/zh
Publication of CN103936461A publication Critical patent/CN103936461A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种青花瓷轴料配方，该配方组分重量份如下：SiO2，50～73份；Al2O3，8～15份；CaO，9～20份；MgO2，12～28份；B2O3，15～28份；ZnO，1-10份；Na2O2，1～6份；Li2O3，1～6份；CuO，1～10份。本发明组方合理，生产出的青花瓷青花清晰、明亮，且使用本配方，产品烧制的时间更度，温度更低，节约了能源，提高了生产效率。

Description

一种青花瓷轴料配方
技术领域
本发明涉及一种青花瓷轴料配方。
背景技术
青花瓷（blue and white porcelain），又称白地青花瓷，常简称青花，是中国瓷器的主流品种之一，属釉下彩瓷。青花瓷是用含氧化钴的钴矿为原料，在陶瓷坯体上描绘纹饰，再罩上一层透明釉，经高温还原焰一次烧成。钴料烧成后呈蓝色，具有着色力强、发色鲜艳、烧成率高、呈色稳定的特点。汉族劳动人民制作瓷器的历史悠久，品种繁多。原始青花瓷于唐宋已见端倪，成熟的青花瓷则出现在元代景德镇的湖田窑。明代青花成为瓷器的主流。清康熙时发展到了顶峰。明清时期，还创烧了青花五彩、孔雀绿釉青花、豆青釉青花、青花红彩、黄地青花、哥釉青花等衍生品种。
发明内容
本发明目的是提供一种配方合理且生产出的青花瓷青花清晰、明亮的轴料配方。
本发明的方案如下：一种青花瓷轴料配方，该配方组分重量份如下：Si02，50 ～ 73 份；Al2O3， 8～ 15 份；Ca0，9 ～ 20 份；Mg02，12 ～ 28 份；B2O3，15 ～ 28 份；Zn0， 1-10 份；Na202 ，1～ 6 份； Li203 ，1～ 6份；CuO，1 ～ 10份。
进一步，该配方组分重量份如下：Si02，50 ～ 63 份；Al2O3，8～ 13 份；Ca0，9 ～ 15 份；Mg02，15 ～ 28 份；B2O3，15 ～ 28 份；Zn0， 1-10 份；Na202 ，1～ 5 份； Li203 ，1～ 4份；CuO，1 ～ 6份。
进一步，该配方组分重量份如下：Si02，70 份；Al2O3， 11份；Ca0，11 份；Mg02，18份；B2O3，21 份；Zn0， 6 份；Na202 ，5份； Li203 ，4份；CuO，8份。
本发明组方合理，生产出的青花瓷青花清晰、明亮，且使用本配方，产品烧制的时间更度，温度更低，节约了能源，提高了生产效率。
具体实施方式
实施例1
Si02，60 份；Al2O3，9 份；Ca0，12 份；Mg02，14 份；B2O3，21 份；Zn0， 5 份；Na202 ，3份； Li203 ，4份；CuO，5份。
实施例2
Si02， 63 份；Al2O3， 13 份；Ca0， 15 份；Mg02，15  份；B2O3，23 份；Zn0，6 份；Na202 ，3 份； Li203 ，3份；CuO，5份。
实施例3
Si02，70 份；Al2O3， 11份；Ca0，11 份；Mg02，18份；B2O3，21 份；Zn0， 6 份；Na202 ，5份； Li203 ，4份；CuO，8份。
尽管上文对本发明的具体实施方式给予了详细描述和说明，但是应该指明的是，我们可以依据本发明的构想对上述实施方式进行各种等效改变和修改，其所产生的功能作用仍未超出说明书所涵盖的精神时，均应在本发明的保护范围之内。 

Claims (3)

1.一种青花瓷轴料配方，其特征在于，该配方组分重量份如下：Si02，50 ～ 73 份；Al2O3， 8～ 15 份；Ca0，9 ～ 20 份；Mg02，12 ～ 28 份；B2O3，15 ～ 28 份；Zn0， 1-10 份；Na202 ，1～ 6 份； Li203 ，1～ 6份；CuO，1 ～ 10份。
2.根据权利要求1所述的一种青花瓷轴料配方，其特征在于，该配方组分重量份如下：Si02，50 ～ 63 份；Al2O3， 8～ 13 份；Ca0，9 ～ 15 份；Mg02，15 ～ 28 份；B2O3，15 ～ 28 份；Zn0， 1-10 份；Na202 ，1～ 5 份； Li203 ，1～ 4份；CuO，1 ～ 6份。
3.一种青花瓷轴料配方，其特征在于，该配方组分重量份如下：Si02，70 份；Al2O3， 11份；Ca0，11 份；Mg02，18份；B2O3，21 份；Zn0， 6 份；Na202 ，5份； Li203 ，4份；CuO，8份。
CN201410135284.5A 2014-04-04 2014-04-04 一种青花瓷轴料配方 Pending CN103936461A (zh)