CN103933605A - Synthetic adhesive self-adhesion elastic bandage and production method thereof - Google Patents
Synthetic adhesive self-adhesion elastic bandage and production method thereof Download PDFInfo
- Publication number
- CN103933605A CN103933605A CN201410194728.2A CN201410194728A CN103933605A CN 103933605 A CN103933605 A CN 103933605A CN 201410194728 A CN201410194728 A CN 201410194728A CN 103933605 A CN103933605 A CN 103933605A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- elastic bandage
- self
- rubber polymer
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a synthetic adhesive self-adhesion elastic bandage and a production method thereof. The synthetic adhesive self-adhesion elastic bandage takes non-woven fabric, cotton fabric or compound cotton fabric as a base material of the bandage, an adhesive is coated on the front side and the back side of the base material of the bandage, and the formula of the adhesive comprises the following ingredients in parts by weight: 60-80 parts of polyisoprene emulsion, 3-30 parts of modifier, 0.5-10 parts of softening agent, and 0.1-10 parts of antioxidant. The synthetic adhesive self-adhesion elastic bandage replaces a solvent type adhesive, used by the like products, with a chemically synthesized emulsion, does not contain an organic solvent having pollution even poison to an environment, and is non-combustible, safe to use, and easy to clean. Furthermore, the content of antigen protein in the product is less than 1PPM, and the content is extremely low, so that the allergic reaction can be effectively avoided.
Description
?
Technical field
The present invention relates to a kind of binder, relate in particular to a kind of self-adhesive elastic bandage made from rubber polymer and production method thereof.
Background technology
Self-adhesive elastic bandage is a kind of elastic bandage with self-adhesion and fine air permeability; be applicable to very much wrapping and the winding of partes corporis humani position; and fixing and dismantle very conveniently, therefore in all trades and professions such as medical wrapping, industrial operation protection, field work, movement protection, generally use.Such as medical wound wrapping and orthopaedics wrapping; In electronics industry, a large amount of manual works operate etc. in order to protect finger to be wound around self-adhesive elastic bandage.
Initial self-adhesive elastic bandage is that main component is made by Heveatex on the market, because wherein antigen protein content is higher, easy sensitization, easily go mouldy, therefore be not suitable for medical, the main product of existing medical market is self-adhesive elastic bandage made from rubber polymer, and this rubber polymer is made adhesive after adopting polyisoprene rubber with gasoline and so on dissolution with solvents more.Though the problem that this self-adhesive elastic bandage made from rubber polymer can effectively solve self-adhesive elastic bandage sensitization, go mouldy, the use because of a large amount of organic solvents in production process, obviously exists suitable pollution even to poison to environment, and safety is difficult to guarantee.
Summary of the invention
The object of this invention is to provide a kind of pollution-free, nonhazardous, safer self-adhesive elastic bandage and preparation method thereof, to solve the problem occurring in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme:
A self-adhesive elastic bandage made from rubber polymer, take non-woven fabrics, cotton or compound cotton as binder base material; The positive and negative of described binder base material scribbles one deck adhesive, and the formulation by weight of this adhesive is as follows: 60～80 parts of methods of polyisoprene emulsion, modifier 3-30 part, softening agent 0.5-10 part, antioxidant 0.1-10 part.
As further scheme of the present invention, described modifier is one or more the mixture in abietic resin, terpene resin, Petropols, polyacrylate.
As further scheme of the present invention, described softening agent is liquid paraffin.
As further scheme of the present invention, described antioxidant is N, N, and-DPD di p phenylenediamine, dibutyl two is dredged for carbaminate, the mixture of one or more in 2,6 di-t-butyl Yue base phenol.
As further scheme of the present invention, described adhesive is not solvent-laden emulsion.
A production method for self-adhesive elastic bandage made from rubber polymer, comprises the following steps:
(1) produce and prepare
A, get binder base material ready;
B, example is ready to adhesive formula material in mass ratio;
(2) preparation adhesive
A, by methods of polyisoprene emulsion water-bath heated and stirred;
B, add modifier, softening agent, antioxidant to stir successively;
C, with sieve, filter and to obtain adhesive;
(3) gluing: adhesive is evenly coated on binder substrate surface by the mode of spraying or blade coating;
(4) dry: utilize baking oven that the binder base material of first-class glue is dried.
As further scheme of the present invention, the temperature of described baking oven is 80-150 degree Celsius, and baking time is 2-5 minute.
The present invention compares with conventional art, has the following advantages:
Self-adhesive elastic bandage made from rubber polymer of the present invention, by adopting the emulsion of chemosynthesis, replaces the solvent-based adhesive that like product is used, and or not containing the organic solvent that has pollution even to poison to environment, does not burn, uses safe, easy to clean.And the antigen protein content in product is less than 1PPM, and content is extremely low, effectively avoids anaphylaxis.
The specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only the present invention's part embodiment, rather than whole embodiment.Embodiment based in the present invention, those of ordinary skills, not making the every other embodiment obtaining under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
First get binder base material ready, and take methods of polyisoprene emulsion 60kg, abietic resin 1 kg, terpene resin 1kg, Petropols 1kg, liquid paraffin 0.5kg, N, N,-DPD di p phenylenediamine 0.1kg, by methods of polyisoprene emulsion water-bath heated and stirred, add successively abietic resin, terpene resin, Petropols, liquid paraffin, N, N ,-DPD di p phenylenediamine also stirs, and with sieve, filters and obtains adhesive; Then by the mode of spraying or blade coating, adhesive is evenly coated on binder substrate surface; Finally, with baking oven, the binder base material of first-class glue dried to (during baking, the temperature of baking oven is 80-150 degree Celsius, and baking time is 2-5 minute), make a kind of self-adhesive elastic bandage made from rubber polymer of the present invention.
Embodiment 2
First get binder base material ready, and take methods of polyisoprene emulsion 70kg, abietic resin 5kg, terpene resin 5kg, polyacrylate 5kg, liquid paraffin 5kg, dibutyl two is dredged for carbaminate 5kg, by methods of polyisoprene emulsion water-bath heated and stirred, add successively abietic resin, terpene resin, polyacrylate, liquid paraffin, dibutyl two is dredged for carbaminate and stirs, and with sieve, filters and obtains adhesive; Then by the mode of spraying or blade coating, adhesive is evenly coated on binder substrate surface; Finally, with baking oven, the binder base material of first-class glue dried to (during baking, the temperature of baking oven is 80-150 degree Celsius, and baking time is 2-5 minute), make a kind of self-adhesive elastic bandage made from rubber polymer of the present invention.
Embodiment 3
First get binder base material ready, and take methods of polyisoprene emulsion 80kg, polyacrylate 30kg, liquid paraffin 10kg, 2,6 di-t-butyl Yue base phenol 10kg, by methods of polyisoprene emulsion water-bath heated and stirred, add polyacrylate successively, liquid paraffin, 2,6 di-t-butyl Yue base phenol also stir, and with sieve, filter and obtain adhesive; Then by the mode of spraying or blade coating, adhesive is evenly coated on binder substrate surface; Finally, with baking oven, the binder base material of first-class glue dried to (during baking, the temperature of baking oven is 80-150 degree Celsius, and baking time is 2-5 minute), make a kind of self-adhesive elastic bandage made from rubber polymer of the present invention.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and in the situation that not deviating from spirit of the present invention or basic feature, can realize the present invention with other concrete form.Therefore, no matter from which point, all should regard embodiment as exemplary, and be nonrestrictive, scope of the present invention is limited by claims rather than above-mentioned explanation, is therefore intended to include in the present invention dropping on the implication that is equal to important document of claim and all changes in scope.
In addition, be to be understood that, although this description is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of description is only for clarity sake, those skilled in the art should make description as a whole, and the technical scheme in each embodiment also can, through appropriately combined, form other embodiments that it will be appreciated by those skilled in the art that.
Claims (7)
1. a self-adhesive elastic bandage made from rubber polymer, take non-woven fabrics, cotton or compound cotton as binder base material; It is characterized in that, the positive and negative of described binder base material scribbles one deck adhesive, and the formulation by weight of this adhesive is as follows: 60～80 parts of methods of polyisoprene emulsion, modifier 3-30 part, softening agent 0.5-10 part, antioxidant 0.1-10 part.
2. a kind of self-adhesive elastic bandage made from rubber polymer according to claim 1, is characterized in that, described modifier is one or more the mixture in abietic resin, terpene resin, Petropols, polyacrylate.
3. a kind of self-adhesive elastic bandage made from rubber polymer according to claim 1, is characterized in that, described softening agent is liquid paraffin.
4. a kind of self-adhesive elastic bandage made from rubber polymer according to claim 1, is characterized in that, described antioxidant is N, N, and-DPD di p phenylenediamine, dibutyl two is dredged for carbaminate, the mixture of one or more in 2,6 di-t-butyl Yue base phenol.
5. a kind of self-adhesive elastic bandage made from rubber polymer according to claim 1, is characterized in that, described adhesive is not solvent-laden emulsion.
6. a production method for the self-adhesive elastic bandage made from rubber polymer as described in claim 1-5 any one, is characterized in that, comprises the following steps:
(1) produce and prepare
A, get binder base material ready;
B, example is ready to adhesive formula material in mass ratio;
(2) preparation adhesive
A, by methods of polyisoprene emulsion water-bath heated and stirred;
B, add modifier, softening agent, antioxidant to stir successively;
C, with sieve, filter and to obtain adhesive;
(3) gluing: adhesive is evenly coated on binder substrate surface by the mode of spraying or blade coating;
(4) dry: utilize baking oven that the binder base material of first-class glue is dried.
7. the production method of a kind of self-adhesive elastic bandage made from rubber polymer according to claim 6, is characterized in that, the temperature of described baking oven is 80-150 degree Celsius, and baking time is 2-5 minute.