CN103923546A - Matte black water-based plastic piece coating for automotive trim - Google Patents
Matte black water-based plastic piece coating for automotive trim Download PDFInfo
- Publication number
- CN103923546A CN103923546A CN201410191760.5A CN201410191760A CN103923546A CN 103923546 A CN103923546 A CN 103923546A CN 201410191760 A CN201410191760 A CN 201410191760A CN 103923546 A CN103923546 A CN 103923546A
- Authority
- CN
- China
- Prior art keywords
- parts
- automotive trim
- weight
- weight part
- abrasion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses matte black water-based plastic piece coating for an automotive trim. The matte black water-based plastic piece coating is composed of, by weight, 40-45 parts of SK6515 acrylic resin, 20-30 parts of deionized water, one to three parts of wetting dispersants, 0.1-0.3 part of flatting agents, 0.1-0.3 part of bentonite, 0.2-0.8 part of wax, three parts of carbon black, 1.2 parts of precipitated barium sulphate, 10 parts of aluminium triphosphate, three to six parts of wear resistant powder and two to four parts of extinction powder. A manufacturing method of the matte black water-based plastic piece coating for the automotive trim is further disclosed. The matte black water-based plastic piece coating for the automotive trim is excellent in performance and good in hand feeling, has the advantages of being strong in adhesive force, resistant to abrasion, resistant to sweat, resistant to cleaning agents, resistant to ageing and the like, and completely meets the environmental protection requirement of the automobile industry for the automotive trim.
Description
Technical field
The present invention relates to a kind of coating, specifically relate to dumb light Heisui River property plastic component coating for a kind of automotive trim; The invention still further relates to the preparation method of automotive trim with dumb light Heisui River property plastic component coating.
Background technology
Automotive upholstery is as operation bench, door-plate etc., and material major part is plastics, in order to reach attractive, decorative and to have good feel, generally wants a coating to reach this effect.Mostly the traditional coating that is applied to automotive upholstery is solvent type, the pollution that solvent based coating causes automobile cab is larger, automobile industry has issued the environmental requirement of automotive trim in the recent period, be that benzopyrene limit value is that < 1mg/kg, 18 kinds of PAH summation limit values are < 10mg/kg, under this mandatory requirement, solvent based coating is difficult to reach requirement, and therefore anxious must developing can meet the water-based plastic part coating that automotive trim plastic parts is used.
Summary of the invention
The technical problem to be solved in the present invention is to provide dumb light Heisui River property plastic component coating for a kind of automotive trim, automotive trim of the present invention has good feel with dumb light Heisui River property plastic component coating for after automotive trim plastic parts film, there is strong adhesion, wear-resisting, sweat proof liquid, resistance to clean-out system and the performance such as ageing-resistant, can meet the environmental requirement of automotive trim simultaneously.
For solving the problems of the technologies described above, dumb light Heisui River property plastic component coating for automotive trim of the present invention, by matrix resin, auxiliary agent, pigment and solvent composition, described matrix resin is SK6515 acrylic resin, described solvent is deionized water, described auxiliary agent is wetting dispersing agent, flow agent, wilkinite and wax, described pigment is carbon black, process white, aluminium triphosphate, abrasion-resistant powder and flatting silica, above-mentioned each ingredients weight parts is respectively: SK6515 acrylic resin is 40-45 part, deionized water is 20-30 part, wetting dispersing agent is 1-3 part, flow agent is 0.1-0.3 part, wilkinite is 0.1-0.3 part, wax is 0.2-0.8 part, carbon black is 3 parts, process white is 12 parts, aluminium triphosphate is 10 parts, abrasion-resistant powder is 3-6 part, flatting silica is 2-4 part.
Wetting dispersing agent in described auxiliary agent is that Borchi Gen0451, flow agent are that BYK-323, swelling king are that 140 wilkinites, wax are that FuoroAQ-60 is cured.
Carbon black in described pigment is that 865 carbon blacks, abrasion-resistant powder are that AN823 abrasion-resistant powder, flatting silica are OK-607 flatting silica.
Automotive trim of the present invention is superior with dumb light Heisui River property plastic component coating property, refers to table 3, has good feel, has strong adhesion, wear-resisting, sweat proof liquid, resistance to clean-out system and the feature such as ageing-resistant, meets the environmental requirement of automobile industry to automotive trim completely.
Automotive trim of the present invention is as follows by the method for making of dumb light Heisui River property plastic component coating: the SK6515 acrylic resin of first getting 30 weight parts, the wetting dispersing agent of the deionized water of 10-15 weight part and 1-3 weight part joins in stirred pot and stirs, then under the mixing speed of 400 revs/min, add successively the process white of 12 weight parts, the carbon black of 3 weight parts, the wilkinite of 0.1-0.3 weight part, the aluminium triphosphate of 10 weight parts, the abrasion-resistant powder of 3-6 weight part, churning time approximately 20 minutes, then above-mentioned mixed solution is ground with sand mill, mixed solution after grinding is placed in described stirred pot again, the SK6515 acrylic resin of 10-15 weight part and the washed with de-ionized water of 10-15 weight part for sand mill afterwards, scavenging solution after cleaning joins in described stirred pot again, finally in the situation that stirring to the flow agent that adds 0.1-0.3 weight part in described stirred pot, the flatting silica of the wax of 0.2-0.8 weight part and 2-4 weight part, after stirring, above-mentioned mixed solution filters and packages with 120 order filter cloths.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail, in these embodiments, all umbers are weight part.
Embodiment 1
First get the SK6515 acrylic resin of 30 parts, the wetting dispersing agent of the deionized water of 15 parts and 1 part joins in stirred pot and stirs, then under the mixing speed of 400 revs/min, add successively the process white of 12 parts, the carbon black of 3 parts, the wilkinite of 0.1 part, the aluminium triphosphate of 10 parts, the abrasion-resistant powder of 3 parts, churning time approximately 20 minutes, then above-mentioned mixed solution is ground with sand mill, mixed solution after grinding is placed in described stirred pot again, the SK6515 acrylic resin of 15 parts and the washed with de-ionized water of 10 parts for sand mill afterwards, scavenging solution after cleaning joins in described stirred pot again, finally in the situation that stirring to the flow agent that adds 0.1 part in described stirred pot, the flatting silica of the wax of 0.2 part and 2 parts, after stirring, above-mentioned mixed solution filters and packages with 120 order filter cloths.
Embodiment 2
First get the SK6515 acrylic resin of 40 parts, the wetting dispersing agent of the deionized water of 15 parts and 2 parts joins in stirred pot and stirs, then under the mixing speed of 400 revs/min, add successively the process white of 12 parts, the carbon black of 3 parts, the wilkinite of 0.2 part, the aluminium triphosphate of 10 parts, the abrasion-resistant powder of 4 parts, churning time approximately 20 minutes, then above-mentioned mixed solution is ground with sand mill, mixed solution after grinding is placed in described stirred pot again, the SK6515 acrylic resin of 5 parts and the washed with de-ionized water of 15 parts for sand mill afterwards, scavenging solution after cleaning joins in described stirred pot again, finally in the situation that stirring to the flow agent that adds 0.2 part in described stirred pot, the flatting silica of the wax of 0.5 part and 3 parts, after stirring, above-mentioned mixed solution filters and packages with 120 order filter cloths.
Embodiment 3
First get the SK6515 acrylic resin of 30 parts, the wetting dispersing agent of the deionized water of 10 parts and 3 parts joins in stirred pot and stirs, then under the mixing speed of 400 revs/min, add successively the process white of 12 parts, the carbon black of 3 parts, the wilkinite of 0.3 part, the aluminium triphosphate of 10 parts, the abrasion-resistant powder of 6 parts, churning time approximately 20 minutes, then above-mentioned mixed solution is ground with sand mill, mixed solution after grinding is placed in described stirred pot again, the SK6515 acrylic resin of 10 parts and the washed with de-ionized water of 20 parts for sand mill afterwards, scavenging solution after cleaning joins in described stirred pot again, finally in the situation that stirring to the flow agent that adds 0.3 part in described stirred pot, the flatting silica of the wax of 0.7 part and 4 parts, after stirring, above-mentioned mixed solution filters and packages with 120 order filter cloths.
In following table 1-table 3, table 1 is property plastic component system component formula in dumb light Heisui River for automotive trim of the present invention; Table 2 is according to the some projects detected result of the coating of table 1 formula preparation; Table 3 is the former paint of dumb light Heisui River property plastic component coating and the main performance index of paint film for automotive trim of the present invention.
Table 1: component formula of the present invention
Table 2: the some projects detected result of the various embodiments described above
Table 3: the performance index of coating of the present invention
Claims (4)
1. a dumb light Heisui River property plastic component coating for automotive trim, it is characterized in that: by matrix resin, auxiliary agent, pigment and solvent composition, described matrix resin is SK6515 acrylic resin, described solvent is deionized water, described auxiliary agent is wetting dispersing agent, flow agent, wilkinite and wax, described pigment is carbon black, process white, aluminium triphosphate, abrasion-resistant powder and flatting silica, above-mentioned each ingredients weight parts is respectively: SK6515 acrylic resin is 40-45 part, deionized water is 20-30 part, wetting dispersing agent is 1-3 part, flow agent is 0.1-0.3 part, wilkinite is 0.1-0.3 part, wax is 0.2-0.8 part, carbon black is 3 parts, process white is 12 parts, aluminium triphosphate is 10 parts, abrasion-resistant powder is 3-6 part, flatting silica is 2-4 part.
2. according to dumb light Heisui River property plastic component coating for automotive trim claimed in claim 1, it is characterized in that: the wetting dispersing agent in described auxiliary agent is that Borchi Gen 0451, flow agent are that BYK-323, swelling king are that 140 wilkinites, wax are that FuoroAQ-60 is cured.
3. according to dumb light Heisui River property plastic component coating for automotive trim claimed in claim 1, it is characterized in that: the carbon black in described pigment is that 865 carbon blacks, abrasion-resistant powder are that AN823 abrasion-resistant powder, flatting silica are OK-607 flatting silica.
4. prepare the method for automotive trim with dumb light Heisui River property plastic component coating for one kind, it is characterized in that: the SK6515 acrylic resin of first getting 30 weight parts, the wetting dispersing agent of the deionized water of 10-15 weight part and 1-3 weight part joins in stirred pot and stirs, then under the mixing speed of 400 revs/min, add successively the process white of 12 weight parts, the carbon black of 3 weight parts, the wilkinite of 0.1-0.3 weight part, the aluminium triphosphate of 10 weight parts, the abrasion-resistant powder of 3-6 weight part, churning time approximately 20 minutes, then above-mentioned mixed solution is ground with sand mill, mixed solution after grinding is placed in described stirred pot again, the SK6515 acrylic resin of 10-15 weight part and the washed with de-ionized water of 10-15 weight part for sand mill afterwards, scavenging solution after cleaning joins in described stirred pot again, finally in the situation that stirring to the flow agent that adds 0.1-0.3 weight part in described stirred pot, the flatting silica of the wax of 0.2-0.8 weight part and 2-4 weight part, after stirring, above-mentioned mixed solution filters and packages with 120 order filter cloths.