CN103922736B - 铌酸钾基v型ptc材料及其制备方法 - Google Patents
铌酸钾基v型ptc材料及其制备方法 Download PDFInfo
- Publication number
- CN103922736B CN103922736B CN201410110312.8A CN201410110312A CN103922736B CN 103922736 B CN103922736 B CN 103922736B CN 201410110312 A CN201410110312 A CN 201410110312A CN 103922736 B CN103922736 B CN 103922736B
- Authority
- CN
- China
- Prior art keywords
- temperature
- 1mol
- ptc
- sintering
- geo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
铌酸钾基V型PTC材料及其制备方法。本发明涉及一种在氮气氛下烧结的具有高电阻非线性系数的NTC‑PTC(V型PTC)陶瓷材料及其制备方法。本发明的V型PTC陶瓷的化学分子式为K(1‑x)MxNbO3,其中x=0.001~0.30,M=Ca、Ba、Sr中的至少一种;另掺1mol%~9mol%的Al2O3和1mol%~5mol%的GeO2。该材料采用传统的陶瓷制备工艺,在氮气中1000~1200℃烧结10~120min可获得V型PTC材料。该材料在转变温度Tb以上具有极好的PTC效应,升阻比最高达105,电阻非线性系数在20%/℃以上;在Tb以下,材料具有很大的NTC效应,在50℃的范围内,电阻可随温度下降4个数量级。
Description
技术领域
本发明涉及一种在氮气气氛下烧结的具有高电阻非线性系数的NTC-PTC(V型PTC)陶瓷材料的制备方法,属于电子陶瓷材料制备工艺技术领域。
背景技术
温度敏感型半导体陶瓷可分为正温度系数热敏电阻材料(PTCR)、负温度系数热敏电阻材料(NTC)和开关型温度敏感材料(CTR)三大类。传统的PTCR元件均为BaTiO3基陶瓷,广泛应用于定温加热、温度传感和补偿、线路限流保护以及过热保护等领域;NTC材料以过渡金属氧化物组成的尖晶石结构材料为代表,在温度补偿、传感等领域应用十分广泛,其产量每年以数千亿只计。V型PTC材料在转变温度前呈现较强的NTC效应,在转变温度以上表现为PTC效应,它集NTC和PTC效应于一身,其应用前景诱人,不仅可实现元器件的多功能化,还能使器件小型化。本发明旨在开发一种全新体系的V型PTC材料,使其既具有很高电阻非线性系数的PTC效应(非线性系数最高达到20%/℃以上),同时在转变温度以下还具有极好的NTC效应(在50℃范围内,电阻可下降3个数量级以上)。通常,BaTiO3基陶瓷PTCR元件在居里温度前也表现出一定的NTC效应,但其NTC效应比较弱,在200℃范围内,其电阻下降也只有3-7倍,达不到实用化的效果。本发明采用与BaTiO3同属钙钛矿型结构且与之有平行相变的铁电体KNbO3材料,添加适量Ba、Sr、Ca等为半导化剂,在氮气气氛下制备KNbO3半导陶瓷,获得V型PTCR材料。
发明内容
本发明的目的在于提供一种具有高的电阻非线性系数的NTC-PTC(V型PTC)的新材料体系。
一种新材料体系的V型热敏陶瓷(V-PTC)的制备方法,其特征具有以下的材料配比及制备工艺:
a)按化学分子式K(1-x)MxNbO3进行配料,其中x=0.001~0.30,M=Ca、Ba、Sr中的至少一种;另外加入1mol%~9mol%的Al2O3和1mol%~5mol%的GeO2烧结助剂。
b)本发明实施过程的初始原材料选自分析纯或试剂级的K2CO3、GeO2、Nb2O5、BaCO3、CaCO3、SrCO3、Al2O3或含有这些金属元素的其它无机盐微米级粉体。材料中所用的KNbO3 为传统的固相反应法制备,即按分子摩尔比 Nb2O5:K2CO3 = 1:1的比列称取上述两种原料的分析纯;以氧化锆球和酒精为介质,将上述的Nb2O5和K2CO3混合料在行星球磨机内球磨1~36小时,烘干后在700~950℃温度下固相反应2~4个小时,获得KNbO3粉体。
c)按照上述配方分子式的摩尔比例取含有各元素的氧化物或者无机盐,精确称量之后,以二氧化锆球和酒精为介质,将上述原料在行星磨上以150~800转/分的转速球磨2~12小时;将烘干后的粉末加2~15wt%的PVA(聚乙烯醇,浓度3~18wt%)造粒,以5~15MPa的压力压制Φ10×2.0mm的圆片;
d)将压制好的圆片于300~700℃下保温0.5~5小时排胶,冷却后将圆片在氮气保护气氛下进行烧结,烧结温度为1000~1200℃,并在该温度下保温10~120min,使其充分烧结和实现固相反应;烧结后的样品经表面打磨光滑以后,于超声波里冲洗5~60min,然后以Ag-Zn浆料涂敷使金属化,最终获得高电阻温度系数的V型热敏陶瓷样品。
本发明PTCR热敏陶瓷电阻材料的电性能可以实现以下参数要求:转变温度Tb:~20℃,最小电阻<104Ω·cm,PTC升阻比Rmax/Rmin>104,电阻温度系数α>20%,在-50℃~Tb温度范围内电阻下降>103(NTC效应)。
本发明的内容通过以上步骤和以下的实施例做更进一步的说明。以下实施例只是符合本发明技术内容的几个实例,并不说明本发明仅限于下述实施例所述的内容。
附图说明
图1、烧结温度为1130℃的KNS系列样品阻温特性曲线;
图2、KNS10样品在不同烧结温度下的阻温特性曲线;
图3a、KNB系列陶瓷材料的阻温特性曲线(低BaCO3含量,烧结温度1130℃);
图3b、KNB系列陶瓷材料的阻温特性曲线(高BaCO3含量,烧结温度1130℃);
图4、KNB07样品在不同烧结温度下的阻温特性曲线;
图5 KNC系列样品的阻温特性曲线;
图6 KNC07样品在不同烧结温度下的阻温特性曲线。
具体实施方式
实施例1
按照化学分子式K(1-x)SrxNbO3+1mol%Al2O3+1.5mol%GeO2的组成,x=0~0.15换算出各原料的质量,然后准确称量,称量质量如表1:
酒精中球磨(料:氧化锆球:酒精=1:2.5:1)以150~800转/分的转速球磨4小时,烘干后加7wt%的PVA(浓度为10wt%)造粒,以12MPa的压力压制成×2.0mm的圆片。将压制好的圆片于500℃保温2小时,冷却后将圆片在氮气气氛下再次进行烧结,烧结温度为1070-1130℃,并在该温度下保温30min烧结。烧结后的样品经表面打磨光滑以后,于超声波里冲洗10min,然后以Ag-Zn浆料涂敷使金属化。以2℃/min的升温速率加热陶瓷样品,测得其电阻-温度特性,其结果如表2和图1所示。
KNS10样品在1070-1130℃下烧结,其电性能如表3和图2所示。
实施例2
按照化学分子式K(1-x)BaxNbO3+1mol%Al2O3+1.5mol%GeO2的组成,x=0.001~0.25换算出各原料的质量,然后准确称量,称量质量如表4:
酒精中球磨(料:氧化锆球:酒精=1:2.5:1)以150~800转/分的转速球磨4小时,烘干后加7wt%的PVA(浓度为10wt%)造粒,以12MPa的压力压制成×2.0mm的圆片。将压制好的圆片于500℃保温2小时,冷却后将圆片在氮气气氛下再次进行烧结,烧结温度为1000-1200℃,并在该温度下保温30min烧结。烧结后的样品经表面打磨光滑以后,于超声波里冲洗10min,然后以Ag-Zn浆料涂敷使金属化。以2℃/min的升温速率加热陶瓷样品,测得其电阻-温度特性,其结果如表5和图3所示。
KNB系列样品的烧结温度范围较宽,可在1050-1150℃内烧结,以KNB07样品为例,在1070-1140℃内进行烧结,其性能如表6和图4所示。
实施例3
按照化学分子式K(1-x)CaxNbO3+1mol%Al2O3+1.5mol%GeO2的组成,x=0~0.15换算出各原料的质量,然后准确称量,称量质量如表7:
酒精中球磨(料:氧化锆球:酒精=1:2.5:1)以150~800转/分的转速球磨4小时,烘干后加7wt%的PVA(浓度为10wt%)造粒,以12MPa的压力压制成×2.0mm的圆片。将压制好的圆片于500℃保温2小时,冷却后将圆片在氮气气氛下再次进行烧结,烧结温度为1070-1130℃,并在该温度下保温30min烧结。烧结后的样品经表面打磨光滑以后,于超声波里冲洗10min,然后以Ag-Zn浆料涂敷使金属化。以2℃/min的升温速率加热陶瓷样品,测得其电阻-温度特性,其结果如表8和图5所示。
KNC07样品在1070-1130℃下烧结,其电性能如表9和图6所示。
。
Claims (1)
1.一种铌酸钾基V型PTC材料,其特征在于:该材料的化学分子式为K(1-x)MxNbO3,其中x=0.001~0.30,M=Ca、Ba、Sr中的至少一种,另外加入1mol%~9mol%的Al2O3和1mol%~5mol%的GeO2烧结助剂,具有以下的制备工艺步骤:
a.按化学分子式K(1-x)MxNbO3进行配料,其中x=0.001~0.30,M=Ca、Ba、Sr中的至少一种,另外加入1mol%~9mol%的Al2O3和1mol%~5mol%的GeO2烧结助剂;初始原材料选自分析纯或试剂级的K2CO3、GeO2、Nb2O5、BaCO3、CaCO3、SrCO3、Al2O3或含有这些金属元素的其它无机盐微米级粉体;材料中所用的KNbO3 为传统的固相反应法制备,即按分子摩尔比 Nb2O5:K2CO3 = 1:1的比列称取上述两种原料的分析纯;以氧化锆球和酒精为介质,将上述的Nb2O5和K2CO3混合料在行星球磨机内球磨1~36小时,烘干后在700~950℃温度下固相反应2~4个小时,获得KNbO3粉体;
b.按照上述配方分子式的摩尔比例取含有各元素的氧化物或者无机盐,精确称量之后,以二氧化锆球和酒精为介质,将上述原料在行星磨上以150~800转/分的转速球磨2~12小时;将烘干后的粉末加2~15wt%的聚乙烯醇(PVA),浓度为3~18wt%,造粒,以5~15MPa的压力压制Φ10×2.0mm的圆片;
c. 将压制好的圆片于300~700℃下保温0.5~5小时排胶,冷却后将圆片在氮气保护气氛下进行烧结,烧结温度为1000~1200℃,并在该温度下保温10~120min,使其充分烧结和实现固相反应;烧结后的样品经表面打磨光滑以后,于超声波里冲洗5~60min,然后以Ag-Zn浆料涂敷使金属化,最终获得V型热敏陶瓷样品。