CN103922647A - Ecological glue for insulated roofing construction and use thereof - Google Patents
Ecological glue for insulated roofing construction and use thereof Download PDFInfo
- Publication number
- CN103922647A CN103922647A CN201410138655.5A CN201410138655A CN103922647A CN 103922647 A CN103922647 A CN 103922647A CN 201410138655 A CN201410138655 A CN 201410138655A CN 103922647 A CN103922647 A CN 103922647A
- Authority
- CN
- China
- Prior art keywords
- powder
- carbon
- fineness
- water
- flour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses ecological glue for insulated roofing construction. The ecological glue is prepared from sticky rice, wheat meal and elm bark powder. The process comprises the following steps: firstly, crushing the sticky rice into powder, and then preparing according to the weight ratio of the sticky rice powder to the wheat meal to the elm bark powder being 50:40:10; adding water after preparing, wherein 100kg of water is added to each kg of mixed power; poaching and continuously stirring until 30 minutes after boiling, so as to form the glue. The ecological glue is reasonable in formula, convenient to manufacture, and good in using effect.
Description
Technical field
The present invention relates to a kind of heat insulation house surface construction ecomaterial.
Background technology
Roof heat insulation is the core of building construction insulation, and roof heat insulation technology, adopt at present loose fill type insulant to comprise expansion scoria both at home and abroad, pearlstone, blast furnace slags etc. comprise porous plastics class sheet material with tabular lagging material, cell concrete coverboard material, expansion scoria sheet material, pearlstone sheet material, certainly adopts above lagging material to carry out roof heat insulation construction and plays certain effect, but material resources is fewer, cost is higher.
Summary of the invention
The object of the present invention is to provide a kind of formula reasonable, the good heat insulation house surface of result of use ecological glue and uses thereof for construction.
Technical solution of the present invention is:
An ecological glue is used in heat insulation house surface construction, it is characterized in that: glutinous rice, wheat-flour, Cortex ulmi pumilae powder, consist of; First glutinous rice is ground into powder, then by sticky rice flour: wheat-flour: the weight ratio of Cortex ulmi pumilae powder=50 ︰ 40 ︰ 10 is configured, and adds water after configuration, and every 1kg mixing powder adds 100 kilograms, water, carries out poach, and constantly stirs, until boil agglutination latter 30 minutes.
A kind of heat insulation house surface construction is built the application in material with ecological glue at roofing, it is characterized in that: orthopaedics, xanthan gum and the water that is 15-25mm by carbon silicon calcium material and particle diameter is by carbon silicon calcium material: orthopaedics: xanthan gum: the weight ratio of water=36 ︰ 35 ︰ 13 ︰ 16 is configured, uniform stirring, then feed intake and build, and vibration compacting.
Described carbon silicon calcium material is comprised of Stalk silk, wooden carbon dust, cement flour, lime powder; Length≤the 4mm of Stalk silk, fineness is in 1mm; Wood carbon dust adopts wooden bamboo to be fired into wooden carbon, and wooden carbon is by pulverizing and sieving, fineness≤1mm; Earth powder adopts common loess, sand or clay, after drying or drying, mills and sieves, and fineness is micron order; Lime is by sieving, and fineness is micron order; After above-mentioned raw material disposal processing, by the weight ratio of Stalk Si Fen ︰ wood Tan Fen ︰ earth Fen ︰ lime powder=30 ︰ 10 ︰ 30 ︰ 30, carry out uniform stirring, form carbon silicon calcium material.
The present invention fills a prescription rationally, easily manufactured, and result of use is good.
Below in conjunction with embodiment, the invention will be further described.
Embodiment
An ecological glue is used in heat insulation house surface construction, it is characterized in that: glutinous rice, wheat-flour, Cortex ulmi pumilae powder, consist of; First glutinous rice is ground into powder, then by sticky rice flour: wheat-flour: the weight ratio of Cortex ulmi pumilae powder=50 ︰ 40 ︰ 10 is configured, and adds water after configuration, and every 1kg mixing powder adds 100 kilograms, water, carries out poach, and constantly stirs, until boil agglutination latter 30 minutes.
A kind of heat insulation house surface construction is built the application in material with ecological glue at roofing, it is characterized in that: orthopaedics, xanthan gum and the water that is 15-25mm by carbon silicon calcium material and particle diameter is by carbon silicon calcium material: orthopaedics: xanthan gum: the weight ratio of water=36 ︰ 35 ︰ 13 ︰ 16 is configured, uniform stirring, then feed intake and build, and vibration compacting.
Described carbon silicon calcium material is comprised of Stalk silk, wooden carbon dust, cement flour, lime powder; Length≤the 4mm of Stalk silk, fineness is in 1mm; Wood carbon dust adopts wooden bamboo to be fired into wooden carbon, and wooden carbon is by pulverizing and sieving, fineness≤1mm; Earth powder adopts common loess, sand or clay, after drying or drying, mills and sieves, and fineness is micron order; Lime is by sieving, and fineness is micron order; After above-mentioned raw material disposal processing, by the weight ratio of Stalk Si Fen ︰ wood Tan Fen ︰ earth Fen ︰ lime powder=30 ︰ 10 ︰ 30 ︰ 30, carry out uniform stirring, form carbon silicon calcium material.
Specifically, when cast-in-place ecological heat preservation roofing is built, according to the following step, carry out:
(1) carbon silicon calcium material is made;
(2) xanthan gum is made: xanthan gum is comprised of glutinous rice, wheat-flour, Cortex ulmi pumilae powder; First glutinous rice is ground into powder;
(3) bamboo reinforcement net is made: bamboo reinforcement net is made 5 years blue or green bamboos of life of material selection, is whittled into bamboo chip, and bamboo chip thickness is 4mm, and width is 10-15mm, adopts cross to wear weave, and mesh specification is 50-60mm;
(4) roofing template is installed: after construction work main body finishes, carry out the installation of roofing template;
(5) bamboo reinforcement net laying is established: bamboo reinforcement net laying is established employing and completely spread method, and lap-joint >=50mm places supporter on end template when bamboo reinforcement net laying is established, make bamboo reinforcement net in LIFT mid-way;
(6) build: build front be 15-25mm by carbon silicon calcium material and particle diameter orthopaedics, xanthan gum and water by carbon silicon calcium material: orthopaedics: xanthan gum: the weight ratio of water=36 ︰ 35 ︰ 13 ︰ 16 is configured, and uniform stirring, then feeds intake and build, and vibration compacting;
(7) maintenance: should maintain after roofing is built, maintenance period is more than 15 days, and coverture is set between defects liability period, should avoid rain evil, freeze injury, solarization to do harm to;
(8) form removal: when eco-concrete roofing is built the expired laggard row form removal of maintenance;
(9) paste aluminium tin pewter coiled material: adopt weld seam method and viscose type to paste aluminium tin pewter coiled material on the ecological heat preservation roofing body of building, plain during laying, not hollowing, sealing < 5mm.
Described aggregate is stone, building waste piece and cinder, and three's weight ratio is 2:2:1; The particle diameter of building waste is 15-20mm.
Claims (3)
1. an ecological glue is used in heat insulation house surface construction, it is characterized in that: glutinous rice, wheat-flour, Cortex ulmi pumilae powder, consist of; First glutinous rice is ground into powder, then by sticky rice flour: wheat-flour: the weight ratio of Cortex ulmi pumilae powder=50 ︰ 40 ︰ 10 is configured, and adds water after configuration, and every 1kg mixing powder adds 100 kilograms, water, carries out poach, and constantly stirs, until boil agglutination latter 30 minutes.
2. a heat insulation house surface construction claimed in claim 1 is built the application in material with ecological glue at roofing, it is characterized in that: orthopaedics, xanthan gum and the water that is 15-25mm by carbon silicon calcium material and particle diameter is by carbon silicon calcium material: orthopaedics: xanthan gum: the weight ratio of water=36 ︰ 35 ︰ 13 ︰ 16 is configured, uniform stirring, then feed intake and build, and vibration compacting.
3. heat insulation house surface construction according to claim 2 is built the application in material with ecological glue at roofing, it is characterized in that: described carbon silicon calcium material is comprised of Stalk silk, wooden carbon dust, cement flour, lime powder; Length≤the 4mm of Stalk silk, fineness is in 1mm; Wood carbon dust adopts wooden bamboo to be fired into wooden carbon, and wooden carbon is by pulverizing and sieving, fineness≤1mm; Earth powder adopts common loess, sand or clay, after drying or drying, mills and sieves, and fineness is micron order; Lime is by sieving, and fineness is micron order; After above-mentioned raw material disposal processing, by the weight ratio of Stalk Si Fen ︰ wood Tan Fen ︰ earth Fen ︰ lime powder=30 ︰ 10 ︰ 30 ︰ 30, carry out uniform stirring, form carbon silicon calcium material.